scholarly journals The Effect of Different Bleaching Protocols, Used with and without Sodium Ascorbate, on Bond Strength between Composite and Enamel

Materials ◽  
2020 ◽  
Vol 13 (12) ◽  
pp. 2710 ◽  
Author(s):  
Maroun Ghaleb ◽  
Giovanna Orsini ◽  
Angelo Putignano ◽  
Sarah Dabbagh ◽  
Georges Haber ◽  
...  
Keyword(s):  
Hydrogen Peroxide ◽  
Bond Strength ◽  
Resin Composite ◽  
Testing Machine ◽  
Sodium Ascorbate ◽  
Control Group ◽  
Carbamide Peroxide ◽  
Total N ◽  
Peroxide Group ◽  
Significant Difference

This in vitro study aims to evaluate whether a solution of 10% sodium ascorbate (SA) may exert a beneficial effect on the bonding of composite to enamel after using different bleaching agents and protocols. Microtensile bond strength (µTBS) was evaluated on 72 freshly extracted human central incisors, divided into eight experimental groups and one control group (total n = 9): Group 1 serves as control (nonbleached). Group 2 was bleached with 5% carbamide peroxide. Group 3 was bleached with 5% carbamide peroxide and then treated with 10% SA. Group 4 was bleached with 10% carbamide peroxide. Group 5 was bleached with 10% carbamide peroxide, then treated with 10% SA. Group 6 was bleached with 16% carbamide peroxide. Group 7 was bleached with 16% carbamide peroxide, then treated with 10% SA. Group 8 was bleached with 6% hydrogen peroxide. Group 9 was bleached with 6% hydrogen peroxide, then treated with 10% SA. All groups were restored immediately after the different treatments using a resin composite. The µTBS values were measured using a universal testing machine and statistical analysis was performed by means of normality and variance analyses, SIDAK test for univariate test and multiple comparisons, and Student test to compare µTBS values of each group with the control. The mean µTBS values in groups 2, 4, 6, 8 were significantly lower than controls. For groups 3, 5, 7, 9, subjected to antioxidant (10% SA) application, all µTBS values increased significantly. However, only for Groups 3 and 5 there was no significant difference with the control. Applying 10% SA for 10 min may improve the bond strength composite/bleached enamel just when whitening is performed with 5% and 10% carbamide peroxide.

scholarly journals Comparative evaluation of superoxide dismutase, alpha-tocopherol, and 10% sodium ascorbate on reversal of shear bond strength of bleached enamel: An in vitro study

2016 ◽  
Vol 10 (01) ◽  
pp. 109-115 ◽  
Author(s):  
Mahendran Kavitha ◽  
Sharmila Selvaraj ◽  
Ambica Khetarpal ◽  
Aruna Raj ◽  
Shakunthala Pasupathy ◽  
...  
Keyword(s):  
Superoxide Dismutase ◽  
Bond Strength ◽  
Shear Bond Strength ◽  
Testing Machine ◽  
Alpha Tocopherol ◽  
Sodium Ascorbate ◽  
Control Group ◽  
Group I ◽  
Antioxidant Agents ◽  
Significant Difference

ABSTRACT Objective: The aim of this study was to investigate the neutralizer effect of antioxidant agents on the bond strength of bleached enamel. Materials and Methods: Sixty enamel slabs were prepared from 60 freshly extracted maxillary central incisors and were divided into six groups. The negative control group received no bleaching treatment and the other groups were bleached with 35% carbamide peroxide (Opalescence Quick; Ultradent, South Jordan, USA). In Group II, composite was built immediately after bleaching and cured without any antioxidants. In Group III, bleached specimens received composite build ups delayed by 1 week. In Groups IV, V, and VI bleached specimens received applications of superoxide dismutase (SOD), sodium ascorbate (SA), and tocopherol solutions, respectively, for 10 min. Following composite bonding, the micro shear bond strength (μSBS) was measured at a speed of 1 mm/min in universal testing machine. Statistical Analysis Used: The μSBS values of all the groups were analyzed using the analysis of variance followed by Tukey honestly significant difference post-hoc test. Results: Bonding of composites to unbleached group (Group I) exhibited the highest mean SBS values and among the antioxidant-treated groups, the highest SBS values were seen with SOD (Group IV) treated samples (23.0040 ± 4.30565 MPa). Conclusions: Application of SA, alpha-tocopherol, and SOD can effectively reverse the bond strength with bleached enamel. SOD gave a comparatively more promising reversal of bond strength than SA and alpha-tocopherol, and deserves further studies.

