Temperature Control in High Performance Concrete

2015 ◽  
Vol 1100 ◽  
pp. 162-165
Author(s):  
Martin Sedlmajer ◽  
Jiri Zach ◽  
Jitka Peterková ◽  
Lenka Bodnárová
Keyword(s):  
High Temperature ◽  
Temperature Distribution ◽  
Heat Source ◽  
High Temperatures ◽  
Temperature Control ◽  
High Performance ◽  
High Performance Concrete ◽  
Cement Composites ◽  
Fire Temperature ◽  
Temperature Observation

The paper addresses the methodology of temperature observation of cement composites, such as concrete. It is mainly the monitoring of the course of hydration temperature and the possibilities of its regulation. Subsequently, the observation of temperature within samples which are exposed to high temperatures. Attention is paid to a variety of temperatures of a concrete segment which is being acted upon by a high-temperature source, e.g. fire. Temperature distribution at a varied distance from the heat source is observed.

scholarly journals Durability of High Performance Concrete (HPC) Subject to Fire Temperature Impact

2016 ◽  
Vol 62 (4) ◽  
pp. 73-94 ◽  
Author(s):  
W. Jackiewicz-Rek ◽  
T. Drzymała ◽  
A. Kuś ◽  
M. Tomaszewski
Keyword(s):  
High Temperature ◽  
High Performance ◽  
High Performance Concrete ◽  
Water Impact ◽  
Fire Temperature ◽  
Extreme Loads ◽  
Concrete Properties ◽  
Concrete Mix ◽  
Temperature Impact ◽  
Aeration Process

AbstractIn the recent years a tendency for design of increasingly slender structures with the use of high performance concrete has been observed. Moreover, the use of high performance concrete in tunnel structures, subject to high loads with possibility of extreme loads occurrence such as fire, has an increasing significance.Presented studies aimed at improving high performance concrete properties in high temperature conditions (close to fire conditions) by aeration process, and determining high temperature impact on the concretes features related to their durability.In this paper it has been proven that it is possible to obtain high performance concretes resistant to high temperatures, and additionally that modification of the concrete mix with aerating additive does not result in deterioration of concrete properties when subject to water impact in various form.

scholarly journals Behaviour of high-performance concrete at high temperatures: some highlights

2017 ◽  
Vol 2 ◽  
pp. 45-52 ◽  
Author(s):  
Pierre Pimienta ◽  
Maria Cruz Alonso ◽  
Robert Jansson McNamee ◽  
Jean-Christophe Mindeguia
Keyword(s):  
High Temperature ◽  
High Temperatures ◽  
High Performance ◽  
High Performance Concrete ◽  
State Of The Art ◽  
Technical Committee ◽  
Rilem Technical Committee ◽  
Civil Structures ◽  
Physicochemical Changes ◽  
Materials Used

High-performance concrete (HPC) is one of the most recent types of concrete among the materials used routinely in building and civil structures. Their development in structures applications and the growing need for the justification of their fire resistance has led several laboratories to carry out research on their properties at high temperature. This letter presents some main aspects related to their physicochemical changes, thermal properties and mechanical properties at high temperature. It introduces a State of The Art prepared by the RILEM Technical Committee 227-HPB (Physical properties and behaviour of High-Performance Concrete at high temperature) and untitled “Behaviour of High-Performance Concrete at high temperatures”. This State of the Art will be publish in a next future.

scholarly journals Effects of Combined Usage of Supplementary Cementitious Materials on the Thermal Properties and Microstructure of High-Performance Concrete at High Temperatures

Materials ◽  
2020 ◽  
Vol 13 (8) ◽  
pp. 1833 ◽  
Author(s):  
Dong Lu ◽  
Zhuo Tang ◽  
Liang Zhang ◽  
Jianwei Zhou ◽  
Yue Gong ◽  
...  
Keyword(s):  
Thermal Conductivity ◽  
High Temperature ◽  
Fly Ash ◽  
High Temperatures ◽  
High Performance ◽  
High Performance Concrete ◽  
Cementitious Materials ◽  
Supplementary Cementitious Materials ◽  
Amorphous Phases ◽  
Micro Cracks

