scholarly journals Mechanical Properties of Self-Compacting Geopolymer Concrete Using Fly Ash and GGBS

2018 ◽  
Vol 7 (1) ◽  
pp. 19-23
Author(s):  
S. Thirupathiraj .
Keyword(s):  
Blast Furnace ◽  
Fly Ash ◽  
Blast Furnace Slag ◽  
Geopolymer Concrete ◽  
Cement Concrete ◽  
Self Compacting Concrete ◽  
Split Tensile Strength ◽  
Granulated Blast Furnace Slag ◽  
Concrete Mix ◽  
Furnace Slag

Cement is the core content for the concrete mix. Manufacturing of cement causes CO2 emission which leads to the pollution, health and environmental problems like global warming to control over the adverse effect we can prefer geopolymer concrete which is not a cement concrete. Factory wastes such as fly ash, ground granulated blast furnace slag (GGBS), silica fume and Metakaolin can be used as alternate for cement. This study mainly focus on the ratio of fly ash and ground granulated blast furnace slag (GGBS) for optimum levels which nearly matches the cement concrete properties. This study involves the various tests like slump flow, compression testing, split tensile strength and flexural strength of self-compacting geopolymer concrete. Self-compacting concrete is a highly flowable concrete that spreads into the form without the need of mechanical vibration. Self-compacting concrete is a non-segregating concrete that is placed by means of its own weight. The advantages include improved constructability, Labour reduction, bond to steel, Flow into complex forms, reduced equipment wear etc. The aim of this study is to achieve an optimum self-compacting concrete geopolymer concrete mix proportion using fly ash and ground granulated blast furnace slag (GGBS). Then the study will be further extended by investigating the durability properties of self-compacting geopolymer concrete.

scholarly journals Effect of Na2SiO3/Naoh on the Compressive Strength of Inorganic Polymer Concrete Mixed with Ground Granulated Blast Furnace Slag (GGBS) At Ambient Condition

2019 ◽  
Vol 9 (2) ◽  
pp. 1222-1228
Keyword(s):  
Compressive Strength ◽  
Blast Furnace ◽  
Blast Furnace Slag ◽  
Ambient Condition ◽  
Polymer Concrete ◽  
Geopolymer Concrete ◽  
Split Tensile Strength ◽  
Standard Size ◽  
Granulated Blast Furnace Slag ◽  
Furnace Slag

This paper aims to investigate the influence of alkaline activators solution i.e, Na2SiO3 / NaOH on compressive strength of geopolymer concrete mixed with Ground Granulated Blast furnace slag (GGBS) for constant molarity 8 M. The ratio of alkali to binder ratio is taken as 0.5 and the ratio of Na2SiO3 / NaOH is 2.5. The geopolymer mix is based on pervious sutdies. As per Indian standard size moulds for the cube, cylinder and prism are cast, cured and tested.The specimens were tested for fresh concrete properties such as slump cone test and hardened properties such as compressive strength for cubes, split tensile strength for cylinders and flexural strength for prism different days of curing under ambient temperature. Also, a microstructural study is done by using Scanning electron microscopy (SEM), Energy dispersive X-ray (EDX) for the tested sample. It is found from the test results that, with the aid of alumino-silicate solution, early strength is achieved by geopolymer concrete within 7 days under ambient condition due to the presence of ground granulated slag.

scholarly journals Mechanical Behavior of Double Skinned Composite Hollow Columns using Geopolymer Concrete

2020 ◽  
Vol 8 (5) ◽  
pp. 4691-4696
Keyword(s):  
Blast Furnace ◽  
Fly Ash ◽  
Blast Furnace Slag ◽  
Steel Tube ◽  
Fine Aggregate ◽  
Geopolymer Concrete ◽  
Ambient Temperatures ◽  
Granulated Blast Furnace Slag ◽  
Heat Curing ◽  
Furnace Slag

