Effects of Nano-Diamond Seeds on Mechanical Properties and Surface Morphology of Diamond-Like Carbon Films

2015 ◽  
Vol 723 ◽  
pp. 502-506
Author(s):  
Yu Luo ◽  
Qing Yun Chen ◽  
Huan Yuan ◽  
Ming Xu ◽  
Shu Long Huang
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Carbon Films ◽  
Diamond Like Carbon ◽  
Mean Square ◽  
Atomic Force ◽  
Indentation Tests ◽  
Scanning Electron ◽  
Sputtering System

The effects of nano-diamond seeds on the performance of diamond-like carbon (DLC) films were investigated. In this study, the high uniform DLC films were deposited on substrates seeded with nano-diamond by using a magnetron sputtering system. Then, the effects of nano-diamond seeds on DLC films were determined. Raman spectroscopy revealed a decrease of sp3 fraction due to the introduction of nano-diamond seeds. Atomic force microscope (AFM) observed all samples have an average root mean square (RMS) roughness of 1.8 nm. Scanning electron microscopy (SEM) displayed that a large number of small size conical hillock geometrical anomalies can be caused by nano-diamond seeds. Indentation tests revealed that nano-diamond seeds can enhance the hardness of DLC films, whose hardness range is from 28.3 GPa to 32.1 GPa in this work.

scholarly journals Corrosion Behavior and Mechanical Properties of a Nanocomposite Superhydrophobic Coating

Coatings ◽  
2021 ◽  
Vol 11 (6) ◽  
pp. 652
Author(s):  
Divine Sebastian ◽  
Chun-Wei Yao ◽  
Lutfun Nipa ◽  
Ian Lian ◽  
Gary Twu
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Atomic Force Microscopy ◽  
Nanocomposite Coating ◽  
Superhydrophobic Coating ◽  
Force Microscopy ◽  
Atomic Force ◽  
Microscopy Images ◽  
Scanning Electron

In this work, a mechanically durable anticorrosion superhydrophobic coating is developed using a nanocomposite coating solution composed of silica nanoparticles and epoxy resin. The nanocomposite coating developed was tested for its superhydrophobic behavior using goniometry; surface morphology using scanning electron microscopy and atomic force microscopy; elemental composition using energy dispersive X-ray spectroscopy; corrosion resistance using atomic force microscopy; and potentiodynamic polarization measurements. The nanocomposite coating possesses hierarchical micro/nanostructures, according to the scanning electron microscopy images, and the presence of such structures was further confirmed by the atomic force microscopy images. The developed nanocomposite coating was found to be highly superhydrophobic as well as corrosion resistant, according to the results from static contact angle measurement and potentiodynamic polarization measurement, respectively. The abrasion resistance and mechanical durability of the nanocomposite coating were studied by abrasion tests, and the mechanical properties such as reduced modulus and Berkovich hardness were evaluated with the aid of nanoindentation tests.

Measuring size-dependent mechanical properties of electrospun polystyrene fibers using in-situ AFM-SEM

2012 ◽  
Vol 1424 ◽  
Author(s):  
Russell J. Bailey ◽  
Beatriz Cortes-Ballesteros ◽  
Hao Zhang ◽  
Congwei Wang ◽  
Asa H. Barber
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Fiber Diameter ◽  
Electrospun Fibers ◽  
Force Microscopy ◽  
Size Dependent ◽  
Atomic Force ◽  
Scanning Electron

ABSTRACTThe mechanical properties of individual electrospun polystyrene fibers with sub-micron diameters were measured using a combination of atomic force microscopy (AFM) and scanning electron microscopy (SEM). The strain to failure of the electrospun fibers was observed to increase as the fiber diameter decreased. This size dependent mechanical behavior in individual electrospun polystyrene fibers indicates a suppression of localized failure and a shift away from crazing that is dominant in bulk samples.

