Effects of accelerating voltage and specimen thickness on the spatial resolution of transmission electron backscatter diffraction in Cu

2017 ◽  
Vol 177 ◽  
pp. 43-52 ◽  
Author(s):  
Jhih-Wun Shih ◽  
Ka-Wei Kuo ◽  
Jui-Chao Kuo ◽  
Tsung-Yuan Kuo
2009 ◽  
Vol 24 (3) ◽  
pp. 647-651 ◽  
Author(s):  
M. Rester ◽  
C. Motz ◽  
R. Pippan

Electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) analyses of small indentations in copper single crystals exhibit only slight changes of the crystal orientation in the surroundings of the imprints. Far-reaching dislocations might be the reason for these small misorientation changes. Using EBSD and TEM technique, this work makes an attempt to visualize the far-propagating dislocations by introducing a twin boundary in the vicinity of small indentations. Because dislocations piled up at the twin boundary produce a misorientation gradient, the otherwise far-propagating dislocations can be detected.


MRS Advances ◽  
2016 ◽  
Vol 1 (43) ◽  
pp. 2947-2952
Author(s):  
L. Chen ◽  
Z.-H. Lu ◽  
T.-M. Lu ◽  
I. Bhat ◽  
S.B. Zhang ◽  
...  

ABSTRACTEpitaxial Ge films are useful as a substrate for high-efficiency solar cell applications. It is possible to grow epitaxial Ge films on low cost, cube textured Ni(001) sheets using CaF2(001) as a buffer layer. Transmission electron microscopy (TEM) analysis indicates that the CaF2(001) lattice has a 45o in-plane rotation relative to the Ni(001) lattice. The in-plane epitaxy relationships are CaF2[110]//Ni[100] and CaF2[$\bar 1$10]//Ni[010]. Energy dispersive spectroscopy (EDS) shows a sharp interface between Ge/CaF2 as well as between CaF2/Ni. Electron backscatter diffraction (EBSD) shows that the Ge(001) film has a large grain size (∼50 μm) with small angle grain boundaries (< 8o). The epitaxial Ge thin film has the potential to be used as a substrate to grow high quality III-V and II-VI semiconductors for optoelectronic applications.


2000 ◽  
Vol 6 (S2) ◽  
pp. 940-941
Author(s):  
A.J. Schwartz ◽  
M. Kumar ◽  
P.J. Bedrossian ◽  
W.E. King

Grain boundary network engineering is an emerging field that encompasses the concept that modifications to conventional thermomechanical processing can result in improved properties through the disruption of the random grain boundary network. Various researchers have reported a correlation between the grain boundary character distribution (defined as the fractions of “special” and “random” grain boundaries) and dramatic improvements in properties such as corrosion and stress corrosion cracking, creep, etc. While much early work in the field emphasized property improvements, the opportunity now exists to elucidate the underlying materials science of grain boundary network engineering. Recent investigations at LLNL have coupled automated electron backscatter diffraction (EBSD) with transmission electron microscopy (TEM)5 and atomic force microscopy (AFM) to elucidate these fundamental mechanisms.An example of the coupling of TEM and EBSD is given in Figures 1-3. The EBSD image in Figure 1 reveals “segmentation” of boundaries from special to random and random to special and low angle grain boundaries in some grains, but not others, resulting from the 15% compression of an Inconel 600 polycrystal.


2015 ◽  
Vol 21 (S3) ◽  
pp. 1671-1672
Author(s):  
Eliot Estrine ◽  
Nicholas Seaton ◽  
Prabesh Dulal ◽  
Bethanie Stadler

2015 ◽  
Vol 21 (6) ◽  
pp. 1387-1397 ◽  
Author(s):  
Leo T.H. de Jeer ◽  
Diego Ribas Gomes ◽  
Jorrit E. Nijholt ◽  
Rik van Bremen ◽  
Václav Ocelík ◽  
...  

AbstractTransmission electron backscatter diffraction (t-EBSD) was used to investigate the effect of dealloying on the microstructure of 140-nm thin gold foils. Statistical and local comparisons of the microstructure between the nonetched and nanoporous gold foils were made. Analyses of crystallographic texture, misorientation distribution, and grain structure clearly prove that during the dealloying manufacturing process of nanoporous materials the crystallographic texture is enhanced significantly with a clear decrease of internal strain, whereas maintaining the grain structure.


Minerals ◽  
2021 ◽  
Vol 11 (9) ◽  
pp. 1018
Author(s):  
Sejin Jung ◽  
Takafumi Yamamoto ◽  
Jun-ichi Ando ◽  
Haemyeong Jung

Amphibole peridotite samples from Åheim, Norway, were analyzed to understand the deformation mechanism and microstructural evolution of olivine and amphibole through the Scandian Orogeny and subsequent exhumation process. Three Åheim amphibole peridotite samples were selected for detailed microstructural analysis. The Åheim amphibole peridotites exhibit porphyroclastic texture, abundant subgrain boundaries in olivine, and the evidence of localized shear deformation in the tremolite-rich layer. Two different types of olivine lattice preferred orientations (LPOs) were observed: B- and A-type LPOs. Electron backscatter diffraction (EBSD) mapping and transmission electron microscopy (TEM) observations revealed that most subgrain boundaries in olivine consist of dislocations with a (001)[100] slip system. The subgrain boundaries in olivine may have resulted from the deformation of olivine with moderate water content. In addition, TEM observations using a thickness-fringe method showed that the free dislocations of olivine with the (010)[100] slip system were dominant in the peridotites. Our data suggest that the subgrain boundaries and free dislocations in olivine represent a product of later-stage deformation associated with the exhumation process. EBSD mapping of the tremolite-rich layer revealed intracrystalline plasticity in amphibole, which can be interpreted as the activation of the (100)[001] slip system.


2015 ◽  
Vol 60 (2) ◽  
pp. 1423-1426 ◽  
Author(s):  
J. Park ◽  
K.H. Jung ◽  
G.A. Lee ◽  
M. Kawasaki ◽  
B. Ahn

Abstract In this study, a continuously casted ZK60A magnesium alloy (Mg-Zn-Zr) was extruded in two different extrusion ratios, 6:1 and 10:1. The evolution of precipitates was investigated on the two extruded materials and compared with that of as-casted material. The microstructural analysis was performed by electron backscatter diffraction and transmission electron microscopy, and the compositional information was obtained using energy-dispersive X-ray spectroscopy. Several distinct morphologies of precipitates were observed, such as dot, rod, and disk shaped. The formation mechanisms of those precipitates were discussed with respect to the heat and strain during the extrusion process.