Low Velocity and Compression-After-Impact Response of Pin-Reinforced Sandwich Composites

1999 ◽  
Author(s):  
Uday K. Vaidya ◽  
Mohan V. Kamath ◽  
Mahesh V. Hosur ◽  
Anwarul Haque ◽  
Shaik Jeelani
Keyword(s):  
Impact Testing ◽  
Low Velocity Impact ◽  
Sandwich Composites ◽  
Low Velocity ◽  
Static Compression ◽  
Velocity Impact ◽  
Transverse Stiffness ◽  
Impact Studies ◽  
Compression After Impact ◽  
The Impact

Abstract In the current work, sandwich composite structures with innovative constructions referred to as Z-pins, or truss core pins are investigated, in conjunction with traditional honeycomb and foam core sandwich constructions, such that they exhibit enhanced transverse stiffness, high damage resistance and furthermore, damage tolerance to impact. While the investigations pertaining to low velocity impact have appeared recently in Vaidya et al. 1999, the current paper deals with compression-after-impact studies conducted to evaluate the residual properties of sandwich composites “with” and “without” reinforced foam cores. The resulting sandwich composites have been investigated for their low velocity (< 5 m/sec) impact loading response using instrumented impact testing at energy levels ranging from 5 J to 50 J impact energy. The transverse stiffness of the cores and their composites has also been evaluated through static compression studies. Compression-after-impact studies were then performed on the sandwich composites with traditional and pin-reinforcement cores. Supporting vibration studies have been conducted to assess the changes in stiffness of the samples as a result of the impact damage. The focus of this paper is on the compression-after-impact (CAI) response and vibration studies with accompanying discussion pertaining to the low velocity impact.

scholarly journals Ultrasonic Analysis of Damage in CFRP Resulting from Static Indentation and Low Velocity Impact

1993 ◽  
Vol 2 (3) ◽  
pp. 096369359300200
Author(s):  
H. Kaczmarek
Keyword(s):  
Impact Testing ◽  
Low Velocity Impact ◽  
Ultrasonic Tomography ◽  
Transverse Impact ◽  
Low Velocity ◽  
Velocity Impact ◽  
Testing Procedures ◽  
Damage Initiation ◽  
Static Indentation ◽  
The Impact

In order to reduce hidden damage caused in CFRP by low velocity transverse impact, testing procedures must be established by understanding the impact phenomena and the roles of various parameters on damage initiation and growth. Hence, composite plates were stressed and an original method, “ultrasonic tomography,” was applied to detect delaminations on the interfaces. The results show the similarity of the damage growth resulting from static indentation and low velocity impact.

Impact Damage and Strength Reduction Behavior of Honeycomb Sandwich Structure Subjected to Low Velocity Impact

2006 ◽  
Vol 306-308 ◽  
pp. 279-284
Author(s):  
Ki Weon Kang ◽  
Jung Kyu Kim ◽  
Heung Seob Kim
Keyword(s):  
Sandwich Structure ◽  
Impact Damage ◽  
Testing Machine ◽  
Strength Reduction ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Reduction Behavior ◽  
Velocity Impact ◽  
The Impact

The goals of the paper are to identify the impact damage and strength reduction behavior of sandwich structure, composed of carbon/epoxy laminates skin and Nomex core with two kinds of thickness (10 and 20mm). For these, low velocity impact tests were conducted using the instrumented impact-testing machine and damages are inspected by SAM. And then, subsequent static tests are conducted under flexural loading to identify the strength reduction behavior of the impacted sandwich structures. The impact damages are mainly delamination in carbon/epoxy skin and their behavior is mostly independent of core thickness. Also, their energy absorbing behavior is identified through calculating the energy absorbed by impact damage. Finally, the strength reduction behavior is evaluated through Caprino’s model, which was proposed on the unidirectional laminates.

scholarly journals The low-velocity impact and compression after impact (CAI) behavior of foam core sandwich panels with shape memory alloy hybrid face-sheets

2019 ◽  
Vol 26 (1) ◽  
pp. 517-530 ◽  
Author(s):  
Ye Wu ◽  
Yun Wan
Keyword(s):  
Shape Memory Alloy ◽  
Shape Memory ◽  
Sandwich Panels ◽  
Image Correlation ◽  
Low Velocity Impact ◽  
Foam Core ◽  
Low Velocity ◽  
Velocity Impact ◽  
Compression After Impact ◽  
The Impact

