Effects of Calcium Sulfate Whiskers on the Mechanical Properties and Light Transmittance of PE Greenhouse Films

Calcium sulfate whisker (CSW) is a kind of fiber crystal material with high orientation structure. The major goal of this research is to study the changes of mechanical properties and light transmittance of PE greenhouse film with different proportions of CSW. The experimental results show that the mechanical properties and light transmittance of PE/CSW films are enhanced compared with the pure PE. For PE/2%CSW, it shows a 18.6% increase in tear strength, a 3.1% increase in luminous transmittance and 17.7% increase in haze. The PE/5%CSW demonstrates a 12.8% higher in tensile strength, a 20.5% higher in tear strength, a 23.9% lower in luminous transmittance and a 53.0% higher in haze. This article gives a new formula to strengthen the mechanical properties of PE greenhouse films and finds the direction for the research and development of astigmatic covering film.

Research on the physical properties of calcium sulfate whisker and the effects of its addition on paper and its printing performance

In this investigation, softwood pulp and bleached wheat straw pulp were used as raw materials, and Calcium Sulfate Whiskers (CSW) were used as fillers. Based on the structural properties and characteristics of CSW, the printing properties of the paper with CSW, such as whiteness, opacity, pH value, uniformity, Z-direction tensile strength and surface strength, were analyzed. The results showed that CSW has low solubility, high retention and fiber-like appearance. The whiteness of the paper is the best when the filling amount of CSW is 20 %. The paper opacity of softwood pulp increases significantly, and the opacity of bleached wheat straw pulp decreases significantly when CSW is more than 30 %. The addition reduces pH and surface strength of the paper. The evenness of the paper does not change obviously. The Z-direction tensile strength of the paper decreases in the softwood paper, but increases obviously in the bleached wheat straw paper.

Research on the Physical Properties of Calcium Sulfate Whisker and the Effects of its Addition on Paper and its Printing Performance

In this investigation, softwood pulp and bleached wheat straw pulp were used as raw materials, and Calcium Sulfate Whiskers (CSW) were used as fillers. Based on the structural properties and characteristics of CSW, the printing properties of the paper with CSW, such as whiteness, opacity, pH value, uniformity, Z-direction tensile strength and surface strength, were analyzed. The results showed that CSW has low solubility, high retention rate and fiber-like appearance. The whiteness of the paper is the best when the filling amount of CSW is 20%. The paper opacity of softwood pulp increases significantly, and the opacity of bleached wheat straw pulp decreases significantly when CSW is more than 30%. The addition reduces pH and surface strength of the paper. The evenness of the paper does not change obviously. The Z-direction tensile strength of the paper decreases in the softwood paper, but increases obviously in the bleached wheat straw paper. Graphic abstract

Efficient activation of persulfate by calcium sulfate whisker supported nanoscale zero-valent iron for methyl orange removal

In order to improve the utilization of nanoscale zero-valent iron (nZVI) in activating persulfate (PS), a composite material of nZVI/CSW with nZVI supported on calcium sulfate whiskers (CSWs) was synthesized in this study.

Shape recovery characteristics of shape memory cyanate ester/epoxy composite reinforced with calcium sulfate whisker

Purpose The purpose of this paper is to study the influence of calcium sulfate whiskers (CSWs) on the thermodynamic properties and shape memory properties of epoxy/cyanate ester shape memory composites. Design/methodology/approach To improve the mechanical properties of shape memory cyanate ester (CE)/epoxy polymer (EP) resin, high performance CSWs were used to reinforce the thermo-induced shape memory CE/EP composites and the shape memory CSW/CE/EP composites were prepared by molding. The effect of CSW on the mechanical properties and shape memory behavior of shape memory CE/EP composites was investigated. Findings After CSW filled the shape memory CE/EP composites, the bending strength of the composites is greatly improved. When the content of CSW is 5 Wt.%, the bending strength of the composite is 107 MPa and the bending strength is increased by 29 per cent compared with bulk CE/EP resin. The glass transition temperature and storage modulus of the composites were improved in CE/EP resin curing system. However, when the content of CSW is more than 10 Wt.%, clusters are easily formed between whiskers and the voids between whiskers and matrix increase, which will lead to the decrease of mechanical properties of composites. The results of shape memory test show that the shape memory recovery time of the composites decreases with the decrease of CSW content at the same temperature. In addition, the shape recovery ratio of the composites decreased slightly with the increase of the number of thermo-induced shape memory cycles. Research limitations/implications A simple way for fabricating thermo-activated SMP composites has been developed by using CSW. Originality/value The outcome of this study will help to fabricate the SMP composites with high mechanical properties and the shape memory CSW/CE/EP composites are expected to be used in space deployable structures.