Investigations on microstructural and mechanical properties of friction stir welded AA 2024-T351

2020 ◽  
Vol 62 (8) ◽  
pp. 793-802
Author(s):  
Şefika Kasman ◽  
Sertan Ozan
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Welded Joints ◽  
Rotational Speed ◽  
Stir Zone ◽  
Tool Rotational Speed ◽  
Friction Stir ◽  
Aa 2024

Abstract In the present study, AA 2024-T351 plates with a thickness of 6 mm were joined using the friction stir welding technique with three different tool rotational speeds and two different pin profiles. Microstructural features and mechanical properties of welded joints were investigated. The grains in recrystallized regions along the stir zone were observed to be almost with invariable sizes. The grain size was revealed to increase with the increase in tool rotational speed. The average grain size was observed to dramatically increase from 2.3 μm to 5.6 μm for welded joints produced with pentagonal shaped pin. All the welded joints were observed to contain defects; the presence of defects exhibited a negative effect on the tensile properties of the welded joint. Most of the defects were observed to localize at the root region of joints. The joint, welded with the tool rotational speed of 250 rpm using pentagonal shaped pin, exhibited ultimate tensile strength with a value of 365 MPa. The ultimate tensile strength of welded joints was found to be higher with the decrease in the tool rotational speed. The welding efficiency of joints was compared with the ultimate tensile strength of base metal; notably, welding efficiency values between 46 % and 80 % were achieved. Microstructural characterizations revealed that Al2Cu (θ phase), Al2CuMg (S phase), and AlCuFeMnSi, Al7Cu2Fe intermetallic particles were dispersed in the stir zone.

scholarly journals Microstructure and Mechanical Properties of Friction Stir Welded Joints Between Commercially Pure Copper and Al 6351 Alloy

2017 ◽  
Vol 62 (3) ◽  
pp. 1819-1825
Author(s):  
V.C. Sinha ◽  
S. Kundu ◽  
S. Chatterjee
Keyword(s):  
Mechanical Properties ◽  
Welded Joints ◽  
Rotational Speed ◽  
Pure Copper ◽  
Stir Zone ◽  
Tool Rotational Speed ◽  
Friction Stir ◽  
Commercially Pure ◽  
Microstructure And Mechanical Properties ◽  
Commercially Pure Copper

AbstractIn the present study, the effect of tool rotational speed on microstructure and mechanical properties of friction stir welded joints between commercially pure copper and 6351 Al alloy was carried out in the range of tool rotational speeds of 300-900 rpm in steps of 150 rpm at 30 mm/minutes travel speed. Up to 450 rpm, the interface of the joints is free from intermetallics and Al4Cu9intermetallic has been observed at the stir zone. However, Al4Cu9intermetallic was observed both at the interface and the stir zone at 600 rpm. At 750 and 900 rpm tool rotational speed, the layers of AlCu, Al2Cu3and Al4Cu9intermetallics were observed at the interface and only Al4Cu9intermetallics has been observed in the stir zone. The maximum ultimate tensile strength of ~207 MPa and yield strength of ~168 MPa along with ~6.2% elongation at fracture of the joint have been obtained when processed at 450 rpm tool rotational speed.

Vibratory weld conditioning during gas tungsten arc welding of al 5052 alloy on the mechanical and micro-structural behavior

2020 ◽  
Vol 17 (6) ◽  
pp. 831-836
Author(s):  
M. Vykunta Rao ◽  
Srinivasa Rao P. ◽  
B. Surendra Babu
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Welded Joints ◽  
Great Influence ◽  
Welding Process ◽  
Microstructural Characterization ◽  
Content Type ◽  
Average Grain Size

Purpose Vibratory weld conditioning parameters have a great influence on the improvement of mechanical properties of weld connections. The purpose of this paper is to understand the influence of vibratory weld conditioning on the mechanical and microstructural characterization of aluminum 5052 alloy weldments. An attempt is made to understand the effect of the vibratory tungsten inert gas (TIG) welding process parameters on the hardness, ultimate tensile strength and microstructure of Al 5052-H32 alloy weldments. Design/methodology/approach Aluminum 5052 H32 specimens are welded at different combinations of vibromotor voltage inputs and time of vibrations. Voltage input is varied from 50 to 230 V at an interval of 10 V. At each voltage input to the vibromotor, there are three levels of time of vibration, i.e. 80, 90 and 100 s. The vibratory TIG-welded specimens are tested for their mechanical and microstructural properties. Findings The results indicate that the mechanical properties of aluminum alloy weld connections improved by increasing voltage input up to 160 V. Also, it has been observed that by increasing vibromotor voltage input beyond 160 V, mechanical properties were reduced significantly. It is also found that vibration time has less influence on the mechanical properties of weld connections. Improvement in hardness and ultimate tensile strength of vibratory welded joints is 16 and 14%, respectively, when compared without vibration, i.e. normal weld conditions. Average grain size is measured as per ASTM E 112–96. Average grain size is in the case of 0, 120, 160 and 230 is 20.709, 17.99, 16.57 and 20.8086 µm, respectively. Originality/value Novel vibratory TIG welded joints are prepared. Mechanical and micro-structural properties are tested.

