scholarly journals Steel Corrosion Evaluation of Basalt Fiber RPC Affected by Crack and Steel-Concrete Interface Damage Using Electrochemical Methods

Sensors ◽  
2020 ◽  
Vol 20 (18) ◽  
pp. 5027
Author(s):  
Hanbing Liu ◽  
Xiang Lyu ◽  
Yuwei Zhang ◽  
Guobao Luo ◽  
Wenjun Li
Keyword(s):  
Basalt Fiber ◽  
Steel Corrosion ◽  
Corrosion Process ◽  
Electrochemical Methods ◽  
Reactive Powder Concrete ◽  
Interface Damage ◽  
Steel Bars ◽  
Corrosion Behaviors ◽  
Reactive Powder ◽  
Concrete Interface

Basalt fiber (BF) is a new anti-corrosion and environmentally friendly material, which is expected to delay the corrosion process of steel bars and improve the durability of reinforced reactive powder concrete (RPC). The electrochemical method is a nondestructive testing and real-time monitoring technique used to characterize the corrosion behaviors of steel bars embedded in concrete structures. In this paper, the electrochemical technique was employed to evaluate the corrosion of steel bars embedded in basalt fiber modified reactive powder concrete (BFRPC). Besides, crack and steel-concrete interface damage (SCID) were considered as typical factors that affect steel corrosion in concrete. Thus, both reinforced fiber-free RPC and BFRPC specimens with crack and SCID were prepared for evaluating the steel corrosion behaviors by electrochemical methods. The results revealed that both crack and SCID would aggravate the steel corrosion, and the crack was the major factor that affects the corrosion process. Moreover, the excellent compactness of BFRPC and the bridging action of BF could effectively prevent the concrete cracking and steel corrosion process of concrete. Using reinforced BFRPC instead of ordinary concrete in practical projects could greatly extend the service life of steel bars.

Experimental Research on Mechanical Properties of Basalt Fiber Reinforced Reactive Powder Concrete

2014 ◽  
Vol 893 ◽  
pp. 610-613 ◽  
Author(s):  
Chong Hai Dong ◽  
Xin Wei Ma
Keyword(s):  
Mechanical Properties ◽  
Impact Resistance ◽  
Basalt Fiber ◽  
Considerable Extent ◽  
Reactive Powder Concrete ◽  
Strengthening Effect ◽  
Static Mechanical ◽  
Experimental Works ◽  
Reactive Powder ◽  
Static Mechanical Properties

This paper investigates the static mechanical properties and flexural impact properties of reactive powder concrete (RPC) reinforced by the basalt fiber through various experimental works. The results indicate that the highest flexural and compressive strength can be obtained when the fiber content is 3kg/m3. Length and diameter of basalt fiber both influence the mechanical properties. The basalt fiber of 25mm long and 18μ in diameter can have an ideal strengthening effect. The static mechanical properties and flexural impact resistance can be improved to a considerable extent.

scholarly journals Effect of Mix Proportion Parameters on Behaviors of Basalt Fiber RPC Based on Box-Behnken Model

2019 ◽  
Vol 9 (10) ◽  
pp. 2031 ◽  
Author(s):  
Hanbing Liu ◽  
Shiqi Liu ◽  
Shurong Wang ◽  
Xin Gao ◽  
Yafeng Gong
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Basalt Fiber ◽  
Fiber Content ◽  
Reactive Powder Concrete ◽  
Basalt Fibers ◽  
Factors Affecting ◽  
Remarkable Effect ◽  
Mix Proportion ◽  
Reactive Powder

Basalt fibers are widely used in the modification of concrete materials due to its excellent mechanical properties and corrosion resistance. In this study, the basalt fibers were used to modify reactive powder concrete (RPC). The effect of four mix proportion parameters on the working and mechanical properties of basalt fiber reactive powder concrete (BFRPC) was evaluated by the response surface methodology (RSM). The fluidity, flexural and compressive strength were tested and evaluated. A statistically experimental model indicated that D (the silica fume to cement ratio) was the key of interactions between factors, affecting other factors and controlling properties of BFRPC. The increase in basalt fiber content had a remarkable effect on increasing the flexural and compressive strength when D = 0.2. The addition of basalt fiber obviously improved the mechanical properties of RPC. While when D = 0.4, the decrease of fiber content and the increase of quartz sand content could increase the compressive strength.

scholarly journals Bending Resistance and Failure Type Evaluation of Basalt Fiber RPC Beam Affected by Notch and Interfacial Damage Using Acoustic Emission

2020 ◽  
Vol 10 (3) ◽  
pp. 1138 ◽  
Author(s):  
Hanbing Liu ◽  
Xiang Lyu ◽  
Yuwei Zhang ◽  
Guobao Luo ◽  
Wenjun Li
Keyword(s):  
Acoustic Emission ◽  
Basalt Fiber ◽  
Steel Fibers ◽  
Bending Test ◽  
Reactive Powder Concrete ◽  
Basalt Fibers ◽  
Interfacial Damage ◽  
Failure Type ◽  
Bending Resistance ◽  
Reactive Powder

Generally, reactive powder concrete (RPC) contains steel fibers often exposed to aggressive environments. Steel fibers in such RPCs are subjected to corrosion in-service, which can significantly change the mechanical properties of the structural components. In this paper, basalt fibers were used to replace steel fibers for preparing a new basalt fiber modified reactive powder concrete (BFRPC). The bending resistance of BFRPC beams was studied, and the crack propagation and failure type of BFRPC beam were monitored by acoustic emission (AE). During the bending test, the failure type of BFRPC was evaluated by AE. Besides, the effects of notch and interfacial damage on the bending resistance and failure type were also studied. During the test, ordinary Reactive Powder Concrete (RPC) without basalt fibers was used as a reference. Results revealed that failure type of the RPC beam and BFRPC beam was mainly caused by shear failure. The notch increased the number of tensile cracks in the beam failure crack, resulting in a decrease in the bending resistance of RPC beam and BFRPC beam. Besides, basalt fiber could improve the toughness and bending resistance of BFRPC beam and increase resistance of the BFRPC beam to notch and interface damage.

