Study on the Crystallinity and Mechanical Properties of PC/PLA/LLDPE/ Montmorillonite Blends

2013 ◽  
Vol 739 ◽  
pp. 38-41
Author(s):  
Yi Chen ◽  
Yue Peng ◽  
Wen Yong Liu ◽  
Guang Sheng Zeng ◽  
Xiang Gang Li ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Lactic Acid ◽  
Impact Strength ◽  
High Performance ◽  
Impact Resistance ◽  
Low Density Polyethylene ◽  
Poly Lactic Acid ◽  
Low Density ◽  
Linear Low Density Polyethylene ◽  
Elongation At Break

Polycarbonate/poly (lactic acid)/(PC/PLA) blend is a kind of novel potential material for introducing the degradability of PLA to high performance PC. However, the bad compatibility between PC and PLA results in poor impact resistance and strength, which limits its applications. For resolving the problem, linear low density polyethylene (LLDPE) was added into blend to improve the mechanical properties, especially the toughness. Meantime, nanosized montmorillonite was also used as an additive for modifying the blend. The results showed that the the tensile and impact strength, the elongation at break of PC/PLA all be improved with the increase of LLDPE, the nanosized montmorillonite could also increase the strength of blends when the content is lower than wt5% of blends.

scholarly journals Low-Temperature Mechanical Properties of High-Density and Low-Density Polyethylene and Their Blends

Polymers ◽  
2021 ◽  
Vol 13 (11) ◽  
pp. 1821
Author(s):  
Ildar I. Salakhov ◽  
Nadim M. Shaidullin ◽  
Anatoly E. Chalykh ◽  
Mikhail A. Matsko ◽  
Alexey V. Shapagin ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Low Temperature ◽  
Impact Strength ◽  
Relative Elongation ◽  
High Density ◽  
Low Density Polyethylene ◽  
Low Density ◽  
Elongation At Break ◽  
Subzero Temperatures ◽  
Izod Impact

Low-temperature properties of high-density polyethylene (HDPE), low-density polyethylene (LDPE), linear low-density polyethylene (LLDPE), and their blends were studied. The analyzed low-temperature mechanical properties involve the deformation resistance and impact strength characteristics. HDPE is a bimodal ethylene/1-hexene copolymer; LDPE is a branched ethylene homopolymer containing short-chain branches of different length; LLDPE is a binary ethylene/1-butene copolymer and an ethylene/1-butene/1-hexene terpolymer. The samples of copolymers and their blends were studied by gel permeation chromatography (GPC), differential scanning calorimetry (DSC), 13С NMR spectroscopy, and dynamic mechanical analysis (DMA) using testing machines equipped with a cryochamber. It is proposed that such parameters as “relative elongation at break at −45 °C” and “Izod impact strength at −40 °C” are used instead of the ductile-to-brittle transition temperature to assess frost resistance properties because these parameters are more sensitive to deformation and impact at subzero temperatures for HDPE. LLDPE is shown to exhibit higher relative elongation at break at −45 °C and Izod impact strength at −20 ÷ 60 °C compared to those of LDPE. LLDPE terpolymer added to HDPE (at a content ≥ 25 wt.%) simultaneously increases flow properties and improves tensile properties of the blend at −45 °C. Changes in low-temperature properties as a function of molecular weight, MWD, crystallinity, and branch content were determined for HDPE, LLDPE, and their blends. The DMA data prove the resulting dependences. The reported findings allow one to understand and predict mechanical properties in the HDPE–LLDPE systems at subzero temperatures.

Mechanical and Morphological Behavior of Blends Obtained from Biopolymers (PLA/PLC)

2014 ◽  
Vol 775-776 ◽  
pp. 24-28
Author(s):  
Taciana Regina de Gouveia Silva ◽  
Bartira Brandão da Cunha ◽  
Pankaj Agrawal ◽  
Edcleide Maria Araújo ◽  
Tomás Jefférson Alves de Mélo
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Lactic Acid ◽  
Elastic Modulus ◽  
Impact Strength ◽  
Polymer Blends ◽  
Poly Lactic Acid ◽  
Elongation At Break ◽  
Morphology Analysis ◽  
Morphological Behavior

