Transmission Electron Microscopy (TEM) Specimen Preparation Technique using Focused Ion Beam (FIB): Application to Material Characterization of Chemical Vapor Deposition of Tungsten (W) and Tungsten Silicides (WSix)

1997 ◽  
Author(s):  
K. Doong ◽  
J.-M. Fu ◽  
Y.-C. Huang
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Focused Ion Beam ◽  
Ion Beam ◽  
Chemical Vapor ◽  
Specimen Preparation ◽  
Preparation Technique ◽  
Transmission Electron

Abstract The specimen preparation technique using focused ion beam (FIB) to generate cross-sectional transmission electron microscopy (XTEM) samples of chemical vapor deposition (CVD) of Tungsten-plug (W-plug) and Tungsten Silicides (WSix) was studied. Using the combination method including two axes tilting[l], gas enhanced focused ion beam milling[2] and sacrificial metal coating on both sides of electron transmission membrane[3], it was possible to prepare a sample with minimal thickness (less than 1000 A) to get high spatial resolution in TEM observation. Based on this novel thinning technique, some applications such as XTEM observation of W-plug with different aspect ratio (I - 6), and the grain structure of CVD W-plug and CVD WSix were done. Also the problems and artifacts of XTEM sample preparation of high Z-factor material such as CVD W-plug and CVD WSix were given and the ways to avoid or minimize them were suggested.

A Methodology to Reduce Ion Beam Induced Damage in TEM Specimens Prepared by FIB

2002 ◽  
Author(s):  
Chin Kai Liu ◽  
Chi Jen. Chen ◽  
Jeh Yan.Chiou ◽  
David Su
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Sample Preparation ◽  
Integrated Circuit ◽  
Focused Ion Beam ◽  
Ion Beam ◽  
Specimen Preparation ◽  
Tem Analysis ◽  
Sensitive Issue ◽  
Transmission Electron

Abstract Focused ion beam (FIB) has become a useful tool in the Integrated Circuit (IC) industry, It is playing an important role in Failure Analysis (FA), circuit repair and Transmission Electron Microscopy (TEM) specimen preparation. In particular, preparation of TEM samples using FIB has become popular within the last ten years [1]; the progress in this field is well documented. Given the usefulness of FIB, “Artifact” however is a very sensitive issue in TEM inspections. The ability to identify those artifacts in TEM analysis is an important as to understanding the significance of pictures In this paper, we will describe how to measure the damages introduced by FIB sample preparation and introduce a better way to prevent such kind of artifacts.

Understanding the Growth Mechanisms of Tin Oxide Nanowires by Chemical Vapor Deposition

2021 ◽  
Vol 21 (4) ◽  
pp. 2538-2544
Author(s):  
Nguyen Minh Hieu ◽  
Nguyen Hoang Hai ◽  
Mai Anh Tuan
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Chemical Vapor ◽  
Chemical Mapping ◽  
X Ray Diffraction ◽  
Lattice Constants ◽  
Transmission Electron ◽  
Scanning Transmission

Tin oxides nanowires were prepared by chemical vapor deposition using shadow mask. X-ray diffraction indicated that the products were tetragonal having crystalline structure with lattice constants a = 0.474 nm and c = 0.318 nm. The high-resolution transmission electron microscopy revealed that inter planar spacing is 0.25 nm. The results chemical mapping in scanning transmission electron microscopy so that the two elements of Oxygen and Tin are distributed very homogeneously in nanowires and exhibit no apparent elements separation. A bottom-up mechanism for SnO2 growth process has been proposed to explain the morphology of SnO2 nanowires.

Microstructures of GaN Films Grown on a LiGaO2 New Substrate by Metalorganic Chemical Vapor Deposition

1997 ◽  
Vol 468 ◽  
Author(s):  
Jing-Hong Li ◽  
Olga M. Kryliouk ◽  
Paul H. Holloway ◽  
Timothy J. Anderson ◽  
Kevin S. Jones
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Metalorganic Chemical Vapor Deposition ◽  
Lattice Mismatch ◽  
Chemical Vapor ◽  
Threading Dislocations ◽  
Transmission Electron ◽  
Metalorganic Chemical

ABSTRACTMicrostructures of GaN films grown on the LiGaO2 by metalorganic chemical vapor deposition (MOCVD) have been characterized by transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). TEM and HRTEM results show that high quality single-crystal wurtzite GaN films have been deposited on the LiGaO2 and that the GaN film and the LiGaO2 have the following orientation relationship: (2110)(0002)GaN ̂ (002)LiGaO2 ^ 5–8°. A higher density of threading dislocations and stacking faults have been observed near the GáN/LiGaO2 interface, even though the lattice mismatch of GaN to LiGaO2 is only ∼1%. Threading dislocations with burgers vector b=<0001> and b=a/3<1120> are predominant in the GaN films. Also the GaN films contain some columnar inversion domain boundaries (IDBs). Both TEM and HRTEM results reveal that there is an unexpected amorphous or nano-crystalline inter-layer between the GaN and the LiGaO2 with a thickness of 50–100 nm.

Sign in / Sign up

Export Citation Format

Share Document