Low Velocity Impact Resistance of CPVC Pipes Exposed to Natural Outdoor Weathering Conditions

2012 ◽  
Vol 445 ◽  
pp. 959-964
Author(s):  
Z. Khan ◽  
Necar Merah ◽  
A. Bazoune ◽  
S. Furquan
Keyword(s):  
Impact Resistance ◽  
Outdoor Exposure ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Pipe Material ◽  
Low Velocity ◽  
Impact Energies ◽  
The Impact ◽  
Impact Events ◽  
Outdoor Weathering

Low velocity drop weight impact testing of CPVC pipes was conducted on 160 mm long pipe sections obtained from 4-inch (100 mm) diameter schedule 80 pipes. Impact test were carried out for the base (as received) pipes and after their exposure to out door natural weathering conditions in Dhahran, Saudi Arabia. The results of the impact testing on the natural (outdoor exposure) broadly suggest that the natural outdoor exposures produce no change in the impact resistance of CPVC pipe material for the impact events carrying low incident energies of 10 and 20J. At the impact energies of 35 and 50J the natural outdoor exposures appear to cause appreciable degradation in the impact resistance of the CPVC pipe material. This degradation is noted only for the longer exposure periods of 12 and 18 months.

scholarly journals Improved impact response of hygrothermally conditioned carbon/epoxy woven composites

2016 ◽  
Vol 23 (6) ◽  
pp. 699-710 ◽  
Author(s):  
Yucheng Zhong ◽  
Sunil Chandrakant Joshi
Keyword(s):  
Carbon Fiber ◽  
Impact Resistance ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Elastic Response ◽  
Woven Composites ◽  
Low Velocity ◽  
Hygrothermal Conditioning ◽  
The Impact ◽  
Carbon Fiber Epoxy

AbstractThe effects of hygrothermal conditioning and moisture on the impact resistance of carbon fiber/epoxy composite laminates were investigated. Specimens were fabricated from carbon fiber/epoxy woven prepreg materials. The fabricated specimens were either immersed in water at 80°C or subjected to hot/wet (at 80°C in water for 12 h) to cold/dry (at -30°C in a freezer for 12 h) cyclic hygrothermal conditions, which resulted in different moisture contents inside the laminates. It was found that the absorbed moisture did not migrate out from composite materials at -30°C. Neither of the hygrothermal conditions in this study had detrimental effects on the microstructure of the laminates. Low-velocity impact testing was subsequently conducted on the conditioned specimens. When attacked by the same level of impact energy, laminates with different moisture levels experienced different levels of impact damage. Moisture significantly alleviated the extent of damage in carbon fiber/epoxy woven laminates. The elastic response of the laminate under impact was improved after hygrothermal conditioning. The mechanism behind the improved impact resistance after absorbing moisture was proposed and deliberated.

TEMPERATURE EFFECT OF LOW VELOCITY IMPACT RESISTANCE OF GLASS/EPOXY LAMINATES

2010 ◽  
Vol 24 (15n16) ◽  
pp. 2657-2663 ◽  
Author(s):  
KI-WEON KANG ◽  
HEUNG-SEOB KIM ◽  
TAE-JIN CHUNG ◽  
SEUNG-KEE KOH
Keyword(s):  
Composite Laminates ◽  
Impact Damage ◽  
Testing Machine ◽  
Impact Resistance ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Effect Of Temperature ◽  
Low Velocity ◽  
Damage Resistance ◽  
The Impact

This paper aims to evaluate the effect of temperature on impact damage resistance of glass/epoxy laminates. A series of impact tests were performed using an instrumented impact-testing machine at temperature ranging from -40°C to +80°C. The resulting impact damage was measured using back light method. The impact resistance parameters were employed to understand the damage resistance. It was observed that temperature has a little effect on the impact responses of composite laminates. The damage resistance of glass/epoxy laminates is somewhat deteriorated at two opposite extremes of the studied temperature range and this behavior is likely due to the property change of glass/epoxy laminates under extreme temperatures

