Fabrication and performance of highly textured electrodeposited ZnO back reflector for nc-Si solar cells

2008 ◽  
Vol 1123 ◽  
Author(s):  
Dinesh Attygalle ◽  
Qi Hua Fan ◽  
Shibin Zhang ◽  
William B. Ingler ◽  
Xianbo Liao ◽  
...  
Keyword(s):  
Solar Cells ◽  
Short Circuit ◽  
Cost Effective ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Solar Cell Efficiency ◽  
Cell Efficiency ◽  
Back Reflectors ◽  
Sputter Deposited ◽  
And Performance

AbstractTo improve the cell efficiency of thin film solar cells textured back reflectors (BR) are widely used. This is particularly important in a-Si:H based solar cells due to low absorption coefficient at longer wavelengths. In this work we present a cost effective way to fabricate uniformly textured ZnO by using electrochemical methods. Further it was observed that Quantum Efficiency (QE) of shorter wavelengths also improved for highly textured ZnO BR. Together this resulted in more than 2mA increment in short circuit current density (Jsc) and 19% relative improvement in solar cell efficiency over sputter deposited BR. A possible mechanism responsible for the improved blue QE is also discussed.

scholarly journals CdTe-Based Thin Film Solar Cells: Past, Present and Future

Energies ◽  
2021 ◽  
Vol 14 (6) ◽  
pp. 1684
Author(s):  
Alessandro Romeo ◽  
Elisa Artegiani
Keyword(s):  
Thin Film ◽  
Solar Cells ◽  
Solar Cell ◽  
Short Circuit ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Open Circuit ◽  
Early Years ◽  
Solar Cell Efficiency ◽  
Cell Efficiency

CdTe is a very robust and chemically stable material and for this reason its related solar cell thin film photovoltaic technology is now the only thin film technology in the first 10 top producers in the world. CdTe has an optimum band gap for the Schockley-Queisser limit and could deliver very high efficiencies as single junction device of more than 32%, with an open circuit voltage of 1 V and a short circuit current density exceeding 30 mA/cm2. CdTe solar cells were introduced at the beginning of the 70s and they have been studied and implemented particularly in the last 30 years. The strong improvement in efficiency in the last 5 years was obtained by a new redesign of the CdTe solar cell device reaching a single solar cell efficiency of 22.1% and a module efficiency of 19%. In this paper we describe the fabrication process following the history of the solar cell as it was developed in the early years up to the latest development and changes. Moreover the paper also presents future possible alternative absorbers and discusses the only apparently controversial environmental impacts of this fantastic technology.

Simulation of Symmetrically Doped Silicon Nanowire Solar Cells

2011 ◽  
Vol 1322 ◽  
Author(s):  
Felix Voigt ◽  
Thomas Stelzner ◽  
Silke H. Christiansen
Keyword(s):  
Solar Cells ◽  
Short Circuit ◽  
Silicon Nanowire ◽  
Short Circuit Current ◽  
Cylindrical Symmetry ◽  
Short Circuit Current Density ◽  
Open Circuit ◽  
Back Surface ◽  
Cell Efficiency ◽  
P Type

ABSTRACTSilicon nanowire solar cells were simulated using the Silvaco TCAD software kit. For optimization of speed the simulations were performed in cylinder coordinates with cylindrical symmetry. Symmetric doping was assumed with a dopant density of 1018 cm-3 in the p-type core and inside the n-type shell. In the implementation a cathode contact was wrapped around the semiconductor nanorod and an anode was assumed at the bottom of the rod. Optimization of cell efficiency was performed with regard to the rod radius and the rod length. In both optimization processes clear maxima in efficiency were visible, resulting in an optimal radius of 66 nm with the pn junction at 43.5 nm and an optimal rod length of about 48 μm. The maximum of efficiency with respect to the rod radius is due to a decrease of short-circuit current density (Jsc) and an increase of open-circuit voltage (Uoc) with radius, while the maximum with respect to the rod length is explained by the combination of an increase of Jsc and a decrease of Uoc. Fill factors stay rather constant at values between 0.6 and 0.8. Further, the influence of a back surface field (BSF) layer was surveyed in simulations. Positioning the BSF next to the cathode contact considerably improved cell efficiency. In addition, simulations with a cathode contact on top of the nanowire structure were undertaken. No severe deterioration of cell performance with increasing radius was observed so far in this configuration. Hence, nanorods with much larger radii can be used for solar cells using this contact scheme. In comparison to simulations with wrapped cathode contacts, Jsc and Uoc and therefore efficiency is considerably improved.

