scholarly journals Development of New 14 Cr ODS Steels by Using New Oxides Formers and B as an Inhibitor of the Grain Growth

Metals ◽  
2020 ◽  
Vol 10 (10) ◽  
pp. 1344
Author(s):  
Alberto Meza ◽  
Eric Macía ◽  
Andrea García-Junceda ◽  
Luis Antonio Díaz ◽  
Paul Chekhonin ◽  
...  

In this work, new oxide dispersion strengthened (ODS) ferritic steels have been produced by powder metallurgy using an alternative processing route and characterized afterwards by comparing them with a base ODS steel with Y2O3 and Ti additions. Different alloying elements like boron (B), which is known as an inhibitor of grain growth obtained by pinning grain boundaries, and complex oxide compounds (Y-Ti-Zr-O) have been introduced to the 14Cr prealloyed powder by using mechanical alloying (MA) and were further consolidated by spark employing plasma sintering (SPS). Techniques such as x-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM) were used to study the obtained microstructures. Micro-tensile tests and microhardness measurements were carried out at room temperature to analyze the mechanical properties of the differently developed microstructures, which was considered to result in a better strength in the ODS steels containing the complex oxide Y-Ti-Zr-O. In addition, small punch (SP) tests were performed to evaluate the response of the material under high temperatures conditions, under which promising mechanical properties were attained by the materials containing Y-Ti-Zr-O (14Al-X-ODS and 14Al-X-ODS-B) in comparison with the other commercial steel, GETMAT. The differences in mechanical strength can be attributed to the precipitate’s density, nature, size, and to the density of dislocations in each ODS steel.

2019 ◽  
Vol 38 (2019) ◽  
pp. 404-410 ◽  
Author(s):  
Weijuan Li ◽  
Haijian Xu ◽  
Xiaochun Sha ◽  
Jingsong Meng ◽  
Zhaodong Wang

AbstractIn this study, oxide dispersion strengthened (ODS) ferritic steels with nominal composition of Fe–14Cr–2W–0.35Y2O3 (14Cr non Zr-ODS) and Fe–14Cr–2W–0.3Zr–0.35Y2O3 (14Cr–Zr-ODS) were fabricated by mechanical alloying (MA) and hot isostatic pressing (HIP) technique to explore the impact of Zr addition on the microstructure and mechanical properties of 14Cr-ODS steels. Microstructure characterization revealed that Zr addition led to the formation of finer oxides, which was identified as Y4Zr3O12, with denser dispersion in the matrix. The ultimate tensile strength (UTS) of the non Zr-ODS steel is about 1201 MPa, but UTS of the Zr-ODS steel increases to1372 MPa, indicating the enhancement of mechanical properties by Zr addition.


2012 ◽  
Vol 706-709 ◽  
pp. 977-982 ◽  
Author(s):  
Fabien Corpace ◽  
A. Monnier ◽  
A. Poulon Quintin ◽  
J P. Manaud

ODS steels (Oxide Dispersion Strengthened) are candidate materials for fuel cladding in Sodium Fast Reactors (SFR). These materials have good mechanical properties at high temperature due to a dispersion of nanometer-sized oxides into the matrix. Previous studies have shown that melting can induce a decrease of the mechanical properties at high temperatures due to modifications of the nanometer-sized oxide dispersion. Therefore the fusion welding techniques are not recommended and the solid state boundings has to be evaluated. This study is focused on resistance upset welding. Welding experiments and numerical simulations are coupled. The numerical simulation is developed in order to have a better understanding of the thermal and the mechanical phenomena occurring during the welding process. The simulation shows that the welding steps can be divided in two stages. First, the temperature of the contact between pieces increases. Second, the heat generation is mainly located in the cladding leading to the collapse and forging the pieces. The microstructural observations confirm that the major deformation is located in the cladding. Oxide dispersion modification and dynamical recrystallisation has been found for welds achieved with a non optimized process parameter set. The deformation and the temperature seem to be of prime importance in the modification of the oxide dispersion.


2012 ◽  
Vol 567 ◽  
pp. 49-53 ◽  
Author(s):  
Jae Hoon Lee

18%Cr-oxide dispersion strengthened (ODS) ferritic steels with and without 5%Al have been produced by mechanical alloying and hot-extrusion. The microstructure of the ODS steels has been characterized by means of electron microscopy (SEM, TEM), showing that in the Al-added ODS steel, the semi-coherent and coherent oxide particles are about 75% and 10%, respectively. It was found that the coherency of oxide particles depends on the size of dispersed particles. Tensile tests performed between room temperature and 973 K denote that the ultimate tensile strength of Al-free ODS steel is higher than that of Al-added one. The ductility values of both materials are sufficiently high. Impact tests reveal that the ductile-to-brittle transition temperature of Al-free ODS steel are higher than that of Al-added ODS steel; however, the upper shelf energy of 18%Cr-ODS steel is substantially smaller in comparison to the Al-added one. It is considered that the difference in mechanical properties between Al-free and Al-added ODS steels is caused by the smaller, stable titania + yttria complex oxides dispersed in the Al-free ODS steel.