In this work, the effect of the PCL content and E-GMA compatibilizer on the mechanical properties and morphology of poly (lactic acid) - PLA/ poly (ε-caprolactone)-PCL blends was investigated. The results of the mechanical properties showed that there was a reduction in the elastic modulus and tensile strength when PCL was added to PLA. The decrease in the modulus was more pronounced when the PCL content was increased from 10 to 20% (wt). The PLA/PCL/E-GMA blend showed the lower modulus and tensile strength. This blend also presented the higher elongation at break and impact strength. The morphology analysis by SEM showed that the PLA/PCL blends where characterized by lack of adhesion between the PLA and PCL phases. The presence of E-GMA in the PLA/PCL/E-GMA blend improved the adhesion between the PLA and PCL phases.Keywords: poly (latic acid); poly (ε-caprolactone); polymer blends; compatibilizer

Phase Structure of Compatibilized Poly(Lactic Acid)/Linear Low-Density Polyethylene Blends

2009 ◽  
Vol 48 (4) ◽  
pp. 823-833 ◽  
Author(s):  
Zhizhong Su ◽  
Qiuying Li ◽  
Yongjun Liu ◽  
Haiyan Xu ◽  
Weihong Guo ◽  
...  
Keyword(s):  
Lactic Acid ◽  
Phase Structure ◽  
Low Density Polyethylene ◽  
Poly Lactic Acid ◽  
Low Density ◽  
Linear Low Density Polyethylene ◽  
Polyethylene Blends

scholarly journals Recycling of Mixed Poly(Ethylene-terephthalate) and Poly(Lactic Acid)

2019 ◽  
Vol 253 ◽  
pp. 02005
Author(s):  
Daniel Gere ◽  
Tibor Czigany
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Lactic Acid ◽  
Impact Strength ◽  
Ethylene Terephthalate ◽  
Poly Lactic Acid ◽  
Elongation At Break ◽  
Poly Ethylene Terephthalate ◽  
Poly Ethylene ◽  
Thermal Stability Of

Nowadays, PLA is increasingly used as a packaging material, therefore it may appear in the petrol-based polymer waste stream. However, with the today’s mechanical recycling technologies PLA and PET bottles cannot be easily or cheaply separated. Therefore, our goal was to investigate the mechanical, morphological and thermal properties of different PET and PLA compounds in a wide range of compositions. We made different compounds from poly(ethylene-terephthalate) (PET) and poly(lactic acid) (PLA) by extrusion, and injection molded specimens from the compounds. We investigated the mechanical properties and the phase morphology of the samples and the thermal stability of the regranulates. PET and PLA are thermodynamically immiscible, therefore we observed a typical island-sea type morphology in SEM micrographs. When PLA was added, the mechanical properties (tensile strength, modulus, elongation at break and impact strength) changed significantly. The Young’s modulus increased, while elongation at break and impact strength decreased with the increase of the weight fraction of PLA. The TGA results indicated that the incorporation of PLA decreased the thermal stability of the PET/PLA blends.

Effect of CaCO3 Particle Size and Size Distribution on Rheological and Mechanical Properties of Polyethylene

2013 ◽  
Vol 734-737 ◽  
pp. 2252-2255
Author(s):  
Fang Wei Qi ◽  
Xue Gang Luo ◽  
Xiao Yan Lin ◽  
Si Zhao Zhang
Keyword(s):  
Mechanical Properties ◽  
Thermal Decomposition ◽  
Particle Size ◽  
Glass Transition ◽  
Size Distribution ◽  
Low Density Polyethylene ◽  
Low Density ◽  
Linear Low Density Polyethylene ◽  
Elongation At Break ◽  
Chain Mobility

In this article, calcium carbonate filled linear low density polyethylene (LLDPE) was prepared and the influences of particle size and size distribution on the rheological and mechanical properties of the composites were investigated. The results showed that the glass transition and thermal decomposition temperatures of LLDPE phase in LLDPE/CaCO3composites were shifted toward higher temperatures by the restriction of CaCO3particles on the segmental and long-range chain mobility of the LLDPE phase. The composites showed shear thinning behaviors and the viscosity decreased with the rational size and size distribution. Additionally, the elongation at break notably improved to some extent.

Mechanical, morphological and thermal properties of linear low density polyethylene/poly(lactic acid) blends

2018 ◽  
Author(s):  
Engku Zaharah Engku Zawawi ◽  
Dzaraini Kamarun ◽  
Rozana Mohd Dahan ◽  
Nor Haleeda Mohammad Adzhar
Keyword(s):  
Lactic Acid ◽  
Thermal Properties ◽  
Low Density Polyethylene ◽  
Poly Lactic Acid ◽  
Low Density ◽  
Linear Low Density Polyethylene
Sign in / Sign up

Export Citation Format

Share Document