Design and Manufacturing of Si-Based Non-Oxide Cellular Ceramic Structures through Indirect 3D Printing

Additive manufacturing of Polymer-Derived Ceramics (PDCs) is regarded as a disruptive fabrication process that includes several technologies such as light curing and ink writing. However, 3D printing based on material extrusion is still not fully explored. Here, an indirect 3D printing approach combining Fused Deposition Modeling (FDM) and replica process is demonstrated as a simple and low-cost approach to deliver complex near-net-shaped cellular Si-based non-oxide ceramic architectures while preserving the structure. 3D-Printed honeycomb polylactic acid (PLA) lattices were dip-coated with two preceramic polymers (polyvinylsilazane and allylhydridopolycarbosilane) and then converted by pyrolysis respectively into SiCN and SiC ceramics. All the steps of the process (printing resolution and surface finishing, cross-linking, dip-coating, drying and pyrolysis) were optimized and controlled. Despite some internal and surface defects observed by topography, 3D-printed materials exhibited a retention of the highly porous honeycomb shape after pyrolysis. Weight loss, volume shrinkage, roughness and microstructural evolution with high annealing temperatures are discussed. Our results show that the sacrificial mold-assisted 3D printing is a suitable rapid approach for producing customizable lightweight highly stable Si-based 3D non-oxide ceramics.

Phase Formation and the Electrical Properties of YSZ/rGO Composite Ceramics Sintered Using Silicon Carbide Powder Bed

Fully stabilized zirconia/graphene composites are very promising advanced structural materials having mixed ion–electron conductivity for energy storage and energy conversion applications. The existing methods of the composite manufacturing have a number of disadvantages that limit their practical use. Thus, the search for new sintering methods is an actively developing area. In this work, we report for the first time the application of the SiC powder bed sintering technique for fully stabilized zirconia (YSZ) composite fabrication. The reduced graphene oxide (rGO) was used as a graphene derivative. As a result, well-formed ceramics with high density and crystallinity, the maximal microhardness of 13 GPa and the values of the ionic conductivity up to 10−2 S/cm at 650 °C was obtained. The effects of the sintering conditions and rGO concentration on the microstructure and conductivities of ceramics are discussed in detail. The suggested powder bed sintering technique in a layered graphite/SiC/graphite powder bed allowed well-formed dense YSZ/rGO ceramics fabrication and can become a suitable alternative to existing methods for various oxide ceramic matrix composite fabrication: both conventional sintering and non-equilibrium (SPS, flash sintering) approaches.

Synthesis and Characterization of Barium-Iron Oxide Based Neodymium, Gadolinium and Praseodymium Doped Ceramic Materials

Neodymium, gadolinium, and praseodymium doped barium-iron oxide ceramic materials were synthesized by polymeric precursor method. No carbon contents or the moisture was observed in infrared spectra of the ceramics. Neodymium and gadolinium doped ceramics were crystallized in cubic lattice form, while praseodymium doped ceramic was formed in hexagonal lattice. Same results were observed from SEM images, Neodymium and gadolinium doped ceramics had similar morphological structures, but praseodymium doped ceramics had slightly different morphology. Neodymium and gadolinium doped ceramics consisted of grain-like structure, while praseodymium doped ceramic material consisted of both grain-like and pillar-like crystal structures.

Toughening Mechanism Analysis of Recycled Rubber-Based Composites Reinforced with Glass Bubbles, Glass Fibers and Alumina Fibers

Recycling of materials attracts considerable attention around the world due to environmental and economic concerns. Recycled rubber is one of the most commonly used recyclable materials in a number of industries, including automotive and aeronautic because of their low weight and cost efficiency. In this research, devulcanized recycled rubber-based composites are designed with glass bubble microsphere, short glass fiber, aluminum chip and fine gamma alumina fiber (γ-Al2O3) reinforcements. After the determination of the reinforcements with matrix, bending strength and fracture characteristics of the composite are investigated by three-point bending (3PB) tests. Halpin–Tsai homogenization model is adapted to the rubber-based composites to estimate the moduli of the composites. Furthermore, the relevant toughening mechanisms for the most suitable reinforcements are analyzed and stress intensity factor, KIc and critical energy release rate, GIc in mode I are determined by 3PB test with single edge notch specimens. In addition, 3PB tests are simulated by finite element analysis and the results are compared with the experimental results. Microstructural and fracture surfaces analysis are carried out by means of scanning electron microscopy (SEM). Mechanical test results show that the reinforcement with glass bubbles, aluminum oxide ceramic fibers and aluminum chips generally increase the fracture toughness of the composites.

In-vitro & In-vivo Investigation of the Silicon Nitride Ceramic Hip Implant’s Safety and Effectiveness Evaluation

Background: With regard to the ceramic hip joint implant, given the concerns in ceramic about the alumina brittleness and zirconia instability, is there any alternative material solution for the orthopaedic implant? Beyond the metastable oxide ceramics, along the echelon of advanced technical ceramics, looking at the non-oxide ceramic, the silicon nitride could be an excellent candidate for the joint implant’s application. The purpose of this study is to investigate the safety, effectiveness and to demonstrate the potential of this silicon nitride hip implant. Methods: According to the related ISO (International Organization for Standardization) standards, a series of in-vitro (nine) & in-vivo (five) tests, which had been accomplished for the aforementioned aim. Especially, the total hip replacement in pigs had been achieved, as per the authors’ knowledge, this is the first time to apply the THA (Total Hip Arthroplasty) in the big animal. Results: Refer to the ISO 6474-2, in comparison with the current monopolized German product, this silicon nitride ceramic hip implant has high strength, high hardness, excellent fracture toughness, lower density, better wear resistance, good biocompatibility, inherent stability, corrosion resistance and bioactivity, bone integration capability. Conclusions: This silicon nitride ceramic will be an admirable alternative solution with superior comprehensive property that can withstand the toughest conditions in the most demanding applications like in orthopedic and beyond.