Effect of Mineralizers on MnNb2O6 Powder Prepared by Hydrothermal Method

2010 ◽  
Vol 156-157 ◽  
pp. 1010-1013
Author(s):  
Yong Ping Pu ◽  
Yong Yong Zhuang ◽  
Kai Chen ◽  
Ning Xu
Keyword(s):  
Electron Microscopy ◽  
Heat Treatment ◽  
Scanning Electron Microscopy ◽  
Particle Size ◽  
Phase Composition ◽  
Hydrothermal Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Highly Dispersed ◽  
Scanning Electron

Pure MnNb2O6 powders was successfully prepared by hydrothermal method using Nb2O5•nH2O and Mn(NO3)2 as precursors and HCl, HF, NaOH, NH4OH solutions as mineralization agent. The phase composition and morphology of the prepared powder were characterized by X-ray diffraction and scanning electron microscopy. The effect of mineralizers on phase formation was investigated. The results show that the MnNb2O6 powders with crystallite size of ~24nm can be obtained with Mn(NO3)2 and Nb2O5•nH2O as precursors in neutral and alkaline solution at 200 for 168h. The particle size of the MnNb2O6 powder was ~300nm after heat treatment at a temperature of 600 . The SEM photographs show that the morphology of the MnNb2O6 powder are rod-like particles and the MnNb2O6 powders are highly dispersed.

Bi2S3 Nanoflowers Synthesized via Hydrothermal Method

2014 ◽  
Vol 989-994 ◽  
pp. 11-14 ◽  
Author(s):  
Xi Liang Chen ◽  
Yan Pei Ji
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Phase Composition ◽  
High Resolution ◽  
Hydrothermal Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Structure Phase ◽  
Hydrothermal Approach ◽  
Scanning Electron

Bi2S3 flowerlike patterns were synthesized via a facile hydrothermal approach without using any surfactant and acid. The morphology, structure, phase composition, of the as-prepared Bi2S3 products were characterized using scanning electron microscopy, X-ray diffraction, high-resolution transmission and electron microscopy, respectively. The experimental results showed that the product possesses good distribution of morphology, well crystallized nanostructure.

UTILIZATION OF FLY ASH AND CONCRETE RESIDUE IN THE PRODUCTION OF GEOPOLYMER BRICKS

2017 ◽  
Vol 12 (1) ◽  
pp. 63-77 ◽  
Author(s):  
Siriporn Sirikingkaew ◽  
Nuta Supakata
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Compressive Strength ◽  
Phase Composition ◽  
Fly Ash ◽  
Industrial Waste ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

This study presents the development of geopolymer bricks synthetized from industrial waste, including fly ash mixed with concrete residue containing aluminosilicate compound. The above two ingredients are mixed according to five ratios: 100:0, 95:5, 90:10, 85:15, and 80:20. The mixture's physico-mechanical properties, in terms of water absorption and the compressive strength of the geopolymer bricks, are investigated according to the TIS 168-2546 standard. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) analyses are used to investigate the microstructure and the elemental and phase composition of the brick specimens. The results indicate that the combination of fly ash and concrete residue represents a suitable approach to brick production, as required by the TIS 168–2546 standard.

scholarly journals Standard Hot Pressing as a Possible Solution to Obtain Dense K0.5Na0.5NbO3 Ceramic Doped by Er2O3 and Yb2O3

Materials ◽  
2019 ◽  
Vol 12 (24) ◽  
pp. 4171 ◽  
Author(s):  
Paweł Rutkowski ◽  
Jan Huebner ◽  
Adrian Graboś ◽  
Dariusz Kata ◽  
Dariusz Grzybek ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Rare Earth ◽  
Phase Composition ◽  
Powder Mixture ◽  
Hot Pressing ◽  
X Ray Diffraction ◽  
X Ray ◽  
Ultrasonic Methods ◽  
Scanning Electron

