Damage and failure mode maps of composite sandwich panel subjected to quasi-static indentation and low velocity impact

2013 ◽  
Vol 101 ◽  
pp. 204-214 ◽  
Author(s):  
Shengqing Zhu ◽  
Gin Boay Chai
Keyword(s):  
Failure Mode ◽  
Sandwich Panel ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Velocity Impact ◽  
Damage And Failure ◽  
Composite Sandwich ◽  
Static Indentation

Study on the Residual Compressive Strength of a Composite Sandwich Panel with Foam Core after Low Velocity Impact

2012 ◽  
Vol 430-432 ◽  
pp. 484-487 ◽  
Author(s):  
Zong Hong Xie ◽  
Jiang Tian ◽  
Jian Zhao ◽  
Wei Li
Keyword(s):  
Compressive Strength ◽  
Failure Criterion ◽  
Sandwich Panel ◽  
Low Velocity Impact ◽  
Foam Core ◽  
Low Velocity ◽  
Velocity Impact ◽  
Residual Compressive Strength ◽  
Composite Sandwich ◽  
The Impact

The residual compressive strength of a foam core sandwich panel after low-velocity impact was studied by using experimental and analytical methods. The test specimens were compressed uniaxially after they were subjected to a low-velocity-impact. From the observation in the test, one can conclude that the subsequent core crushing around the impact region is the major failure mode in the sandwich structure. A failure criterion named Damage Propagation Criterion was proposed to predict the residual compressive load bearing capability of the low-velocity impacted composite sandwich panel. The characteristic value used in this failure criterion can be calculated by an analytical model developed or by conducting the Sandwich Compression after Impact test.

Low Velocity Impact Response of Composite/Sandwich Structures

2016 ◽  
Vol 725 ◽  
pp. 127-131 ◽  
Author(s):  
Kumar V. Akshaj ◽  
P. Surya ◽  
M.K. Pandit
Keyword(s):  
Sandwich Structures ◽  
Weight Ratio ◽  
Impact Response ◽  
Low Velocity Impact ◽  
Core Material ◽  
Design Parameters ◽  
Low Velocity ◽  
Velocity Impact ◽  
Composite Sandwich ◽  
Set Up

Dent resistance of structures is one of the important design parameters to consider in automotive, aerospace, packaging and transportation of fragile goods, civil engineering and marine industries. It is important to study the dynamic impact response of various combinations of skin and core materials which can provide desired fracture toughness and highest strength to weight ratio for such applications. This paper discusses the low velocity impact response of sandwich structures having unique combination of mild steel as skin material bonded to thermoplastics/PU foam as core material. HDPE, LDPE and polypropylene were the choice of thermoplastics and an optimum combination of materials for the sandwich structure was evaluated using drop-weight experimental set up. It is observed that LDPE is the best choice of core material for the sandwich structures considered.