Synthesis and characterization of biobased polyurethanes from modified castor oil and palm oil based isocyanate Effect of NCO OH molar ratio

2015 ◽  
Author(s):  
PRIYANKA PANDEY ◽  
SANJAY KUMAR ◽  
SMITA MOHANTY ◽  
SONALEE DAS
Keyword(s):  
Palm Oil ◽  
Castor Oil ◽  
Molar Ratio ◽  
Synthesis And Characterization

scholarly journals Synthesis and Characterization of Novel Castor Oil-Based Polyol for Potential Applications in Coatings

2019 ◽  
Vol 7 (1) ◽  
pp. 31-40 ◽  
Author(s):  
Azam Sardari ◽  
Ali Asghar Sabbagh Alvani ◽  
Seyed Reza Ghaffarian
Keyword(s):  
Castor Oil ◽  
Synthesis And Characterization ◽  
Potential Applications

Synthesis and Characterization of Poly(Aryl Ether Quinoxaline)s with Controlled Molecular Weight

2011 ◽  
Vol 391-392 ◽  
pp. 826-829
Author(s):  
Song Ya Zhang ◽  
Zhong Xiao Li ◽  
Jia Ling Pu
Keyword(s):  
Molecular Weight ◽  
Glass Transition ◽  
Strong Acid ◽  
Decomposition Temperature ◽  
Molar Ratio ◽  
Synthesis And Characterization ◽  
Aryl Ether ◽  
Good Solubility ◽  
Step Procedure

Novel poly(aryl ether quinoxaline)s (PEQs) were prepared via a two-step procedure. First, poly (ether benzil) (PEB) was synthesized by the polycondensation of 4,4’-difluorobenzil and 4,4’-isopropylidenediphenol.Then, PEB was reacted with 1,2-diaminobenzene and 4,4'-oxydibenzene-1,2-diamine to give the PEQs. The molecular weight of the PEQs could be adjusted easily by varying the molar ratio of 1,2-diaminobenzene to 4,4'-oxydibenzene-1,2-diamine. The PEQs exhibited good solubility in common organic solvents such as NMP, DMAc, DMF, cyclohexanone and chloroform. In addition, the PEQs also had high glass transition (Tg) temperatures and good thermal properties, with an initial thermal decomposition temperature above 475 oC and glass transition temperatures above 210 oC. They also exhibited excellent resistance to strong acid and alkali.

Synthesis and characterization of Au, Pt supported on graphene aerogel catalysts for CO oxidation at low temperature

2021 ◽  
Vol 11 (1) ◽  
pp. 118-122
Author(s):  
Chuyen Phan Thi ◽  
Hang Tran Thi Thanh ◽  
Phong Pham Nam ◽  
Ha Vu Thi Thu
Keyword(s):  
Low Temperature ◽  
Ambient Temperature ◽  
Co Oxidation ◽  
Pt Nanoparticles ◽  
Molar Ratio ◽  
Synthesis And Characterization ◽  
Graphene Aerogel ◽  
Highly Dispersed ◽  
Average Size

Au, Pt supported on graphene aerogel catalysts (PtAu/rGOA) with molar ratio of Pt and Au of 1:1, and total metal concentration of 5 % were successfully synthesized by hydrothermal method.  The obtained catalysts were characterized by Raman, XRD, XPS, HR-TEM, BET. It revealed that Au and Pt nanoparticles with average size of 3 – 5 nm were highly dispersed on aerogel graphene. The activity of these catalysts was tested  in CO oxidation. The results showed that the conversion of CO at ambient temperature was 100% during 25 minutes. Accordingly, PtAu/rGOA could be considered as a potential catalysts for CO oxidation at low temperature.

Synthesis and Characterization of Alkyd Resin Based on Soybean Oil Polyols

2011 ◽  
Vol 239-242 ◽  
pp. 1721-1724 ◽  
Author(s):  
Xiao Qing Zheng ◽  
Li Ting Yang ◽  
Kun Peng Wang
Keyword(s):  
Maleic Anhydride ◽  
Soybean Oil ◽  
Phthalic Anhydride ◽  
Alkyd Resin ◽  
Ring Opening ◽  
Molar Ratio ◽  
Synthesis And Characterization ◽  
Hydroxyl Value

Soybean oil-based alkyd resin was prepared using soy-based polyol, maleic anhydride and phthalic anhydride. The soy-based polyol was obtained through the epoxidization of soybean oil, followed by ring-opening with methanol and, the hydroxyl values of soybean oil-based polyols used in this reaction is 169.93 mgKOH/g. In the reactions of soy-based polyol, maleic anhydride and phthalic anhydride, the molar ratio of hydroxyl value is equal to carboxyl value and the molar ratio of maleic anhydride to phthalic anhydride is 2:1, 1:1 and 1:2, respectively. 1% hydroquinone based on total reactants was used as inhibitor of polymerization, 1% dibutyltin oxide was used as catalyst.

Synthesis and Characterization of a New Phosphorus-Containing Curing Agent PPDTA

2019 ◽  
Vol 953 ◽  
pp. 185-190
Author(s):  
Yong Li Peng ◽  
Ni An Zhuo ◽  
Can Zhang
Keyword(s):  
Infrared Spectroscopy ◽  
Reaction Time ◽  
Reaction Temperature ◽  
Orthogonal Experiment ◽  
Molar Ratio ◽  
Synthesis And Characterization ◽  
Curing Agent ◽  
Phosphorus Containing ◽  
Three Factor

A new phosphorus-containing flame-retardant curing agent PPDTA was synthesized from phenylphosphonic dichloride (PPD) and 3-amino-1,2,4-triazole (TA) in tetrahydrofuran solvent to improve the flame retardancy of epoxy resin. The structure of the compound was analyzed and confirmed by infrared spectroscopy. The effects of reaction time, reaction temperature and ratio of reactants on yield were studied by using three-factor three-level orthogonal experiment. The results show that the yield of PPDTA can reach 86.4%, when the reaction time is 10h, reaction temperature is 70 °Cand the molar ratio of TA to PPD is 2.2:1.