scholarly journals Effect of loading rate on tensile and fracture behavior of AA2050-T84 alloy at high temperature

2021 ◽  
Vol 2070 (1) ◽  
pp. 012163
Author(s):  
Nagaraj Ekabote ◽  
Krishnaraja G Kodancha
Keyword(s):  
High Temperature ◽  
Strain Rate ◽  
Tensile Tests ◽  
Rate Variation ◽  
Strain Rates ◽  
Rate Dependency ◽  
Commercial Aircraft ◽  
Fracture Failure ◽  
Load Rate ◽  
Increased Susceptibility

Abstract AA2050-T84 alloy is commonly used in the fabrication of modern commercial aircraft wing parts. Load and temperature variation during aircraft take-off, flight, and landing at different environmental conditions is substantial. Mechanical properties variation of AA2050-T84 alloy at sub-zero and room temperatures are significant and well documented in the literature. In the present work, at a high temperature of 200°C, the effect of load rate variation on tensile and fracture properties of AA2050-T84 alloy are experimentally and numerically studied. The load rates represented in strain rates were applied at 0.01, 0.1, and 1s−1. Experimental tensile tests exhibited the positive strain rate dependency on the yield and ultimate strength of the alloy. 2D numerical elastic-plastic fracture analysis was carried out using Abaqus 6.14. Similar to tensile results, the fracture parameters dependency on strain rates was witnessed. Overall, higher strain rate causes the increased susceptibility of fracture failure with the increase in yield stress of the material.

scholarly journals Strain rate sensitivity of the aluminium-magnesium-scandium alloy - Scalmalloy®

2021 ◽  
Vol 250 ◽  
pp. 05014
Author(s):  
Puneeth Jakkula ◽  
Georg Ganzenmüller ◽  
Florian Gutmann ◽  
Stefan Hiermaier
Keyword(s):  
Strain Rate ◽  
Strain Rate Sensitivity ◽  
Testing Machine ◽  
Rate Sensitivity ◽  
Tensile Tests ◽  
Image Correlation ◽  
Strain Rates ◽  
Rate Dependency ◽  
Strain Rate Dependency ◽  
Scandium Alloy

This work investigates the strain rate sensitivity of the aluminiummagnesium-scandium alloy Scalmalloy, which is used extensively for additive manufacturing of lightweight structures. This high strength aluminium alloy combines very good weldability, machinability and mechanical strength: it can be heat-treated to reach nominal ultimate tensile strengths in excess of 500 MPa. We report tensile tests at strain rates ranging from 10−3 /s to 103 /s at room temperature. It is well known that Al-Mg alloys exhibit a negative strain rate dependency in combination with serrated flow caused by the Portevin-Le Chatelier effect, which describes the interaction of Mg solutes with dislocation propagations. In contrast, in Al-Sc alloys, the flow stress increases with increasing strain rate and displays positive strain rate dependency. Additionally, the presence of Sc in the form of Al3-Sc provides a fine-grained microstructure which allows higher tensile and fatigue strength. This research shows how these combined effects interact in the case of Scalmalloy, which contains both Mg and Sc. Tests are performed at quasi-static, intermediate and high strain rates with a servohydraulic testing machine and a Split-Hopkinson tension bar. Local specimen strain was performed using 2D Digital Image Correlation.

scholarly journals New Approach In The Properties Evaluation Of Ultrafine-Grained OFHC Copper

2015 ◽  
Vol 60 (2) ◽  
pp. 605-614 ◽  
Author(s):  
T. Kvačkaj ◽  
A. Kováčová ◽  
J. Bidulská ◽  
R. Bidulský ◽  
R. Kočičko
Keyword(s):  
Mechanical Properties ◽  
Strain Rate ◽  
Tensile Tests ◽  
Coarse Grained ◽  
Wear Behaviour ◽  
Ofhc Copper ◽  
Strain Rates ◽  
Ultrafine Grained ◽  
Reduction Of Area ◽  
Pin On Disk

