Decorative Film Formation by Inkjet Printing with Gold Nanoparticles for Synthetic Resin Crafts

The crafts such as lacquerware have made unique strides through decorating techniques using gold such as “Makie”, the technique to draw picture by scattering powdered gold, and “Chinkin”, the technique to rub gold into the design engraved by carving knives. In conventional techniques, practical knowledge and ability are essential to produce craft products. Therefore, screen printing which consists of simple processes has been developed. However, screen printing requires a masking plate made of silk or nylon to create patterns for transcribing ink into objects. This paper presents the formation of a decorative film by inkjet printing with gold nanoparticles for crafts such as lacquerware. The proposed method consists of on-demand process, which makes design changeable without masking. The aims are threefold: 1) to establish a sintering process of gold nanoparticles for acrylonitrile butadiene styrene (ABS) and phenol resin substrates used for synthetic resin products; 2) to characterize the sintered gold film; 3) to examine applicability to industry. The major results obtained are as follows: the appearance and the reflectance spectra of the gold nanoparticle film vary with heat conditions; the proper heat conditions which prevent thermal damage to substrates are the temperature of 373 K or below for the ABS resin substrate, and 423 K or below for the phenol resin substrate, respectively; the gold nanoparticle film possessed a good surface integrity without any voids when the sintering temperature is higher than 323 K for 1 h. Moreover, the film had such a high adhesion to substrates that no separation occurred after cross-cut test; the proposed method applied a lacquerware product made of ABS resin, yielding the decorative film