Investigations of CuInSe2 Thin Films and Contact

1990 ◽  
Vol 187 ◽  
Author(s):  
S. Raud ◽  
Quat T. Vu ◽  
M-A. Nicolet ◽  
G. A. Pollock ◽  
K. W. Mitchell ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
X Ray Diffraction ◽  
X Ray ◽  
Contact Stability ◽  
The Individual

AbstractWe study the properties of CuInSe2 thin films grown on glass and on Mo substrates. The investigation is carried out with X-ray diffraction, RBS, XTEM and SEM.CuInSe2/Mo contact stability is investigated after annealing at 600°C. RBS reveals that this treatment induces an interdiffusion between the metal and the chalcopyrite. To clarify this reaction, we have investigated the individual thin-film couples upon annealing. RBS and X-ray diffraction reveal insignificant interaction between Mo/Cu and Mo/In, but Se reacts with Mo.

A New Method for Measuring the Residual Stresses in Multi-Layered Thin Film Systems

2012 ◽  
Vol 591-593 ◽  
pp. 884-890
Author(s):  
Mei Liu ◽  
Hai Hui Ruan ◽  
Liang Chi Zhang
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Residual Stresses ◽  
Single Point ◽  
X Ray Diffraction ◽  
Xrd Pattern ◽  
X Ray ◽  
Xrd Techniques ◽  
The Individual ◽  
Layered Thin Film

To meet different electrical or optical functionalities, thin films are often of multiple layers processed at high temperatures. Substantial residual stresses can therefore develop in such thin film systems due to the disparate thermal properties of the individual material layers. High stresses can lead to mechanical failure of the systems and thus understanding the residual stresses in thin film systems is important. This paper presents a systematic way to characterize the residual stresses in epitaxial, polycrystalline and amorphous layers by using X-ray diffraction (XRD) techniques. The single-point XRD pattern renders the stresses of crystalline layers and the scanning XRD gives the curvature of the whole film. Based on the newly-developed analytical model, the residual stresses of each layer can all be determined.

Palladium Nanowire Thin Films via Template Growth

2003 ◽  
Vol 775 ◽  
Author(s):  
Donghai Wang ◽  
David T. Johnson ◽  
Byron F. McCaughey ◽  
J. Eric Hampsey ◽  
Jibao He ◽  
...  
Keyword(s):  
Thin Film ◽  
Electron Microscopy ◽  
Thin Films ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Conductive Substrate ◽  
Palladium Nanowires ◽  
Efficient Route ◽  
Silica Thin Film

AbstractPalladium nanowires have been electrodeposited into mesoporous silica thin film templates. Palladium continually grows and fills silica mesopores starting from a bottom conductive substrate, providing a ready and efficient route to fabricate a macroscopic palladium nanowire thin films for potentially use in fuel cells, electrodes, sensors, and other applications. X-ray diffraction (XRD) and transmission electron microscopy (TEM) indicate it is possible to create different nanowire morphology such as bundles and swirling mesostructure based on the template pore structure.

Al1-x ScxN Thin Film Structures for Pyroelectric Sensing Applications

MRS Advances ◽  
2016 ◽  
Vol 1 (39) ◽  
pp. 2711-2716 ◽  
Author(s):  
V. Vasilyev ◽  
J. Cetnar ◽  
B. Claflin ◽  
G. Grzybowski ◽  
K. Leedy ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Pyroelectric Coefficient ◽  
X Ray Diffraction ◽  
Ir Detectors ◽  
Pyroelectric Properties ◽  
X Ray ◽  
Sensing Applications ◽  
Pyroelectric Material ◽  
Deposited Films

ABSTRACTAlN thin film structures have many useful and practical piezoelectric and pyroelectric properties. The potential enhancement of the AlN piezo- and pyroelectric constants allows it to compete with more commonly used materials. For example, combination of AlN with ScN leads to new structural, electronic, and mechanical characteristics, which have been reported to substantially enhance the piezoelectric coefficients in solid-solution AlN-ScN compounds, compared to a pure AlN-phase material.In our work, we demonstrate that an analogous alloying approach results in considerable enhancement of the pyroelectric properties of AlN - ScN composites. Thin films of ScN, AlN and Al1-x ScxN (x = 0 – 1.0) were deposited on silicon (004) substrates using dual reactive sputtering in Ar/N2 atmosphere from Sc and Al targets. The deposited films were studied and compared using x-ray diffraction, XPS, SEM, and pyroelectric characterization. An up to 25% enhancement was observed in the pyroelectric coefficient (Pc = 0.9 µC /m2K) for Sc1-xAlxN thin films structures in comparison to pure AlN thin films (Pc = 0.71 µC/m2K). The obtained results suggest that Al1-x ScxN films could be a promising novel pyroelectric material and might be suitable for use in uncooled IR detectors.