Concrete has low porosity and compact microstructure, and thus can be vulnerable to high temperature, and the increasing application of various types of supplementary cementitious materials (SCMs) in concrete makes its high-temperature resistant behavior more complex. In this study, we investigate the effects of four formulations with typical SCMs combinations of fly ash (FA), ultra-fine fly ash (UFFA) and metakaolin (MK), and study the effects of SCMs combinations on the thermal performance, microstructure, and the crystalline and amorphous phases evolution of concrete subjected to high temperatures. The experimental results showed that at 400 °C, with the addition of 20% FA (wt %), the thermal conductivity of the sample slightly increased to 1.5 W/(m·K). Replacing FA with UFFA can further increase the thermal conductivity to 1.7 W/(m·K). Thermal conductivity of concrete slightly increased at 400 °C and significantly reduced at 800 °C. Further, combined usage of SCMs delayed and reduced micro-cracks of concrete subjected to high temperatures. This study demonstrates the potential of combining the usage of SCMs to promote the high-temperature performance of concrete and explains the micro-mechanism of concrete containing SCMs at high temperatures.

scholarly journals Insight into the Mechanical Performance of the UHPC Repaired Cementitious Composite System after Exposure to High Temperatures

Materials ◽  
2021 ◽  
Vol 14 (15) ◽  
pp. 4095
Author(s):  
Qing Chen ◽  
Zhiyuan Zhu ◽  
Rui Ma ◽  
Zhengwu Jiang ◽  
Yao Zhang ◽  
...  
Keyword(s):  
Compressive Strength ◽  
High Temperature ◽  
High Temperatures ◽  
Bonding Strength ◽  
Composite System ◽  
Mechanical Performance ◽  
High Performance Concrete ◽  
Interfacial Structure ◽  
Cementitious Composite ◽  
Average Percentage

In this paper, the mechanical performance of an ultra-high-performance concrete (UHPC) repaired cementitious composite system, including the old matrix and the new reinforcement (UHPC), under various high temperature levels (20 °C, 100 °C, 300 °C, and 500 °C) was studied. In this system, UHPC reinforced with different contents of steel fibers and polypropylene (PP) fibers was utilized. Moreover, the physical, compressive, bonding, and flexural behaviors of the UHPC repaired system after being exposed to different high temperatures were investigated. Meanwhile, X-ray diffraction (XRD), baseline evaluation test (BET), and scanning electron microscope (SEM) tests were conducted to analyze the effect of high temperature on the microstructural changes in a UHPC repaired cementitious composite system. Results indicate that the appearance of the bonded system changed, and its mass decreased slightly. The average percentage of residual mass of the system was 99.5%, 96%, and 94–95% at 100 °C, 300 °C, and 500 °C, respectively. The residual compressive strength, bonding strength, and flexural performance improved first and then deteriorated with the increase of temperature. When the temperature reached 500 °C, the compressive strength, bonding strength, and flexural strength decreased by about 20%, 30%, and 15% for the UHPC bonded system, respectively. Under high temperature, the original components of UHPC decreased and the pore structure deteriorated. The cumulative pore volume at 500 °C could reach more than three times that at room temperature (about 20 °C). The bonding showed obvious deterioration, and the interfacial structure became looser after exposure to high temperature.