The N, N-Dimethylformamide Annealing for Enhanced Performance of Perovskite Solar Cells Fabricated in Ambient Air

NANO ◽  
2018 ◽  
Vol 13 (09) ◽  
pp. 1850102
Author(s):  
Xiude Yang ◽  
Debei Liu ◽  
Ping Li ◽  
Bo Wu ◽  
Haishen Huang ◽  
...  
Keyword(s):  
Solar Cells ◽  
Short Circuit ◽  
Perovskite Solar Cells ◽  
Solution Process ◽  
Cost Effective ◽  
Short Circuit Current ◽  
Ambient Air ◽  
Short Circuit Current Density ◽  
Coating Method ◽  
One Step

By adopting N, N-Dimethylformamide (DMF) atmosphere annealing at room temperature, planar perovskite solar cells with a p-i-n structure of ITO/PEDOT:PSS/Perovskite/PCBM/C[Formula: see text]/Al are fabricated by a simple one-step solution process in ambient air with humidity around 50%, and the influence of DMF atmosphere on perovskite solar cells (PSCs) is systematically investigated. Compared to the reference device without DMF reaction, the perovskite films treated by modest DMF annealing show a better distribution and a higher densification, and thus the power conversion efficiency (PCE), short circuit current density ([Formula: see text] and fill factor (FF) are increased by about 17%, 8% and 6%, respectively. This work displays the importance of solvent annealing for perovskite film prepared by the one-step spin-coating method, and possibly provides a simple and cost-effective way to efficiently fabricate PSCs in ambient air.

Study the Effect of Doping Ratios the n-type Silicon SWCNTm / PLA on Solar Cell Efficiency

2021 ◽  
Vol 19 (9) ◽  
pp. 01-05
Author(s):  
Maan Abd-Alameer Salih ◽  
Q.S. Kareem ◽  
Mohammed Hadi Shinen
Keyword(s):  
Short Circuit ◽  
Short Circuit Current ◽  
Energy Conversion Efficiency ◽  
Short Circuit Current Density ◽  
Open Circuit ◽  
Silicon Substrates ◽  
Solar Cell Efficiency ◽  
Cell Efficiency ◽  
Power Point Presentation ◽  
Power Point

In this work, SWCNTm / PLA was employed as a fundamental compound, and nanofilms of SWCNTm / PLA were coated onto n-kind silicon substrates. The spin coated technique was used to determine the thickness in (SWCNTm / PLA). Various thicknesses in (SWCNTm / PLA) (162, 100, and 82) n.m are procured via at vary spin spades (1500, 3000, and 4500) r.pm.' light (100 mw/cm2) and dark (J-V) requirements were used to produce the current denisity-volt features. The characteristics of the photovoltaic models namely, open circuit voltage (Voc), short–circuit current density (Jsc), foll ratio (FF), and energy conversion efficiency (ɳ) were calculated. The better thickness of (SWCNTm / PLA) films for highest (ɳ), (Jsc) and greatest power point presentation' is 100 n m, according to our findings.

scholarly journals Control of Porphyrin Dye Aggregation Using Bis(4-pyridyl)Alkanes in Dye Sensitized Solar Cells

2019 ◽  
pp. 63
Author(s):  
B. Baptayev ◽  
A. Rysbekova ◽  
D. Kalpakov ◽  
A. Aukenova ◽  
D. Mustazheb ◽  
...  
Keyword(s):  
Solar Cells ◽  
Short Circuit ◽  
Photovoltaic Performance ◽  
Dye Sensitized Solar Cells ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Cell Efficiency ◽  
Dye Sensitized ◽  
Dye Aggregation ◽  
Sensitized Solar Cells

