Pulsed Laser Deposition of Collagen Thin Films

1995 ◽  
Vol 414 ◽  
Author(s):  
J. A. Conklin ◽  
C. M. Cotell ◽  
T. W. Barnett ◽  
D. C. Hansen
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Helical Structure ◽  
Film Deposition ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
Deposition Parameter ◽  
Si Substrates ◽  
Vapor Quenching

AbstractThin films of collagen were prepared by pulsed laser deposition (PLD) at room temperature on Si substrates using a KrF laser (248 nm) over a fluence range from 0.2–1.5 Jcm-2. The effects on film composition and morphology of ambient gas (Ar, Ar/H2O vapor), quenching atmosphere (Ar, Ar/H2O vapor), and fluence were examined. Fourier transform infrared spectroscopy (FT- IR) demonstrated that, independent of deposition parameter, the PLD films contained the characteristic Amide I and II functionalities of the collagen target and indicated that the secondary structure was altered by the PLD process. The surface morphology of the films was a function of the laser fluence and the gas environment during either film deposition or quenching at the end of deposition. Preliminary gel electrophoresis examination of deposited films suggested the collagen had not maintained the triple helical structure of the native collagen. X-Ray diffraction (XRD) indicated that all of the films, deposited under any conditions, were predominantly amorphous.

ZrC Thin Films Grown by Pulsed Laser Deposition

2003 ◽  
Vol 780 ◽  
Author(s):  
V. Craciun ◽  
D. Craciun ◽  
J. M. Howard ◽  
R. K. Singh
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Photoelectron Spectroscopy ◽  
Pulsed Laser ◽  
Surface Region ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
X Ray ◽  
Si Substrates ◽  
Crystalline Films

AbstractZrC thin films were grown on Si substrates by the pulsed laser deposition (PLD) technique. X- ray photoelectron spectroscopy, x-ray diffraction and reflectivity, variable angle spectroscopic ellipsometry, and four point probe measurements were used to investigate the composition, density, thickness, surface morphology, optical and electrical properties of the grown structures. It has been found that crystalline films could be grown only by using fluences above 6 J/cm2 and substrate temperatures in excess of 500 °C. For a fluence of 10 J/cm2 and a substrate temperature of 700 °C, highly (100)-textured ZrC films exhibiting a cubic structure (a=0.469 nm) and a density of 6.7 g/cm3 were deposited. The use of a low-pressure atmosphere of C2H2 had a beneficial effect on crystallinity and stoichiometry of the films. All films contained high levels of oxygen contamination, especially in the surface region, because of the rather reactive nature of Zr atoms.

Microstructural and Electrical Characterization of Barium Strontium Titanatebased Solid Solution Thin Films Deposited on Ceramic Substrates by Pulsed Laser Deposition

2002 ◽  
Vol 720 ◽  
Author(s):  
Costas G. Fountzoulas ◽  
Daniel M. Potrepka ◽  
Steven C. Tidrow
Keyword(s):  
Thin Films ◽  
Dielectric Constant ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Electrical Characterization ◽  
Field Variable ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
Ceramic Substrates ◽  
Nominal Thickness

AbstractFerroelectrics are multicomponent materials with a wealth of interesting and useful properties, such as piezoelectricity. The dielectric constant of the BSTO ferroelectrics can be changed by applying an electric field. Variable dielectric constant results in a change in phase velocity in the device allowing it to be tuned in real time for a particular application. The microstructure of the film influences the electronic properties which in turn influences the performance of the film. Ba0.6Sr0.4Ti1-y(A 3+, B5+)yO3 thin films, of nominal thickness of 0.65 μm, were synthesized initially at substrate temperatures of 400°C, and subsequently annealed to 750°C, on LaAlO3 (100) substrates, previously coated with LaSrCoO conductive buffer layer, using the pulsed laser deposition technique. The microstructural and physical characteristics of the postannealed thin films have been studied using x-ray diffraction, scanning electron microscopy, and nano indentation and are reported. Results of capacitance measurements are used to obtain dielectric constant and tunability in the paraelectric (T>Tc) regime.

