High Strength Offshore Steel with Excellent Weldability

2012 ◽  
Vol 482-484 ◽  
pp. 1650-1653
Author(s):  
Yan Tang Chen ◽  
Kai Guang Zhang
Keyword(s):  
Mechanical Properties ◽  
Impact Toughness ◽  
Yield Strength ◽  
Thermal Cycle ◽  
Hsla Steel ◽  
High Strength ◽  
High Impact ◽  
Weld Thermal Cycle ◽  
Offshore Engineering ◽  
Base Steel

A new high strength low alloy (HSLA) steel in 370MPa yield strength grade with low susceptivity to weld cold cracking has been developed for offshore engineering. The microstructure feature of base steel and weld heat affected zone (HAZ) has been investigated. The systematic studies showed that the developed steel exhibited high strength(yield strength≥370MPa)、high impact toughness and excellent weldability. The complex inclusions containing fine oxides in HAZ promoted the acicular ferrite formation in weld thermal cycle and resulted in desired mechanical properties of HAZ.

Design of a novel HSLA steel with a combination of high strength (140–160 ksi) and excellent toughness

2021 ◽  
Vol 112 (10) ◽  
pp. 800-811
Author(s):  
Mehdi Soltan Ali Nezhad ◽  
Sadegh Ghazvinian ◽  
Mahmoud Amirsalehi ◽  
Amir Momeni
Keyword(s):  
Impact Toughness ◽  
Yield Strength ◽  
Hsla Steel ◽  
Charpy Impact ◽  
High Strength ◽  
Controlled Rolling ◽  
The Other ◽  
Grain Structure ◽  
Charpy Impact Toughness ◽  
Fine Grain

Abstract Three steels were designed based on HSLA-100 with additional levels of Mn, Ni, Cr and Cu. The steels were prepared by controlled rolling and tempered at temperatures in range of 550–700°C. The continuous cooling time curves were shifted to longer times and lower temperatures with the increased tendency for the formation of martensite at lower cooling rates. The microstructures revealed that controlled rolling results in austenite with uniform fine grain structure. The steel with the highest amount of Mn showed the greatest strength after tempering at 750 °C. The top strength was attributed to the formation of Cu-rich particles. The steel with 1.03 wt.% Mn, tempered at 650 °C exhibited the best Charpy impact toughness at –85°C. On the other hand, the steel that contained 2.11 wt.% Mn and tempered at 700 °C showed the highest yield strength of 1 097.5 MPa (∼159 ksi) and an impact toughness of 41.6 J at –85°C.

scholarly journals Effect of enhanced weld cooling on the mechanical properties of a structural steel with a yield strength of 700 MPa

2020 ◽  
Vol 2 (11) ◽  
Author(s):  
Juhani Laitila ◽  
Lassi Keränen ◽  
Jari Larkiola
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Fatigue Strength ◽  
Impact Toughness ◽  
Yield Strength ◽  
Uniform Elongation ◽  
High Strength ◽  
Low Alloy Steel ◽  
External Cooling ◽  
Welding Processes

AbstractIn this study, we present the effect of enhanced cooling on the mechanical properties of a high-strength low-alloy steel (having a yield strength of 700 MPa) following a single-pass weld process. The properties evaluated in this study include uniform elongation, impact toughness, yield, tensile and fatigue strengths alongside the cooling time of the weld. With the steel used in this study, the enhanced cooling resulted in a weld joint characterized with excellent cross-weld uniform elongation, yield and fatigue strength. The intensified cooling reduced the time it takes for the weld to reach 100 °C by around 190 s. Not only the fusion line of the weld was less pronounced, but also the grain size of the CGHAZ was greatly refined as a result of the enhanced cooling. The results indicate that combining external cooling to the welding processes can be beneficial for the studied high-strength steel.

