In-Plane Uniaxial Magnetic Anisotropy of Cobalt Doped Y3Fe5O12 Epitaxial Films

1999 ◽  
Vol 603 ◽  
Author(s):  
Darren Dale ◽  
G. Hu ◽  
Vincent Balbarin ◽  
Y. Suzuki
Keyword(s):  
Uniaxial Anisotropy ◽  
Pulsed Laser ◽  
Epitaxial Films ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
X Ray ◽  
Garnet Films ◽  
Integrated Devices ◽  
Potential Applications ◽  
Order Of Magnitude

AbstractIn an effort to develop a magnetic biasing layer for potential applications in integrated devices, we have grown thin films of Y3Fe5O12 with increased uniaxial anisotropy by doping with varying Co2+, concentration. To compensate for the charge differential between Co2+ and Fe3+, Ge4+ and Ce4+ are substituted for Fe3+ and y3+, respectively. These garnet films, prepared using pulsed laser deposition on (110) oriented Gd3Ga5O12 substrates, exhibit excellent crystallinity as determined from X-ray diffraction and Rutherford backscattering spectroscopy. The addition of Co2+ in Y3Fe5O12 films enhances the in-plane uniaxial anisotropy over an order of magnitude, depending on composition.

Growth of Epitaxial a-Axis and c-Axis Oriented Sr2RuO4 Films

1995 ◽  
Vol 401 ◽  
Author(s):  
S. Madhavan ◽  
B. J. Gibbons ◽  
A. Dabkowski ◽  
H. A. Dabkowska ◽  
S. Trolier-Mckinstry ◽  
...  
Keyword(s):  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Epitaxial Films ◽  
Temperature Measurements ◽  
Laser Deposition ◽  
Metallic Films ◽  
X Ray Diffraction ◽  
X Ray ◽  
Oriented Films

AbstractEpitaxial films of Sr2RuO4 have been grown in situ by pulsed laser deposition on (100) LaAlO3 and (100) LaSrGaO4 substrates. X-ray diffraction results show that the films are single domain and grow c-axis oriented on (100) LaAlO3 and a-axis oriented on (100) LaSrGaO4 substrates. X-ray ø-scans indicate epitaxial alignment of the film and substrate in-plane axes in both cases. Resistivity versus temperature measurements reveal that the as-grown c-axis oriented films are semiconducting and the a-axis oriented films are metallic. The metallic films grown so far were found to be non-superconducting down to 50 mK.

Thin Films of Semiconducting SnSi Alloys Grown by Pulsed Laser Deposition

1994 ◽  
Vol 358 ◽  
Author(s):  
Randolph E. Treece ◽  
J. S. Horwitz ◽  
D. B. Chrisey ◽  
J. Tang ◽  
R. S. Williams
Keyword(s):  
Pulsed Laser Deposition ◽  
Photoelectron Spectroscopy ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
X Rays ◽  
X Ray Diffraction ◽  
Temperature Dependent ◽  
Target Holder ◽  
X Ray ◽  
Potential Applications

ABSTRACTSemiconducting SnxSi1−x (0≤x≤0.6) thin-film alloys have been grown by pulsed laser deposition (PLD). These new materials are amorphous to X-rays and display small positive optical band gaps, suggesting potential applications in solar cells. The tin silicide films were grown by depositing very thin (1–30 Å) alternating atomic layers from individual Sn and Si targets utilizing an automated multi-target holder coupled to a conventional PLD system. The value of x was selected by controlling the thickness of the atomic layers. The films were characterized by X-ray diffraction, optical absorption, Rutherford backscattering spectroscopy, temperature-dependent resistivity, and X-ray photoelectron spectroscopy. Tin segregation is prevented by keeping the Sn layer thickness below a critical value. Compositions beyond x > 0.6 led to semimetallic SnxSi1−x films with tin crystallites.

Polydomain Structure of Epitaxial PbTiO3 films on MgO

1997 ◽  
Vol 493 ◽  
Author(s):  
S. P. Alpay ◽  
A. S. Prakash ◽  
S. Aggarwal ◽  
R. Ramesh ◽  
A. L. Roytburd ◽  
...  
Keyword(s):  
Domain Structure ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
X Ray ◽  
Theoretical Predictions ◽  
The Stability ◽  
Increasing Temperature ◽  
Stable Domains ◽  
Domain Stability

ABSTRACTA PbTiO3(001) film grown on MgO(001) by pulsed laser deposition is examined as an example to demonstrate the applications of the domain stability map for epitaxial perovskite films which shows regions of stable domains and fractions of domains in a polydomain structure. X-ray diffraction studies indicate that the film has a …c/a/c/a… domain structure in a temperature range of °C to 400°C with the fraction of c-domains decreasing with increasing temperature. These experimental results are in excellent agreement with theoretical predictions based on the stability map.