Study of Raman Spectrum of Fe Doped CeO2 Thin Films Grown by Pulsed Laser Deposition

2010 ◽  
Vol 123-125 ◽  
pp. 375-378 ◽  
Author(s):  
Ram Prakash ◽  
Shalendra Kumar ◽  
Chan Gyu Lee ◽  
S.K. Sharma ◽  
Marcelo Knobel ◽  
...  
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Single Phase ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Fe Doping ◽  
Full Width ◽  
Deposition Technique ◽  
X Ray Diffraction ◽  
X Ray

Ce1-xFexO2 (x=0, 0.01, 0.03 and 0.0 5) thin films were grown by pulsed laser deposition technique on Si and LaAlO3 (LAO) substrates. These films were deposited in vacuum and 200 mTorr oxygen partial pressure for both the substrates. These films were characterized by x-ray diffraction XRD and Raman spectroscopy measurements. XRD results reveal that these films are single phase. Raman results show F2g mode at ~466 cm-1 and defect peak at 489 cm-1 for film that deposited on LAO substrates, full width at half maximum (FWHM) is increasing with Fe doping for films deposited on both the substrates.

Structural Analysis of CdO2(1-X) AlX Thin Films Prepared by Pulsed-Laser Deposition

2021 ◽  
Vol 19 (10) ◽  
pp. 34-40
Author(s):  
B.Y. Taher ◽  
A.S. Ahmed ◽  
Hassan J. Alatta
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Doping Concentration ◽  
Pulsed Laser ◽  
Interplanar Distance ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
Diffraction Angle ◽  
Standard Value ◽  
Diffraction Patterns

In this study, CdO2 (1-X) AlX thin films were prepared by pulsed-laser deposition. The X-ray diffraction patterns reveal that the films were polycrystalline with a cubic structure, and the composition of the material changed from CdO at the target to CdO2 in the deposited thin films. The intensity of the diffraction peak (or the texture factor) decreases with increasing hkl and has a maximum value for the (111) plane, the interplanar distance and diffraction angle has a high deviation from the standard value for the (111) plane and. This deviation is affected by doping concentration and shows its highest deviation at a doping concentration of 0.1 wt.% for the (111) and (200), and the 0.3 and 0.5 wt.% for the (210) and (220) planes, respectively. The crystalline size take a less value at plane has a high texture factor that is (111) plane and decreases with increase the doping concentration.

Terahertz Transmission Properties of VO2 Thin Films Deposited on c-and m-Plane Sapphire Substrates by Pulsed Laser Deposition

2013 ◽  
Vol 710 ◽  
pp. 25-28 ◽  
Author(s):  
Xiao Qiang Kou ◽  
Ji Ming Bian ◽  
Zhi Kun Zhang
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
Terahertz Time Domain Spectroscopy ◽  
Transmission Properties ◽  
Sapphire Substrates ◽  
Dense Distribution ◽  
Terahertz Transmission

Vanadium dioxide (VO2) films were grown on c-and m-plane sapphire substrates by pulsed laser deposition (PLD) technique with VO2ceramic target. The VO2films with preferred growth orientation and uniform dense distribution have been achieved on both substrates, as confirmed by X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). The terahertz (THz) transmission properties of VO2thin films were studied by terahertz time-domain spectroscopy (THz-TDS). The results indicate that the THz transmission properties of VO2films are strongly influenced by the sapphire substrate orientation, suggesting that VO2films are ideal material candidates for THz modulation.

Characterization of low resistivity Ga-doped ZnO thin films on Si substrates prepared by pulsed laser deposition

2019 ◽  
Vol 6 (10) ◽  
pp. 106421
Author(s):  
Guankong Mo ◽  
Jiahui Liu ◽  
Guotao Lin ◽  
Zhuoliang Zou ◽  
Zeqi Wei ◽  
...  
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Zno Thin Films ◽  
Low Resistivity ◽  
Si Substrates ◽  
Doped Zno

CRYSTALLINE SrTiO3 THIN FILMS ON SILICON BY PULSED LASER DEPOSITION

2005 ◽  
Vol 19 (01n03) ◽  
pp. 533-535
Author(s):  
J. H. HAO ◽  
J. GAO
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Perovskite Oxide ◽  
Deposition Technique ◽  
X Ray Diffraction ◽  
Rocking Curve ◽  
X Ray ◽  
Silicon Materials

We have developed a process to grow SrTiO 3 ( STO ) thin films showing single (110) orientation directly on Si by means of pulsed laser deposition technique. The growth of STO films directly on Si has been described. The crystallinity of the grown STO films was characterized by X-ray diffraction analysis of θ-2θ scan and rocking curve. Our results may be of interest for better understanding of the growth based on the perovskite oxide thin films on silicon materials.

