scholarly journals Studies on Properties of Sisal Fiber Reinforced Self Compacting Concrete

2021 ◽  
Vol 9 (10) ◽  
pp. 1642-1648
Author(s):  
A. Narendiran
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Impact Strength ◽  
Flexural Strength ◽  
Reducing Agent ◽  
Sisal Fiber ◽  
Fiber Reinforced ◽  
Self Compacting Concrete

Abstract: To evaluate the mechanical properties of self compacting concrete (M30) with sisal fibers.Self-compacting concrete (SCC) mixes are produced by replacing the cement with Fly ash and with addition of sisal fiber of 0, 0.5%, 1%, 1% and1.5% and length of fibers considered are 5mm, 10mm, and 20mm to the SCC concrete. Sulphonated naphthalene Formaldehyde condensates based SP is used as water reducing agent. Compressive strength and Flexural strength of SCC mix has to be determined at 14 and 28 days. Impact strength of SCC mix has to be determined at 28 days.

scholarly journals Experimental Investigation of Flow and Mechanical Properties of Fibrofor Fiber Reinforced Self-Compacting Concrete

2019 ◽  
Vol 8 (2) ◽  
pp. 8-15
Author(s):  
H. R. Arun Kumar ◽  
B. Shivakumaraswamy
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Flexural Strength ◽  
Volume Fraction ◽  
Working Environment ◽  
Fiber Reinforced ◽  
Self Compacting Concrete ◽  
Split Tensile Strength ◽  
Hardened Properties

Self Compacting Concrete is a material used in the construction that has excellent deformability in the fresh state and high resistance of segregation, and can be replaced and compacted under its self-weight without applying vibration which leads to substantial advantages related to better homogeneity, enhancement of working environment and improvement in the productivity by increasing the speed of construction. Concrete can be formulated with high compressive strength but always has lower tensile strength. Tensile strength and other properties of concrete can be enhanced by adding fibers due to which the workability of concrete mix reduces and in order to achieve the desired Workability super-plasticizers is added. In the present work the use of fibrofor fiber in the production of self-compacting concrete (SCC) has been studied to identify how fresh and hardened properties of SCC are affected by the addition of fibers. The fibrofor fiber of 19mm standard length is incorporated into the SCC mixtures as 0.5kg/m3, 1.0kg/m3, 1.5kg/m3of concrete. Test on fresh SCC like slump Flow test, T50, V-Funnel test, J-Ring slump test and L-Box test were performed for an understanding of flow of SCC and tests on hardened properties like flexural strength, compressive strength and split tensile strength have been conducted to identify the hardened properties of SCC produced with fibrofor fiber. A comparative study between plain concrete, SCC without fiber and SCC with fiber has been done. Mix design for M40 grade concrete has been done according to EFNARC guidelines. The results reveal that the use of fibro for fiber decreases the workability but increases the mechanical properties of SCC. The optimum volume fraction of fibrofor fiber is determined as 1kg/m3 considering the optimized flexural strength and split tensile strength based properties of SCC. Due to increase in strength properties of fiber reinforced SCC that can be used for pavement construction and various other structures such as buildings, water retaining structures, reservoir structures and tunnel etc.

Study on Mechanical Properties and Mechanism of Sisal Fiber Cement Mortar

2014 ◽  
Vol 1044-1045 ◽  
pp. 111-114
Author(s):  
Feng Lv ◽  
Zi Ye He ◽  
Xiao Ming He ◽  
Jun Yi Qian ◽  
Ding Liu
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Flexural Strength ◽  
Cement Mortar ◽  
Reducing Agent ◽  
Fiber Content ◽  
Sisal Fiber ◽  
Mixing Proportion ◽  
Base Group

This paper comparatively study on fluidity, flexural strength, compressive strength and other mechanical properties of sisal fiber cement mortar and the base mortar. The results show that fluidity of sisal fiber makes sisal fiber cement mortar than that of the base group decreased about by 11.1%;When sisal fiber content is 4.5 kg/m3, water reducing agent is 2.78 kg/m3, the best mixing proportion of sisal fiber cement mortar for water: glue: sand = 0.45:1.:2.5, flexural strength improved by 52.4%, 54.3%, 20.1% respectively, compressive strength increased by-1.5%, 6.5% and-2.1%.And analyzed the mechanism of flexural and compressive from the chemistry of sisal fiber and cement.

scholarly journals Assessment of the Rheological and Mechanical Properties of Geopolymer Concrete Comprising Fly Ash and Fluid Catalytic Cracking Residue as Aluminosilicate Precursor

2021 ◽  
Vol 11 (7) ◽  
pp. 3032
Author(s):  
Tuan Anh Le ◽  
Sinh Hoang Le ◽  
Thuy Ninh Nguyen ◽  
Khoa Tan Nguyen
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Elastic Modulus ◽  
Fly Ash ◽  
Flexural Strength ◽  
Catalytic Cracking ◽  
Fluid Catalytic Cracking ◽  
High Alumina ◽  
Geopolymer Concrete ◽  
Sem Images