scholarly journals Improving shear bond strength of metallic brackets after whitening

2020 ◽  
Vol 25 (5) ◽  
pp. 38-43
Author(s):  
Juan Fernando Aristizábal ◽  
Angela Patricia Polanía González ◽  
James A. McNamara
Keyword(s):  
Hydrogen Peroxide ◽  
Bond Strength ◽  
Shear Bond Strength ◽  
Artificial Saliva ◽  
Tooth Bleaching ◽  
Sodium Ascorbate ◽  
Control Group ◽  
Antioxidant Treatment ◽  
Significance Level ◽  
Significant Difference

ABSTRACT Objective: To evaluate a protocol for bonding metallic brackets after bleaching with hydrogen peroxide (HP). Methods: 60 extracted maxillary premolar were randomly divided into an unbleached control group and two groups bleached with a solution of 35% hydrogen peroxide prior to bonding. The teeth in one of the treated groups were bonded immediately after bleaching; while the other group was treated with 10% sodium ascorbate immediately after bleaching and before bonding. The teeth in all groups were stored in an artificial saliva solution for 7 days after bonding. The shear bond strength data was measured in megapascals (MPa) and the fail attempts were verified. The significance level was established at p< 0.05. Results: The unbleached group, in which brackets were bonded to untreated enamel, had the highest bond strength values (11.0 ± 5.7MPa) in comparison to the bleached group (7.14 ± 40MPa), in which brackets were bonded to recently bleached enamel. Slightly improved bond strength was observed in the antioxidant group (8.13 ± 5.4MPa), in which the teeth were bleached and then the antioxidant was applied to the teeth before bonding. Unbleached and bleached groups showed statistically significant difference for shear bond strength (p=0.03) and load strength (p=0.03); no significant differences were noted between unbleached and antioxidant groups (p=0.52). Conclusion: The antioxidant treatment applied immediately after bleaching was effective in reversing the reduction in shear bond strength of brackets after tooth bleaching.

scholarly journals Effect of chitosan nanoparticles on microtensile bond strength of resin composite to dentin: an in vitro study

2020 ◽  
Vol 23 (2) ◽  
Author(s):  
Amr Mohsen Mohamed ◽  
Sameh Mahoud Nabih ◽  
Mohamed Ahmed Wakwak
Keyword(s):  
Bond Strength ◽  
Resin Composite ◽  
Testing Machine ◽  
Chitosan Nanoparticles ◽  
Tooth Surface ◽  
Control Group ◽  
Microtensile Bond Strength ◽  
Significant Difference ◽  
Self Etch

