Pulsed Plasma Enhanced Chemical Vapor Deposition from CH2F2, C2H2F4, and CHCIF2

1998 ◽  
Vol 511 ◽  
Author(s):  
Catherine B. Labelle ◽  
Kenneth K. S. Lau ◽  
Karen K. Gleason
Keyword(s):  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Photoelectron Spectroscopy ◽  
Chemical Vapor ◽  
Dielectric Constants ◽  
Pulsed Plasma ◽  
Dielectric Measurements ◽  
X Ray ◽  
Hexafluoropropylene Oxide ◽  
Deposited Films

ABSTRACTPulsed plasma enhanced chemical vapor deposition films have been grown from C2H2F4, CH2F2, and CHCLF2. C-Is x-ray photoelectron spectroscopy (XPS) indicates a prevalence of C-CF species in the films from C2H2F4 and CH2F2, whereas CF2 species dominate the films from CHC1F2. The CFx species distributions for the films are largely controlled by the competition between CF2-producing and HF elimination reactions in the pulsed plasmas. Dominance by HF elimination produces films with high C-CF and CF concentrations (e.g., CH2F2), whereas dominance by CF2-producing reactions leads to films with higher CF2 concentrations (e.g., CHCIF2). The % CF3 in the film is lowest for the precursor having the lowest F:H ratio, CH2F2. Little or no hydrogen was detected in the deposited films. Thermal degradation of films from C2H2F4 and CH2F2, as probed by solid-state nuclear magnetic resonance (NMR) spectroscopy, shows a loss through CF3 detachment and HF elimination. Pulsed plasma films from all three precursors gave dielectric constants of 2.4, with loss tangents on the order of 10−2. Dielectric measurements of pulsed plasma films from hexafluoropropylene oxide (HFPO) gave a dielectric constant of 2.0 ± 0.1 with a loss tangent of 0.009.

The Realization of Molecular Control Over Solid State Structure: Chemical Vapor Deposition of Gallium and Indium Sulfide Films

1992 ◽  
Vol 282 ◽  
Author(s):  
Michael B. Power ◽  
Andrew N. Macinnes ◽  
Aloysius F. Hepp ◽  
Andrew R. Barron
Keyword(s):  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Photoelectron Spectroscopy ◽  
Chemical Vapor ◽  
Molecular Control ◽  
X Ray ◽  
Gallium Sulfide ◽  
Transmission Electron ◽  
Precursor Molecules ◽  
Deposited Films

ABSTRACTThe chemical vapor deposition of cubic gallium sulfide and tetragonalindium sulfide films is reported. The structure of the deposited films was demonstrated to be defined not solely by thermodynamics, but bythe predesigned molecular motif of the precursor molecules. Analysis of the deposited films has been obtained by transmission electron microscopy (TEM), with associated energy dispersive X-ray analysis (EDX) and X-ray photoelectron spectroscopy (XPS).

High Quality GaAs Mis Diodes With Very Low Surface State Density

1990 ◽  
Vol 209 ◽  
Author(s):  
Yoshihisa Fujisaki ◽  
Sumiko Sakai ◽  
Saburo Ataka ◽  
Kenji Shibata
Keyword(s):  
Chemical Vapor Deposition ◽  
Density Of States ◽  
Vapor Deposition ◽  
Photoelectron Spectroscopy ◽  
Chemical Vapor ◽  
State Density ◽  
High Quality ◽  
Metal Insulator ◽  
X Ray ◽  
Mis Devices

ABSTRACTHigh quality GaAs/SiO2 MIS( Metal Insulator Semiconductor ) diodes were fabricated using (NH4)2S treatment and photo-assisted CVD( Chemical Vapor Deposition ). The density of states at the GaAs and SiO2 interface is the order of 1011 cm-2eV-1 throughout the forbidden energy range, which is smaller by the order of two than that of the MIS devices made by the conventional CVD process. The mechanism attributable to the interface improvement was investigated through XPS( X-ray Photoelectron Spectroscopy ) analyses.

