Study of Hydrophilic Properties of Polysaccharides

In this research, the structural characteristics, specific surface area, sorption of water vapor, and wetting enthalpy of various polysaccharides (cellulose, hemicelluloses, starch, pectin, chitin, and chitosan) have been studied. It was confirmed that crystallites are inaccessible for water, and therefore water molecules can interact only with polar groups in noncrystalline (amorphous) domains of biopolymers. The isotherms of water vapor sorption for various polysaccharides had sigmoid shapes, which can be explained by the absorption of water molecules in heterogeneous amorphous domains having clusters with different packing densities. The method of contributions of polar groups to sorption of water molecules was used, which allowed to derivate a simple calculating equation to describe the shape of sorption isotherms. The wetting of biopolymers with water was accompanied by a high exothermic thermal effect, in direct proportion to the amorphicity degree. The sorption values and wetting enthalpies of amorphous domains of biopolymers were calculated, which allowed to find the hydrophilicity index and compare the hydrophilicity of the various polysaccharides.

Analysis of Spontaneous Ignition of Grass: Chemical Oxidation and Water Vapor Sorption

Self-heating of biomass by chemical oxidation, which can cause spontaneous ignition, is a safety and management concern. This process can be accelerated by aerobic fermentation and water vapor sorption. The chemical oxidation and water vapor sorption of grass were studied in a laboratory oven, measuring the variations in weight and the internal temperature of a sphere with grass within a flexible polymeric network. Both processes were simulated to prove that the proposed mathematical model could fit the experimental data. It was observed that the water vapor sorption capacity of the grass was high, so the experimental increase in the internal temperature of a spherical body was around 47 K, from 73°C to 120°C. This fact can be very important because the chemical oxidation of grass accelerates at high temperatures. For scaling, simulation programs were used to study the sorption and oxidation processes with an increase in internal temperature in spherical bodies and infinite plane slabs. These results can be used to obtain those of other geometric symmetries by interpolation. It was deduced that at 70°C and with vapor sorption, the ignition time can be around 3 days to 5 days, while without vapor sorption, the ignition times can be around 110 days to 140 days. For 35°C the ignition times with vapor sorption can be around 12 days to 18 days, while without vapor sorption the ignition times can be around 3700 days to 4500 days. These results can be of interest for warehouses of similar biomass and for forestry research and management groups of wildfires. Graphical Abstract

Fire Performance of Intumescent Waterborne Coatings with Encapsulated APP for Wood Constructions

In this work, intumescent coatings were prepared for protection of wood from fire. The fire-retardant chemical ammonium polyphosphate (APP) is known to have poor resistance to water and high humidity as it is hygroscopic in nature. To improve the water resistance, durability and fire resistance of the intumescent coating, APP was modified using a hybrid organic-inorganic polysiloxane encapsulation shell prepared by the sol–gel method. The physical and chemical properties of the intumescent mix containing microencapsulated ammonium polyphosphate (EAPP) particles were characterized by X-ray fluorescence (XRF), Fourier transform infrared spectroscopy (FTIR), water absorption, dynamic vapor sorption (DVS) and thermogravimetric analysis (TGA). The EAPP mix showed 50% reduction in water absorption, 75% reduction in water vapor sorption and increased thermal stability when compared to the APP mix. The intumescent coatings were applied on wood samples, and their fire performance was evaluated using a cone calorimeter test. The intumescent coatings containing EAPP mix showed better fire retarding properties with longer time to ignition, lower heat release rate and shorter heat release peak when compared to the coating without EAPP mix. The prepared intumescent coating shows higher resistance to water and moisture, and it has great potential to be used in bio-based construction industry for enhancing the fire resistance of wood.