Alloy 617 and Alloy 230 are solid-solution strengthened nickel based superalloys, which have been considered two of the most promising structural materials for the Very-High-Temperature Reactor (VHTR). In order to have a better understanding of the degradation process of the materials in the VHTR, long-term aging experiments have been carried out to investigate the dynamic process of microstructure evolution at 900 and 1000°C for Alloy 617 and Alloy 230. The microstructural evolution process in different aging periods (up to 3000 hours) was analyzed by Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM) and Electron Backscatter Diffraction (EBSD). A diffusion-controlled precipitation and coarsening of carbide particles (mainly M23C6 and M6C) for both alloys was observed. The corresponding characteristics of the precipitates, i.e. type, size and coherence, were analyzed. The coarsening rate of the intergranular precipitates in Alloy 617 was found to be much faster compared to Alloy 230’s. The inhomogeneous precipitation process in the transverse plane of Alloy 617 was observed, which may be attributed to the alignment of the inclusion particles induced by the hot rolling. Hardness and tensile tests were carried out to investigate the aging impacts on materials’ strength. Both alloys obtained increased hardness and strength during early stages of aging and softened after elongated time. The results of mechanical tests were in a good agreement with the microstructure evolution process.
The influence of two different fluoride-based activator salts (NH4F and AlF3) was studied for diffusion aluminide coatings obtained via pack cementation on a Ni-based superalloy (René 108DS). The resistance to oxidation and hot corrosion was assessed as a function of the concentration of activator salts used during the synthesis process by means of pack cementation. Two different concentrations were selected for activator salts (respecting the equimolarity of fluoride in the synthesis) and the obtained diffusion coatings were compared in terms of morphology, thickness and composition, as well as in terms of microstructural evolution after high temperature exposure. Isothermal oxidation tests were conducted at 1050 °C in air for 100 h in a tubular furnace. The oxidation kinetics were evaluated by measuring the weight variation with exposure time. The microstructural evolution induced by the high temperature exposure was investigated by SEM microscopy, EDS analysis and X-ray diffraction. Results showed that the coatings obtained with AlF3 activator salt are thicker than those obtained using NH4F as a consequence of different growth mechanism during pack-cementation. Despite this evidence, it was found that the NH4F coatings show a better oxidation resistance, both in terms of total mass gain and of quality of the microstructure of the thermally grown oxide. On the other hand, coatings produced with high concentration of AlF3 exhibited a better resistance in hot corrosion conditions, showing negligible mass variations after 200 h of high temperature exposure to aggressive NaCl and Na2SO4 salts.
Abstract
HR-120 alloy is an alloy designed for thermal processing. It possesses excellent strength, oxidizing hot corrosion resistance, good carburization resistance, and oxidation resistance through 1093 deg C (2000 deg F). This datasheet provides information on composition, physical properties, hardness, elasticity, and tensile properties as well as creep. It also includes information on high temperature performance as well as forming, heat treating, machining, and joining. Filing Code: Ni-561. Producer or source: Rolled Alloys.
The oxidation behavior and microstructural evolution of the nanostructure of Fe-Cr-Al oxide dispersion strengthened (ODS) alloys prepared by spark plasma sintering were investigated by high-temperature oxidation experiments in air at 1200 °C for 100 h. The formation of Al2O3 scale was observed by X-ray diffraction (XRD) and scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDS) line scans. The oxidation rate of Fe-Cr-Al ODS alloys is lower than that of conventional Fe-Cr-Al alloys, and the oxide layer formed on the Fe-Cr-Al alloy appeared loose and cracked, whereas the oxide layer formed on the Fe-Cr-Al ODS alloys was adherent and flat. This is due to the high density of dispersed nano-oxides hindering the diffusion of Al element and the formation of vacancies caused by them. In addition, the nano-oxides could also adhere to the oxide layer. Besides, the microstructure of the Fe-Cr-Al ODS alloy had excellent stability during high-temperature oxidation.
Diffusion Aluminide Coatings for Hot Corrosion and Oxidation Protection of Nickel-Based Superalloys: Effect of Fluoride-Based Activator Salts