Temperature Control and Anti-Cracking Measures for a High-Performance Concrete Aqueduct

2013 ◽  
Vol 405-408 ◽  
pp. 2739-2742 ◽  
Author(s):  
Zhen Hong Wang ◽  
Shu Ping Yu ◽  
Yi Liu
Keyword(s):  
Temperature Control ◽  
Temperature Difference ◽  
High Performance ◽  
High Performance Concrete ◽  
Concrete Structures ◽  
Apparent Temperature ◽  
Mass Concrete ◽  
Water Pipe ◽  
Thin Walled ◽  
Water Pipe Cooling

To solve the problem of cracks developing on thin-walled concrete structures during construction, the authors expound on the causes of cracks and the crack mechanism. The difference between external and internal temperatures, basic temperature difference and constraints are the main reasons of crack development on thin-walled concrete structures. Measures such as optimizing concrete mixing ratio, improving construction technology, and reducing temperature difference can prevent thin-walled concrete structures from cracking. Moreover, water-pipe cooling technology commonly used in mass concrete can be applied to thin-walled concrete structures to reduce temperature difference. This method is undoubtedly a breakthrough in anti-cracking technology for thin-walled concrete structures, particularly for thin-walled high-performance concrete structures. In addition, a three-dimensional finite element method is adopted to simulate the calculation of temperature control and anti-cracking effects f. Results show the apparent temperature controlling effect of water-pipe cooling for thin-walled concrete structures.

High Temperature Composite of Aluminous Cement with Addition of Metakaolin and Ground Bricks Dust

2013 ◽  
Vol 486 ◽  
pp. 406-411 ◽  
Author(s):  
Ondřej Holčapek ◽  
Pavel Reiterman ◽  
Petr Konvalinka
Keyword(s):  
Mechanical Properties ◽  
High Temperature ◽  
High Temperatures ◽  
Raw Materials ◽  
Cement Composites ◽  
Basalt Fibers ◽  
Aluminous Cement ◽  
The Common ◽  
Temperature Exposure ◽  
Sufficient Strength

The following article deals with the study of mechanical properties of aluminous cement composites exposure to high temperatures. The newly designed mixtures that resist the action of high temperatures 1000 °C find their application in various fields of industrial production or in the form of fire wall for protection bearing structures. All the mechanical properties such as compressive strength and tensile strength in bending were measured on samples 160x40x40 mm. These samples were exposed to temperatures 600 °C and 1000 °C and one group of samples was reference and stayed in laboratory condition. Aluminous cement unlike the common Portland cement keeps sufficient strength even after high temperature exposure. For ensuring required ductility the basalt fibers were added to the mixture. In an effort to use of secondary raw materials as a replacement for cement as well as a suitable binder was used metakaolin and ground brick dust. Very convenient characteristics of these components are their latent hydraulic potential that makes interesting hydration products.

Material Properties of Ultra - High Performance Concrete in Extreme Conditions

2016 ◽  
Vol 711 ◽  
pp. 157-162 ◽  
Author(s):  
David Citek ◽  
Milan Rydval ◽  
Stanislav Rehacek ◽  
Jiří Kolísko
Keyword(s):  
Mechanical Properties ◽  
High Temperature ◽  
Material Properties ◽  
High Performance ◽  
High Performance Concrete ◽  
High Strength ◽  
Accurate Information ◽  
Extreme Conditions ◽  
Ultra High Performance Concrete ◽  
Freeze Thaw

The Ultra High Performance Concrete (UHPC) is a very promising material suitable for application in special structures. However, the knowledge of performance of this relatively new material is rather limited. The exceptional mechanical properties of UHPC allow for a modification of the design rules, which are applicable in ordinary or high strength concrete. This paper deals in more detail with impact of thermal stress on bond properties between prestressing strands and UHPC and an influence of high temperature to final material properties of different UHPC mixtures. Specimens in the first experimental part were subjected to the cycling freeze-thaw testing. The relationship between bond behavior of both type of material (UHPC and ordinary concrete) and effect of cycling freeze-thaw tests was investigated. The second part of experimental work was focused on mechanical properties of UHPC exposure to the high temperature (Tmax = 200°C to Tmax = 1000°C). Tested mechanical properties were compressive and flexural strengths, the fracture properties will be presented in the next paper. The obtained experimental data serve as a basis for further systematic experimental verification and more accurate information about the significantly higher material properties of UHP(FR)C and its behavior in extreme conditions.

Sign in / Sign up

Export Citation Format