Emerging Opportunities in Manufacturing Bulk Soft-Magnetic Alloys for Energy Applications: A Review

Soft-magnetic alloys exhibit exceptional functional properties that are beneficial for a variety of electromagnetic applications. These alloys are conventionally manufactured into sheet or bar forms using well-established insgot metallurgy practices that involve hot- and cold-working steps. However, recent developments in process metallurgy have unlocked opportunities to directly produce bulk soft-magnetic alloys with improved, and often tailorable, structure–property relationships that are unachievable conventionally. The emergence of unconventional manufacturing routes for soft-magnetic alloys is largely motivated by the need to improve the energy efficiency of electromagnetic devices. In this review, literature that details emerging manufacturing approaches for soft-magnetic alloys is overviewed. This review covers (1) severe plastic deformation, (2) recent advances in melt spinning, (3) powder-based methods, and (4) additive manufacturing. These methods are discussed in comparison with conventional rolling and bar processing. Perspectives and recommended future research directions are also discussed.

Effect of Annealing on the Magnetic Properties of FeCoNiCuNbSiB Soft Magnetic Alloys

A series of nanocrystalline soft magnetic alloys with nominal compositions of Fe66.8-xCo10NixCu0.8Nb2.9Si11.5B8 (x = 1–15 at%) were developed and studied. Effects of annealing on the soft magnetic properties, crystallization behavior, and domain structure were investigated. The alloys with higher Ni content were prone to exhibit stronger magnetic anisotropy. The Fe66.8Co10Ni10Cu0.8Nb2.9Si11.5B8 alloy exhibited excellent soft magnetic properties, including the low permeability of 2000, low coercivity of about 0.6 A/m, and low remanence of 2.4 mT, together with a temperature gap of 128 K between two crystallization onset temperatures. It has been found that the Ni content and the annealing process possess significant effects on the soft magnetic property of the nanocrystalline alloys. It shows that the developed Fe66.8Co10Ni10Cu0.8Nb2.9Si11.5B8 nanocrystalline alloy exhibits great potentials for applying in the field of common mode chokes or current transformers, due to its ability to resist the direct current.

Chemical synthesis of nanostructured magnetic hardened alloy of the Nd-Fe-B system

Hard magnetic nanopowders of the Nd15Fe78B7 alloy were synthesized from mixtures of Nd, Fe and Fe-B oxides with CaH2 in a hydrogen atmosphere at 800 °C by a reduction-diffusion process. Nd, Fe, Fe-B oxides were synthesized by chemical deposition. The resulting particles had a granular shape with an average size: Nd2O3 — 50 nm, Fe2O3 — 95 nm, Fe3BO6 — 57 nm. The particle size of the Nd15Fe78B7 alloy was 45–140 nm. It is shown that the proposed method is suitable for obtaining nanopowders of hard magnetic alloys of the Nd-Fe-B system.

Characterization and Analysis of Nanocrystalline Soft Magnetic Alloys: Fe Based

Soft magnetic nanocrystalline alloys have been widely analysed and studied during the past years. However, optimisation of specific chemical compositions is still being developed. The applicability of these soft nanocrystalline alloys depends mainly on the presence of the desired nanocrystalline phases within the alloy. In this study, the analysed alloys are manufactured by mechanical alloying. The analyses performed on the samples include a microstructural analysis, a thermal analysis, and a complementary functional analysis in the form of the thermomagnetic response of some samples. Regarding Fe-based alloys, thermal stability for samples containing B was higher than those containing P (crystal growth peaks in the range between 895–905 K and 775–800 K respectively). The higher magnetization of saturation, Ms, was found in Fe–Mn alloys, whereas the addition of boron provoked a decrease of Ms and the nanocrystals size.