Ferroelectric C-Axis Oriented Pb5Ge3O11 Thin Films for One Transistor Memory Application

1998 ◽  
Vol 541 ◽  
Author(s):  
Tingkai Li ◽  
Fengyan Zhang ◽  
Sheng Teng Hsu
Keyword(s):  
Thin Films ◽  
Ferroelectric Properties ◽  
Hysteresis Loops ◽  
Chemical Vapor ◽  
Dielectric Constants ◽  
Memory Devices ◽  
Leakage Currents ◽  
Fatigue Characteristics ◽  
Ferroelectric Memory ◽  
Memory Applications

AbstractOne transistor memory devices have been proposed recently. To meet the needs of one transistor memory applications, C-axis oriented Pb5Ge3O11 (PGO) thin films were prepared using metalorganic chemical vapor deposition (MOCVD) and rapid thermal processing (RTP). It was found that the nucleation of C-axis Pb5Ge3O11 phase started at a deposition temperature below 400°C and grain growth dominated at 500°C or above. With increasing annealing temperature, the remanent polarization (Pr) and coercive field (Ec) values increased, and the hysteresis loops of the Pb5Ge3O11 films were well saturated and symmetrical after the post-annealing. The C-axis PGO thin film showed good ferroelectric properties at 5V: 2Pr and 2Ec values were 2.0 - 4.0 µC/cm2 and 90 - 110 kV/cm, respectively. The films also showed excellent fatigue characteristics: no fatigue was observed up to 1 × 109 switching cycles. The retention and imprint properties have also been studied. The leakage currents of the PGO films were 2 - 5 × 10−7 A/cm2 at 100 kV/cm and dielectric constants were 40 - 70. The high quality MOCVD Pb5Ge3O11 films can be used for single transistor ferroelectric memory devices.

Metalorganic chemical vapor deposition of very thin Pb(Zr,Ti)O3 thin films at low temperatures for high-density ferroelectric memory applications

2001 ◽  
Vol 16 (12) ◽  
pp. 3583-3591 ◽  
Author(s):  
Hye Ryoung Kim ◽  
Seehwa Jeong ◽  
Chung Bae Jeon ◽  
Oh Seong Kwon ◽  
Cheol Seong Hwang ◽  
...  
Keyword(s):  
Thin Films ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Metalorganic Chemical Vapor Deposition ◽  
Ferroelectric Properties ◽  
Chemical Vapor ◽  
High Density ◽  
Pt Electrode ◽  
Ferroelectric Memory ◽  
Metalorganic Chemical

The metalorganic chemical vapor deposition of very thin (<50 nm) Pb(Zr,Ti)O3 (PZT) thin films was performed for high density (>32 mega bit) ferroelectric memory devices. The growth temperatures were set between 450 and 530 °C to obtain a smooth surface morphology and prevent damage to the underlying reaction barrier layer. The average grain size of a 50-nm-thick film on a Pt electrode was about 34 nm with a size distribution (σ2) of 11 nm. These values are much smaller than the sol-gel-derived PZT films (55 and 25 nm, respectively). Very thin films with a thickness of approximately 30 nm were prepared at wafer temperatures ranging from 500 to 525 °C. Even with the very small thickness, the films showed good ferroelectric properties with a typical remanent polarization from 10 to 15 μC/cm2 and an extremely low coercive voltage of 0.3 V. However, the leakage current density was rather high resulting in nonsaturating polarization versus voltage curves. Even though good ferroelectric properties were obtained, the formation of PtxPby alloys on top of the Pt electrode was consistently observed. This precludes the reliable control of film composition and electrical performance. The adoption of an Ir electrode successfully eliminated intermetallic alloy formation and resulted in better and reproducible process control. A 50-nm-thick PZT film on an Ir/IrO2/SiO2/Si substrate also showed a reasonable ferroelectric performance.