Effect of Al2O3 nanoparticles on microstructure and mechanical properties of friction stir-welded dissimilar aluminum alloys AA7075-T6 and AA6061-T6

2021 ◽  
pp. 095440892110655
Author(s):  
Sumit Jain ◽  
R.S. Mishra
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Rotational Speed ◽  
Traverse Speed ◽  
Particle Dispersion ◽  
Al2o3 Nanoparticles ◽  
Tool Rotational Speed ◽  
Micro Hardness ◽  
Friction Stir ◽  
Dissimilar Aluminum Alloys

In this research, a defect-free dissimilar weld joint of AA7075-T6 and AA6061-T6 reinforced with Al2O3 nanoparticles was fabricated via friction stir welding (FSW). The influence of tool rotational speed (700, 900 and 1100 rpm), traverse speed (40, 50 and 60 mm/min) with varying volume fractions of Al2O3 nanoparticles (4%, 7% and 10%) on microstructural evolution and mechanical properties were investigated. The augmentation of various mechanical properties is based on the homogeneity of particle dispersion and grains refinement in the SZ of the FSWed joint. The findings revealed that the remarkable reduction in grain size in the SZ was observed owing to the incorporation of Al2O3 nanoparticles produces the pinning effect, which prevents the growth of grain boundaries by dynamic recrystallization (DRX). The increasing volume fraction of Al2O3 nanoparticles enhanced the mechanical properties such as tensile strength, % elongation and micro-hardness. Agglomeration of particles was observed in the SZ of the FSWed joints produced at lower tool rotational speed of 700 rpm and higher traverse speed of 60 mm/min due to unusual material flow. Homogenous particle dispersion and enhanced material mixing ensue at higher rotational speed of 1100 rpm and lower traverse speed of 40 mm/min exhibit higher tensile strength and micro-hardness.

Evaluating the Strength of the Friction Stir Welded Joints at Various Rotational Speeds

2013 ◽  
Vol 446-447 ◽  
pp. 312-315
Author(s):  
Ramaraju Ramgopal Varma ◽  
Abdullah Bin Ibrahim ◽  
B. Ravinder Reddy
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Friction Stir Welding ◽  
Yield Strength ◽  
Welded Joints ◽  
Rotational Speed ◽  
Testing Machine ◽  
Friction Stir ◽  
Universal Testing ◽  
Welding Technique

The present research paper aims in evaluating the strength of the welded AA6351 alloy plates of 6 mm thick by using friction stir welding technique at different rotational speeds The applied welding technique is capable of achieving the mechanical properties of the alloy close to that of the original alloy. In the present investigation, the speeds of the spindle were varied from 1100 rpm to 1500 rpm with a constant transverse speed of 20 mm/min. The tensile strength of the joints is determined by an universal testing machine. The results from the present investigation show that the values of the yield strength were very much closer to the values of the AA6351Alloy prior to welding. It has been found from the experiments that the strength of the joints increases with the increase in the rotational speed; however, the same is decreasing after achieving certain speed.

Investigations on the Mechanical Properties of Friction Stir Processed AZ31B Magnesium Alloy

2012 ◽  
Vol 622-623 ◽  
pp. 210-214
Author(s):  
K. Ganesa Balamurugan ◽  
D. Peter Pushpanathan ◽  
K. Mahadevan
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Magnesium Alloy ◽  
Rotational Speed ◽  
Tool Rotational Speed ◽  
Az31b Magnesium Alloy ◽  
Friction Stir ◽  
Mechanical And Tribological Properties ◽  
Full Factorial ◽  
Level 2

The present study investigates the effect of process parameters like tool rotational speed and tool feed on the mechanical and tribological properties of friction stir processed AZ31B magnesium alloy. The experiments were conducted with 3 level 2 factors full factorial design with two replications. The responses were tensile strength, microhardness and wear. The results were analyzed with the help microstructures of the processed samples. The study reveals that, for all responses, the most significant influencing process parameter is the tool rotational speed.