Crystallization of Zn-rich and P-rich amorphous Zn3P2 thin films

1988 ◽  
Vol 66 (5) ◽  
pp. 373-375 ◽  
Author(s):  
C. J. Arsenault ◽  
D. E. Brodie
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Activation Energy ◽  
Electrical Properties ◽  
Structural Properties ◽  
Crystallization Process ◽  
X Ray Diffraction ◽  
Electrical Measurements ◽  
Conductivity Activation Energy ◽  
X Ray

Zn-rich and P-rich amorphous Zn3P2 thin films were prepared by co-evaporation of the excess element during the normal Zn3P2 deposition. X-ray diffraction techniques were used to investigate the structural properties and the crystallization process. Agglomeration of the excess element within the as-made amorphous Zn3P2 thin film accounted for the structural properties observed after annealing the sample. Electrical measurements showed that excess Zn reduces the conductivity activation energy and increases the conductivity, while excess P up to 15 at.% does not alter the electrical properties significantly.

Synthesis of CaWO4:(Eu3+,Tb3+) Thin Films by a Two-Step Method at Room Temperature

2013 ◽  
Vol 710 ◽  
pp. 170-173
Author(s):  
Lian Ping Chen ◽  
Yuan Hong Gao
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Phase Composition ◽  
Room Temperature ◽  
Electrochemical Techniques ◽  
Luminescent Properties ◽  
X Ray Diffraction ◽  
Step Method ◽  
X Ray ◽  
Rare Earth Doped

It is hardly possible to obtain rare earth doped CaWO4thin films directly through electrochemical techniques. A two-step method has been proposed to synthesize CaWO4:(Eu3+,Tb3+) thin films at room temperature. X-ray diffraction, energy dispersive X-ray analysis, spectrophotometer were used to characterize their phase, composition and luminescent properties. Results reveal that (Eu3+,Tb3+)-doped CaWO4films have a tetragonal phase. When the ratio of n (Eu)/n (Tb) in the solution is up to 3:1, CaWO4:(Eu3+,Tb3+) thin film will be enriched with Tb element; on the contrary, when the ratio in the solution is lower than 1:4, CaWO4:(Eu3+,Tb3+) thin film will be enriched with Eu element. Under the excitation of 242 nm, sharp emission peaks at 612, 543, 489 and 589 nm have been observed for CaWO4:(Eu3+,Tb3+) thin films.

Synthesis and Characterizations of Strontium Substituted Hydroxyapatite Thin Films

2010 ◽  
Vol 93-94 ◽  
pp. 231-234
Author(s):  
B. Hongthong ◽  
Satreerat K. Hodak ◽  
Sukkaneste Tungasmita
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Composition ◽  
Spin Coating ◽  
Phase Structure ◽  
Sol Gel ◽  
Cross Linking ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process

Strontium substituted hydroxyapatite(SrHAp) were fabricated both in the form of powder as reference and thin film by using inorganic precursor reaction. The sol-gel process has been used for the deposition of SrHAp layer on stainless steal 316L substrate by spin coating technique, after that the films were annealed in air at various temperatures. The chemical composition of SrHAp is represented (SrxCa1-x)5(PO4)3OH, where x is equal to 0, 0.5 and 1.0. Investigations of the phase structure of SrHAp were carried out by using X-ray diffraction technique (XRD). The results showed that strontium is incorporated into hydroxyapatite where its substitution for calcium increases in the lattice parameters, and Sr3(PO4)2 can be detected at 900°C. The SEM micrographs showed that SrHAp films exhibited porous structure before develop to a cross-linking structure.

scholarly journals Structural and Electrochemical Properties of Lithium Nickel Oxide Thin Films

2014 ◽  
Vol 2014 ◽  
pp. 1-5 ◽  
Author(s):  
Gyu-bong Cho ◽  
Tae-hoon Kwon ◽  
Tae-hyun Nam ◽  
Sun-chul Huh ◽  
Byeong-keun Choi ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Electrochemical Properties ◽  
Discharge Capacity ◽  
Oxygen Deficiency ◽  
Oxide Phase ◽  
Rf Magnetron Sputtering ◽  
X Ray Diffraction ◽  
X Ray ◽  
Lithium Nickel Oxide

