Deformation Behavior and Dynamic Recrystallization of Hot Deformed GH625 Superalloy

2010 ◽  
Vol 146-147 ◽  
pp. 798-804
Author(s):  
Qing Miao Guo ◽  
De Fu Li ◽  
Sheng Li Guo
Keyword(s):  
Dynamic Recrystallization ◽  
Deformation Temperature ◽  
Volume Fraction ◽  
Optical Microscope ◽  
Strain Rates ◽  
Compression Tests ◽  
Continuous Dynamic Recrystallization ◽  
Transmission Electron ◽  
Lower Strain ◽  
Continuous Dynamic

Microstructure evolution during dynamic recrystallization (DRX) of hot deformed GH625 superalloy was investigated by optical microscope (OP) and transmission electron microscope (TEM). Hot compression tests were conducted using Gleeble-1500 simulator. It was found that the nucleation mechanism of DRX for the alloy deformed at 1150°C is composed of discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX) in the vicinity of the serrated grain boundaries. With the increasing strain, the fraction of the DRX grains increases, while the size of the DRX grains almost remains in the same range. As the deformation temperature increasing, the size and fraction of the DRX grains increase, and no precipitation of intergranular carbides are found when the deformation temperature increases to 1150°C. At lower strain rate, the size and volume fraction of DRX grains decrease with the increasing strain rates. However, the size and volume fraction of DRX grains increase at higher strain rates due to the deformation thermal effect.

Dynamic Recrystallization of Zircaloy-4 during Working within the Upper α-Range

2004 ◽  
Vol 467-470 ◽  
pp. 1151-1156 ◽  
Author(s):  
Cédric Chauvy ◽  
Pierre Barbéris ◽  
Frank Montheillet
Keyword(s):  
Dynamic Recrystallization ◽  
Large Strain ◽  
Large Angle ◽  
Rate Sensitivity ◽  
Large Strains ◽  
Strain Rates ◽  
Compression Tests ◽  
Continuous Dynamic Recrystallization ◽  
Ebsd Technique ◽  
Continuous Dynamic

Compression tests were used to simulate simple deformation paths within the upper a-range of Zircaloy-4 (i.e. 500°C-750°C). The mechanical behaviour reveals two different domains : at low temperatures and large strain rates, strain hardening takes place before flow softening, whereas this first stage disappears at lower flow stress levels. Strain rate sensitivity and activation energy were determined for both domains. Dynamic recrystallization was investigated using the Electron BackScattering Diffraction (EBSD) technique. It appears that the mechanism involved here is continuous dynamic recrystallization (CDRX), based on the increasing misorientation of subgrain boundaries and their progressive transformation into large angle boundaries. At low strains (e £ 0.3), CDRX kinetics are similar whatever the deformation conditions, while higher temperatures and lower strain rates promote recrystallization at large strains.

scholarly journals Strain Compensation Constitutive Model and Parameter Optimization for Nb-Contained 316LN

Metals ◽  
2019 ◽  
Vol 9 (2) ◽  
pp. 212 ◽  
Author(s):  
Jingdan Li ◽  
Jiansheng Liu
Keyword(s):  
Flow Stress ◽  
Constitutive Model ◽  
Dynamic Recrystallization ◽  
Strain Rate ◽  
Compression Tests ◽  
Continuous Dynamic Recrystallization ◽  
Transmission Electron ◽  
Strain Compensation ◽  
Temperature Ranges ◽  
Continuous Dynamic

Hot deformation behavior of Nb-contained 316LN was investigated using a series of compression tests performed on a Gleeble-1500D simulator at temperature of 950–1200 °C and strain rate of 0.01~1 s−1. Based on the strain compensation method, a modified Arrhenius constitutive model considering the comprehensive effects of temperature, strain rate, and strain on flow stress was established, and the accuracy of the proposed model was evaluated by introducing correlation coefficient (R) and average relative error (AARE). The values of R and AARE were calculated as 0.995 and 4.48%, respectively, proving that the modified model has a high accuracy in predicting the flow stress of Nb-contained 316LN. The microstructure evolution and the dynamic recrystallization (DRX) mechanism of the experimental material were explicated by optical microscopy (OM), electron back scattered diffraction (EBSD), and transmission electron microscopy (TEM). It was found that continuous dynamic recrystallization (CDRX) characterized by subgrain evolution and discontinuous dynamic recrystallization (DDRX) featured by grain boundary nuclei are two main dynamic recrystallization (DRX) mechanisms of Nb-contained 316LN. Furthermore, based on the results of microstructure analyses, optimum parameters were obtained as temperature ranges of 1100~1200 °C and strain rate ranges of 0.01~1 s−1.

