scholarly journals Fabrication of (SiC-AlN)/ZrB2 Composite with Nano-Micron Hybrid Microstructure via PCS-Derived Ceramics Route

Materials ◽  
2021 ◽  
Vol 14 (2) ◽  
pp. 334
Author(s):  
Aidong Xia ◽  
Jie Yin ◽  
Xiao Chen ◽  
Zhengren Huang ◽  
Xuejian Liu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Raw Materials ◽  
Secondary Phase ◽  
Pressing Temperature ◽  
Xrd Pattern ◽  
Mean Grain Size ◽  
The Mean

In this work, a (SiC-AlN)/ZrB2 composite with outstanding mechanical properties was prepared by using polymer-derived ceramics (PDCs) and hot-pressing technique. Flexural strength reached up to 460 ± 41 MPa, while AlN and ZrB2 contents were 10 wt%, and 15 wt%, respectively, under a hot-pressing temperature of 2000 °C. XRD pattern-evidenced SiC generated by pyrolysis of polycarbosilane (PCS) was mainly composed by 2H-SiC and 4H-SiC, both belonging to α-SiC. Micron-level ZrB2 secondary phase was observed inside the (SiC-AlN)/ZrB2 composite, while the mean grain size (MGS) of SiC-AlN matrix was approximately 97 nm. This unique nano-micron hybrid microstructure enhanced the mechanical properties. The present investigation provided a feasible tactic for strengthening ceramics from PDCs raw materials.

Influence of Hot Pressing Temperature and SiC Content on the Microstructure and Mechanical Properties of ZrB2-SiC

2010 ◽  
Vol 434-435 ◽  
pp. 189-192
Author(s):  
Yong Zhang ◽  
Ping Hu ◽  
Xing Hong Zhang
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Volume Percent ◽  
Pressing Temperature ◽  
Sic Ceramics ◽  
Opposite Trend ◽  
Microstructure And Mechanical Properties ◽  
Dense Ceramic

The influence of hot pressing temperature and SiC content on the microstructure and mechanical properties of ZrB2-SiC ceramics was investigated. ZrB2 containing 20 volume percent SiC were prepared by hot pressing at 1850, 1900 and 1950°C for 60 min. Fully dense ceramic was obtained after hot pressing at temperature of 1950°C. In addition, the materials with SiC content of 0, 10vol.%, 15 vol.%, 20 vol.% and 30 vol.% hot pressed at 1950°C were also investigated. Results showed that the grain size of the ZrB2 significantly reduced on adding 10vol.% SiC and then decreased slightly with further increasing SiC content, whereas the grain size of SiC exhibited a opposite trend. The flexural strength of ZrB2-SiC ceramics remarkedly increased on adding 10vol.% SiC due to the significant decrease of ZrB2 particle size and then slightly increased with increasing SiC content up to 20vol.%. However, further increasing SiC content led to a reduction of the flexural strength.

Ultrafine WC-Ni-SiCw Cemented Carbides Fabricated by Spark Plasma Sintering

2012 ◽  
Vol 512-515 ◽  
pp. 924-927
Author(s):  
Hui Yong Rong ◽  
Zhi Jian Peng ◽  
Xiao Yong Ren ◽  
Ying Peng ◽  
Cheng Biao Wang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Flexural Strength ◽  
Spark Plasma Sintering ◽  
Cemented Carbides ◽  
Plasma Sintering ◽  
Mean Grain Size ◽  
Spark Plasma ◽  
The Mean ◽  
Inhomogeneous Microstructure

Ultrafine WC-Ni cemented carbides with addition of SiC whisker (SiCw) were fabricated by spark plasma sintering. The microstructure and mechanical properties of the fabricated cemented carbides were investigated. It was found that the addition of SiC whisker had no obvious influence on the phase compositions of the cemented carbides, but the mean grain size of the cemented carbides decreased as the addition fraction of SiC whisker increased. The fabricated WC-Ni cemented carbides presented the highest hardness when 0.75 wt% SiC whisker was added. However, the addition of SiC whisker was detrimental to the flexural strength of the cemented carbides because of the formation of inhomogeneous microstructure in the WC-Ni cemented carbides.

