Multiple inoculations of ductile iron and the effects on properties

2015 ◽  
Vol 4 (4) ◽  
pp. 526
Author(s):  
Adebayo Badmos ◽  
Kelvin Fakehinde
Keyword(s):  
Mechanical Properties ◽  
Cast Iron ◽  
Ductile Iron ◽  
Primary Inoculation ◽  
The Matrix

Multiple inoculation of ductile iron and the effects on the structure and mechanical properties have being investigated. Samples of ductile iron were produced with inoculation carried out either once or twice and with different materials as inoculants. Ferrosilicon was used for the primary inoculation and either ferrosilicon or nickel-ferrosilicon for the secondary inoculation. It is observed that the nodules produced are more and finer with multiple inoculations and the effect is more pronounced with nickel-ferrosilicon as the secondary inoculant. Multiple inoculations produce an increase in the hardness of ductile iron when ferrosilicon is used as the secondary inoculant while a decrease in the hardness is observed with nickel-ferrosilicon despite the finer nodules. This is explained by the fact that nickel enhances graphitization in cast iron thereby depleting carbon in the matrix and making the cast iron weaker but with more nodules.

scholarly journals ADI after Austenitising from Intercritical Temperature

2013 ◽  
Vol 13 (1) ◽  
pp. 81-88
Author(s):  
A. Kowalskia ◽  
S. Kluska-Nawarecka ◽  
K. Regulski
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Fuzzy Logic ◽  
Cast Iron ◽  
Chemical Composition ◽  
Ductile Iron ◽  
Logic Model ◽  
Plastic Properties ◽  
The Matrix ◽  
Different Temperatures

Abstract ADI subjected to austenitising at intercritical temperatures contains in its matrix the precipitates of pre-eutectoid ferrite. Studies were carried out on the ductile iron of the following chemical composition: C = 3,80%, Si = 2,30%, Mn = 0,28%, P = 0,060%, S = 0,010%, Mg = 0,065%, Ni = 0,60%, Cu = 0,70%, Mo = 0,21% This cast iron was austenitised at three different temperatures, i.e. 800, 815 and 830oC and austempered at 360 and 380oC. For each variant of the cast iron heat treatment, the mechanical properties, i.e. YS, TS, EL and Hardness, were measured, and structure of the matrix was examined. Higher plastic properties were obtained owing to the presence of certain amount of pre-eutectoid ferrite. The properties were visualised using fuzzy logic model in a MATLAB. software.

scholarly journals Structural iron with compact forms of graphite

2015 ◽  
Vol 2015 (3) ◽  
pp. 24-29
Author(s):  
Денис Болдырев ◽  
Denis Boldyrev ◽  
Сергей Давыдов ◽  
Sergey Davydov ◽  
Виталий Сканцев ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Cast Iron ◽  
Ductile Iron ◽  
Energy Intensity ◽  
Strength Properties ◽  
Compact Form ◽  
Structural Iron

The identity of the mechanical properties of ductile iron (QP) and cast iron with compact forms of graphite, in particular, with nodular and vermicular graphite (CSWG). Given the fundamental differences in techniques of obtaining QP and CSUG in terms of their labor, material and energy intensity at virtually the identical strength properties shown to be technically and economically preferable for the manufacture of castings of CSWG and other cast iron with a compact form of graphite.

Influence of Charge Composition on EN-GJS-500-7 Ductile Iron Properties in Foundry Operating Conditions

2020 ◽  
Vol 998 ◽  
pp. 42-47
Author(s):  
Alena Pribulová ◽  
Peter Futaš ◽  
Marcela Pokusova
Keyword(s):  
Mechanical Properties ◽  
Cast Iron ◽  
Ductile Iron ◽  
Ductile Cast Iron ◽  
Operating Conditions ◽  
Production Costs ◽  
Steel Scrap ◽  
Charge Composition ◽  
Iron Castings ◽  
Worldwide Production

Worldwide production of ductile iron castings reached in year 2017 26,428,148 metric tons, which is 34% of the total weight of all castings made from cast iron. The most significant increase in ductile iron castings was recorded in Slovakia, up to 78.6%. Castings from ductile iron have a very huge utilization thanks their very good foundry and mechanical properties. The current economic situation in all industries forces entrepreneurs and producers to rationalize production and reduce production costs, with a worldwide trend to increase the share of steel scrap, a technology for the production of ductile cast iron. The paper describes the results of research focused on the effect of charge composition, mainly the share of scrap steel on the final properties and structure of ductile iron EN-GJS-500-7 under the operating conditions of foundry. Six melts with different charge composition were made. The samples from all melts were taken and chemical analysis, microstructure analysis and testing on mechanical properties were made on them. The mechanical properties of produced globular cast irons were according with the relevant standard. It is important to mention that there has been a significant increase in strength characteristics in melts in which the carbon content exceeded 4% (CE = 4.7 and 4.8%, respectively).