scholarly journals Investigation into Microstructure Evolution of Co–Ni–Cr–W–Based Superalloy During Hot Deformation

2021 ◽  
Vol 8 ◽  
Author(s):  
Wei Zhang ◽  
Baohong Zhu ◽  
Shuaishuai Wu ◽  
Shutian Tao
Keyword(s):  
Dynamic Recrystallization ◽  
Microstructure Evolution ◽  
Hot Deformation ◽  
Electron Backscatter Diffraction ◽  
Strain Rates ◽  
Compression Tests ◽  
Continuous Dynamic Recrystallization ◽  
Nucleation Mechanisms ◽  
Ebsd Technique ◽  
Continuous Dynamic

Hot compression tests were conducted using a Gleeble 3500 thermomechanical simulator at temperatures ranging from 1,000 to 1,200°C with the strain rate ranging from 0.1 to 10 s−1. Electron backscatter diffraction (EBSD) technique was employed by investigating the microstructure evolution during hot deformation. Microstructure observations reveal that deformation temperatures and strain rates have a significant effect on the DRX process. It is found that the fraction and grain size of DRX increase with the decreasing deformation temperature, along with the increasing high-angle grain boundaries (HAGBs). The fraction of DRX first decreases and then increases with the increase of strain rates. It is noted that there are both the nucleation mechanisms of discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX) during the DRX process for Co–Ni–Cr–W–based superalloys. DDRX and CDRX are the primary and subsidiary nucleation mechanisms of DRX, respectively. It is also found that deformation temperatures and strain rates have almost no effect on the primary and subsidiary nucleation mechanisms of DRX. At the temperature above 1,150°C, the complete DRX occurred with the average grain sizes of about 25.32–29.01 μm. The homogeneity and refinement of microstructure can be obtained by selecting the suitable hot deformation parameters.

scholarly journals Investigation on Sub-Solvus Recrystallization Mechanisms in an Advanced γ-γ’ Nickel-Based Superalloy GH4151

Materials ◽  
2020 ◽  
Vol 13 (20) ◽  
pp. 4553
Author(s):  
Shaomin Lv ◽  
Jinbin Chen ◽  
Xinbo He ◽  
Chonglin Jia ◽  
Kang Wei ◽  
...  
Keyword(s):  
Dynamic Recrystallization ◽  
Hot Deformation ◽  
Energy Surface ◽  
Electron Backscatter Diffraction ◽  
True Strain ◽  
Continuous Dynamic Recrystallization ◽  
Nickel Based Superalloy ◽  
Transmission Electron ◽  
Continuous Dynamic ◽  
Backscatter Diffraction

Sub-solvus dynamic recrystallization (DRX) mechanisms in an advanced γ-γ’ nickel-based superalloy GH4151 were investigated by isothermal compression experiments at 1040 °C with a strain rate of 0.1 s−1 and various true strain of 0.1, 0.3, 0.5, and 0.7, respectively. This has not been reported in literature before. The electron backscatter diffraction (EBSD) and transmission electron microscope (TEM) technology were used for the observation of microstructure evolution and the confirmation of DRX mechanisms. The results indicate that a new dynamic recrystallization mechanism occurs during hot deformation of the hot-extruded GH4151 alloy. The nucleation mechanism can be described as such a feature, that is a primary γ’ (Ni3(Al, Ti, Nb)) precipitate embedded in a recrystallized grain existed the same crystallographic orientation, which is defined as heteroepitaxial dynamic recrystallization (HDRX). Meanwhile, the conventional DRX mechanisms, such as the discontinuous dynamic recrystallization (DDRX) characterized by bulging grain boundary and continuous dynamic recrystallization (CDRX) operated through progressive sub-grain merging and rotation, also take place during the hot deformation of the hot-extruded GH4151 alloy. In addition, the step-shaped structures can be observed at grain boundaries, which ensure the low-energy surface state during the DRX process.