This paper comprises of the experimental study of double skinned (DSCFT) Composite hollow columns using Geopolymer concrete. The diameter-thickness (D/t) ratio and the hollowness ratio were consideredas main parameters in designing the specimens. The Geopolymer Concrete used in this project is the most promising technique. It is composed of fly-ash, fine aggregate, coarse aggregate and alkaline solution. By using large volume of ordinary Portland cement (OPC) concrete, the production of cement increases 3% annually. The production of one ton of cement directly liberates about 1 ton of CO2 and indirectly liberates 0.4 ton of CO2 to atmosphere. Among the greenhouse gases, CO2 contributes about 67% of global warming. In this respect fly ash based geopolymer mortar is highly considerable. But most of the previous works on fly ash-based geopolymers concrete reveals that hardening is due to heat curing, which is considered as a limitation for cast in situ applications at low ambient temperatures. In order to overcome this situation, replacing the Ground blast furnace slag with fly ash for various proportions to achieve geopolymer concrete suitable for curing without elevated heat. The Scope of this project is to find optimization level of Ground Granulated blast furnace slag in geopolymer concrete for curing in ambient condition and to analyze the compressive Strength of optimized GGBS based Geopolymer Concrete filled double skinned steel tube by varying the size of the steel tubes.

scholarly journals Characteristics of Blended Geopolymer Concrete Using Ultrafine Ground Granulated Blast Furnace Slag and Copper Slag

2020 ◽  
Vol 44 (6) ◽  
pp. 433-439
Author(s):  
Vijayasarathy Rathanasalam ◽  
Jayabalan Perumalsami ◽  
Karthikeyan Jayakumar
Keyword(s):  
Blast Furnace ◽  
Fly Ash ◽  
Sodium Hydroxide ◽  
Blast Furnace Slag ◽  
Copper Slag ◽  
Fine Aggregate ◽  
Geopolymer Concrete ◽  
Strength Performance ◽  
Granulated Blast Furnace Slag ◽  
Furnace Slag

This paper presents the properties of blended geopolymer concrete manufactured using fly ash and ultrafine Ground Granulated Blast Furnace Slag (UFGGBFS), along with the copper slag (CPS) as replacement of fine aggregate (crushed stone sand). Various parameters considered in this study include different sodium hydroxide concentrations (10M, 12M and 14M); 0.35 as alkaline liquid to binder ratio; 2.5 as sodium silicate to sodium hydroxide ratio and cured in ambient curing condition. Further, geopolymer concrete was manufactured using fly ash as the prime source material which is replaced with UFGGBFS (0%, 5%, 10% and 15%). Copper slag has been used as replacement of fine aggregate in this study. Properties of the fresh manufactured geopolymer concrete were studied by slump test. Compressive strength of the manufactured geopolymer concrete was tested and recorded after curing for 3, 7 and 28 days. Microstructure Characterization of Geopolymer concrete specimens was done by Scanning Electron Microscope (SEM) analysis. Experimental results revealed that the addition of UFGGBFS resulted in an increased strength performance of geopolymer concrete. Also, this study demonstrated that the strength of geopolymer concrete increased with an increase in sodium hydroxide concentration. SEM results revealed that the addition of UFGGBFS resulted in a dense structure.

Effect of alkali activator dosage on compressive and tensile strength of ground granulated blast furnace slag based geopolymer concrete

2021 ◽  
Author(s):  
Ashita Singh ◽  
Sudhir Singh Bhadauria ◽  
Manish Mudgal ◽  
Suresh Singh Kushwah
Keyword(s):  
Tensile Strength ◽  
Blast Furnace ◽  
Sodium Hydroxide ◽  
Blast Furnace Slag ◽  
Sodium Metasilicate ◽  
Geopolymer Concrete ◽  
Split Tensile Strength ◽  
Granulated Blast Furnace Slag ◽  
Furnace Slag ◽  
Geopolymer Binder