Impact Damage Resistance of Glass/Epoxy Laminates with Embedded Shape Memory Alloy

2007 ◽  
Vol 345-346 ◽  
pp. 1529-1532 ◽  
Author(s):  
Ki Weon Kang ◽  
H.J. Kim ◽  
J.H. Kim ◽  
Heung Seob Kim ◽  
Yong Su Kim ◽  
...  
Keyword(s):  
Shape Memory Alloy ◽  
Shape Memory ◽  
Impact Damage ◽  
Testing Machine ◽  
Impact Resistance ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Damage Resistance ◽  
The Impact

This paper deals with the damage resistance of glass/epoxy laminates with embedded shape memory alloy (SMA) subjected to low-velocity impact at various temperatures. For this goal, the impact tests were performed by using an instrumented impact-testing machine at three temperatures: +20°C, -10°C and -40°C. And the resultant damages were inspected through the scanning acoustic microscope (SAM). Also, based on the impact force history and the damage configuration, the impact resistance parameters were employed to evaluate damage resistance of laminates with embedded SMA wires. As results, it was found that the damage resistance of glass/epoxy laminates with embedded SMA wires is dependent on the service temperature.

Low Velocity and Compression-After-Impact Response of Pin-Reinforced Sandwich Composites

1999 ◽  
Author(s):  
Uday K. Vaidya ◽  
Mohan V. Kamath ◽  
Mahesh V. Hosur ◽  
Anwarul Haque ◽  
Shaik Jeelani
Keyword(s):  
Impact Testing ◽  
Low Velocity Impact ◽  
Sandwich Composites ◽  
Low Velocity ◽  
Static Compression ◽  
Velocity Impact ◽  
Transverse Stiffness ◽  
Impact Studies ◽  
Compression After Impact ◽  
The Impact

Abstract In the current work, sandwich composite structures with innovative constructions referred to as Z-pins, or truss core pins are investigated, in conjunction with traditional honeycomb and foam core sandwich constructions, such that they exhibit enhanced transverse stiffness, high damage resistance and furthermore, damage tolerance to impact. While the investigations pertaining to low velocity impact have appeared recently in Vaidya et al. 1999, the current paper deals with compression-after-impact studies conducted to evaluate the residual properties of sandwich composites “with” and “without” reinforced foam cores. The resulting sandwich composites have been investigated for their low velocity (< 5 m/sec) impact loading response using instrumented impact testing at energy levels ranging from 5 J to 50 J impact energy. The transverse stiffness of the cores and their composites has also been evaluated through static compression studies. Compression-after-impact studies were then performed on the sandwich composites with traditional and pin-reinforcement cores. Supporting vibration studies have been conducted to assess the changes in stiffness of the samples as a result of the impact damage. The focus of this paper is on the compression-after-impact (CAI) response and vibration studies with accompanying discussion pertaining to the low velocity impact.

scholarly journals Ultrasonic Analysis of Damage in CFRP Resulting from Static Indentation and Low Velocity Impact

1993 ◽  
Vol 2 (3) ◽  
pp. 096369359300200
Author(s):  
H. Kaczmarek
Keyword(s):  
Impact Testing ◽  
Low Velocity Impact ◽  
Ultrasonic Tomography ◽  
Transverse Impact ◽  
Low Velocity ◽  
Velocity Impact ◽  
Testing Procedures ◽  
Damage Initiation ◽  
Static Indentation ◽  
The Impact

In order to reduce hidden damage caused in CFRP by low velocity transverse impact, testing procedures must be established by understanding the impact phenomena and the roles of various parameters on damage initiation and growth. Hence, composite plates were stressed and an original method, “ultrasonic tomography,” was applied to detect delaminations on the interfaces. The results show the similarity of the damage growth resulting from static indentation and low velocity impact.