RUUKKI RAEX 300

Alloy Digest ◽  
2012 ◽  
Vol 61 (2) ◽  
Keyword(s):  
Fracture Toughness ◽  
Wear Resistance ◽  
Shear Strength ◽  
Impact Toughness ◽  
Yield Strength ◽  
Physical Properties ◽  
Tensile Properties ◽  
High Strength ◽  
Structural Components ◽  
Wear Resistant

Abstract RUUKKI RAEX 300 (typical yield strength 900 MPa) is part of the Raex family of high-strength and wear-resistant steels with favorable hardness and impact toughness to extend life and decrease wear in structural components. This datasheet provides information on composition, physical properties, hardness, elasticity, tensile properties, and shear strength as well as fracture toughness. It also includes information on wear resistance as well as forming, machining, and joining. Filing Code: SA-643. Producer or source: Rautaruukki Corporation.

scholarly journals Overview of HSS Steel Grades Development and Study of Reheating Condition Effects on Austenite Grain Size Changes

Materials ◽  
2021 ◽  
Vol 14 (8) ◽  
pp. 1988
Author(s):  
Tibor Kvackaj ◽  
Jana Bidulská ◽  
Róbert Bidulský
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
High Strength Steel ◽  
Single Phase ◽  
Hsla Steel ◽  
High Strength ◽  
Strength Properties ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Steel Grades

This review paper concerns the development of the chemical compositions and controlled processes of rolling and cooling steels to increase their mechanical properties and reduce weight and production costs. The paper analyzes the basic differences among high-strength steel (HSS), advanced high-strength steel (AHSS) and ultra-high-strength steel (UHSS) depending on differences in their final microstructural components, chemical composition, alloying elements and strengthening contributions to determine strength and mechanical properties. HSS is characterized by a final single-phase structure with reduced perlite content, while AHSS has a final structure of two-phase to multiphase. UHSS is characterized by a single-phase or multiphase structure. The yield strength of the steels have the following value intervals: HSS, 180–550 MPa; AHSS, 260–900 MPa; UHSS, 600–960 MPa. In addition to strength properties, the ductility of these steel grades is also an important parameter. AHSS steel has the best ductility, followed by HSS and UHSS. Within the HSS steel group, high-strength low-alloy (HSLA) steel represents a special subgroup characterized by the use of microalloying elements for special strength and plastic properties. An important parameter determining the strength properties of these steels is the grain-size diameter of the final structure, which depends on the processing conditions of the previous austenitic structure. The influence of reheating temperatures (TReh) and the holding time at the reheating temperature (tReh) of C–Mn–Nb–V HSLA steel was investigated in detail. Mathematical equations describing changes in the diameter of austenite grain size (dγ), depending on reheating temperature and holding time, were derived by the authors. The coordinates of the point where normal grain growth turned abnormal was determined. These coordinates for testing steel are the reheating conditions TReh = 1060 °C, tReh = 1800 s at the diameter of austenite grain size dγ = 100 μm.

Physical Simulation of Weldability of Weldox 1300 Steel

2013 ◽  
Vol 762 ◽  
pp. 551-555 ◽  
Author(s):  
Marek Stanislaw Węglowski ◽  
Marian Zeman ◽  
Miroslaw Lomozik
Keyword(s):  
Mechanical Properties ◽  
Impact Toughness ◽  
Physical Simulation ◽  
High Strength ◽  
Parent Material ◽  
Cooling Time ◽  
Electron Microscopies ◽  
Transmission Electron ◽  
Transformation Diagrams ◽  
The Impact