Microstructure and Mechanical Performance of AZ31-1.7 Wt.% Si Alloy Processed by Cyclic Channel Die Compression

2010 ◽  
Vol 667-669 ◽  
pp. 457-461
Author(s):  
Wei Guo ◽  
Qu Dong Wang ◽  
Man Ping Liu ◽  
Tao Peng ◽  
Xin Tao Liu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Mechanical Performance ◽  
Chinese Script ◽  
Cast State ◽  
Microstructure And Mechanical Properties ◽  
Mean Grain Size ◽  
The Matrix ◽  
The Mean

Cyclic channel die compression (CCDC) of AZ31-1.7 wt.% Si alloy was performed up to 5 passes at 623 K in order to investigate the microstructure and mechanical properties of compressed alloys. The results show that multi-pass CCDC is very effective to refine the matrix grain and Mg2Si phases. After the alloy is processed for 5 passes, the mean grain size decreases from 300 μm of as-cast to 8 μm. Both dendritic and Chinese script type Mg2Si phases break into small polygonal pieces and distribute uniformly in the matrix. The tensile strength increases prominently from 118 MPa to 216 MPa, whereas the hardness of alloy deformed 5 passes only increase by 8.4% compared with as-cast state.

Thermal Conductivity of Si₃N₄ Ceramics Fabricated From Carbothermal-reduction-derived Powder

2021 ◽  
Author(s):  
Yuelong Wang ◽  
Xingyu Li ◽  
Haoyang Wu ◽  
Baorui Jia ◽  
Deyin Zhang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermal Conductivity ◽  
Fracture Toughness ◽  
Grain Size ◽  
Flexural Strength ◽  
Grain Boundaries ◽  
Carbothermal Reduction ◽  
Secondary Phase ◽  
Gas Pressure ◽  
Gas Pressure Sintering

Abstract Si3N4-based ceramic (Si3N4-5wt%Y2O3-3wt%MgO) was obtained from carbothermal-reduction-derived powder combined with gas pressure sintering. The phase, microstructure, thermal conductivity and mechanical properties of Si3N4 ceramics were comprehensively analyzed. Dense Si3N4 ceramic with uniform grain size was obtained after sintering at 1900°C for 7 h under a N2 pressure of 1.2 MPa. The secondary phase consisted of Y4Si2O7N2 and Y2Si3O3N4 was found to gather around triangular grain boundaries. The thermal conductivity, flexural strength, hardness and fracture toughness of the Si3N4 ceramics were 95.7 W·m-1·k-1, 715 MPa, 17.2 GPa and 7.2 MPa·m1/2, respectively. The results were compared with product derived from commercial powder, the improvement of thermal conductivity (~8.3%) and fracture toughness (~4.3%) demonstrating the superiority of Si3N4 ceramics prepared from carbothermal-reduction-derived powder.

Microstructure and Mechanical Properties of SiC Whisker-Reinforced ZrB2 Ultra-High Temperature Ceramic

2008 ◽  
Vol 368-372 ◽  
pp. 1730-1732 ◽  
Author(s):  
Ping Hu ◽  
Xing Hong Zhang ◽  
Jie Cai Han ◽  
Song He Meng ◽  
Bao Lin Wang
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
High Temperature ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Room Temperature ◽  
Pressing Temperature ◽  
Sintering Time ◽  
Microstructure And Mechanical Properties ◽  
Ultra High Temperature

SiC whisker-reinforced ZrB2 matrix ultra-high temperature ceramic were prepared at 2000°C for 1 h under 30MPa by hot pressing and the effects of whisker on flexural strength and fracture toughness of the composites was examined. The flexural strength and fracture toughness are 510±25MPa and 4.05±0.20MPa⋅m1/2 at room temperature, respectively. Comparing with the SiC particles-reinforced ZrB2 ceramic, no significant increase in both strength and toughness was observed. The microstructure of the composite showed that the SiC whisker was destroyed because the SiC whisker degraded due to rapid atom diffusivity at high temperature. The results suggested that some related parameters such as the lower hot-pressing temperature, a short sintering time should be controlled in order to obtain SiC whiskerreinforced ZrB2 composite with high properties.

Simulation of Fabrication for Single-Phase Al2O3 Ceramic Tool Materials at Different Fabrication Temperature

2010 ◽  
Vol 150-151 ◽  
pp. 1358-1363
Author(s):  
Bin Fang ◽  
Chuan Zhen Huang ◽  
Chong Hai Xu ◽  
Sheng Sun
Keyword(s):  
Mechanical Properties ◽  
Computer Simulation ◽  
Grain Size ◽  
Monte Carlo ◽  
Single Phase ◽  
Two Dimensional ◽  
Ceramic Tool ◽  
Tool Materials ◽  
Mean Grain Size ◽  
The Mean

The fabrication is a key process for the preparation of ceramic tool materials, which governs the mechanical properties of ceramic tool materials under the condition of the same compositions. A computer simulation coupled with fabrication temperature for the hot-pressing process of single-phase ceramic tool materials has been developed using a two-dimensional hexagon lattice model mapped from the realistic microstructure without considering the presence of pores. The fabrication of single-phase Al2O3 is simulated. The mean grain size of simulated microstructure by Monte Carlo Potts model integrated with fabrication temperature increases with an increase in fabrication temperature, which is consistent with the experiment results.