AbstractIn this study, static, dynamic and tribological properties of ultrafine-grained (UFG) oxygen-free high thermal conductivity (OFHC) copper were investigated in detail. In order to evaluate the mechanical behaviour at different strain rates, OFHC copper was tested using two devices resulting in static and dynamic regimes. Moreover, the copper was subjected to two different processing methods, which made possible to study the influence of structure. The study of strain rate and microstructure was focused on progress in the mechanical properties after tensile tests. It was found that the strain rate is an important parameter affecting mechanical properties of copper. The ultimate tensile strength increased with the strain rate increasing and this effect was more visible at high strain rates$({\dot \varepsilon} \sim 10^2 \;{\rm{s}}^{ - 1} )$. However, the reduction of area had a different progress depending on microstructural features of materials (coarse-grained vs. ultrafine-grained structure) and introduced strain rate conditions during plastic deformation (static vs. dynamic regime). The wear behaviour of copper was investigated through pin-on-disk tests. The wear tracks examination showed that the delamination and the mild oxidational wears are the main wear mechanisms.

High Temperature Deformation Mechanism Maps of NiAl

2004 ◽  
Vol 449-452 ◽  
pp. 57-60
Author(s):  
I.G. Lee ◽  
A.K. Ghosh
Keyword(s):  
High Temperature ◽  
Strain Rate ◽  
Deformation Mechanism ◽  
Calculation Method ◽  
Deformation Behavior ◽  
Tensile Tests ◽  
High Temperature Deformation ◽  
Temperature Deformation ◽  
Grain Sizes ◽  
Temperature Strain

In order to analyze high temperature deformation behavior of NiAl alloys, deformation maps were constructed for stoichiometric NiAl materials with grain sizes of 4 and 200 µm. Relevant constitute equations and calculation method will be described in this paper. These maps are particularly useful in identifying the location of testing domains, such as creep and tensile tests, in relation to the stress-temperature-strain rate domains experienced by NiAl.

The Effects of Physical Ageing and of Prior Immersion on the Esc Behaviour of Polycarbonate in Ethanol

1993 ◽  
Vol 305 ◽  
Author(s):  
J. C. Arnold ◽  
A. R. Eccott
Keyword(s):  
Strain Rate ◽  
Immersion Time ◽  
Constant Strain Rate ◽  
Tensile Tests ◽  
Strain Rates ◽  
Physical Ageing ◽  
Diffusion Effects ◽  
Craze Initiation ◽  
Comparison Of Tests

AbstractThe effects of physical ageing and prior immersion time on the ESC behaviour of polycarbonate in ethanol were studied. Constant strain rate tensile tests were performed at a range of strain rates for samples with ageing times varying from 100 hours to 3000 hours and for prior immersion times of between 1 hour and 500 hours. Comparison of tests performed in ethanol and in air gave a good indication of the point of craze initiation. The results showed that there was a reduction in strain to crazing as the strain rate decreased, apart from with the lowest strain rate used. A longer prior immersion time also promoted craze formation. Both of these results are attributable to diffusion effects. Physical ageing had little effect on the ESC behaviour, due to the large amounts of deformation encountered in this system.

scholarly journals Influence of strain rate and heat treatments on tensile and creep properties of Zn-0.15Cu-0.07Ti alloys

DYNA ◽  
2016 ◽  
Vol 83 (195) ◽  
pp. 77-83 ◽  
Author(s):  
María José Quintana Hernández ◽  
José Ovidio García ◽  
Roberto González Ojeda ◽  
José Ignacio Verdeja
Keyword(s):  
Strain Rate ◽  
Room Temperature ◽  
Rolling Direction ◽  
Tensile Tests ◽  
Strain Rates ◽  
Creep Tests ◽  
Design Problems ◽  
Creep Properties ◽  
Heat Treated ◽  
Zn Alloys

The use of Cu and Ti in Zn alloys improves mechanical properties as solid solution and dispersoid particles (grain refiners) may harden the material and reduce creep deformation. This is one of the main design problems for parts made with Zn alloys, even at room temperature. In this work the mechanical behavior of a Zn-Cu-Ti low alloy is presented using tensile tests at different strain rates, as well as creep tests at different loads to obtain the value of the strain rate coefficient m in samples parallel and perpendicular to the rolling direction of the Zn strip. The microstructure of the alloy in its raw state, as well as heat treated at 250°C, is also analyzed, as the banded structure produced by rolling influences the strengthening mechanisms that can be achieved through the treatment parameters.

scholarly journals Experimental investigations of the human oesophagus: anisotropic properties of the muscular layer in large deformation