In the present study, the investigation of weldability of new ultra-high strength - Weldox 1300 steel has been presented. The thermal simulated samples were used to investigate the effect of welding cooling time t8/5 on the microstructure and mechanical properties of the heat affected zone (HAZ). In the frame of these investigation the microstructure was studied by the light (LM) and transmission electron microscopies (TEM). It has been shown that the microstructure of the Weldox 1300 steel is composed of tempered martensite, and inside the laths the minor precipitations mainly V(CN) and molybdenum carbide Mo2C were observed. Mechanical properties of parent material were analysed by the tensile, impact and hardness tests. In details the influence of cooling time in the range of 2,5 - 300 s. on hardness, impact toughness and microstructure of simulated HAZ was studied by using welding thermal simulation test. The results show that the impact toughness and hardness decrease with the increase of t8/5 under the condition of a single thermal cycle in simulated HAZ. The continuous cooling transformation diagrams (CCT-W for welding conditions) of Weldox 1300 steel for welding purposes was also elaborated. The steel Weldox 1300 for cooling time in the range of 2,5 - 4 s showed martensite microstructure, for time from 4 s to 60 s mixture of martensite and bainite, and for longer cooling time mixture of ferrite, bainite and martensite. The results indicated that the weldability of Weldox 1300 steel is limited and to avoid the cold cracking the preheating procedure or medium net linear heat input should be used.

Effect of weld thermal cycle on behaviour of Ti–Nb carbonitrides in HSLA steel

1989 ◽  
Vol 5 (10) ◽  
pp. 1034-1036 ◽  
Author(s):  
J. T. Bowker ◽  
J. Ng-Yelim ◽  
T. F. Malis
Keyword(s):  
Thermal Cycle ◽  
Hsla Steel ◽  
Weld Thermal Cycle

Paradox of Strength and Ductility in Metals Processed Bysevere Plastic Deformation

2002 ◽  
Vol 17 (1) ◽  
pp. 5-8 ◽  
Author(s):  
R. Z. Valiev ◽  
I. V. Alexandrov ◽  
Y. T. Zhu ◽  
T. C. Lowe
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Grain Size ◽  
Yield Strength ◽  
Mechanical Behavior ◽  
High Strength ◽  
High Ductility ◽  
Elongation To Failure ◽  
Failure Ductility ◽  
Strength And Ductility

It is well known that plastic deformation induced by conventional forming methodssuch as rolling, drawing or extrusion can significantly increase the strength of metalsHowever, this increase is usually accompanied by a loss of ductility. For example, Fig.1 shows that with increasing plastic deformation, the yield strength of Cu and Almonotonically increases while their elongation to failure (ductility) decreases. Thesame trend is also true for other metals and alloys. Here we report an extraordinarycombination of high strength and high ductility produced in metals subject to severeplastic deformation (SPD). We believe that this unusual mechanical behavior is causedby the unique nanostructures generated by SPD processing. The combination ofultrafine grain size and high-density dislocations appears to enable deformation by newmechanisms. This work demonstrates the possibility of tailoring the microstructures ofmetals and alloys by SPD to obtain both high strength and high ductility. Materialswith such desirable mechanical properties are very attractive for advanced structuralapplications.

Study on Non-Halogen Flame-Retarded HIPS with High Strength HIPS

2008 ◽  
Vol 47-50 ◽  
pp. 1245-1249
Author(s):  
Zhong Wei Wu ◽  
Qing Jie Jiao ◽  
Chong Guang Zang ◽  
Hui Lan
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Impact Strength ◽  
High Strength ◽  
High Impact ◽  
High Impact Polystyrene ◽  
Flame Retarded ◽  
Notch Impact Strength

PPO was a better intensifier and charred material for High-impact polystyrene (HIPS), it could make HIPS achieve UL94V-0 with APP, MC, RDP. Especially, RDP not only improved the flame-retarded property but also controlled the hole producing, and had the best consistent with matrix which could improve the mechanical properties. SBS and SEBS were better consistent with matrix, especially SEBS was tiny granule, which could be dispersed in matrix easily. The properties of SEBS toughened the non-halogen flame-retarded HIPS was followed: tensile strength: 18.83MPa; izod notch impact strength: 15.7kJ/m2; UL94V-0.

Sign in / Sign up

Export Citation Format

Share Document