The characterization and preparation of porous low dielectric films using various cyclodextrins as template materials

2003 ◽  
Vol 766 ◽  
Author(s):  
Jin-Heong Yim ◽  
Jung-Bae Kim ◽  
Hyun-Dam Jeong ◽  
Yi-Yeoul Lyu ◽  
Sang Kook Mah ◽  
...  
Keyword(s):  
Thin Film ◽  
Mechanical Properties ◽  
Dielectric Constant ◽  
Pore Structure ◽  
Pore Diameter ◽  
Dielectric Films ◽  
Low Dielectric Constant ◽  
Cyclodextrin Derivatives ◽  
Low Dielectric ◽  
Low K

AbstractPorous low dielectric films containing nano pores (∼20Å) with low dielectric constant (<2.2), have been prepared by using various kinds of cyclodextrin derivatives as porogenic materials. The pore structure such as pore size and interconnectivity can be controlled by changing functional groups of the cyclodextrin derivatives. We found that mechanical properties of porous low-k thin film prepared with mCSSQ (modified cyclic silsesquioxane) precursor and cyclodextrin derivatives were correlated with the pore interconnection length. The longer the interconnection length of nanopores in the thin film, the worse the mechanical properties of the thin film (such as hardness and modulus) even though the pore diameter of the films were microporous (∼2nm).

Robust spin-on-glass poly(methyl)silsesquioxane-based low-k materials derived from a cyclic siloxane precursor

RSC Advances ◽  
2015 ◽  
Vol 5 (82) ◽  
pp. 66511-66517 ◽  
Author(s):  
Albert S. Lee ◽  
Sung Yeoun Oh ◽  
Seung-Sock Choi ◽  
He Seung Lee ◽  
Seung Sang Hwang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Dielectric Constant ◽  
Low Dielectric Constant ◽  
Cyclic Siloxane ◽  
Low Dielectric ◽  
Methyl Silsesquioxane ◽  
Low K

Low dielectric constant poly(methyl)silsesquioxane spin-on-glass resins incorporating a cyclic precursor exhibited exceptional mechanical properties to withstand CMP processes.

Characterization of Pore Structure in a Nanoporous Low-Dielectric-Constant Thin Film by Neutron Porosimetry and X-ray Porosimetry

Langmuir ◽  
2004 ◽  
Vol 20 (16) ◽  
pp. 6658-6667 ◽  
Author(s):  
Ronald C. Hedden ◽  
Hae-Jeong Lee ◽  
Christopher L. Soles ◽  
Barry J. Bauer
Keyword(s):  
Thin Film ◽  
Dielectric Constant ◽  
Pore Structure ◽  
Low Dielectric Constant ◽  
X Ray ◽  
Low Dielectric

The Effect of Porogen on Physical Properties in MTMS-BTMSE Spin-on Organosilicates

2005 ◽  
Vol 875 ◽  
Author(s):  
B.R. Kim ◽  
J. M. Son ◽  
J.W. Kang ◽  
K.Y. Lee ◽  
K.K. Kang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Dielectric Constant ◽  
Low Dielectric Constant ◽  
Porous Films ◽  
Low Dielectric ◽  
Lower Dielectric Constant ◽  
Superior Mechanical Properties ◽  
Lift Off ◽  
Rc Delay ◽  
Low K

AbstractDecreasing the circuit dimensions is driving the need for low-k materials with a lower dielectric constant to reduce RC delay, crosstalk, and power consumption. In case of spin-on organosilicate low-k films, the incorporation of a porogen is regarded as the only foreseeable route to decrease dielectric constant of 2.2 or below by changing a packing density. In this study, MTMS-BTMSE copolymers that had superior mechanical properties than MSSQ were blended with decomposable polymers as pore generators. While adding up to 40 wt % porogen into MTMS:BTMSE=100:50 matrix, optical, electrical, and mechanical properties were measured and the pore structure was also characterized by PALS. The result confirmed that there existed a tradeoff in attaining the low dielectric constant and desirable mechanical strength, and no more pores than necessary to achieve the dielectric objective should be incorporated. When the dielectric constant was fixed to approximately 2.3 by controlling BTMSE and porogen contents simultaneously, the thermo-mechanical properties of the porous films were also investigated for the comparison purpose. Under the same dielectric constant, the increase in BTMSE and porogen contents led to improvement in modulus measured by the nanoindentation technique but deterioration of adhesion strength obtained by the modified edge lift-off test.