Cylinder Liner in Ductile Cast Iron for High Loaded Combustion Diesel Engines

2011 ◽  
Author(s):  
Edney Deschauer Rejowski ◽  
Edmo Soares ◽  
Ingo Roth ◽  
Steffen Rudolph
Keyword(s):  
Mechanical Properties ◽  
Cast Iron ◽  
Wall Thickness ◽  
Diesel Engines ◽  
Ductile Iron ◽  
Gray Cast Iron ◽  
Young Modulus ◽  
Gray Cast ◽  
Cast Material ◽  
Cylinder Liners

With the increase of combustion loading and the trend to reduce engine size, there is a need for thinner but stronger wet cylinder liners. While most of the current cylinder liners are made of gray cast iron, due to its good tribological behavior, machinability performance and competitive price, alternative casting materials like compact graphite iron, ductile iron and even steel are being considered to cover the future engine demands. In this paper, a new ductile iron (DI) cast material for wet cylinder liners is presented. The material has about 60 and 70% higher limits respectively for tensile stress and fatigue resistance as compared to conventional gray cast irons, but without penalty on the tribological properties. There is also a potential improvement to avoid cavitation on the outside surface due to its higher young modulus, which also equates to a higher stiffness. The tested cylinder liners were induction hardened on the running surface and a slide hone process was used to improve wear and scuffing resistance. The liners were tested in a HDD engine with PCP of 245 bar and showed similar wear as observed with conventional cylinder liners of gray cast iron material. The DI cylinder liners were also tested in an abusive scuffing engine test without any concern. The improved mechanical properties of the described new DI material introduce possibilities to reduce liner wall thickness or increase specific output. The preliminary evaluation in this paper showed that this new material is feasible for HDD diesel engines with PCP up to 250 bar. In cases that the customer needs to increase the bore diameter for output reasons there is the potential to reduce the liner wall thickness up to 25% based on high mechanical properties (UTS, Young Modulus and fatigue strength). In both cases, it’s recommended a FEA analysis to support the new component design.

scholarly journals Effect of Processing Parameters on the Mechanical Properties of Heavy Section Ductile Iron

2015 ◽  
Vol 2015 ◽  
pp. 1-11 ◽  
Author(s):  
Mohamed Mahmoud Mourad ◽  
Shimaa El-Hadad ◽  
Mervat Mohamed Ibrahim ◽  
Adel Abdelmonem Nofal
Keyword(s):  
Mechanical Properties ◽  
Ductile Iron ◽  
Processing Parameters ◽  
Ductile Cast Iron ◽  
Heavy Section ◽  
The Matrix ◽  
Cast Alloys ◽  
One Step ◽  
Inoculation Procedure ◽  
Inoculation Treatment

The main objective of the current work is to investigate the influence of different inoculation conditions on the microstructure and mechanical properties of heavy section ductile iron (DI) castings. Inoculation treatment was done via one step and double step treatments with different amounts of inoculants. The mechanical properties of the fabricated samples were evaluated. The best inoculation procedure in terms of graphite nodules characteristics and mechanical properties was double inoculation with 0.8% inoculants added at first and 0.2% in the late inoculation step. The presence of Sb in one of the cast alloys controlled the growth of graphite nodules in these heavy section ductile iron castings; however low impact toughness was recorded. The matrix structure of ductile cast iron showed a significant influence not only on the strength and impact properties but also on the fracture mode during testing.

The Influence of Boron on Structure and Mechanical Properties of Bainite Ductile Iron in the Step Austempering in Room Temperature Machine Oil

2010 ◽  
Vol 139-141 ◽  
pp. 235-238
Author(s):  
De Qiang Wei
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Cast Iron ◽  
Impact Strength ◽  
Ductile Iron ◽  
Room Temperature ◽  
Solute Drag ◽  
Ductile Cast Iron ◽  
Treatment Technique ◽  
The Impact

In this paper, the low alloy bainite ductile cast iron has been obtained by a new heat treatment technique of the step austempering in room-temperature machine oil. The effects of element boron, manganese and copper on structure and mechanical properties of the bainite ductile cast Iron in above-mentioned process are investigated. The phenomenon, hardness lag of the alloyed bainite ductile cast Iron, has been discussed. It shows that after the step austempering in room-temperature machine oil, the hardness will increases with the time. It is found that boron and manganese can increase the hardness and reduce the impact strength while copper can increase the impact strength. The results show that reasonable alloyed elements can improve mechanical properties of the bainite ductile cast Iron. Essentially, hardness lag of the alloyed bainite ductile cast Iron is resulted from solute drag-like effect.