Frequency and Temperature Dependence of Dielectric Properties of Orthorhombic HoMnO3 Thin Films

2014 ◽  
Vol 1025-1026 ◽  
pp. 427-431
Author(s):  
Ping Gao ◽  
Wei Zhang ◽  
Wei Tian Wang
Keyword(s):  
Dielectric Properties ◽  
Pulsed Laser ◽  
Signal Amplitude ◽  
Debye Model ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
X Ray ◽  
Force Microscopy ◽  
Atomic Force ◽  
Cole Diagram

Orthorhombic HoMnO3 films were prepared epitaxially on Nb-doped SrTiO3 single crystal substrates by using pulsed laser deposition technique. The films showed perfectly a-axis crystallographic orientations. X-ray diffraction and atomic force microscopy were used to characterize the films. The complex dielectric properties were measured as functions of frequency (40 Hz~1 MHz) and temperature (80 K~300 K) with a signal amplitude of 50 mv. The respective dielectric relaxation peaks shifted to higher frequency as the measuring temperature increased, with the same development of real part of the complex permittivity. The cole-cole diagram was obtained according to the Debye model, and the effects of relaxation process were discussed.

Influence of LaNiO3 as an Electrode on the Properties of Ferroelectric Oxides

2000 ◽  
Vol 623 ◽  
Author(s):  
R. Kalare ◽  
M. Vedawyas ◽  
A. Kumar
Keyword(s):  
Ferroelectric Properties ◽  
Ferroelectric Thin Film ◽  
Memory Device ◽  
Epitaxial Films ◽  
Laser Deposition ◽  
Oxide Materials ◽  
X Ray Diffraction ◽  
X Ray ◽  
Potential Electrode ◽  
Ferroelectric Oxides

AbstractAn electrode plays an important role in realising a ferroelectric thin film as a potential memory device. We have investigated LaNiO3 (LNO) as a potential electrode material and evaluated the ferroelectric properties of oxide materials like strontium bismuth tantalate (SBT) and barium titanate(BT). We have successfully deposited epitaxial films of LNO on Pt coated Si(100) and LaAlO3 (LAO) substrates using the pulsed excimer laser deposition technique. We are able to grow high quality SBT and BT films on top of this LNO layer. The X-ray diffraction revealed the epitaxy of the LNO, SBT and BT films. The ferroelectric properties of SBTand BT were investigated using the RT66A ferroelectric tester.

Study of Raman Spectrum of Fe Doped CeO2 Thin Films Grown by Pulsed Laser Deposition

2010 ◽  
Vol 123-125 ◽  
pp. 375-378 ◽  
Author(s):  
Ram Prakash ◽  
Shalendra Kumar ◽  
Chan Gyu Lee ◽  
S.K. Sharma ◽  
Marcelo Knobel ◽  
...  
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Single Phase ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Fe Doping ◽  
Full Width ◽  
Deposition Technique ◽  
X Ray Diffraction ◽  
X Ray

Ce1-xFexO2 (x=0, 0.01, 0.03 and 0.0 5) thin films were grown by pulsed laser deposition technique on Si and LaAlO3 (LAO) substrates. These films were deposited in vacuum and 200 mTorr oxygen partial pressure for both the substrates. These films were characterized by x-ray diffraction XRD and Raman spectroscopy measurements. XRD results reveal that these films are single phase. Raman results show F2g mode at ~466 cm-1 and defect peak at 489 cm-1 for film that deposited on LAO substrates, full width at half maximum (FWHM) is increasing with Fe doping for films deposited on both the substrates.