Dependence of Ferroelectric Properties of SBT Based Capacitors on the Electrode Material

1998 ◽  
Vol 541 ◽  
Author(s):  
S. Tirumala ◽  
S. O. Ryu ◽  
K. B. Lee ◽  
R. Vedula ◽  
S. B. Desu
Keyword(s):  
Thin Films ◽  
Electrode Material ◽  
Electrode Materials ◽  
Perovskite Phase ◽  
Ferroelectric Properties ◽  
Si Substrates ◽  
Non Volatile Memory ◽  
Metal Organic ◽  
Sputter Deposited ◽  
Memory Applications

AbstractThe effect of various electrode materials on the ferroelectric properties of SrBi2Ta2O9 (SBT) thin films has been investigated for non-volatile memory applications. Two sets of electrode structures, viz., Pt-Ir based and Pt-Rh based, were sputter deposited in-situ on Si substrates. SBT thin films were deposited on these electrodes using a metal-organic solution deposition technique followed by a post-deposition anneal at 750 °C in oxygen. Structural characterization revealed a polycrystalline nature with predominant perovskite phase in SBT thin films. Ferroelectric properties were studied in capacitor mode by depositing top electrodes, where the top electrode material is identical to that of the bottom electrode. Extensive analysis of the ferroelectric properties signify the important role played by the electrode material in establishing the device applicability is reported in this work.

Synthesis and Ferroelectric Properties of Sol–Gel Derived Intergrowth-Superlattice-Structured SrBi4Ti4O15-Bi4Ti3O12 Thin Films

2011 ◽  
Vol 197-198 ◽  
pp. 1781-1784
Author(s):  
Hua Wang ◽  
Jian Li ◽  
Ji Wen Xu ◽  
Ling Yang ◽  
Shang Ju Zhou
Keyword(s):  
Thin Films ◽  
Remanent Polarization ◽  
Annealing Temperature ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
Hysteresis Loops ◽  
Si Substrates ◽  
Gel Processing ◽  
Coercive Electric Field ◽  
Clockwise Hysteresis

Intergrowth-superlattice-structured SrBi4Ti4O15–Bi4Ti3O12(SBT–BIT) films prepared on p-Si substrates by sol-gel processing. Synthesized SBT–BIT films exhibit good ferroelectric properties. As the annealing temperature increases from 600°C to 700°C, the remanent polarization Prof SBT–BIT films increases, while the coercive electric field Ecdecreases. SBT–BIT films annealed at 700°C have a Prvalue of 18.9µC/cm2which is higher than that of SBT (16.8µC/cm2) and BIT (14.6µC/cm2), and have the lowest Ecof 142 kV/cm which is almost the same as that of SBT and BIT. The C-V curves of Ag/SBT-BIT/p-Si heterostructures show the clockwise hysteresis loops which reveal the memory effect due to the polarization. The memory window in C-V curve of Ag/SBT-BIT/p-Si is larger than that of Ag/SBT/p-Si heterostructure or Ag/BIT/p-Si heterostructure.

Characterization of Highly Textured PZT Thin Films Grown on LaNiO3 Coated Si Substrates by MOCVD

1997 ◽  
Vol 493 ◽  
Author(s):  
C. H. Lin ◽  
B. M. Yen ◽  
Haydn Chen ◽  
T. B. Wu ◽  
H. C. Kuo ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Thin Films ◽  
Fatigue Behavior ◽  
Chemical Vapor ◽  
Dielectric Constants ◽  
Preferential Orientation ◽  
Organic Chemical ◽  
Pzt Thin Films ◽  
Si Substrates ◽  
Transmission Electron

ABSTRACTHighly textured PbZrxTi1−xO3 (PZT) thin films with x= 0-0.6 were grown on LaNiO3 coated Si substrates at 600 °C by metal-organic chemical vapor deposition (MOCVD). The preferred crystalline orientation of PZT thin films with various Zr concentration were characterized by X-ray diffraction (XRD). Microstructures were studied by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The dielectric constants, hysteresis and fatigue behavior of these thin films were also measured. The relationship between growth rate and the preferential orientation is discussed. Furthermore, the dependence of the electrical properties on Zr concentration and preferential orientation is demonstrated.

Electrical Characteristics of Chemical Solution Deposited Nd3+ Doped PZT (53/47) Thin Films in Planar Electrode Configuration

2000 ◽  
Vol 655 ◽  
Author(s):  
S.B. Majumder ◽  
B. Perez ◽  
B. Roy ◽  
A. Martinez ◽  
R.S. Katiyar
Keyword(s):  
Thin Films ◽  
Ferroelectric Properties ◽  
Hysteresis Loops ◽  
Electrode Configuration ◽  
Electrical Characteristics ◽  
Chemical Solution ◽  
Solution Deposition ◽  
Planar Electrode ◽  
Pzt Films ◽  
Formation Behavior