The use of fluid catalytic cracking (FCC) by-products as aluminosilicate precursors in geopolymer binders has attracted significant interest from researchers in recent years owing to their high alumina and silica contents. Introduced in this study is the use of geopolymer concrete comprising FCC residue combined with fly ash as the requisite source of aluminosilicate. Fly ash was replaced with various FCC residue contents ranging from 0–100% by mass of binder. Results from standard testing methods showed that geopolymer concrete rheological properties such as yield stress and plastic viscosity as well as mechanical properties including compressive strength, flexural strength, and elastic modulus were affected significantly by the FCC residue content. With alkali liquid to geopolymer solid ratios (AL:GS) of 0.4 and 0.5, a reduction in compressive and flexural strength was observed in the case of geopolymer concrete with increasing FCC residue content. On the contrary, geopolymer concrete with increasing FCC residue content exhibited improved strength with an AL:GS ratio of 0.65. Relationships enabling estimation of geopolymer elastic modulus based on compressive strength were investigated. Scanning electron microscope (SEM) images and X-ray diffraction (XRD) patterns revealed that the final product from the geopolymerization process consisting of FCC residue was similar to fly ash-based geopolymer concrete. These observations highlight the potential of FCC residue as an aluminosilicate source for geopolymer products.

scholarly journals Kajian Karakteristik Beton Memadat Sendiri yang Menggunakan Serat Ijuk (Hal. 54-65)

2018 ◽  
Vol 4 (4) ◽  
pp. 54
Author(s):  
Iis Nurjamilah ◽  
Abinhot Sihotang
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Coarse Aggregate ◽  
Fresh Concrete ◽  
High Strength ◽  
Self Compacting Concrete ◽  
Palm Fiber ◽  
Fiber Concrete ◽  
Dilute Mixture

ABSTRAKKajian karakteristik beton memadat sendiri yang menggunakan serat ijuk merupakan sebuah kajian yang dilakukan untuk mengetahui pengaruh penambahan serat ijuk terhadap karakteristik beton memadat sendiri (SCC). Beton memadat sendiri yang menggunakan serat ijuk (PFSCC) didesain memiliki campuran yang encer, bermutu tinggi (= 40 MPa) dan memiliki persentase kekuatan lentur yang lebih baik. PFSCC  didapatkan dari hasil pencampuran antara semen sebanyak 85%, fly ash 15%, superplastizicer 1,5%, serat ijuk 0%, 0,5%; 1%; 1,5%; 2% dan 3% dari berat binder (semen + fly ash), kadar air 190 kg/m3, agregat kasar 552,47 kg/m3 dan pasir 1.063 kg/m3. Semakin banyak persentase penambahan serat ijuk ke dalam campuran berdampak terhadap menurunnya workability beton segar. Penambahan serat ijuk yang paling baik adalah sebanyak 1%, penambahan tersebut dapat meningkatkan kekuatan tekan beton sebesar 13% dan lentur sebesar 1,8%.Kata kunci: beton memadat sendiri (SCC), beton berserat, beton memadat sendiri yang menggunakan serat ijuk (PFSCC), serat ijuk ABSTRACTThe study of characteristics self compacting concrete using palm fibers is a study conducted to determine the effect of adding palm fibers to characteristics of self compacting concrete (SCC). palm fibers self compacting concrete (PFSCC) is designed to have a dilute mixture, high strength (= 40 MPa), and have better precentage flexural strength. PFSCC was obtained from mixing of 85% cement, 15% fly ash, 1.5% superplastizicer, 0%, 0.5%, 1%, 1.5%, 2% and 3% palm fibers from the weight of binder  (cement + fly ash), water content 190 kg/m3, coarse aggregate 552.47 kg/m3 and sand 1,063 kg/m3. The more persentage palm fibers content added to the mixture makes workability of fresh concrete decreases. The best addition of palm fiber is 1%, this addition can increases the compressive strength 13% and flexural strength 1.8%.Keywords: self compacting concrete (SCC), fiber concrete, Palm fiber self compacting concrete (PFSCC), palm fiber

scholarly journals Strength Characteristics of High Strength Concrete (HSC) with and without Coarse Aggregate

2019 ◽  
Vol 9 (2) ◽  
pp. 4701-4704
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Silica Fume ◽  
High Strength Concrete ◽  
Mechanical Characteristics ◽  
Coarse Aggregate ◽  
High Strength ◽  
Set Up

This paper aimed to investigate the mechanical characteristics of HSC of M60 concrete adding 25% of fly ash to cement and sand and percentage variations of silica fumes 0%,5% and 10% to cement with varying sizes of 10mm,6mm,2mm and powder of granite aggregate with w/c of 0.32. Specimens are tested for compressive strength using 10cm X 10cmX10cm cubes for 7,14,28 days flexural strength was determined by using 10cmX10cmX50cm beam specimens at 28 days and 15cm diameter and 30cm height cylinder specimens at 28 days using super plasticizers of conplast 430 as a water reducing agent. In this paper the experimental set up is made to study the mechanical properties of HSC with and without coarse aggregate with varying sizes as 10mm, 6mm, 2mm and powder. Similarly, the effect of silica fume on HSC by varying its percentages as 0%, 5% and 10% in the mix studied. For all mixes 25% extra fly ash has been added for cement and sand.