Objective: The purpose of this study was to evaluate the effect of chitosan nanoparticles on microtensile bond strength of resin composite to dentin using self etch adhesive after aging. Material and Methods: A total number of 90 freshly extracted, sound human molar teeth. Flat tooth surface was gained after cut of the occlusal surface. Three main groups according to pretreatment of dentin before adhesive application; 0.2 % chitosan, 2.5 % chitosan and no treatment control group. Universal self etch adhesive were applied according to manufacture instruction and 4 mm of Feltik Z250 xt composite. Storage of specimens for 1 day, 3 months and 6 months in 37O C distilled water. After that, the tooth was sectioned to beams of 1 mm x8 mm sticks for microtensile bond strength test using universal testing machine. Scanning electron microscope (SEM) was used to evalute the effect of chitosan nanoparticles on dentin and smear layer. Kruskal-Wallis test was used to compare between the three groups as well as the three aging periods. Dunn’s test was used for pair-wise comparisons. The significance level was set at P ≤ 0.05. Results: chitosan 0.2% is statistically significant increase in bond strength than chitosan 2.5% and control in one day group. Three months chitosan 0.2 % groups have statistically significant increase in bond strength than chitosan 2.5%. It was found in 6 months that control and chitosan 0.2 % have statistically significant increase in bond strength than chitosan 2.5%. There was statistically significant difference found between the three studied groups regarding bond strength at different storage times . Conclusion: Microtensile bond strength was influenced by different chitosan concentration. Different aging periods had no effect on the microtensile bond strength without application of chitosan and with application of 2.5% chitosan concentration.KEYWORDSChitosan nanoparticles; Microtensile bond strength; MMPs.

scholarly journals Evaluation of shear bond strength of orthodontic brackets bonded on the tooth surface after internal bleaching

2014 ◽  
Vol 43 (3) ◽  
pp. 209-213
Author(s):  
Nadia de Souza FERREIRA ◽  
Patrícia Campos Ferreira da ROSA ◽  
Raffaela Di Iorio Jeronymo FERREIRA ◽  
Marcia Carneiro VALERA
Keyword(s):  
Bond Strength ◽  
Testing Machine ◽  
Orthodontic Brackets ◽  
Tooth Bleaching ◽  
Tooth Surface ◽  
Control Group ◽  
Sodium Perborate ◽  
Safe Procedure ◽  
Carbamide Peroxide ◽  
Significant Difference

Introduction: There is great demand for esthetic treatment by patients who have discolored teeth, because currently aesthetic standards have become stricter and many patients have tooth bleaching procedures performed before or during orthodontic treatment. Objective: To evaluate the bonding of orthodontic brackets to human molars after internal tooth bleaching. Material and method: Forty molars were divided into four groups according to the bleaching agent used: PS) sodium perborate + water; PC) carbamide peroxide; PC + PS) carbamide peroxide + sodium perborate; Cont) water (control group). Bleaching agents placed inside the pulp chambers were replaced every 7 days for 2 weeks, and the brackets were bonded 30 days after the end of bleaching. The shear strength test was performed in a universal testing machine (Emic). Result: ANOVA with a significance level of 5% (p > 0.05), showed no statistically significant difference between groups (p = 0.1214). Conclusion: It was concluded that the different bleaching agents studied did not interfere with the bond strength of brackets to enamel and bonding the brackets 30 days after internal bleaching is a safe procedure.

The Effect of Prophylaxis Method on Microtensile Bond Strength of Indirect Restorations to Dentin

2012 ◽  
Vol 37 (6) ◽  
pp. 602-609 ◽  
Author(s):  
CJ Soares ◽  
JC Pereira ◽  
SJB Souza ◽  
MS Menezes ◽  
SR Armstrong
Keyword(s):  
Hydrogen Peroxide ◽  
Bond Strength ◽  
Aluminum Oxide ◽  
Sodium Bicarbonate ◽  
Resin Composite ◽  
Testing Machine ◽  
Resin Cement ◽  
Control Group ◽  
Air Abrasion ◽  
Cross Sectional