scholarly journals Effect of Heat-treatment Parameters of Cast Iron GJS-X350NiMnCu7-3-2 on its Structure and Mechanical Properties

2017 ◽  
Vol 17 (1) ◽  
pp. 121-126 ◽  
Author(s):  
D. Medyński ◽  
A. Janus ◽  
S. Zaborski
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Cast Iron ◽  
High Hardness ◽  
Spheroidal Graphite ◽  
Air Cooling ◽  
Material Hardness ◽  
The Matrix ◽  
Lower Material

Abstract The paper presents influence of soaking parameters (temperature and time) on structure and mechanical properties of spheroidal graphite nickel-manganese-copper cast iron, containing: 7.2% Ni, 2.6% Mn and 2.4% Cu. Raw castings showed austenitic structure and relatively low hardness (150 HBW) guaranteeing their good machinability. Heat treatment consisted in soaking the castings within 400 to 600°C for 2 to 10 hours followed by air-cooling. In most cases, soaking caused changes in structure and, in consequence, an increase of hardness in comparison to raw castings. The highest hardness and tensile strength was obtained after soaking at 550°C for 6 hours. At the same time, decrease of the parameters related to plasticity of cast iron (elongation and impact strength) was observed. This resulted from the fact that, in these conditions, the largest fraction of fine-acicular ferrite with relatively high hardness (490 HV0.1) was created in the matrix. At lower temperatures and after shorter soaking times, hardness and tensile strength were lower because of smaller degree of austenite transformation. At higher temperatures and after longer soaking times, fine-dispersive ferrite was produced. That resulted in slightly lower material hardness.

scholarly journals Investigation of the Nodularisation Propensity of Calcined Cashew-Nut Shell-Ash in Cast-Iron Melt Graphite

2021 ◽  
Vol 18 (1) ◽  
pp. 1-8
Author(s):  
O.I. Sekunowo ◽  
J.O. Ugboaja ◽  
J.A. Tiamiyu
Keyword(s):  
Mechanical Properties ◽  
Cast Iron ◽  
Ductile Iron ◽  
Microstructural Analysis ◽  
Ductile Cast Iron ◽  
Cashew Nut ◽  
Melt Treatment ◽  
Master Alloys ◽  
Molten Cast Iron ◽  
Cashew Nut Shell

Production of ductile iron using ferrosilicon-magnesium master alloy in melt treatment is currently fraught with challenges bothering on cost and availability. In this study the suitability of cashew nut shells ash (CNSA) as a viable alternative to magnesium master alloys employed in the treatment of molten cast iron for enhanced mechanical properties was studied. The carbonized CNSA used varied from 2-10 wt. % to treat different heat batches; CA1-CA5 containing varied amount of CNSA, CaO and FeSi in the molten cast iron. The cast samples were subjected to both mechanical characterisation (tensile, hardness and impact) and microstructural analysis using Instron electromechanical machine, impact tester and scanning electron microscope (SEM) coupled with energy dispersive spectroscope (EDS). Results show that the 8 wt. % CNSA addition demonstrated the best mechanical properties comparable to ASTM A536 ferritic ductile cast iron. Specifically, the 8 wt. % CNSA cast samples exhibited 433 MPa tensile strength, 144HRC hardness and ductility of 14.7%. Contributions to improved mechanical properties may be attributed to the development of sufficient fractions of graphite nodules during melt treatment with CNSA. These outcomes are a boost both to the production of quality ductile irons and a cleaner environment. Keywords: Nodularisation, ductile-iron, cashew-nut, ferrosilicon-magnesium alloy, mechanical properties

scholarly journals Properties and Structure of High-Silicone Austempered Ductile Iron

2014 ◽  
Vol 14 (2) ◽  
pp. 91-94 ◽  
Author(s):  
A. Krzyńska ◽  
A. Kochański
Keyword(s):  
Mechanical Properties ◽  
Cast Iron ◽  
Ductile Iron ◽  
Tensile Testing ◽  
Hardness Measurement ◽  
Austempered Ductile Iron ◽  
Ferritic Matrix ◽  
Heat Treated

Abstract The results presented in this paper are a continuation of the previously published studies. The results of hest treatment of ductile iron with content 3,66%Si and 3,80% Si were produced. The experimental castings were subjected to austempering process for time 30, 60 and 90 minutes at temperature 300°C. The mechanical properties of heat treated specimens were studied using tensile testing and hardness measurement, while microstructures were evaluated with conventional metallographic observations. It was again stated that austempering of high silicone ferritic matrix ductile iron allowed producing ADI-type cast iron with mechanical properties comparable with standard ADI.

Sign in / Sign up

Export Citation Format

Share Document