Use of Ordinary Portland cement contributes to environmental deterioration by releasing enormous quantity of CO2.To reduce use of cement, this research focuses on preparation of solely ground granulated blast furnace slag based geopolymer binder, activated by a combination of sodium hydroxide and sodium metasilicate cured under ambient temperature at 27°C. Engineering properties of geopolymer binder are evaluated and compared with conventional cement to assess its suitability as a binder for making geopolymer concrete. Compressive strength, flexure strength and split tensile strength are determined for geopolymer concrete. Microstructural analysis of geopolymer is performed by XRD, FTIR, FESEM and EDAX tests. The concentration of alkali activators is optimized by trials in laboratory and maximum compressive, flexural and split tensile strength of 44.07 MPa, 5.60 MPa and 4.39 MPa respectively, is obtained for geopolymer concrete at 2M concentration of sodium hydroxide solution with ratio of sodium metasilicate to sodium hydroxide taken as 2.0

scholarly journals Influence of Curing Time on the Drying Shrinkage of Concretes with Different Binders and Water-to-Binder Ratios

2017 ◽  
Vol 2017 ◽  
pp. 1-10 ◽  
Author(s):  
Jun Yang ◽  
Qiang Wang ◽  
Yuqi Zhou
Keyword(s):  
Blast Furnace ◽  
Fly Ash ◽  
Blast Furnace Slag ◽  
Drying Shrinkage ◽  
Mineral Admixture ◽  
Curing Time ◽  
Cement Concrete ◽  
Fly Ash Concrete ◽  
Granulated Blast Furnace Slag ◽  
Furnace Slag

Plain cement concrete, ground granulated blast furnace slag (GGBS) concrete, and fly ash concrete were designed. Three wet curing periods were employed, which were 2, 5, and 8 days. The drying shrinkage values of the concretes were measured within 1 year after wet curing. The results show that the increasing rate of the drying shrinkage of concrete containing a mineral admixture at late age is higher than that of plain cement concrete regardless of the wet curing time. With the reduction of wet curing time, the increment of total drying shrinkage of concrete decreases with the decrease of the W/B ratio. The negative effects on the drying shrinkage of fly ash concrete due to the reduction of the wet curing time are much more obvious than those of GGBS concrete and plain cement concrete. Superfine ground granulated blast furnace slag (SGGBS) can reduce the drying shrinkage of GGBS concrete and fly ash concrete when the wet curing time is insufficient.

scholarly journals Utilization of Industrial By-Products/Waste to Manufacture Geopolymer Cement/Concrete

2021 ◽  
Vol 13 (2) ◽  
pp. 873
Author(s):  
Numanuddin M. Azad ◽  
S.M. Samindi M.K. Samarakoon
Keyword(s):  
Mechanical Properties ◽  
Blast Furnace ◽  
Fly Ash ◽  
Blast Furnace Slag ◽  
Industrial Waste ◽  
Cement Concrete ◽  
Granulated Blast Furnace Slag ◽  
Geopolymer Cement ◽  
Furnace Slag ◽  
By Products

There has been a significant movement in the past decades to develop alternative sustainable building material such as geopolymer cement/concrete to control CO2 emission. Industrial waste contains pozzolanic minerals that fulfil requirements to develop the sustainable material such as alumino-silicate based geopolymer. For example, industrial waste such as red mud, fly ash, GBFS/GGBS (granulated blast furnace slag/ground granulated blast furnace slag), rice husk ash (RHA), and bagasse ash consist of minerals that contribute to the manufacturing of geopolymer cement/concrete. A literature review was carried out to study the different industrial waste/by-products and their chemical composition, which is vital for producing geopolymer cement, and to discuss the mechanical properties of geopolymer cement/concrete manufactured using different industrial waste/by-products. The durability, financial benefits and sustainability aspects of geopolymer cement/concrete have been highlighted. As per the experimental results from the literature, the cited industrial waste has been successfully utilized for the synthesis of dry or wet geopolymers. The review revealed that that the use of fly ash, GBFS/GGBS and RHA in geopolymer concrete resulted high compressive strength (i.e., 50 MPa–70 MPa). For high strength (>70 MPa) achievement, most of the slag and ash-based geopolymer cement/concrete in synergy with nano processed waste have shown good mechanical properties and environmental resistant. The alkali-activated geopolymer slag, red mud and fly ash based geopolymer binders give a better durability performance compared with other industrial waste. Based on the sustainability indicators, most of the geopolymers developed using the industrial waste have a positive impact on the environment, society and economy.

Sign in / Sign up

Export Citation Format

Share Document