Flow Behavior and Dynamic Recrystallization of BT25y Titanium Alloy During Hot Deformation

2018 ◽  
Vol 37 (2) ◽  
pp. 181-192 ◽  
Author(s):  
Xuemei Yang ◽  
Hongzhen Guo ◽  
Zekun Yao ◽  
Shichong Yuan
Keyword(s):  
Dynamic Recrystallization ◽  
Hot Deformation ◽  
Volume Fraction ◽  
Flow Behavior ◽  
Strain Rates ◽  
Recrystallization Behavior ◽  
Lower Strain ◽  
Deformation Activation Energy ◽  
Strain Data ◽  
Dynamic Recrystallization Behavior

AbstractThe high-temperature plastic deformation and dynamic recrystallization behavior of BT25y alloy were investigated within the deformation temperatures of 1,213–1,293 K and strain rates of 0.001–1.0 s–1 on a Gleeble-1500 thermo-mechanical simulator. Results showed that the dynamic recrystallization (DRX) mechanism played an important role in the hot deformation of BT25y alloy. Based on the regression analysis of the true stress–strain data, the stress exponent and deformation activation energy of BT25y alloy were calculated to be 3.4912 and 288.0435 kJ/mol, respectively. The θ-σ and dθ/dσ–σ curves were plotted to further obtain the critical stress and critical strain for the occurrence of DRX. Based on the analysis results, the DRX kinetic model was established. The model was validated by the comparison between predicted and experimental volume fraction of DRX. As the DRX evolution was sensitive to deformation temperature and strain rate, quantities of dynamically recrystallized grains appeared at higher temperatures and lower strain rates.

Effect of Hot Deformation Parameters on Flow Behavior and Microstructure of Ti-6Al-4V-0.2O Alloy

2017 ◽  
Vol 898 ◽  
pp. 137-143
Author(s):  
Lin Xiang ◽  
Bin Tang ◽  
Hong Chao Kou ◽  
Jie Shao ◽  
Jin Shan Li
Keyword(s):  
Strain Rate ◽  
Hot Deformation ◽  
Deformation Temperature ◽  
Dynamic Recovery ◽  
Volume Fraction ◽  
Flow Behavior ◽  
Strain Rates ◽  
Compression Tests ◽  
Height Reduction ◽  
Deformation Parameters

Isothermal compression tests were conducted to investigate the effect of hot deformation parameters on flow behavior and microstructure of Ti-6Al-4V-0.2O alloy. The experimental results show that the strain rate and height reduction have little effect on the volume fraction of primary α at a deformation temperature of 860 ̊C. At a deformation temperature of 940 ̊C, the volume fraction of primary α at a high strain rate (10s-1) is about 10% less than that at low strain rates (0.01s-1~1s-1). It may be one of the reasons for the significantly discontinuous yielding phenomenon. Another reason is that the dislocation density decreased suddenly due to the dynamic recovery. With the increasing strain rate and the decreasing deformation temperature, the volume fraction of irregular secondary α increases and lamellar secondary α decreases. And with height reduction increasing, the irregular secondary α increases firstly and then tends to be steady because of dynamic recovery and recrystallization.

scholarly journals Effects of Repetitive Upsetting Extrusion on the Microstructure and Texture of GWZK124 Alloy under Different Starting Temperatures

Materials ◽  
2019 ◽  
Vol 12 (15) ◽  
pp. 2437
Author(s):  
Guanshi Zhang ◽  
Zhimin Zhang ◽  
Yingze Meng ◽  
Zhaoming Yan ◽  
Xin Che ◽  
...  
Keyword(s):  
Grain Size ◽  
Dynamic Recrystallization ◽  
Grain Refinement ◽  
Volume Fraction ◽  
Bimodal Microstructure ◽  
Continuous Dynamic Recrystallization ◽  
Average Grain Size ◽  
Second Phases ◽  
Continuous Dynamic ◽  
Weak Texture

The effects of repetitive upsetting extrusion under different starting temperatures on the microstructure and texture of GWZK124 alloy were investigated. The results clearly showed that the particles and second phases induced dynamic recrystallization (DRX), which can be explained by the particle-stimulated nucleation (PSN) mechanism. It was shown that grain refinement during repetitive upsetting extrusion (RUE) is dominated by a complicated combination of continuous dynamic recrystallization and discontinuous dynamic recrystallization. The RUEed alloys under different starting temperatures exhibited a bimodal microstructure comprising fine DRXed grains with weak texture and coarse deformed grains with strong texture. The DRXed grains could weaken the texture. As the RUE starting temperature decreased, the average grain size increased and the volume fraction of DRXed grains decreased.