The Shallow Implantation of Bismuth During the Growth of Bismuth Nanocrystals in Al2O3 by Pulsed Laser Deposition

2003 ◽  
Vol 780 ◽  
Author(s):  
A. Suárez-García ◽  
J-P. Barnes ◽  
R. Serna ◽  
A. K. Petford-Long ◽  
C. N. Afonso ◽  
...  
Keyword(s):  
Energy Density ◽  
Cross Section ◽  
Laser Energy ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Laser Energy Density ◽  
X Ray ◽  
Continuous Layer ◽  
Transmission Electron ◽  
Order Of Magnitude

AbstractThe effect of the laser energy density used to deposit Bi onto amorphous aluminum oxide (a-Al2O3) on the growth of Bi nanocrystals has been investigated using transmission electron microscopy of cross section samples. The laser energy density on the Bi target was varied by one order of magnitude (0.4 to 5 J cm-2). Across the range of energy densities, in addition to the Bi nanocrystals nucleated on the a-Al2O3 surface, a dark and apparently continuous layer appears below the nanocrystals. Energy dispersive X-ray analysis on the layer have shown it is Bi rich. The separation from the Bi layer to the bottom of the nanocrystals on top is consistent with the implantation range of Bi species in a-Al2O3. As the laser energy density increases, the implantation range has been measured to increase. The early stages of the Bi growth have been analyzed in order to determine how the Bi implanted layer develops.

Control of Crystallinity of Hydroxyapatite Sheet

2013 ◽  
Vol 583 ◽  
pp. 47-50 ◽  
Author(s):  
Masanobu Kusunoki ◽  
Taiyo Matsuda ◽  
Naoki Fujita ◽  
Yasuhiro Sakoishi ◽  
Ryou Iguchi ◽  
...  
Keyword(s):  
Cell Culture ◽  
Annealing Temperature ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
X Ray Diffraction ◽  
Free Standing ◽  
X Ray ◽  
Electric Oven ◽  
Diffraction Peaks ◽  
Conventional Annealing

A technique to control the crystallinity of hydroxyapatite (HA) was investigated for applications such as dentistry, regenerative medicine, cell culture scaffolding, and bio-sensors. An amorphous HA film was first produced by pulsed laser deposition. After deposition, it was separated from a substrate as a free-standing sheet. Annealing was then performed to control the crystallinity of the sheet. It was found that conventional annealing in an electric oven was not suitable for HA sheets, because it led to curling and cracking. Since such problems were assumed to be caused by thermal stress, annealing was next carried out with the HA sheet enclosed in HA powder in the center of a metal capsule. This method allowed annealing to be successfully carried out without causing any curling or cracking. Uniform pieces with dimensions of 10 mm × 10 mm cut from a large HA sheet were annealed at temperatures of 200 to 800 ºC and then examined using X-ray diffraction. It was found that the intensity of the diffraction peaks associated with crystalline HA changed with annealing temperature, and that the strongest peaks were observed for the sample annealed at 500 ºC. These results indicate that the crystallinity of the HA sheet can be controlled using the proposed method.

CRYSTALLINE SrTiO3 THIN FILMS ON SILICON BY PULSED LASER DEPOSITION

2005 ◽  
Vol 19 (01n03) ◽  
pp. 533-535
Author(s):  
J. H. HAO ◽  
J. GAO
Keyword(s):  
Thin Films ◽  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Perovskite Oxide ◽  
Deposition Technique ◽  
X Ray Diffraction ◽  
Rocking Curve ◽  
X Ray ◽  
Silicon Materials

We have developed a process to grow SrTiO 3 ( STO ) thin films showing single (110) orientation directly on Si by means of pulsed laser deposition technique. The growth of STO films directly on Si has been described. The crystallinity of the grown STO films was characterized by X-ray diffraction analysis of θ-2θ scan and rocking curve. Our results may be of interest for better understanding of the growth based on the perovskite oxide thin films on silicon materials.

Epitaxial Pd-Doped LaFeO3 Films Grown on (100) SrTiO3 by Pulsed Laser Deposition

2014 ◽  
Vol 936 ◽  
pp. 282-286
Author(s):  
Ying Wen Duan
Keyword(s):  
Pulsed Laser Deposition ◽  
Pulsed Laser ◽  
Film Surface ◽  
Laser Deposition ◽  
Structural Quality ◽  
Deposition Technique ◽  
X Ray Diffraction ◽  
Orientation Relationships ◽  
X Ray ◽  
Transmission Electron

Single-crystalline, epitaxial LaFeO3 films with 5 at. % substitution of Pd on the Fe site are grown on (100) SrTiO3 substrate by pulsed-laser deposition technique. The epitaxial orientation relationships are (110)[001]LFPO||(100)[001]STO. X-ray diffraction and transmission electron microscopy reveal that the LFPO films have high structural quality and an atomically sharp LFPO/STO interface. After reduction treatments of as-grown LFPO films, very little Pd escaped the LFPO lattice onto the film surface, the formed Pd (100) particles are oriented epitaxially, and parallel to the LFPO films surface.

Sign in / Sign up

Export Citation Format

Share Document