2021 ◽  
Author(s):  
Ciara Durcan ◽  
Mokarram Hossain ◽  
Gregory Chagnon ◽  
Djordje Peric ◽  
Lara Bsiesy ◽  
...  
Keyword(s):  
Strain Rate ◽  
Ex Vivo ◽  
Longitudinal Direction ◽  
Tensile Tests ◽  
Endoscopic Biopsy ◽  
Circumferential Direction ◽  
Experimental Investigations ◽  
Uniaxial Tensile ◽  
Rate Dependency ◽  
Muscular Layer

Technological advancements in the field of robotics have led to endoscopic biopsy devices able to extract diseased tissue from between the layers of the gastrointestinal tract. Despite this, the layer-dependent properties of these tissues have yet to be mechanically characterised using human tissue. In this study, the ex vivo mechanical properties of the passive muscularis propia layer of the human oesophagus were extensively investigated. For this, a series of uniaxial tensile tests were conducted. The results displayed hyperelastic behaviour, while the differences between loading the tissue in both the longitudinal and circumferential directions showcased its anisotropy. The anisotropy of the muscular layer was present at different strain rates, with the longitudinal direction being consistently stiffer than the circumferential one. The circumferential direction was found to have little strain-rate dependency, while the longitudinal direction results suggest pronounced strain-rate-dependent behaviour. The repeated trials showed larger variation in terms of stress for a given strain in the longitudinal direction compared to the circumferential direction. The possible causes of variation between trials are discussed, and the experimental findings are linked to the histological analysis which was carried out via various staining methods. Finally, the direction-dependent experimental data was simulated using an anisotropic, hyperelastic model.

Tensile Stress-Strain Curves Modeling of Four Kinds of Solders with Temperature and Rate Dependence

2005 ◽  
Vol 297-300 ◽  
pp. 905-911 ◽  
Author(s):  
Xu Chen ◽  
Li Zhang ◽  
Masao Sakane ◽  
Haruo Nose
Keyword(s):  
Tensile Stress ◽  
Constitutive Model ◽  
Strain Rate ◽  
Constant Strain Rate ◽  
Tensile Tests ◽  
Strain Rate Range ◽  
Rate Dependence ◽  
Strain Rates ◽  
Stress Strain ◽  
Rate Range

A series of tensile tests at constant strain rate were conducted on tin-lead based solders with different Sn content under wide ranges of temperatures and strain rates. It was shown that the stress-strain relationships had strong temperature- and strain rate- dependence. The parameters of Anand model for four solders were determined. The four solders were 60Sn-40Pb, 40Sn-60Pb, 10Sn-90Pb and 5Sn-95Pb. Anand constitutive model was employed to simulate the stress-strain behaviors of the solders for the temperature range from 313K to 398K and the strain rate range from 0.001%sP -1 P to 2%sP -1 P. The results showed that Anand model can adequately predict the rate- and temperature- related constitutive behaviors at all test temperatures and strain rates.

Strain Rate Effect on Shear Behavior of Open-Graded Aggregates

2017 ◽  
Vol 2655 (1) ◽  
pp. 64-70 ◽  
Author(s):  
Thomas Gebrenegus ◽  
Jennifer E. Nicks ◽  
Michael T. Adams
Keyword(s):  
Strain Rate ◽  
Axial Strain ◽  
Shear Behavior ◽  
Strain Rate Effect ◽  
Rate Effect ◽  
Strength Parameter ◽  
Strain Rates ◽  
Rate Dependency ◽  
Confining Stress ◽  
Dilation Angle

Despite their wide application as construction materials in various earthworks built by state and local transportation agencies, the role of physical and mechanical factors in the strength and deformation behavior of crushed, manufactured open-graded aggregates (OGAs) is not well studied. In this investigation, the strain rate dependency of strength–deformation behaviors of two commonly employed crushed aggregates with small (12.7 mm) and large (38.1 mm) sizes is investigated. A 150-mm diameter triaxial testing device was used to conduct a drained compression test at five strain rates, ranging from 0.000083%/s to 0.0083%/s. To evaluate the significance of confining stress and density on the effect of strain rates, the shear tests were conducted at 34 kPa and 207 kPa effective confining stress levels, with the samples compacted at loose (30%) and dense (95%) relative densities. The peak friction angle, maximum dilation angle, secant modulus, and axial strain at which the aggregates started to dilate were determined to evaluate the strain rate effect on the shear behavior of OGAs. The results demonstrate that within the imposed quasistatic strain rate ranges, only the dilation angle showed an increasing trend with the increase in strain rate, whereas other extracted strength parameters were less sensitive to strain rate for both OGAs tested. Hence, the selection of strain rates according to ASTM specifications is appropriate for conducting strength parameter tests, used by practitioners for the design of geotechnical structures, on OGAs under quasistatic conditions.