AbstractDue to the properties of shape memory effect and super-elasticity, shape memory alloy (SMA) is added into glass fiber reinforced polymer (GFRP) face-sheets of foam core sandwich panels to improve the impact resistence performance by many researchers. This paper tries to discuss the failure mechanism of sandwich panels with GF/ epoxy face-sheets embedded with SMA wires and conventional 304 SS wire nets under low-velocity impact and compression after impact (CAI) tests. The histories of contact force, absorbed energy and deflection during the impact process are obtained by experiment. Besides, the failure modes of sandwich panels with different ply modes are compared by visual inspection and scanning electron microscopy (SEM). CAI tests are conducted with the help of digital image correlation (DIC) technology. Based on the results, the sandwich panels embedded with SMA wires can absorb more impact energy, and show relatively excellent CAI performance. This is because the SMA wires can absorb and transmit the energy to the outer region of GFRP face-sheet due to the super-elasticity-behavior. The failure process and mechanism of the CAI test is also discussed.

Investigation of the Effects of Core Thickness on Low Velocity Impact Behaviors of Aluminum Honeycomb Composites

2021 ◽  
Author(s):  
Kasım Karataş ◽  
Okan Özdemir
Keyword(s):  
Sheet Material ◽  
Energy Levels ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Core Material ◽  
Low Velocity ◽  
Velocity Impact ◽  
Impact Tests ◽  
Aluminum Honeycomb ◽  
The Impact

Honeycomb structures are used where the weight to strength ratio is important. They are also preferred to absorb the energy from the blows received. In this study, low velocity impact behavior of aluminum honeycomb composites with different core thicknesses were investigated. Aluminum honeycombs used in this study are AL3003 honeycombs of 10 mm and 15 mm thicknesses. Glass fiber reinforced epoxy sheets with a thickness of 2 mm were used as the surface sheet material. Composite plates were produced by vacuum infusion method. The upper and lower face plates were cut in dimensions of 100x100 mm. The cut plates were attached to the core material with adhesive and a sandwich structure was formed. After bonding, low velocity impact tests were performed on these test samples at 40J, 100J and 160J energy levels using the composite CEAST Fractovis Plus impact testing machine. According to the results obtained from the impact tests, at higher energy levels, 15 mm thick composites have 10-15% higher energy absorption capacity than 10 mm.

Study on the Low-Velocity Impact Behavior of CFRP with Nanoclay-Filled Epoxy Matrix

2008 ◽  
Vol 47-50 ◽  
pp. 1205-1208 ◽  
Author(s):  
Iqbal Kosar ◽  
Khan Shafi Ullah ◽  
Jang Kyo Kim ◽  
Arshad Munir
Keyword(s):  
Impact Damage ◽  
Low Velocity Impact ◽  
Impact Behavior ◽  
Low Velocity ◽  
Damage Resistance ◽  
Velocity Impact ◽  
Compression After Impact ◽  
The Impact ◽  
Carbon Fiber Epoxy ◽  
Insight Into

The influence of nanoclay on the impact damage resistance of carbon fiber-epoxy (CFRP) composites has been investigated using the low-velocity impact and compression after impact tests. The load-energy vs time relations were analyzed to gain insight into the damage behaviors of the materials. Compression-after-impact (CAI) test was performed to measure the residual compressive strength. The CFRPs containing organoclay brought about a significant improvement in impact damage resistance and damage tolerance. The composites containing organoclay exhibited an enhanced energy absorption capability with less damage areas and higher CAI strengths compared to those made from neat epoxy. A 3wt% phr was shown to be an optimal content with the highest damage resistance.

Experimental and numerical behaviors of GFRP laminates under low velocity impact

2020 ◽  
Vol 54 (21) ◽  
pp. 2999-3007
Author(s):  
Hüseyin E Yalkın ◽  
Ramazan Karakuzu ◽  
Tuba Alpyıldız
Keyword(s):  
Contact Force ◽  
Impact Energy ◽  
Damage Mechanics ◽  
Matrix Material ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Velocity Impact ◽  
Wide Range ◽  
The Impact

The aim of the study is to investigate the behavior of laminated composites under low velocity impact both experimentally and numerically. With this aim, the effects of wide range impact energy values between 10 J and 60 J were evaluated experimentally and numerically for the laminate of [±45/(0/90)2]S oriented unidirectional E-glass as reinforcing material and epoxy resin for matrix material. Different impactor velocities were used to maintain the impact energy values and experimental impact tests were generated with drop weight impact testing machine at room temperature. Numerical simulations were performed using LS-DYNA finite element analysis software with a continuum damage mechanics-based material model MAT058. Contact force between impactor and laminate, and transverse deflection at the center of laminate results were obtained as a function of time and used to plot contact force–time curves, contact force–deflection curves and absorbed energy-impact energy curves. Also, delamination area was examined. Finally, numerical results were compared with experimental results and a good correlation between them was observed.