Metals ◽  
2022 ◽  
Vol 12 (1) ◽  
pp. 155
Author(s):  
Feng Su ◽  
Guangtao Xu ◽  
Zhenhua Yao ◽  
Huachen Liu ◽  
Yikun Chen

High density of thermally stable Y-Si-O nanoparticles dispersed in the Fe matrix play a primary role in oxide dispersion strengthened (ODS) steel. In this study, the binding energies of solutes Y, O and Si with vacancies have been calculated in the framework of first-principles density functional theory. According to the calculations, any two solutes of Y, O and Si bound with each other strongly in the second nearest neighboring (NN) sites while not in 1NN. A vacancy (v) bounds strongly with Y and O in 1NN site. The binding sequence of solutes with v followed O-v → Y-v → Si-v, and the affinity of Y, Si and v with O followed O-Y → O-v → O-Si. The nucleation mechanism of Y-O-Si nanoclusters was determined, which gave the feasibility of adding Si to ODS steels. The core (consisting of Si and O)-shell (enriched Fe and Cr) structure of the microparticles was found in ODS steels containing Si, fabricated by mechanical alloying (MA) and vacuum sintering. Moreover the nanoparticles of monoclinic cubic Y2O3, Y2SiO5 and Y2Si2O7 with sizes of 5 ~ 12 nm were observed in ODS steel. Si reduced the sintering temperature by maximizing densities and mechanical properties at a lower sintering temperature. The steel with 3 wt% Si was sintered at 1280 °C, exhibiting the best comprehensive mechanical properties. The tensile strength, hardness and relative density were 1025 MPa, 442.44 HV and 95.3%, respectively.


Metals ◽  
2020 ◽  
Vol 10 (3) ◽  
pp. 348 ◽  
Author(s):  
Andrea García-Junceda ◽  
Eric Macía ◽  
Dariusz Garbiec ◽  
Marta Serrano ◽  
José M. Torralba ◽  
...  

Two different zirconium contents (0.45 and 0.60 wt.%) have been incorporated into a Fe-14Cr-5Al-3W-0.4Ti-0.25Y2O3 oxide dispersion-strengthened (ODS) steel in order to evaluate their effect on the final microstructure and mechanical properties. The powders with the targeted compositions were obtained by mechanical alloying (MA), and subsequently processed by spark plasma sintering (SPS) at two different heating rates: 100 and 400 °C·min−1. Non-textured bimodal microstructures composed of micrometric and ultrafine grains were obtained. The increase in Zr content led to a higher percentage of Zr nano-oxides and larger regions of ultrafine grains. These ultrafine grains also seem to be promoted by higher heating rates. The effective pinning of the dislocations by the Zr dispersoids, and the refining of the microstructure, have significantly increased the strength exhibited by the ODS steels during the small punch tests, even at high temperatures (500 °C).


Materials ◽  
2021 ◽  
Vol 14 (24) ◽  
pp. 7767
Author(s):  
Yingying Li ◽  
Liye Zhang ◽  
Dijun Long ◽  
Liming Yu ◽  
Huijun Li

Two oxide-dispersion-strengthened (ODS) steels with different compositions (14Cr-ODS and 14Cr-Zr-ODS) were investigated to reveal the influences of microalloying element addition on the microstructure and to clarify the refining mechanism of precipitated particles. TEM and HRTEM results indicated that precipitated particles in the Zr-containing ODS steel had finer sizes and dispersed more homogeneously within the grains. It was found that rhombohedral Y4Zr3O12 particles with complex lattice structures were formed and could pin the migration of the grain boundaries during heat treatment due to their high thermal stability. In addition, the Zr-containing ODS steel exhibited a finer and more uniform grain morphology. Tensile tests showed that microalloying element addition could significantly improve the comprehensive mechanical properties of 14Cr ODS steels at room temperature.


2002 ◽  
Vol 740 ◽  
Author(s):  
Mats Carlsson ◽  
Mats Johnsson ◽  
Annika Pohl

ABSTRACTCeramic composites containing 2 and 5vol. % of nanosized commercially available TiN and SiC particles in alumina were prepared via a water based slurry processing route followed by spark plasma sintering (SPS) at 75 MPa in the temperature range 1200–1600°C. Some of the samples could be fully densified by use of SPS already after five minutes at 1200°C and 75 MPa. The aim was to control the alumina grain growth and thus obtain different nano-structure types. The microstructures have been correlated to some mechanical properties; e.g. hardness and fracture toughness.


2010 ◽  
Vol 638-642 ◽  
pp. 2309-2314
Author(s):  
Kei Shinozuka ◽  
Hisao Esaka ◽  
M. Tamura ◽  
Hiroyasu Tanigawa

In international thermonuclear experimental reactor (ITER), reduced activation ferritic/martensitic steels will be used for plasma-facing materials. However, it is necessary to raise the temperature of operation in order to elevate efficiency of electric power generation by using the material which is more excellent in strength at elevated temperature. Oxide dispersion strengthened (ODS) steels are promising candidate for high temperature materials of a nuclear fusion reactor. There are many reports that ODS steels show very high creep strength, but there are few reports on creep deformation mechanism. In this work, creep deformation behavior of 8 wt% Cr ODS steel was investigated. This ODS steel had high density of fine dispersed Y2Ti2O7 particles and -ferrite grains elongated along the hot-rolling direction. The creep curve showed a low creep strain rate until specimen ruptured. Vickers hardness of the gauge part of specimens in interrupted creep tests decreased with increasing the loading time. However, that of the grip part did not change significantly. Accordingly, although dynamic recovery occurred in the ODS steel, it had not affected the creep deformation rate.