Low Temperature Nitridatio of SiO2 Films using a Catalytic-CVD System

2000 ◽  
Vol 611 ◽  
Author(s):  
Akira Izumi ◽  
Hidekazu Sato ◽  
Hideki Matsumura
Keyword(s):  
Chemical Vapor Deposition ◽  
Low Temperature ◽  
Silicon Dioxide ◽  
Vapor Deposition ◽  
Photoelectron Spectroscopy ◽  
Chemical Vapor ◽  
Catalytic Decomposition ◽  
Catalytic Chemical Vapor Deposition ◽  
Sio2 Films ◽  
X Ray

ABSTRACTThis paper reports a procedure for low-temperature nitridation of silicon dioxide (SiO2) surfaces using species produced by catalytic decomposition of NH3 on heated tungsten in catalytic chemical vapor deposition (Cat-CVD) system. The surface of SiO2/Si(100) was nitrided at temperatures as low as 200°C. X-ray photoelectron spectroscopy measurements revealed that incorporated N atoms are bound to Si atoms and O atoms and located top-surface of SiO2.

Chemical Vapor Deposition of Niobium Carbide using a Novel Organometallic Precursor.

1989 ◽  
Vol 168 ◽  
Author(s):  
Paul D. Stupik ◽  
Linda K. Cheatham ◽  
John J. Graham ◽  
Andrew R. Barron
Keyword(s):  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Photoelectron Spectroscopy ◽  
Atmospheric Pressure ◽  
Niobium Carbide ◽  
Chemical Vapor ◽  
Stoichiometric Ratio ◽  
X Ray ◽  
Organometallic Precursor ◽  
Scanning Electron

AbstractChemical vapor deposition from (MeCp)2Nb(allyl) at atmospheric pressure yields niobium carbide films at temperatures as low as 300°C. X-ray photoelectron spectroscopy (XPS) studies indicate that the bulk films contain a carbide phase and a nearly stoichiometric ratio of niobium to carbon. The morphology of the films has been examined by scanning electron microscopy (SEM).

Growth of Highly Oriented Zinc Oxide Thin Films by Plasma Enhanced Chemical Vapor Deposition

2006 ◽  
Vol 321-323 ◽  
pp. 1687-1690 ◽  
Author(s):  
Hee Joon Kim ◽  
Dong Young Jang ◽  
Prem Kumar Shishodia ◽  
Akira Yoshida
Keyword(s):  
Thin Films ◽  
Zinc Oxide ◽  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Photoelectron Spectroscopy ◽  
Visible Region ◽  
Chemical Vapor ◽  
Zno Films ◽  
X Ray ◽  
Crystalline Films

In the paper, zinc oxide (ZnO) thin films are deposited by plasma enhanced chemical vapor deposition (PECVD) at different substrate temperatures. The ZnO films are characterized by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The analysis results indicate that highly crystalline films with high orientation can be obtained at a substrate temperature of 300 oC with 50 ml/min flow rate from Diethylzinc (DEZ). Furthermore, the investigation of optical property shows that ZnO films are transparent, and the peak transmittance in the visible region is as high as 85%.

Synthesis of Crystalline Carbon Nitride by Microwave Plasma Chemical Vapor Deposition

2005 ◽  
Vol 480-481 ◽  
pp. 71-76 ◽  
Author(s):  
Jin Chun Jiang ◽  
Wen Juan Cheng ◽  
Yang Zhang ◽  
He Sun Zhu ◽  
De Zhong Shen
Keyword(s):  
Chemical Vapor Deposition ◽  
Vapor Deposition ◽  
Photoelectron Spectroscopy ◽  
Carbon Nitride ◽  
Microwave Plasma ◽  
Chemical Vapor ◽  
Chemical Vapor Deposition Method ◽  
Plasma Chemical ◽  
X Ray ◽  
Plasma Chemical Vapor Deposition

Carbon nitride films were grown on Si substrates by a microwave plasma chemical vapor deposition method, using mixture of N2, CH4 and H2 as precursor. Scanning electron microscopy shows that the films consisted of a large number of hexagonal crystallites. The dimension of the largest crystallite is about 3 µm. The X-ray photoelectron spectroscopy suggests that nitrogen and carbon in the films are bonded through hybridized sp2 and sp3 configurations. The X-ray diffraction pattern indicates that the major part of the films is composed of α-, β-, pseudocubic C3N4 and graphitic C3N4. The Raman peaks match well with the calculated Raman frequencies of α- and β-C3N4, revealing the formation of the α- and β-C3N4 phase.

Sign in / Sign up

Export Citation Format

Share Document