Failure mechanism of Ω-shape 3D orthogonal woven composite component under transverse low-velocity impact and subsequent axial compression load

2021 ◽  
pp. 105678952110365
Author(s):  
Zhongxiang Pan ◽  
Mingling Wang ◽  
Zhiping Ying ◽  
Xiaoying Cheng ◽  
Zhenyu Wu
Keyword(s):  
Failure Mechanism ◽  
Damage Zone ◽  
High Stress ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Complex Deformation ◽  
Velocity Impact ◽  
Compression After Impact ◽  
Impact Side ◽  
The Impact

Failure mechanism of complex profile component is always different from that of conventional plate counterpart due to the coupling effect of material and structure. In this work, the low-velocity impact (LVI) and compression after impact (CAI) behaviors of Ω-shape hybrid carbon/Kevlar 3 D orthogonal woven (3DOW) composite made for vehicle B-pillar were comprehensively studied by mechanical tests and mesoscale finite element (FE) analysis at component level, high-speed infrared (IR) thermal imaging, acoustic emission (AE) detection, and microscopic damage morphology characterization. It is found that a through-thickness stress concentration ring leads to high stress state and damage zone penetrating from the impact side to non-impact side along the ring path instead of at the lowest impactor position. The slope effect can not only help the stress conduction downward, but also inhibit the damage propagation from the impact side to the slope. Impact-induced cracks are concentrated around the R corners and extended along the axial direction of the specimen, forming the strip-shaped damage concentration zone along the upper eave of the slope. The Progressive Top-Down Crushing (PTDC) mode of compression after impact is due to the complex deformation process of each yarn such as squeezing, folding and eversion in the crushing process from the top of specimen. And the Middle Indentation Fracture (MIF) mode is the result of bending instability and abrupt fracture. This work presents a reference significance for the further development of composite strengthening components in vehicle bodywork.

scholarly journals Fabrication and low-velocity impact response of pyramidal lattice stitched foam sandwich composites

2020 ◽  
Vol 27 (1) ◽  
pp. 245-257
Author(s):  
Jiale Jia ◽  
Shi Yan
Keyword(s):  
Numerical Simulation ◽  
Failure Modes ◽  
Absorption Capacity ◽  
Low Velocity Impact ◽  
Sandwich Composite ◽  
Foam Core ◽  
Sandwich Composites ◽  
Low Velocity ◽  
Velocity Impact ◽  
The Impact

AbstractIn this study, the foam sandwich panels were manufactured by integrating top facesheet and bottom facesheet with pyramidal lattice stitched core to overcome the weak interface between the core and skins of the sandwich structures. Low-velocity impact test and numerical simulation were conducted to reveal the failure mechanisms and energy absorption capacity at sandwich composite with foam core, different strut stitched foam core under different impact energy. The experimental results show showed that the strut core can improve the impact resistance of the specimen, and which is closely related to the diameter of the strut core. Compared with foam sandwich structure, pyramidal lattice stitched foam sandwich composites have comparable specific energy absorptions. The failure modes were also analyzed which is: fiber breakage, delamination, foam deformation and strut core breakage. The research presented here confirms that numerical simulation show good agreement with the experiment.

scholarly journals Impact and Post Impact Behavior of Hybrid Composites

2018 ◽  
Vol 11 (4) ◽  
pp. 46-52
Author(s):  
Aidel Kadum Jassim Al-shamary
Keyword(s):  
Impact Energy ◽  
Hybrid Composites ◽  
Energy Levels ◽  
Testing Machine ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Impact Behavior ◽  
Low Velocity ◽  
Velocity Impact ◽  
The Impact

In this study, the effect of low velocity impact  response of Kevlar/carbon hybrid composite has been investigated. Then the impacted specimens were subjected to compression and buckling tests at room temperature experimentally. The height, width and thickness of the specimens are 150, 100 and 2.1 mm, respectively. Impact tests have been performed under different impact energy levels by using low velocity impact testing machine. Compression and buckling tests were conducted by Shimadzu testing machine. According to obtained results, the damage increases by increasing the impact energy level in the subjected specimens to impact test.  Compression strength value is higher about 3  times than buckling strength value.

Sign in / Sign up