Impact Damage and Strength Reduction Behavior of Honeycomb Sandwich Structure Subjected to Low Velocity Impact

2006 ◽  
Vol 306-308 ◽  
pp. 279-284
Author(s):  
Ki Weon Kang ◽  
Jung Kyu Kim ◽  
Heung Seob Kim
Keyword(s):  
Sandwich Structure ◽  
Impact Damage ◽  
Testing Machine ◽  
Strength Reduction ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Reduction Behavior ◽  
Velocity Impact ◽  
The Impact

The goals of the paper are to identify the impact damage and strength reduction behavior of sandwich structure, composed of carbon/epoxy laminates skin and Nomex core with two kinds of thickness (10 and 20mm). For these, low velocity impact tests were conducted using the instrumented impact-testing machine and damages are inspected by SAM. And then, subsequent static tests are conducted under flexural loading to identify the strength reduction behavior of the impacted sandwich structures. The impact damages are mainly delamination in carbon/epoxy skin and their behavior is mostly independent of core thickness. Also, their energy absorbing behavior is identified through calculating the energy absorbed by impact damage. Finally, the strength reduction behavior is evaluated through Caprino’s model, which was proposed on the unidirectional laminates.

scholarly journals Enhanced Impact-Resistance of Aeronautical Quasi-Isotropic Composite Plates Through Diffused Water Molecules in Epoxy

2020 ◽  
Author(s):  
Furqan Ahmad ◽  
Fethi Abbassi ◽  
Mazhar Ul-Islam ◽  
Frédéric JACQUEMIN ◽  
Jung-Wuk Hong
Keyword(s):  
Carbon Fiber ◽  
Impact Resistance ◽  
Composite Plates ◽  
Hot Water ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Segmental Mobility ◽  
Impact Tests ◽  
Isotropic Composite ◽  
The Impact

Abstract In order to elucidate the hygroscopic effects on impact-resistance of carbon fiber/epoxy quasi-isotropic composite plates, low-velocity impact tests are conducted on dry and hygroscopically conditioned plates, respectively, under identical configurations. For the impact tests, plates were immersed in the hot water at 80 °C to absorb a different amount of moisture content (MC). Experimental results reveal that the presence of the MC plays a pivotal role by improving the impact-resistance of composite plates. Plates with higher percentage of MC could behave elastically to a larger strain, yielding larger deflection under impact loading. From SEM fractographies, it is observed that small disbanding grows at the interface of epoxy and carbon fiber due to absorbed MC. After absorbing MC, most of impact enegy is dissipated in hygroscopic conditioned composite plates throught elastic deformation and overall less damage is induced in wet composite plates compare to the dry plate. We can postulate that the presence of MC increases the elastic limit as well as ductility of the epoxy by promoting chain segmental mobility of the polymer molecules, which eventually leads to the enhancement of the impact-resistance of wet quasi-isotropic composite plates in comparison with the dry plate.

scholarly journals Effect of Fibres on the Failure Mechanism of Composite Tubes under Low-Velocity Impact

Materials ◽  
2020 ◽  
Vol 13 (18) ◽  
pp. 4143
Author(s):  
Jie Xiao ◽  
Han Shi ◽  
Lei Tao ◽  
Liangliang Qi ◽  
Wei Min ◽  
...  
Keyword(s):  
Failure Mechanism ◽  
Impact Resistance ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Basalt Fibre ◽  
Composite Tubes ◽  
Velocity Impact ◽  
Fibre Breakage ◽  
Reinforced Composite ◽  
The Impact