In this study, the influence of the addition of rare earth oxides on the phase composition and density of KNN piezoelectric ceramics was investigated. The initial powders of Na2CO3 and K2CO3 were dried at 150 °C for 2 h. Then, a powder mixture for synthesis was prepared by adding a stoichiometric amount of Nb2O5 and 5 and 10 wt % overabundance of Na2CO3. All powders were mixed by ball-milling for 24 h and synthesized at 950 °C. The phase composition of the reaction bed was checked by means of X-ray diffraction (XRD). It had an appearance of tetragonal and monoclinic K0.5Na0.5NbO3 (KNN) phases. Then, 1 and 2 wt % of Er2O3 and Yb2O3, were added to the mixture. Green samples of 25 mm diameter and 3 mm thickness were prepared and sintered by hot pressing at 1000 °C for 2 h under 25 MPa pressure. The final samples were investigated via scanning electron microscopy (SEM)-energy-dispersive X-ray spectroscopy (EDS), XRD, Rietveld, and ultrasonic methods. Phase analysis showed tetragonal and orthorhombic KNN phases, and a contamination of (K2CO3·1.5H2O) was present. The obtained KNN polycrystals had a relative density above 95%. Texturing of the material was confirmed as a result of hot pressing.

Microstructure and Phase Composition of AlN/Al Composite Fabricated by Directed Melt Nitridation

2008 ◽  
Vol 368-372 ◽  
pp. 977-979
Author(s):  
Sheng Li Jin ◽  
Ya Wei Li ◽  
Jing Liu ◽  
Yuan Bing Li ◽  
Lei Zhao ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Phase Composition ◽  
Sandwich Structure ◽  
Ceramic Composite ◽  
Growth Direction ◽  
X Ray Diffraction ◽  
X Ray ◽  
Al Composite ◽  
Scanning Electron

AlN/Al ceramic composite was fabricated by directed melt nitridation of pure Al block covered with 10wt% Mg powder at 1300°C in a high purity flowing N2. Microstructure and phase composition of the composite were investigated by scanning electron microscopy with energy dispersive spectroscopy and X-ray diffraction. Results showed that AlN is the main phase in the composite and its lattice parameters of a and c are 3.1110Å and 4.9806Å, respectively. The phase composition of the composite changes along the growth direction and a gradient sandwich structure forms. The surface of the composite is made up of a dense and thin nodular AlN layer, underneath which an AlN/Al layer appears, followed by an AlN/Al/MgAl2O4 layer. Thermodynamic calculations predicted the formation of possible phases with the addition of Mg. It suggested that the content of Mg at the reaction frontier of nitridation is considerably lower to 0.15wt% where MgAl2O4 was stable, because of escape and reaction exhaustion of Mg. Once Mg is lower than 0.05wt%, only a dense AlN layer can exist, which prevents the further nitridation of Al melt.

Biomorphic SiC Prepared from Carbonized Millet by Sol-Gel and Carbothermal Reduction Processing

2010 ◽  
Vol 152-153 ◽  
pp. 1683-1686
Author(s):  
Qing Wang ◽  
Ya Hui Zhang
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Silicon Carbide ◽  
Phase Composition ◽  
Carbothermal Reduction ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
X Ray ◽  
Carbon Template ◽  
Scanning Electron

Biomorphic silicon carbide (bioSiC) was prepared by high temperature pyrolysis and sol-gel and carbothermal reduction processing at 1600 oC. The morphology and microstructure of carbon-silica composites and purified bioSiC samples were characterized by scanning electron microscopy. The phase composition of the resulting sample was analyzed by X-ray diffraction. The results suggest that the bioSiC mainly consists of cubic ß-SiC, and principally replicates the shape and microstructure of the carbon template.

Biomorphic TiO2 Ceramics Prepared from Cotton Stalk

2012 ◽  
Vol 602-604 ◽  
pp. 526-529
Author(s):  
Qing Wang ◽  
Lin Zhang ◽  
Ya Hui Zhang
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Phase Composition ◽  
High Temperature ◽  
Sol Gel ◽  
Cotton Stalk ◽  
X Ray Diffraction ◽  
X Ray ◽  
Carbon Template ◽  
Scanning Electron

Biomorphic TiO2 was prepared by high temperature pyrolysis and a modified sol-gel route. The morphology and microstructure of TiO2 samples were characterized by scanning electron microscopy. The phase composition of the resulting sample was analyzed by X-ray diffraction. The results suggest that the biomorphic TiO2 mainly consists of rutile TiO2, and replicates the shape and part microstructure of the carbon template.