The aggregation of sensitizer molecules on the surface of photoanode is a serious issue that can affect the photovoltaic performance of dye-sensitized solar cells. Prevention of dye agglomeration, therefore, is critical. Traditional methods of aggregation control are either synthetically challenging or technologically difficult and expensive. In this article, the use of bis(4-pyridyl)alkanes to control porphyrin dye aggregation is presented. Three bis(4-pyridyl)alkanes – bis(4-pyridyl)butane L4, bis(4-pyridyl)octane L8 and bis(4-pyridyl)decane L10 were synthesized. These bis(4-pyridyl)alkane ligands are axially attached to the metallic center of synthesized porphyrin dye P. The complexes was obtained by mixing the solutions of dye P and each ligand (L) in 2:1 ratio 1 h before the soaking step. As a result three cells were prepared: P-L4, P-L8 and P-L10. The performance of these cells were compared with a reference cell which was prepared from porphyrin dye P only. IPCE analysis demonstrated the highest dye load in P-L4 cell which was ascribed to lowered dye aggregation. Photovoltaic analysis showed improved short circuit current density due to suppressed dye aggregation caused by the complexation of the porphyrin dye P with the linker L4. As a result the overall cell efficiency increased to 42% demonstrating the successful utilization of the (4-pyridyl)alkane linker complexes with porphyrin dye.

Determining the exciton diffusion length of copper phthalocyanine in operating planar-heterojunction organic solar cells

2020 ◽  
Vol 89 (3) ◽  
pp. 30201 ◽  
Author(s):  
Xi Guan ◽  
Shiyu Wang ◽  
Wenxing Liu ◽  
Dashan Qin ◽  
Dayan Ban
Keyword(s):  
Solar Cells ◽  
Organic Solar Cells ◽  
Diffusion Length ◽  
Copper Phthalocyanine ◽  
Short Circuit ◽  
Thick Layer ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Exciton Diffusion ◽  
Exciton Diffusion Length

Organic solar cells based on planar copper phthalocyanine (CuPc)/C60 heterojunction have been characterized, in which a 2 nm-thick layer of bathocuproine (BCP) is inserted into the CuPc layer. The thin layer of BCP allows hole current to tunnel it through but blocks the exciton diffusion, thereby altering the steady-state exciton profile in the CuPc zone (zone 1) sandwiched between BCP and C60. The short-circuit current density (JSC) of device is limited by the hole-exciton scattering effect at the BCP/CuPc (zone 1) interface. Based on the variation of JSC with the width of zone 1, the exciton diffusion length of CuPc is deduced to be 12.5–15 nm. The current research provides an easy and helpful method to determine the exciton diffusion lengths of organic electron donors.

scholarly journals The Influence of the Thickness of Compact TiO2 Electron Transport Layer on the Performance of Planar CH3NH3PbI3 Perovskite Solar Cells

Materials ◽  
2021 ◽  
Vol 14 (12) ◽  
pp. 3295
Author(s):  
Andrzej Sławek ◽  
Zbigniew Starowicz ◽  
Marek Lipiński
Keyword(s):  
Solar Cells ◽  
Electron Transport ◽  
Short Circuit ◽  
Photovoltaic Performance ◽  
Perovskite Solar Cells ◽  
Precursor Solution ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Transport Layer ◽  
Electron Transport Layer

In recent years, lead halide perovskites have attracted considerable attention from the scientific community due to their exceptional properties and fast-growing enhancement for solar energy harvesting efficiency. One of the fundamental aspects of the architecture of perovskite-based solar cells (PSCs) is the electron transport layer (ETL), which also acts as a barrier for holes. In this work, the influence of compact TiO2 ETL on the performance of planar heterojunction solar cells based on CH3NH3PbI3 perovskite was investigated. ETLs were deposited on fluorine-doped tin oxide (FTO) substrates from a titanium diisopropoxide bis(acetylacetonate) precursor solution using the spin-coating method with changing precursor concentration and centrifugation speed. It was found that the thickness and continuity of ETLs, investigated between 0 and 124 nm, strongly affect the photovoltaic performance of PSCs, in particular short-circuit current density (JSC). Optical and topographic properties of the compact TiO2 layers were investigated as well.

scholarly journals Ultrathin Cu(In,Ga)Se2 Solar Cells with Ag/AlOx Passivating Back Reflector

Energies ◽  
2021 ◽  
Vol 14 (14) ◽  
pp. 4268
Author(s):  
Jessica de Wild ◽  
Gizem Birant ◽  
Guy Brammertz ◽  
Marc Meuris ◽  
Jef Poortmans ◽  
...  
Keyword(s):  
Surface Roughness ◽  
Solar Cells ◽  
Short Circuit ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Open Circuit ◽  
Electron Microscopic ◽  
Current Increase ◽  
Time Resolved ◽  
Cigs Solar Cells