Filament-wound composite tubular structures are frequently used in transmission systems, pressure vessels, and sports equipment. In this study, the failure mechanism of composite tubes reinforced with different fibres under low-velocity impact (LVI) and the radial residual compression performance of the impacted composite tubes were investigated. Four fibres, including carbon fiber-T800, carbon fiber-T700, basalt fibre, and glass fibre, were used to fabricate the composite tubes by the winding process. The internal matrix/fibre interface of the composite tubes before the LVI and their failure mechanism after the LVI were investigated by scanning electric microscopy and X-ray micro-computed tomography, respectively. The results showed that the composite tubes mainly fractured through the delamination and fibre breakage damage under the impact of 15 J energy. Delamination and localized fibre breakage occur in the glass fibre-reinforced composite (GFRP) and basalt fibre-reinforced composite (BFRP) tubes when subjected to LVI. While fibre breakage damage occurs globally in the carbon fibre-reinforced composite (CFRP) tubes. The GFRP tube showed the best impact resistance among all the tubes investigated. The basalt fibre-reinforced composite (BFRP) tube exhibited the lowest structural impact resistance. The impact resistance of the CFRP-T700 and CFRP-T800 tube differed slightly. The radial residual compression strength (R-RCS) of the BFRP tube is not sensitive to the impact, while that of the GFRP tube is shown to be highly sensitive to the impact.

The Effect of the Impactor Diameter and Boundary Conditions on Low Velocity Impact Composites Behaviour

2007 ◽  
Vol 7-8 ◽  
pp. 217-222 ◽  
Author(s):  
Ana M. Amaro ◽  
Paulo N.B. Reis ◽  
A.G. Magalhães ◽  
Marcelo F.S.F. de Moura
Keyword(s):  
Boundary Conditions ◽  
Damage Model ◽  
Testing Machine ◽  
Three Dimensional ◽  
Experimental Tests ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Velocity Impact ◽  
Impact Energies ◽  
The Impact

The aim of present work is to study the influence of the impactor diameter and boundary conditions on low velocity impact on carbon-fibre-reinforced epoxy laminates. Experimental tests were performed on [04,904]s laminates, using a drop weight-testing machine. Circular plates were tested under low velocity impacts for two diameters of the hemispherical impactor, 12.7 mm and 20 mm, and considering similar impact energies, 2.6 J for the first impactor and 3 J for the second one. Rectangular and square plates were analysed under low velocity impacts with different boundary conditions. The impacted plates were inspected by X-radiography. Numerical simulations were also performed considering interface finite elements compatible with three-dimensional solid elements including a cohesive mixed-mode damage model, which allows to model delamination between layers. The impact tests showed that both the impactor’s diameter and boundary conditions have influence on the delaminated area. Good agreement between experimental and numerical analysis for shape, orientation and size of damage was obtained.

Investigation of the Effects of Core Thickness on Low Velocity Impact Behaviors of Aluminum Honeycomb Composites

2021 ◽  
Author(s):  
Kasım Karataş ◽  
Okan Özdemir
Keyword(s):  
Sheet Material ◽  
Energy Levels ◽  
Impact Testing ◽  
Low Velocity Impact ◽  
Core Material ◽  
Low Velocity ◽  
Velocity Impact ◽  
Impact Tests ◽  
Aluminum Honeycomb ◽  
The Impact

Honeycomb structures are used where the weight to strength ratio is important. They are also preferred to absorb the energy from the blows received. In this study, low velocity impact behavior of aluminum honeycomb composites with different core thicknesses were investigated. Aluminum honeycombs used in this study are AL3003 honeycombs of 10 mm and 15 mm thicknesses. Glass fiber reinforced epoxy sheets with a thickness of 2 mm were used as the surface sheet material. Composite plates were produced by vacuum infusion method. The upper and lower face plates were cut in dimensions of 100x100 mm. The cut plates were attached to the core material with adhesive and a sandwich structure was formed. After bonding, low velocity impact tests were performed on these test samples at 40J, 100J and 160J energy levels using the composite CEAST Fractovis Plus impact testing machine. According to the results obtained from the impact tests, at higher energy levels, 15 mm thick composites have 10-15% higher energy absorption capacity than 10 mm.

Sign in / Sign up

Export Citation Format

Share Document