Reactive Synthesis and Mechanical Properties of ZrB2-SiC-ZrC Composites

2008 ◽  
Vol 368-372 ◽  
pp. 1758-1760 ◽  
Author(s):  
Wen Wen Wu ◽  
Guo Jun Zhang ◽  
Yan Mei Kan ◽  
Pei Ling Wang
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Raw Materials ◽  
Reactive Synthesis ◽  
Reactive Hot Pressing

ZrB2-SiC based composites with 0,5 and 15 vol% addition of ZrC were synthesized via reactive hot pressing at 1800°C using Zr, Si and B4C as raw materials. The mechanical properties of the composites were investigated. The composite of ZSC15 that contained 15 vol% of ZrC has the highest hardness. ZSC5 with 5 vol% of ZrC owns a most homogenous microstructure and the highest fracture toughness and flexural strength.

Mechanical Properties of Porous Nanophase Materials Measured by Instrumental Indentation

1995 ◽  
Vol 400 ◽  
Author(s):  
H. Van Swygenhoven ◽  
W. Wagner ◽  
J. Löffler
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Annealing Temperature ◽  
X Ray Diffraction ◽  
X Ray ◽  
Gas Condensation ◽  
Mean Grain Size ◽  
Nanophase Materials ◽  
The Mean ◽  
Instrumental Indentation

AbstractMechanical properties of nanostructured intermetallic Ni3Al synthesized by the inert-gas condensation technique are studied by means of instrumental indentation using the ICT-CSEMEX indenter. This instrument is a microindenter which continously measures load and displacement. Load-displacement curves are performed as function of grain size, consolidation- and annealing temperature. The mean grain size of the samples are studied by means of x-ray diffraction and small-angle neutron scattering.

Microstructure and Mechanical Properties of Hot Pressed ZrC-SiC-ZrB2 Composites

2010 ◽  
Vol 434-435 ◽  
pp. 173-177 ◽  
Author(s):  
Bao Xia Ma ◽  
Wen Bo Han ◽  
Xing Hong Zhang
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Grain Size ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Ceramic Composites ◽  
Strong Function ◽  
Slight Tendency ◽  
Microstructure And Mechanical Properties

Ternary ZrC-SiC-ZrB2 ceramic composites were prepared by hot pressing at 1900 °C for 60 min under a pressure of 30 MPa in argon. The influence of ZrB2 content on the microstructure and mechanical properties of ZrC-SiC-ZrB2 composites was investigated. Examination of SEM showed that the microstructure of the composites consisted of the equiaxed ZrB2, ZrC and SiC grains, and there was a slight tendency of reduction for grain size in ZrC with increasing ZrB2 content. The hardness increased considerably from 23.3 GPa for the ZS material to 26.4 GPa for the ZS20B material. Flexural strength was a strong function of ZrB2 content, increasing from 407 MPa without ZrB2 addition to 627 MPa when the ZrB2 content was 20vol.%. However, the addition of ZrB2 has little influence on the fracture toughness, ranging between 5.5 and 5.7 MPam1/2.

Effect of Processing Condition on the Microstructure and Mechanical Properties of Ti3SiC2/SiC Composites

2010 ◽  
Vol 658 ◽  
pp. 352-355 ◽  
Author(s):  
Hong Feng Yin ◽  
Lin Lin Lu
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Flexural Strength ◽  
Hot Pressing ◽  
Processing Condition ◽  
High Porosity ◽  
Pressing Temperature ◽  
Pressing Method ◽  
Microstructure And Mechanical Properties ◽  
Sic Composites

Ti3SiC2/SiC composites were fabricated by reactive hot pressing method. Effect of processing condition on the microstructure and mechanical properties of the composites were investigated. The results showed that: (1) Hot-pressing temperature influenced the phase constituent of Ti3SiC2/SiC composites. The flexural strength and fracture toughness of composites increased with hot pressing temperature. (2) The flexural strength and fracture toughness of composites increased when the content of SiC was increased. When the SiC content was 30wt% the flexural strength and fracture toughness of Ti3SiC2/SiC composite were 371MPa and 6.9MPa•m1/2 respectively. However, when the content of SiC reached 50wt%, the flexural strength and fracture toughness of composites decreased due to high porosity in the composites. (3) The flexural strength and fracture toughness of composites increased with the particle size of SiC added in composites. (4) Ti3SiC2/SiC composites were non-brittle at room temperature.