Electron Microscopic Observation of the Longitudinal Organization of Poly (p-Phenylene Terephthalamide) Fibers

1982 ◽  
Vol 40 ◽  
pp. 680-681
Author(s):  
Li Li-Sheng ◽  
L.F. Allard ◽  
W.C. Bigelow
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Microscopic Observation ◽  
Electron Microscopic Observation ◽  
Electron Microscopic ◽  
Aromatic Polyamides ◽  
Radial Arrangement ◽  
Scanning Electron ◽  
Better Than

The aromatic polyamides form a class of fibers having mechanical properties which are much better than those of aliphatic polyamides. Currently, the accepted morphology of these fibers as proposed by M.G. Dobb, et al. is a radial arrangement of pleated sheets, with the plane of the pleats parallel to the axis of the fiber. We have recently obtained evidence which supports a different morphology of this type of fiber, using ultramicrotomy and ion-thinning techniques to prepare specimens for transmission and scanning electron microscopy.

scholarly journals Analysis of PLA Composite Filaments Reinforced with Lignin and Polymerised-Lignin-Treated NFC

Polymers ◽  
2021 ◽  
Vol 13 (13) ◽  
pp. 2174
Author(s):  
Diana Gregor-Svetec ◽  
Mirjam Leskovšek ◽  
Blaž Leskovar ◽  
Urška Stanković Elesini ◽  
Urška Vrabič-Brodnjak
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Tensile Strength ◽  
Glassy State ◽  
Nanofibrillated Cellulose ◽  
Dynamic Mechanical Properties ◽  
Initial Modulus ◽  
Surface Modified ◽  
Scanning Electron

Polylactic acid (PLA) is one of the most suitable materials for 3D printing. Blending with nanoparticles improves some of its properties, broadening its application possibilities. The article presents a study of composite PLA matrix filaments with added unmodified and lignin/polymerised lignin surface-modified nanofibrillated cellulose (NFC). The influence of untreated and surface-modified NFC on morphological, mechanical, technological, infrared spectroscopic, and dynamic mechanical properties was evaluated for different groups of samples. As determined by the stereo and scanning electron microscopy, the unmodified and surface-modified NFCs with lignin and polymerised lignin were present in the form of plate-shaped agglomerates. The addition of NFC slightly reduced the filaments’ tensile strength, stretchability, and ability to absorb energy, while in contrast, the initial modulus slightly improved. By adding NFC to the PLA matrix, the bending storage modulus (E’) decreased slightly at lower temperatures, especially in the PLA samples with 3 wt% and 5 wt% NFC. When NFC was modified with lignin and polymerised lignin, an increase in E’ was noticed, especially in the glassy state.

Research on compatibility and surface of high impact bio-based polyamide

2021 ◽  
pp. 095400832110055
Author(s):  
Yang Wang ◽  
Yuhui Zhang ◽  
Yuhan Xu ◽  
Xiucai Liu ◽  
Weihong Guo
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Differential Scanning Calorimetry ◽  
Crystallization Behavior ◽  
High Impact ◽  
X Ray Diffraction ◽  
Scanning Calorimetry ◽  
X Ray ◽  
Scanning Electron

The super-tough bio-based nylon was prepared by melt extrusion. In order to improve the compatibility between bio-based nylon and elastomer, the elastomer POE was grafted with maleic anhydride. Scanning Electron Microscopy (SEM) and Thermogravimetric Analysis (TGA) were used to study the compatibility and micro-distribution between super-tough bio-based nylon and toughened elastomers. The results of mechanical strength experiments show that the 20% content of POE-g-MAH has the best toughening effect. After toughening, the toughness of the super-tough nylon was significantly improved. The notched impact strength was 88 kJ/m2 increasing by 1700%, which was in line with the industrial super-tough nylon. X-ray Diffraction (XRD) and Differential Scanning Calorimetry (DSC) were used to study the crystallization behavior of bio-based PA56, and the effect of bio-based PA56 with high crystallinity on mechanical properties was analyzed from the microstructure.

Sign in / Sign up

Export Citation Format

Share Document