Dynamic Recrystallization Behavior of Biomedical CCM Alloys in Hot Compression Process

2010 ◽  
Vol 654-656 ◽  
pp. 1275-1278 ◽  
Author(s):  
Yun Ping Li ◽  
Shingo Kurosu ◽  
Emi Onodera ◽  
Hiroaki Matsumoto ◽  
Akihiko Chiba
Keyword(s):  
Dynamic Recrystallization ◽  
Hot Forging ◽  
Stacking Faults ◽  
Recrystallization Behavior ◽  
Compression Tests ◽  
Compression Process ◽  
Continuous Dynamic Recrystallization ◽  
Computer Aided ◽  
Dynamic Recrystallization Behavior ◽  
Continuous Dynamic

Dynamic recrystallization behavior of Co-29Cr-6Mo-0.16N alloy was analyzed in details. Compression tests were carried out in a computer aided Thermecmaster- Z hot forging simulator. The results showed that uniformly distributed superfine grain size could be obtained by continuous dynamic recrystallization (DRX) process; Texture-free microstructure with uniformly distributed equiaxed fine grains was obtained. The formation of profuse stacking faults and their subsequent intersections are considered to be the principle mechanisms of DRX.

scholarly journals Evolution of Dynamic Recrystallization in 5CrNiMoV Steel during Hot Forming

2020 ◽  
Vol 2020 ◽  
pp. 1-13
Author(s):  
Zhiqiang Hu ◽  
Kaikun Wang
Keyword(s):  
Grain Size ◽  
Dynamic Recrystallization ◽  
Strain Rate ◽  
Volume Fraction ◽  
True Strain ◽  
True Stress ◽  
Hot Forming ◽  
Strain Rates ◽  
Stress Strain ◽  
Lower Strain

The dynamic recrystallization (DRX) behavior of 5CrNiMoV steel was investigated through hot compression at temperatures of 830–1230°C and strain rates of 0.001–10 s−1. From the experimental results, most true stress-strain curves showed the typical nature of DRX that a single peak was reached at low strains followed by a decrease of stress and a steady state finally at relatively high strains. The constitutive behavior of 5CrNiMoV steel was analyzed to deduce the operative deformation mechanisms, and the correlation between flow stress, temperature, and strain rate was expressed as a sine hyperbolic type constitutive equation. Based on the study of characteristic stresses and strains on the true stress-strain curves, a DRX kinetics model was constructed to characterize the influence of true strain, temperature, and strain rate on DRX evolution, which revealed that higher temperatures and lower strain rates had a favorable influence on improving the DRX volume fraction at the same true strain. Microstructure observations indicated that DRX was the main mechanism and austenite grains could be greatly refined by reducing the temperature of hot deformation or increasing the strain rate when complete recrystallization occurred. Furthermore, a DRX grain size model of 5CrNiMoV was obtained to predict the average DRX grain size during hot forming.

Dynamic Recrystallization of Ferrite in Low Carbon Steels

2007 ◽  
Vol 558-559 ◽  
pp. 617-622 ◽  
Author(s):  
Zu Qing Sun ◽  
Long Fei Li ◽  
Wang Yue Yang
Keyword(s):  
Carbon Steel ◽  
Dynamic Recrystallization ◽  
Low Carbon Steel ◽  
Carbon Steels ◽  
Low Carbon ◽  
Compression Tests ◽  
Hollomon Parameter ◽  
Low Carbon Steels ◽  
Continuous Dynamic Recrystallization ◽  
Continuous Dynamic

Dynamic recrystallization(DRX) of ferrite in low carbon steels was investigated by hot compression tests at temperatures of 550 to 700oC at strain rates of 0.001 to 10s-1. The results indicate that DRX of ferrite can occur in low carbon steels and lead to grain refinement. With increasing Zener-Hollomon parameter Z, its mechanism changes from discontinuous dynamic recrystallization to continuous dynamic recrystallization, the turning point is approximately at Z=1×1016s-1 for a low carbon steel with 0.171wt% C. The results also indicate that changing the minor constituents of the low carbon steel from pearlite colonies to fine cementite particles has an effect on promoting DRX of ferrite, and the increase of Mn content and the presence of tiny Nb precipitates have opposite effects respectively. However, all these changes are of benefit to the refinement of recrystallized grains.

Sign in / Sign up

Export Citation Format

Share Document