Effects of Fly Ash Addition on Compressive Strength and Flexural Strength of Foamed Cement Composites

2013 ◽  
Vol 795 ◽  
pp. 664-668 ◽  
Author(s):  
Roshasmawi Abdul Wahab ◽  
Mohd Noor Mazlee ◽  
Shamsul Baharin Jamaludin ◽  
Khairul Nizar Ismail
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Cement Composites ◽  
Volume Percent ◽  
Foaming Agent ◽  
Cement Ratio ◽  
Water To Cement Ratio

In this study, the mixing of polystyrene (PS) beads and fly ash as a sand replacement material in foamed cement composites (FCC) has been investigated. Specifically, the mechanical properties such as compressive strength and flexural strength were measured. Different proportions of fly ash were added in cement composites to replace the sand proportion at 3 wt. %, 6 wt. %, 9 wt. % and 12 wt. % respectively. The water to cement ratio was fixed at 0.65 meanwhile ratios of PS beads used was 0.25 volume percent of samples as a foaming agent. All samples at different mixed were cured at 7 and 28 days respectively. Based on the results of compressive strength, it was found that the compressive strength was increased with the increasing addition of fly ash. Meanwhile, flexural strength was decreased with the increasing addition of fly ash up to 9 wt. %. The foamed cement composites with 12 wt. % of fly ash produced the highest strength of compressive strength meanwhile 3 wt. % of fly ash produced the highest strength of flexural strength.

Influence of Variable Temperature Curing on Mechanical Properties of Fly Ash Concrete

2011 ◽  
Vol 250-253 ◽  
pp. 178-181
Author(s):  
Ya Ding Zhao ◽  
Xue Ying Li ◽  
Ling Chao Kong ◽  
Wei Du
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Elastic Modulus ◽  
Fly Ash ◽  
Flexural Strength ◽  
Variable Temperature ◽  
Improve Performance ◽  
Curing Conditions ◽  
Fly Ash Concrete ◽  
Better Than

Under variable temperature curing conditions(30 oC ~70 oC), concrete with fly ash whose compressive strength, flexural strength, and dynamic elastic modulus are better than ones without fly ash.Compared with constant temperature 20oC, 50 oC and 70 oC, variable temperature curing(VTC) is benefit for the improvement of mechanical properties of 30% fly ash concrete, but which is no advantage to improve performance of 50% fly ash concrete.

Experimental Study on Mechanical Properties of Synthetic Macro-Fiber Reinforced Reactive Powder Concrete

2014 ◽  
Vol 496-500 ◽  
pp. 2402-2406
Author(s):  
Kui He ◽  
Hui Yang ◽  
Fang Fang Jia ◽  
Er Po Wang ◽  
Zhen Bao Lu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Experimental Study ◽  
Compressive Strength ◽  
Fracture Mechanics ◽  
Flexural Strength ◽  
Fracture Energy ◽  
Ductile Fracture ◽  
Reactive Powder Concrete ◽  
Fiber Reinforced ◽  
Reactive Powder

Workability, strength and fracture mechanics of polypropylene macro-fiber reinforced Reactive powder concrete (RPC) were studied in this work. The results showed that the incorporation of macro-fiber could influence the workability of RPC, the slump of RPC decreased with the increasing of macro-fiber content; compressive strength decreased while splitting strength increased with the increasing of macro-fiber, meanwhile the flexural strength invariant. Macro-fiber could strongly enhance the flexural toughness of RPC and changed the failure mode from brittle to ductile; fracture energy tends to increase linearly with the increasing of macro-fiber.

scholarly journals Effect of fly ash on physical and mechanical properties of mortar

2019 ◽  
Vol 17 (6) ◽  
pp. 35
Author(s):  
Vu-An Tran
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Water Absorption ◽  
Thermal Power ◽  
Setting Time ◽  
Physical And Mechanical Properties ◽  
Flow Density ◽  
Control Specimen

This research investigates the physical and mechanical properties of mortar incorporating fly ash (FA), which is by-product of Duyen Hai thermal power plant. Six mixtures of mortar are produced with FA at level of 0%, 10%, 20%, 30%, 40%, and 50% (by volume) as cement replacement and at water-to-binder (W/B) of 0.5. The flow, density, compressive strength, flexural strength, and water absorption tests are made under relevant standard in this study. The results have shown that the higher FA content increases the flow of mortar but significantly decreases the density of mixtures. The water absorption and setting time increases as the samples incorporating FA. Compressive strength of specimen with 10% FA is approximately equal to control specimen at the 91-day age. The flexural strength of specimen ranges from 7.97 MPa to 8.94 MPa at the 91-day age with the best result for samples containing 10% and 20% FA.

Sign in / Sign up

Export Citation Format

Share Document