LiNiO2thin films were fabricated by RF magnetron sputtering. The microstructure of the films was determined by X-ray diffraction and field-emission scanning electron microscopy. The electrochemical properties were investigated with a battery cycler using coin-type half-cells. The LiNiO2thin films annealed below 500°C had the surface carbonate. The results suggest that surface carbonate interrupted the Li intercalation and deintercalation during charge/discharge. Although the annealing process enhanced the crystallization of LiNiO2, the capacity did not increase. When the annealing temperature was increased to 600°C, the FeCrNiO4oxide phase was generated and the discharge capacity decreased due to an oxygen deficiency in the LiNiO2thin film. The ZrO2-coated LiNiO2thin film provided an improved discharge capacity compared to bare LiNiO2thin film suggesting that the improved electrochemical characteristic may be attributed to the inhibition of surface carbonate by ZrO2coating layer.

Formation of ZnO Doped with Mn Thin Film by Electrodeposition and Magnetic Behaviour.

2005 ◽  
Vol 879 ◽  
Author(s):  
M. Abid ◽  
C. Terrier ◽  
J-P Ansermet ◽  
K. Hjort
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Room Temperature ◽  
Magnetic Behaviour ◽  
Spectroscopic Methods ◽  
X Ray Diffraction ◽  
X Ray ◽  
Doped Zno ◽  
Mn Doped ◽  
Weak Ferromagnetic

AbstractFollowing the theory, ferromagnetism is predicted in Mn- doped ZnO, Indeed, ferromagnetism above room temperature was recently reported in thin films as well as in bulk samples made of this material. Here, we have prepared Mn doped ZnO by electrodeposition. The samples have been characterized by X-ray diffraction and spectroscopic methods to ensure that the dopants are substitutional. Some samples exhibit weak ferromagnetic properties at room temperature, however to be useful for spintronics this material need additional carriers provided by others means.

Electrical Properties of Multilayer Synthesized CuInSi Thin Film

2011 ◽  
Vol 383-390 ◽  
pp. 822-825
Author(s):  
Ping Luan ◽  
Jian Sheng Xie ◽  
Jin Hua Li
Keyword(s):  
Thin Film ◽  
Crystal Structure ◽  
Thin Films ◽  
Electrical Properties ◽  
Annealing Temperature ◽  
Time Effect ◽  
X Ray Diffraction ◽  
Testing Instrument ◽  
X Ray ◽  
Conductivity Type

Using magnetron sputtering technology, the CuInSi thin films were prepared by multilayer synthesized method. The structure of CuInSi films were detected by X-ray diffraction(XRD), the main crystal phase peak is at 2θ=42.458°; The resistivity of films were measured by SDY-4 four-probe meter; The conductive type of the films were tested by DLY-2 conductivity type testing instrument. The results show that the annealing temperature and time effect on the crystal resistivity and crystal structure greatly.

A Novel Technique to Determine Elastic Constants of Thin Films

2008 ◽  
Vol 1139 ◽  
Author(s):  
Klaus Martinschitz ◽  
Rostislav Daniel ◽  
Christian Mitterer ◽  
Keckes Jozef
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Elastic Moduli ◽  
Elastic Anisotropy ◽  
Interaction Model ◽  
X Ray Diffraction ◽  
X Ray ◽  
Anisotropic Factor ◽  
Polycrystalline Thin Films ◽  
Cu Thin Film

AbstractA new X-ray diffraction technique to determine elastic moduli of polycrystalline thin films deposited on monocrystalline substrates is demonstrated. The technique is based on the combination of sin2ψ and X-ray diffraction wafer curvature techniques which are used to characterize X-ray elastic strains and macroscopic stress in thin film. The strain measurements must be performed for various hkl reflections. The stresses are determined from the substrate curvature applying the Stoney's equation. The stress and strain values are used to calculate hkl reflection dependent X-ray elastic moduli. The mechanical elastic moduli can be then extrapolated from X-ray elastic moduli considering film macroscopic elastic anisotropy. The derived approach shows for which reflection and corresponding value of the X-ray anisotropic factor Γ the X-ray elastic moduli are equal to their mechanical counterparts in the case of fibre textured cubic polycrystalline aggregates. The approach is independent of the crystal elastic anisotropy and depends on the fibre texture type, the texture sharpness, the amount of randomly oriented crystallites and on the supposed grain interaction model. The new method is demonstrated on a fiber textured Cu thin film deposited on monocrystalline Si(100) substrate. The advantage of the new technique remains in the fact that moduli are determined non-destructively, using a static diffraction experiment and represent volume averaged quantities.

Sign in / Sign up

Export Citation Format

Share Document