Structire, Properties, and Process Characteristics of Low-K Materials Prepared by PECVD

1999 ◽  
Vol 565 ◽  
Author(s):  
Y. Shimogaki ◽  
S. W. Lim ◽  
E. G. Loh ◽  
Y. Nakano ◽  
K. Tada ◽  
...  
Keyword(s):  
Growth Rate ◽  
Dielectric Constant ◽  
Gas Flow ◽  
Structural Changes ◽  
Silicon Oxide ◽  
Reactive Species ◽  
Low Dielectric Constant ◽  
Low Dielectric ◽  
Step Coverage ◽  
Low K

AbstractLow dielectric constant F-doped silicon oxide films (SiO:F) can be prepared by adding fluorine source, like as CF4 to the conventional PECVD processes. We could obtain SiO:F films with dielectric constant as low as 2.6 from the reaction mixture of SiH4/N2 O/CF4. The structural changes of the oxides were sensitively detected by Raman spectroscopy. The three-fold ring and network structure of the silicon oxides were selectively decreased by adding fluorine into the film. These structural changes contribute to the decrease ionic polarization of the film, but it was not the major factor for the low dielectric constant. The addition of fluorine was very effective to eliminate the Si-OH in the film and the disappearance of the Si-OH was the key factor to obtain low dielectric constant. A kinetic analysis of the process was also performed to investigate the reaction mechanism. We focused on the effect of gas flow rate, i.e. the residence time of the precursors in the reactor, on growth rate and step coverage of SiO:F films. It revealed that there exists two species to form SiO:F films. One is the reactive species which contributes to increase the growth rate and the other one is the less reactive species which contributes to have uniform step coverage. The same approach was made on the PECVD process to produce low-k C:F films from C2F4, and we found ionic species is the main precursor to form C:F films.

scholarly journals Electrical and Reliability Characteristics of Self-Forming Barrier for CuNd/SiOCH Films in Cu Interconnects

Coatings ◽  
2020 ◽  
Vol 10 (2) ◽  
pp. 155
Author(s):  
Yi-Lung Cheng ◽  
Chih-Yen Lee ◽  
Wei-Fan Peng ◽  
Giin-Shan Chen ◽  
Jau-Shiung Fang
Keyword(s):  
Dielectric Film ◽  
Alloy Film ◽  
Dielectric Films ◽  
Low Dielectric Constant ◽  
Electrical Characteristics ◽  
Sputtering Deposition ◽  
Cu Interconnects ◽  
Low Dielectric ◽  
Reliability Characteristics ◽  
Low K

In this study, Cu-2.2 at. % Nd alloy films using a co-sputtering deposition method were directly deposited onto porous low-dielectric-constant (low-k) films (SiOCH). The effects of CuNd alloy film on the electrical properties and reliability of porous low-k dielectric films were studied. The electrical characteristics and reliability of the porous low-k dielectric film with CuNd alloy film were enhanced by annealing at 425 °C. The formation of self-forming barrier at the CuNd/SiOCH interface was responsible for this improvement. Therefore, integration with CuNd and porous low-k dielectric is a promising process for advanced Cu interconnects.

Chemical-Mechanical Planarization of Low-k Polymers for Advanced IC Structures

2002 ◽  
Vol 124 (4) ◽  
pp. 362-366 ◽  
Author(s):  
Christopher L. Borst ◽  
Dipto G. Thakurta ◽  
William N. Gill ◽  
Ronald J. Gutmann
Keyword(s):  
Dielectric Constant ◽  
Surface Chemistry ◽  
Chemical Mechanical Planarization ◽  
Low Dielectric Constant ◽  
Chemical Company ◽  
Low Dielectric ◽  
Scale Models ◽  
Physically Based ◽  
Thickness Measurements ◽  
Low K

Successful integration of copper and low dielectric constant (low-k) materials is dependent on robust chemical-mechanical planarization (CMP) during damascene patterning. This process includes the direct removal of copper and interaction of the copper slurry with the underlying dielectric. Experiments were designed and performed to examine the CMP of two low-k polymers from Dow Chemical Company, bis-benzocyclobutene (BCB*, k=2.65) and “silicon-application low-k material” (SiLK* resin, k=2.65) with both acidic slurries suitable for copper damascene patterning and a KH phthalate-based model slurry developed for SiLK. Blanket polymer films were polished in order to determine the interactions that occur when copper and liner materials are removed by the damascene CMP process. Removal rates were obtained from material thickness measurements, post-CMP surface topography from AFM scans, and post-CMP surface chemistry from XPS measurements. Physically based wafer-scale models are presented which are compatible with the experimental results.

Sign in / Sign up

Export Citation Format

Share Document