Effect of High Temperature Caliber Rolling on Microstructure and Room Temperature Tensile Properties of Mg-3Al-1Zn (AZ31) Alloy

2013 ◽  
Vol 209 ◽  
pp. 6-9 ◽  
Author(s):  
Rajendra Doiphode ◽  
S.V.S. Narayana Murty ◽  
Nityanand Prabhu ◽  
Bhagwati Prasad Kashyap
Keyword(s):  
Tensile Strength ◽  
High Temperature ◽  
Yield Strength ◽  
Strain Rate ◽  
Tensile Properties ◽  
Room Temperature ◽  
Tensile Tests ◽  
Az31 Alloy ◽  
Rolling Temperature ◽  
Grain Sizes

Mg-3Al-1Zn (AZ31) alloy was caliber rolled at 250, 300, 350, 400 and 450 °C. The effects of caliber rolling temperature on the microstructure and tensile properties were investigated. The room temperature tensile tests were carried out to failure at a strain rate of 1 x 10-4s-1. The nature of stress-strain curves obtained was found to vary with the temperature employed in caliber rolling. The yield strength and tensile strength followed a sinusoidal behaviour with increasing caliber rolling temperature but no such trend was noted in ductility. These variations in tensile properties were explained by the varying grain sizes obtained as a function of caliber rolling temperature.

Stress-Strain Equations for Some Near-Eutectic Tin-Lead Solders

1991 ◽  
Vol 113 (4) ◽  
pp. 475-484 ◽  
Author(s):  
K. P. Jen ◽  
J. N. Majerus
Keyword(s):  
Strain Rate ◽  
Printed Circuit Boards ◽  
Volume Fraction ◽  
Total Error ◽  
Tensile Tests ◽  
Elastic Behavior ◽  
Plastic Behavior ◽  
Strain Rates ◽  
Stress Strain ◽  
Engineering Strain

This paper presents the evaluation of the stress-strain behavior, as a function of strain-rate, for three tin-lead solders at room temperature. This behavior is critically needed for reliability analysis of printed circuit boards (PCB) since handbooks list minimal mechanical properties for the eutectic solder used in PCBs. Furthermore, most handbook data are for stable eutectic microstructure whereas PCB solder has a metastable microstructure. All three materials were purchased as “eutectics.” However, chemical analysis, volume fraction determination, and microhardness tests show some major variations between the three materials. Two of the materials have a eutectic composition, and one does not. The true stress-strain equations of one eutectic and the one noneutectic material are determined from compressive tests at engineering strain-rates between 0.0002/s and 0.2/s. The second eutectic material is evaluated using tensile tests with strain-rates between 0.00017/s and 0.042/s. The materials appear to exhibit linear elastic behavior only at extremely small strains, i.e., less than 0.0005. However, this “elastic” behavior showed considerable variation, and depended upon the strain rate. In both tension and compression the eutectic alloy exhibits nonlinear plastic behavior, i.e., strain-softening followed by strain-hardening, which depends upon the strain rate. A quadratic equation σy = σy(ε˚/ε˚0) + A(ε˚/ε˚0)ε + B(ε˚/ε˚0)ε2 fit to the data gives correlation coefficients R2 > 0.91. The coefficients σy(ε˚/ε˚0), A(ε˚/ε˚0), B(ε˚/ε˚0) are fitted functions of the normalized engineering strain rate ε˚/ε˚0. Replicated experiments are used at each strain-rate so that a measure of the statistical variation could be estimated. Measures of error associated with the regression analysis are also obtained so that an estimate of the total error in the stress-strain relations can be made.

Sign in / Sign up

Export Citation Format

Share Document