SUMMARY The aim of this study was to evaluate the effect of different materials used for dentin prophylaxis on the microtensile bond strengths (μTBS) of adhesively cemented indirect composite restorations. Sixty bovine incisors had the buccal surface ground with wet #600-grit silicon carbide abrasive paper to obtain a flat exposed superficial dentin and were submitted to different prophylaxis protocols, as follows: 3% hydrogen peroxide (HydP); 0.12% chlorhexidine (Chlo); sodium bicarbonate jet (SodB); 50-μm aluminum oxide air abrasion (AirA); pumice paste (PumP), and control group–water spray (Cont). After prophylaxis protocols a resin composite block (3.0 mm × 5.0 mm × 5.0 mm) was adhesively cemented using dual resin cement (Rely X ARC). After 24 hours of water storage, specimens were serially sectioned perpendicular to the bonded interface into 1-mm-thick slices. Each specimen was trimmed with a diamond bur to an hourglass shape with a cross-sectional area of approximately 1.0 mm2 at the bonded area. Specimens were tested (μTBS) at 0.5 mm/min using a universal testing machine. Scanning electron microscopy was used to examine the effects of prophylaxis techniques on dentin. Bond strength data (MPa) were analyzed by one-way analysis of variance and failure mode by Fisher test (α=0.05). μTBS data, means (SD), were (different superscripted letters indicate statistically significant differences): AirA, 25.2 (7.2)a; PumP, 24.1 (7.8)a; Chlo, 21.5 (5.6)a; Cont, 20.6 (8.1)a; HydP, 15.5 (7.6)b; and SodB, 11.5 (4.4)c. The use of aluminum oxide air abrasion, pumice paste, and chlorhexidine before acid etching did not significantly affect μTBS to dentin; however, the use of hydrogen peroxide and sodium bicarbonate jet significantly reduced μTBS.

scholarly journals The Effect of Different Disinfecting Agents on Bond Strength of Resin Composites

2014 ◽  
Vol 2014 ◽  
pp. 1-7 ◽  
Author(s):  
Ahmed Mohammed Hassan ◽  
Ahmed Ali Goda ◽  
Kusai Baroudi
Keyword(s):  
Bond Strength ◽  
Sodium Hypochlorite ◽  
Shear Bond Strength ◽  
Resin Composite ◽  
Testing Machine ◽  
Control Group ◽  
Posterior Teeth ◽  
Surface Pretreatment ◽  
Dentin Surface ◽  
Post Hoc

Objective. The aim of this study was to evaluate the effect of different disinfectant agents on bond strength of two types of resin composite materials.Methods. A total of 80 sound posterior teeth were used. They were divided into four groups(n=20)according to the dentin surface pretreatment (no treatment, chlorhexidine gluconate 2%, sodium hypochlorite 4%, and EDTA 19%). Each group was divided into two subgroups according to the type of adhesive (prime and bond 2.1 and Adper easy one). Each subgroup was further divided into two subgroups according to the type of resin composite (TPH spectrum and Tetric EvoCeram). Shear bond strength between dentin and resin composite was measured using Universal Testing Machine. Data collected were statistically analyzed byt-test and one-way ANOVA followed by Tukey’spost hoctest.Results. It was found that dentin treated with EDTA recorded the highest shear bond strength values followed by sodium hypochlorite and then chlorhexidine groups while the control group showed the lowest shear bond strength.Conclusions. The surface treatment of dentin before bonding application has a great effect on shear bond strength between resin composite and dentin surface.

scholarly journals Effect of Using Nano and Micro Airborne Abrasive Particles on Bond Strength of Implant Abutment to Prosthesis

2015 ◽  
Vol 26 (1) ◽  
pp. 50-55 ◽  
Author(s):  
Mansour Rismanchian ◽  
Amin Davoudi ◽  
Elham Shadmehr
Keyword(s):  
Bond Strength ◽  
Testing Machine ◽  
Control Group ◽  
Abrasive Particles ◽  
Significant Difference ◽  
Implant Abutments ◽  
Implant Abutment ◽  
Roughened Surface ◽  
Bond Strengths ◽  
Spss Software