Investigation of Microstructural and Hardness Properties of Al-Al2O3 Nano Surface Composite

2017 ◽  
Vol 15 ◽  
pp. 36-45
Author(s):  
A. Karthikeyan ◽  
S. Nallusamy
Keyword(s):  
Mechanical Properties ◽  
Rotational Speed ◽  
Volume Fraction ◽  
Traverse Speed ◽  
Stir Zone ◽  
Tool Rotational Speed ◽  
Micro Hardness ◽  
Volume Percentage ◽  
Phase Volume Fraction ◽  
Friction Stir

In present scenario, nanocomposites are playing an imperative role in most of the industrial application due to their outstanding performances with good mechanical properties. The aim of this research is to study the effect of tool rotational speed and traverse speed on micro structural and hardness properties of fabricated surface nanocomposites of Al-Al2O3. By varying tool rotational and traverse speed at a constant volume percentage the surface nanocomposites were produced by applying one pass of friction stir processing. A clear view of material flow and defect characterization in the stir zone were studied. Optimum condition of tool rotational speed of 1120 rpm and tool traverse speed of 16 mm/min was obtained to produce a defect free surface nanocomposite. Microstructure observations were carried out through optical microscope and micro hardness test were conducted by using Vickers micro hardness tester. From the phase volume fraction analysis, it was observed that the Al2O3 nanoparticles were well dispersed in the stir zone. It was found that, the tool speed and traverse speed had a significant impact on microstructure properties as well as mechanical properties of the fabricated surface nanocomposite. From the final results it was found that a mixture of dynamically restored ultra fine grins with a mean size of ~80 nm and the average micro hardness value of 130HV were achieved through a fabricated aluminium Al2O3 nanocomposite.

Investigation on the anisotropy behavior of copper strips processed by a combination of FSP and ECAP

2021 ◽  
pp. 146442072110095
Author(s):  
PM Keshtiban ◽  
R Abdi Behnagh ◽  
F Bashirzadeh ◽  
Rasol Javadzadeh ◽  
Abolfazl Mohsenzadeh
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Base Metal ◽  
Pure Copper ◽  
Copper Sheet ◽  
Friction Stir ◽  
Refined Microstructure ◽  
Average Grain Size

In this study, friction stir processed (FSP) pure copper sheet was equal channel angular pressed (ECAP). The purpose was to investigate the influence of ECAP on the microstructure and mechanical properties of the FSP-treated copper sheet. The dynamically recrystallized grained structure with the average grain size of ∼13 µm was found in the stir zone of the FSP. It was also revealed that FSP caused the enhancement of ultimate tensile strength compared to that of the base metal. Also, it was observed that ECAP led to further grain refinement and a tighter distribution of grains. A refined microstructure with an average grain size of ∼ 2 µm was achieved in copper sheets through FSP, followed by ECAP. The tensile strengths of the ECAP specimens were significantly increased to about 61 and 50% compared to the strengths of base metal and FSP, respectively. An overview of the results of this study showed that combined FSP/ECAP is an effective method for the mechanical improvement of the pure copper sheets.

Prediction of mechanical properties and optimization of process parameters in friction-stir-welded dissimilar aluminium alloys

2020 ◽  
Vol 17 (4) ◽  
pp. 519-526 ◽  
Author(s):  
Senthilnathan T. ◽  
Sujay Aadithya B. ◽  
Balachandar K.
Keyword(s):  
Experimental Data ◽  
Mechanical Properties ◽  
Tensile Strength ◽  
Process Parameters ◽  
Rotational Speed ◽  
Traverse Speed ◽  
Tool Rotational Speed ◽  
Content Type ◽  
Friction Stir ◽  
Grey Relational

Purpose This study aims to predict the mechanical properties such as equivalent tensile strength and micro-hardness of friction-stir-welded dissimilar aluminium alloy plates AA 6063-O and AA 2014-T6, using artificial neural network (ANN). Design/methodology/approach The ANN model used for the experiment was developed through back propagation algorithm. The input parameter of the model consisted of tool rotational speed and weld-traverse speed whereas the output of the model consisted of mechanical properties (tensile strength and hardness) of the joint formed by friction-stir welding (FSW) process. The ANN was trained for 60% of the experimental data. In addition, the impact of the process parameters (tool rotational speed and weld-traverse speed) on the mechanical properties of the joint was determined by Taguchi Grey relational analysis. Findings Subsequently, testing and validation of the ANN were done using experimental data, which were not used for training the network. From the experiment, it was inferred that the outcomes of the ANN are in good agreement with the experimental data. The result of the analyses showed that the tool rotational speed has more impact than the weld-traverse speed. Originality/value The developed neural network can be used to predict the mechanical properties of the weld. Results indicate that the network prediction is similar to the experiment results. Overall regression value computed for training, validation and testing is greater than 0.9900 for both tensile strength and microhardness. In addition, the percentage error between experimental and predicted values was found to be minimal for the mechanical properties of the weldments. Therefore, it can be concluded that ANN is a potential tool for predicting the mechanical properties of the weld formed by FSW process. Similarly, the results of Taguchi Grey relational analysis can be used to optimize the process parameters of the weld process and it can be applied extensively to ascertain the most prominent factor. The results of which indicates that rotational speed of 1,270 rpm and traverse speed of 30 mm/min are to be the optimized process parameters. The result also shows that tool rotational speed has more impact on the mechanical properties of the weld than that of traverse speed.