Preparation and Properties of CaF2 Nano-Powder

2016 ◽  
Vol 680 ◽  
pp. 257-260
Author(s):  
Meng Yun Dong ◽  
Cheng Zhang ◽  
Jin Feng Xia ◽  
Hong Qiang Nian ◽  
Dan Yu Jiang
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Particle Size ◽  
Sintering Temperature ◽  
Raw Materials ◽  
X Ray Diffraction ◽  
X Ray ◽  
Nano Powder ◽  
Direct Precipitation ◽  
Scanning Electron

CaF2 nano-power was prepared by direct precipitation methods with Ca(NO3)2 and KF as raw materials. The influences of presintering temperature and sintering temperature on the particle size and distribution of CaF2 nano-power were studied by X-ray diffraction (XRD) and field-emission scanning electron microscopy (FESEM). This study provided an experimental method for preparation of CaF2 nano-power. The results show that the best presintering temperature of CaF2 nano-power is 500°C and the best sintering temperature of CaF2 ceramic is 900°C.

CYCLIC IMPROVEMENT OF LiNi0.5Mn1.5O4 POLYHEDRAL SPINELS FOR 5.0 V LITHIUM ION BATTERIES

2010 ◽  
Vol 03 (03) ◽  
pp. 185-188 ◽  
Author(s):  
XIAOYUN ZHAN ◽  
ZHAOHUI LI ◽  
JIAOJUN TANG ◽  
QIZHEN XIAO ◽  
GANGTIE LEI ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Particle Size ◽  
Lithium Ion ◽  
Electrochemical Measurement ◽  
Cycling Performance ◽  
Small Particle Size ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

Highly crystallized and microsized particles of LiNi0.5Mn1.5O4 spinels with different morphologies have been successfully synthesized using polystyrene (PS) as the sacrificial template, and were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical measurement. The spinels obtained at 700°C possess abundant porosity with about 200 nm in diameter, while the spinels calcined at 900°C exhibit a well-defined polyhedral morphology with particle size ranged from 0.2 to 2 μm. The materials prepared at 900°C display an excellent cycling performance due probably to better crystallinity and small particle size.

scholarly journals Evolution of Free Volumes in Polycrystalline BaGa2O4 Ceramics Doped with Eu3+ Ions

Crystals ◽  
2021 ◽  
Vol 11 (12) ◽  
pp. 1515
Author(s):  
Halyna Klym ◽  
Ivan Karbovnyk ◽  
Andriy Luchechko ◽  
Yuriy Kostiv ◽  
Viktorija Pankratova ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Phase Composition ◽  
Grain Boundaries ◽  
Solid Phase ◽  
X Ray Diffraction ◽  
Spectroscopy Technique ◽  
X Ray ◽  
Positron Annihilation Lifetime ◽  
Scanning Electron

BaGa2O4 ceramics doped with Eu3+ ions (1, 3 and 4 mol.%) were obtained by solid-phase sintering. The phase composition and microstructural features of ceramics were investigated using X-ray diffraction and scanning electron microscopy in comparison with energy-dispersive methods. Here, it is shown that undoped and Eu3+-doped BaGa2O4 ceramics are characterized by a developed structure of grains, grain boundaries and pores. Additional phases are mainly localized near grain boundaries creating additional defects. The evolution of defect-related extended free volumes in BaGa2O4 ceramics due to the increase in the content of Eu3+ ions was studied using the positron annihilation lifetime spectroscopy technique. It is established that the increase in the number of Eu3+ ions in the basic BaGa2O4 matrix leads to the agglomeration of free-volume defects with their subsequent fragmentation. The presence of Eu3+ ions results in the expansion of nanosized pores and an increase in their number with their future fragmentation.

Preparation and Characterizations of a-Fe2O3 Nanorods and their Properties

2016 ◽  
Vol 852 ◽  
pp. 346-348
Author(s):  
Hong Cai ◽  
Qing Bo Du ◽  
Ji Gui Xu ◽  
Hong Wei Shi ◽  
Jun Zhu
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Hydrothermal Method ◽  
Magnetic Measurement ◽  
Remnant Magnetization ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Fundamental Research ◽  
Scanning Electron

a-Fe2O3 nanorods over large areas were successfully synthesized by hydrothermal method, using FeCl3 as iron source and PVP as surfactant. The as-synthesized a-Fe2O3 nanorods were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and magnetic measurement system (SQUID-VSM) . The results show that the nanorods prepared by hydrothermal method with the diameter of about 70 nm and the length of about 300 nm. The magnetic properties of the synthesized nanorods were studied, and the remnant magnetization and coercivity of the α-Fe2O3 nanorods at 300K are found to be 0.07emu/g and 2300Oe, respectively. The a-Fe2O3 nanorods reported here may have opportunities for both fundamental research and technological applications.

Sign in / Sign up

Export Citation Format

Share Document