Connecting prostheses to the implant abutments has become a concern and achieving a satisfactory retention has been focused in cement-retention prostheses recently. Sandblasting is a method to make a roughened surface for providing more retention. The aim of this study was to compare effects of nano and micro airborne abrasive particles (ABAP) in roughening surface of implant abutments and further retention of cemented copings. Thirty Xive abutments and analogues (4.5 D GH1) were mounted vertically in self-cured acrylic blocks. Full metal Ni-Cr copings with a loop on the top were fabricated with appropriate marginal adaptation for each abutment. All samples were divided into 3 groups: first group (MPS) was sandblasted with 50 µm Al2O3 micro ABAP, second group (NSP) was sandblasted with 80 nm Al2O3 nano ABAP, and the third group (C) was assumed as control. The samples were cemented with provisional cement (Temp Bond) and tensile bond strength of cemented copings was evaluated by a universal testing machine after thermic cycling. The t test for independent samples was used for statistical analysis by SPSS software (version 15) at the significant level of 0.05. Final result showed significant difference among all groups (p<0.001) and MPS manifested the highest mean retention (207.88±45.61 N) with significant difference among other groups (p<0.001). The control group showed the lowest bond strength as predicted (48.95±10.44 N). Using nano or micro ABAP is an efficient way for increasing bond strengths significantly, but it seems that micro ABAP was more effective.

scholarly journals The Impact of Chlorhexidine Mouth Rinse on the Bond Strength of Polycarbonate Orthodontic Brackets

2014 ◽  
Vol 15 (6) ◽  
pp. 688-692 ◽  
Author(s):  
Sukumaran Anil ◽  
Farouk Ahmed Hussein ◽  
Mohammed Ibrahim Hashem ◽  
Elna P Chalisserry
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Testing Machine ◽  
Test Group ◽  
Orthodontic Brackets ◽  
Control Group ◽  
Mouth Rinse ◽  
Significant Difference ◽  
Bond Strengths ◽  
The Impact

ABSTRACT Objective The purpose of the current in-vivo study was to assess the effect of using 0.12% chlorhexidine (CHX) mouth rinse, before bonding, on shear bond strength of polycarbonate brackets bonded with composite adhesive. Subjects and methods Eighteen orthodontic patients with a mean age 21.41 ± 1.2 years, who were scheduled to have 2 or more first premolars extracted, were included in this study. Patients were referred for an oral prophylaxis program which included, in part, the use of a mouth rinse. Patients were divided into 2 groups, a test group of 9 patients who used 0.12% CHX gluconate mouth rinse twice daily and a control group of 9 patients who used a mouth rinse without CHX, but with same color. After 1 week, polycarbonate brackets were bonded to first premolars with Transbond XT composite adhesive. Premolars were extracted after 28 days and tested for shear bond strength on a universal testing machine. Student's t-test was used to compare shear bond strengths of both groups. Results No statistically significant difference was found in bond strengths’ values between both groups. The test group (with CHX) has mean shear bond strength of 14.21 ± 2.42 MPa whereas the control group (without CHX) revealed a mean strength of 14.52 ± 2.31 MPa. Conclusion The use of 0.12% CHX mouth rinse, for one week before bonding, did not affect the shear bond strength of polycarbonate brackets bonded with Transbond composite. Furthermore, these brackets showed clinically acceptable bond strength. How to cite this article Hussein FA, Hashem MI, Chalisserry EP, Anil S. The Impact of Chlorhexidine Mouth Rinse on the Bond Strength of Polycarbonate Orthodontic Brackets. J Contemp Dent Pract 2014;15(6):688-692.

scholarly journals Effect of Surface Treatments on the Bond Strength to Turkom-Cera All-ceramic Material

2016 ◽  
Vol 17 (11) ◽  
pp. 920-925 ◽  
Author(s):  
Bandar MA Al-Makramani ◽  
Fuad A Al-Sanabani ◽  
Abdul AA Razak ◽  
Mohamed I Abu-Hassan ◽  
Ibrahim Z AL-Shami ◽  
...  
Keyword(s):  
Bond Strength ◽  
Ceramic Material ◽  
Failure Modes ◽  
Testing Machine ◽  
Surface Treatments ◽  
Resin Cement ◽  
Control Group ◽  
Significant Difference ◽  
All Ceramic ◽  
Effect Of Surface

