Abstract. The processes of creation of fire-retardant varnish for wood consisting of a mixture of inorganic and polymeric substances are investigated in the work. It is established that the optimization of the inorganic component leads to a directional ratio of mineral acids and urea capable of effective fire protection of the material. Studies have shown that at the initial temperature of gaseous combustion products T = 68 °C, when exposed to the radiation panel, the untreated sample ignited after 146 s, the flame spread over the entire surface, instead, the sample fire-protected varnish did not ignite, the maximum temperature was 105 °C. In this case, as evidenced by the results of heat resistance, there is a change in the structure of the protective film of the coating. The thickness of the protective layer increases due to the decomposition of the composition, which leads to inhibition of oxidation in the gas and condensed phase, change the direction of decomposition towards the formation of non-combustible gases and combustible coke residue, reduce material combustion and increase flammability index. The coating under the influence of high temperature promotes the formation of a heat-insulating layer of coke, which prevents burning and the passage of high temperature to the material, which is confirmed by the absence of the process of ignition of fire-retardant wood. Features of braking of process of ignition and distribution of a flame of the wood processed by a varnish which consist in several aspects are established. This is the formation of a heat-insulating layer of coke, which prevents burning and the passage of high temperatures to the material, which is confirmed by the absence of the process of ignition of fire-retardant reeds. This indicates the possibility of targeted control of high temperature transfer processes to organic material through the use of special coatings for wood products.
Characteristics of Evaporation and Entrainment of Spray Flow Droplets in High-Temperature Oil Combustion Products: Insight into Academic Research Experience