Experimental Study on Compressive Property of Basalt Fiber Reactive Powder Concrete

2020 ◽  
Vol 984 ◽  
pp. 239-244
Author(s):  
Lu Liang Wang ◽  
Hai Long Zhao ◽  
De Hong Wang ◽  
Jun Feng Bai
Keyword(s):  
Test Piece ◽  
Failure Process ◽  
Basalt Fiber ◽  
Strain Curve ◽  
Reactive Powder Concrete ◽  
Compressive Property ◽  
Fiber Volume ◽  
Stress Strain ◽  
Reactive Powder ◽  
Relationship Of

In order to study the stress-strain relationship of basalt fiber reactive powder concrete (RPC), the compressive stress-strain curve test of four groups of basalt fiber RPC was carried out. The test parameters including two kinds of basalt fiber length and three fiber volume fractions showed that the deformability of the test piece was improved and the failure process was delayed after incorporating basalt fiber. The optimum fiber fraction of the test piece with 12 mm long fiber was 0.10%. According to the experimental data, the stress-strain of the basalt fiber RPC was drawn. For the curve, the constitutive relation is fitted by the piecewise equation, and compared with the experimental curve, the fitting result is better.

scholarly journals Flexural Strength and Acoustic Damage Characteristics of Steel Bar Reactive Powder Concrete

2021 ◽  
Vol 11 (15) ◽  
pp. 7017
Author(s):  
Tingyou Yi ◽  
Hua Wang ◽  
Juntao Xie ◽  
Wensheng Wang
Keyword(s):  
Flexural Strength ◽  
Fracture Process ◽  
Average Frequency ◽  
Bending Test ◽  
Reactive Powder Concrete ◽  
Shear Cracks ◽  
Tensile Cracks ◽  
Steel Bar ◽  
Steel Bars ◽  
Reactive Powder

In this paper, the steel bar was used to prepare steel bar reactive powder concrete (SBRPC). The three-point bending test was adopted to investigate the effect of the number of steel bars on the flexural strength of SBRPC. The acoustic emission (AE) was used to monitor the fracture process of SBRPC in real time. In addition, the parameter RA and AF ratio (RF) was defined to analyze the distribution of shear cracks and tensile cracks during the fracture process. The experimental results showed that with the increases in the number of the steel bar, the flexural strength of SBRPC gradually increased. The fracture stage of SBRPC can be accurately divided according to the curve slope change in hits and cumulative counts. Moreover, the early warning of SBRPC damage can be realized by observing the amplitude of the AE amplitude value. The dynamic changes in the rising angle (RA) and average frequency (AF) values can be used to determine the cracks mode and fracture mode. Based on the results of RF analysis, adding steel bars will improve the proportion for tensile cracks during its fracture process.

scholarly journals Mechanical Properties and Freeze–Thaw Durability of Basalt Fiber Reactive Powder Concrete

2020 ◽  
Vol 10 (16) ◽  
pp. 5682
Author(s):  
Wenjun Li ◽  
Hanbing Liu ◽  
Bing Zhu ◽  
Xiang Lyu ◽  
Xin Gao ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Loss Rate ◽  
Steel Fiber ◽  
Basalt Fiber ◽  
Reactive Powder Concrete ◽  
Chloride Salt ◽  
Freeze Thaw ◽  
Thaw Cycle ◽  
Freeze Thaw Cycle ◽  
Reactive Powder

Basalt fiber has a great advantage on the mechanical properties and durability of reactive powder concrete (RPC) because of its superior mechanical properties and chemical corrosion resistance. In this paper, basalt fiber was adopted to modified RPC, and plain reactive powder concrete (PRPC), basalt fiber reactive powder concrete (BFRPC) and steel fiber reactive powder concrete (SFRPC) were prepared. The mechanical properties and freeze–thaw durability of BFRPC with different basalt fiber contents were tested and compared with PRPC and SFRPC to investigate the effects of basalt fiber contents and fiber type on the mechanical properties and freeze–thaw durability of RPC. Besides, the mass loss rate and compressive strength loss rate of RPC under two freeze–thaw conditions (fresh-water freeze–thaw and chloride-salt freeze–thaw) were tested to evaluate the effects of freeze–thaw conditions on the freeze–thaw durability of RPC. The experiment results showed that the mechanical properties and freeze–thaw resistance of RPC increased as the basalt fiber content increase. Compared with the fresh-water freeze–thaw cycle, the damage of the chloride-salt freeze–thaw cycle on RPC was great. Based on the freeze–thaw experiment results, it was found that SFRPC was sensitive to the corrosion of chloride salts and compared with the steel fiber, the improvement of basalt fiber on the freeze–thaw resistance of RPC was great.

Sign in / Sign up

Export Citation Format

Share Document