AbstractElectrical characteristics of ferroelectric thin films in planar electrode configuration are important to characterize these materials for their applications in micro electro mechanical (MEM) and tunable microwave devices. In the present work we have prepared polycrystalline Pb1划3x/2Ndx(Zr0.53Ti0.47)O3 (x = 0.0 to 10.0 at %) thin films on platinized silicon substrate by chemical solution deposition (CSD) technique. The films were characterized in terms of their dielectric and ferroelectric properties by depositing planar interdigital finger electrodes on the surface of the films by electron beam lithography. The capacitance and loss tangent of undoped and 4 at % Nd doped PZT films measured at 100 kHz were found to be 138 pF, 0.033 and 95 pF, 0.019 respectively. Saturated hysteresis loops were obtained in undoped PZT film by applying 100 V across 10 μm electrode separation. Nd doped PZT films on the other hand, electrically shorted at comparatively lower voltage. The electrical characteristics of these films are correlated with their phase formation behavior and microstructural features.

Structural and Ferroelectric Properties of Epitaxial PbZr0.52Ti0.48O3 and BaTiO3 Thin Films Prepared on SrRuO3/SrTiO3(100) Substrates

2001 ◽  
Vol 688 ◽  
Author(s):  
J. Rodríguez Contreras ◽  
J. Schubert ◽  
U. Poppe ◽  
O. Trithaveesak ◽  
K. Szot ◽  
...  
Keyword(s):  
Thin Films ◽  
Rutherford Backscattering Spectrometry ◽  
Ferroelectric Properties ◽  
Hysteresis Loops ◽  
Tunnel Current ◽  
Single Crystalline ◽  
Force Microscopy ◽  
Atomic Force ◽  
Transmission Electron ◽  
Ferroelectric Hysteresis

AbstractWe have prepared single crystalline epitaxial PbZr0.52Ti0.48O3 (PZT) and BaTiO3 (BTO) thin films on single crystalline epitaxial SrRuO3 (SRO) thin films grown on SrTiO3 (100) (STO) substrates. PZT and SRO thin films were grown using high-pressure on-axis sputtering and BTO using pulsed laser deposition (PLD). The film thickness ranged between 12 to 165 nm. Their excellent structural properties, surface smoothness and interface sharpness were demonstrated by X-Ray Diffraction measurements (XRD), High Resolution Transmission Electron Microscopy (HRTEM) and Atomic Force Microscopy (AFM). Rutherford Backscattering Spectrometry and Channeling measurements (RBS/C) were used to analyze stoichiometry and crystalline quality. Ferroelectric hysteresis loops were obtained for all films of a thickness down to 12 nm showing a decrease in the remanent polarization Pr and an increase in the coercive field Ec towards thinner film thicknesses. Furthermore we have prepared tunneling junctions with a PZT or BTO barrier thickness of 3-6 nm. Reproducible bi-stable I-V-curves and bias dependence of the conductance were obtained suggesting an influence of the ferroelectric properties of the barrier material on the tunnel current.

Preparation of PZT/YBCO/YAIO Heterostructure Thin Films by KrF Excimer Laser Ablation

1998 ◽  
Vol 526 ◽  
Author(s):  
Kenji Ebihara ◽  
Hiromnitsu Kurogi ◽  
Yukihiko Yamagata ◽  
Tomoaki Ikegami ◽  
Alexander M. Grishin
Keyword(s):  
Thin Films ◽  
Laser Ablation ◽  
Excimer Laser ◽  
Ferroelectric Properties ◽  
Perovskite Oxide ◽  
Excimer Laser Ablation ◽  
Fatigue Characteristics ◽  
Krf Excimer Laser ◽  
Operation Frequency ◽  
Deposition Conditions

AbstractThe perovskite oxide YBa2Cu3O7-x (YBCO) and Pb(ZrxTi1-x)O3 (PZT) thin films have been deposited for superconducting-ferroelectric devices. KrF excimer laser ablation technique was used at the deposition conditions of 200-600mTorr O2, 2-3J/cm2 and 5-10 Hz operation frequency. Heterostructures of PZT-YBCO-YAlO3:Nd show the zero resistivity critical temperature of 82K and excellent ferroelectric properties of remnant polarization 32 μC/cm2, coercive force of 80kV/cm and dielectric constant 800. Cycling fatigue characteristics and leakage current are also discussed.