ABSTRACT Aim The aim of this study was to evaluate the effect of surface treatments on shear bond strength (SBS) of Turkom-Cera (Turkom-Ceramic (M) Sdn. Bhd., Puchong, Malaysia) all-ceramic material cemented with resin cement Panavia-F (Kuraray Medical Inc., Okayama, Japan). Materials and methods Forty Turkom-Cera ceramic disks (10 mm × 3 mm) were prepared and randomly divided into four groups. The disks were wet ground to 1000-grit and subjected to four surface treatments: (1) No treatment (Control), (2) sandblasting, (3) silane application, and (4) sandblasting + silane. The four groups of 10 specimens each were bonded with Panavia-F resin cement according to manufacturer's recommendations. The SBS was determined using the universal testing machine (Instron) at 0.5 mm/min crosshead speed. Failure modes were recorded and a qualitative micromorphologic examination of different surface treatments was performed. The data were analyzed using the one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests. Results The SBS of the control, sandblasting, silane, and sandblasting + silane groups were: 10.8 ± 1.5, 16.4 ± 3.4, 16.2 ± 2.5, and 19.1 ± 2.4 MPa respectively. According to the Tukey HSD test, only the mean SBS of the control group was significantly different from the other three groups. There was no significant difference between sandblasting, silane, and sandblasting + silane groups. Conclusion In this study, the three surface treatments used improved the bond strength of resin cement to Turkom-Cera disks. Clinical significance The surface treatments used in this study appeared to be suitable methods for the cementation of glass infiltrated all-ceramic restorations. How to cite this article Razak AAA, Abu-Hassan MI, AL-Makramani BMA, AL-Sanabani FA, AL-Shami IZ, Almansour HM. Effect of Surface Treatments on the Bond Strength to Turkom-Cera All-Ceramic Material. J Contemp Dent Pract 2016;17(11):920-925.

scholarly journals Influence of curing mode of resin luting cements on bond strength to dentin

2017 ◽  
Vol 15 (4) ◽  
pp. 258
Author(s):  
Marcelo Giannini ◽  
Andreia Assis Carvalho ◽  
Ariovaldo Stefani ◽  
Wladimir Franco de Sá Barbosa ◽  
Lawrence Gonzaga Lopes
Keyword(s):  
Bond Strength ◽  
Testing Machine ◽  
Resin Cement ◽  
Control Group ◽  
Resin Cements ◽  
Luting Cements ◽  
Halogen Light ◽  
Significant Difference ◽  
Tooth Surfaces ◽  
Light Curing

Self-adhesive, dual-polymerizing resin cements require no treatment to the prepared tooth surfaces before cementation. Aim: The aim of this study was to evaluate the influence of curing mode on bond strength (BS) of three cementing systems to bovine dentin. Methods: The buccal enamel surfaces of 50 bovine incisors were removed to expose dentin and to flat the surface. The teeth were divided into five groups (n=10), which consisted of two resin cements (Multilink and Clearfil SA Cement) that were tested in dual- (halogen light for 40 s) and self-cured modes, and a control (RelyX ARC). Two cylinders of resin cements (1.0 mm X 0.75 mm) were prepared on each bonded dentin surface. After 24h at 37oC, resin cylinders were subjected to micro-shear testing in a universal testing machine (4411/Instron - 0.5 mm/min). Data were statistically analyzed by two-way ANOVA, Tukey and Dunnett`s test (5%). Results: Multilink showed higher BS than those observed on Clearfil SA. Light-curing resulted in higher BS for both Multilink and Clearfil SA. When Multilink was light-cured, no significant difference on BS was demonstrated between it and RelyX ARC. Conclusions: The highest BS values were obtained in control group and light-cured Multilink resin cement.

Sign in / Sign up

Export Citation Format

Share Document