Ultrathin Cu(In,Ga)Se2 (CIGS) absorber layers of 550 nm were grown on Ag/AlOx stacks. The addition of the stack resulted in solar cells with improved fill factor, open circuit voltage and short circuit current density. The efficiency was increased from 7% to almost 12%. Photoluminescence (PL) and time resolved PL were improved, which was attributed to the passivating properties of AlOx. A current increase of almost 2 mA/cm2 was measured, due to increased light scattering and surface roughness. With time of flight—secondary ion mass spectroscopy, the elemental profiles were measured. It was found that the Ag is incorporated through the whole CIGS layer. Secondary electron microscopic images of the Mo back revealed residuals of the Ag/AlOx stack, which was confirmed by energy dispersive X-ray spectroscopy measurements. It is assumed to induce the increased surface roughness and scattering properties. At the front, large stains are visible for the cells with the Ag/AlOx back contact. An ammonia sulfide etching step was therefore applied on the bare absorber improving the efficiency further to 11.7%. It shows the potential of utilizing an Ag/AlOx stack at the back to improve both electrical and optical properties of ultrathin CIGS solar cells.

scholarly journals Effects of Different Doping Ratio of Cu Doped CdS on QDSCs Performance

2015 ◽  
Vol 2015 ◽  
pp. 1-4
Author(s):  
Xiaojun Zhu ◽  
Xiaoping Zou ◽  
Hongquan Zhou
Keyword(s):  
Solar Cells ◽  
Quantum Dot ◽  
Short Circuit ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Open Circuit ◽  
Photoelectric Conversion Efficiency ◽  
Photoelectric Conversion ◽  
Sensitized Solar Cells ◽  
Doping Ratio

We use the successive ionic layer adsorption and reaction (SILAR) method for the preparation of quantum dot sensitized solar cells, to improve the performance of solar cells by doping quantum dots. We tested the UV-Vis absorption spectrum of undoped CdS QDSCs and Cu doped CdS QDSCs with different doping ratios. The doping ratios of copper were 1 : 100, 1 : 500, and 1 : 1000, respectively. The experimental results show that, under the same SILAR cycle number, Cu doped CdS quantum dot sensitized solar cells have higher open circuit voltage, short circuit current density photoelectric conversion efficiency than undoped CdS quantum dots sensitized solar cells. Refinement of Cu doping ratio are 1 : 10, 1 : 100, 1 : 200, 1 : 500, and 1 : 1000. When the proportion of Cu and CdS is 1 : 10, all the parameters of the QDSCs reach the minimum value, and, with the decrease of the proportion, the short circuit current density, open circuit voltage, and the photoelectric conversion efficiency are all increased. When proportion is 1 : 500, all parameters reach the maximum values. While with further reduction of the doping ratio of Cu, the parameters of QDSCs have a decline tendency. The results showed that, in a certain range, the lower the doping ratio of Cu, the better the performance of quantum dot sensitized solar cell.

scholarly journals SCAPS Simulation on P3HT:Graphene Nanocomposites Based Bulk-Heterojunction Organic Solar Cells

2019 ◽  
Vol 9 (1) ◽  
pp. 28
Author(s):  
Nur Shakina Mohd Shariff ◽  
Puteri Sarah Mohamad Saad ◽  
Mohamad Rusop Mahmood
Keyword(s):  
Solar Cells ◽  
Organic Solar Cells ◽  
Fill Factor ◽  
Bulk Heterojunction ◽  
Short Circuit ◽  
Short Circuit Current ◽  
Short Circuit Current Density ◽  
Open Circuit ◽  
Simulation Software ◽  
Capacitance Voltage

There has been an increasing interest towards organic solar cells after the discovery of conjugated polymer and bulk-heterojunction concept. Eventhough organic solar cells are less expensive than inorganic solar cells but the power conversion energy is still considered low. The main objective of this research is to investigate the effect of the P3HT’s thickness and concentration towards the efficiency of the P3HT:Graphene solar cells. A simulation software that is specialize for photovoltaic called SCAPS is used in this research to simulate the effect on the solar cells. The solar cell’s structure will be drawn inside the simulation and the parameters for each layers is inserted. The result such as the open circuit voltage (Voc), short circuit current density (Jsc), fill factor (FF), efficiency (η), capacitance-voltage (C-V) and capacitance-frequency (C-f) characteristic will be calculated by the software and all the results will be put into one graph.

Sign in / Sign up

Export Citation Format

Share Document