Electrical Properties of ZnO Thin Films Deposited by Pulsed Laser Deposition.

2004 ◽  
Vol 829 ◽  
Author(s):  
S. P. Heluani ◽  
G. Simonelli ◽  
M. Villafuerte ◽  
G. Juarez ◽  
A. Tirpak ◽  
...  
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Zno Thin Films ◽  
Axis Orientation ◽  
Si Substrates ◽  
N2 Atmosphere ◽  
Doping Effects ◽  
High O2

ABSTRACTStructural and electronic transport properties of polycrystalline ZnO thin films, prepared by pulsed laser deposition, have been investigated. The films were deposited on glass and Si3N4/Si substrates using O2 and N2 atmospheres. X-ray analysis revealed preferential c-axis orientation perpendicular to the sample substrate. Films deposited under relatively high O2 pressure were highly resistive. However, the conductivity σ increased while the films were irradiated with ultraviolet light, showing an Arrhenius (In σ ∝ T-1) dependence as a function of temperature. The ZnO film deposited in N2 atmosphere exhibited at room temperature a resistivity ∼ 1 Ω cm, and a sheet carrier concentration ∼ 5 1012 cm-2. The variation of the conductivity with temperature, in the range 60 – 150 K, follows a In σ ∝ T-1/4 dependence characteristic of variable range hopping. An analysis of the experimental results of conductivity as a function of temperature, in terms of possible doping effects, as well as conduction mechanisms is presented.

Stability and Structural Characterization of Epitaxial NdNiO3 Films Grown by Pulsed Laser Deposition

2000 ◽  
Vol 658 ◽  
Author(s):  
Trong-Duc Doan ◽  
Cobey Abramowski ◽  
Paul A. Salvador
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Substrate Surface ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
Force Microscopy ◽  
Atomic Force ◽  
Monoclinic Distortion

ABSTRACTThin films of NdNiO3 were grown using pulsed laser deposition on single crystal substrates of [100]-oriented LaAlO3 and SrTiO3. X-ray diffraction and reflectivity, scanning electron microscopy, and atomic force microscopy were used to characterize the chemical, morphological and structural traits of the thin films. Single-phase epitaxial films are grown on LaAlO3 and SrTiO3 at 625°C in an oxygen pressure of 200 mTorr. At higher temperatures, the films partially decompose to Nd2NiO4 and NiO. The films are epitaxial with the (101) planes (orthorhombic Pnma notation) parallel to the substrate surface. Four in-plane orientational variants exist that correspond to the four 90° degenerate orientations of the film's [010] with respect to the in-plane substrate directions. Films are observed to be strained in accordance with the structural mismatch to the underlying substrate, and this leads, in the thinnest films on LaAlO3, to an apparent monoclinic distortion to the unit cell.

Growth of CaFeOX/LaFeO3 Superlattice on SrTiO3(100) Substrates

2011 ◽  
Vol 1292 ◽  
Author(s):  
Nobuyuki Iwata ◽  
Mark Huijben ◽  
Guus Rijnders ◽  
Hiroshi Yamamoto ◽  
Dave H. A. Blank
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Layer Growth ◽  
Laser Deposition ◽  
Growth Mode ◽  
Layer By Layer ◽  
X Ray Diffraction ◽  
Reciprocal Space Mapping ◽  
X Ray

ABSTRACTThe CaFeOX(CFO) and LaFeO3(LFO) thin films as well as superlattices were fabricated on SrTiO3(100) substrates by pulsed laser deposition (PLD) method. The tetragonal LFO film grew with layer-by-layer growth mode until approximately 40 layers. In the case of CFO, initial three layers showed layer-by-layer growth, and afterward the growth mode was transferred to two layers-by-two layers (TLTL) growth mode. The RHEED oscillation was observed until the end of the growth, approximately 50nm. Orthorhombic twin CaFeO2.5 (CFO2.5) structure was obtained. However, it is expected that the initial three CFO layers are CaFeO3 (CFO3) with the valence of Fe4+. The CFO and LFO superlattice showed a step-terraces surface, and the superlattice satellite peaks in a 2θ-θ and reciprocal space mapping (RSM) x-ray diffraction (XRD) measurements, indicating that the clear interfaces were fabricated.

Sign in / Sign up

Export Citation Format

Share Document