Optical Property of Spark Plasma Sintered Translucent AlN Ceramics

2007 ◽  
Vol 336-338 ◽  
pp. 545-548
Author(s):  
Y. Xiong ◽  
Zheng Yi Fu ◽  
Hang Wang
Keyword(s):  
Grain Size ◽  
Optical Property ◽  
Grain Boundaries ◽  
Spark Plasma Sintering ◽  
Secondary Phases ◽  
Fine Grain ◽  
Sintering Additive ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
Good Optical Property

Translucent AlN ceramics were fabricated using spark plasma sintering (SPS) technique with 3wt% CaF2 as sintering additive. The samples achieved 52.4% maximum transmittance in medium IR region after 10 min holding time by spark plasma sintering at 1800°C and 30 MPa pressure in N2. The results from XRD, SEM, TEM and EDX showed that the sintered bodies were densely compacted and highly pure with fine grain size and uniform microstructures. No secondary phases were observed at the grain boundaries and triple grain junctions, which guaranteed good optical property of the sintered bodies.

Densification and Thermal Conductivity of Y2O3-Doped AlN Ceramics by Spark Plasma Sintering

2007 ◽  
Vol 352 ◽  
pp. 227-231 ◽  
Author(s):  
Qiang Shen ◽  
Z.D. Wei ◽  
Mei Juan Li ◽  
Lian Meng Zhang
Keyword(s):  
Thermal Conductivity ◽  
Grain Boundaries ◽  
Spark Plasma Sintering ◽  
Particle Surface ◽  
Boundary Phase ◽  
Homogeneous Microstructure ◽  
Densification Mechanism ◽  
Sintering Additive ◽  
Plasma Sintering ◽  
Spark Plasma

AlN ceramics doped with yttrium oxide (Y2O3) as the sintering additive were prepared via the spark plasma sintering (SPS) technique. The sintering behaviors and densification mechanism were mainly investigated. The results showed that Y2O3 addition could promote the AlN densification. Y2O3-doped AlN samples could be densified at low temperatures of 1600-1700oC in 20-25 minutes. The AlN samples were characterized with homogeneous microstructure. The Y-Al-O compounds were created on the grain boundaries due to the reactions between Y2O3 and Al2O3 on AlN particle surface. With increasing the sintering temperature, AlN grains grew up, and the location of grain boundaries as well as the phase compositions changed. The Y/Al ratio in the aluminates increased, from Y3Al5O12 to YAlO3 and to Y4Al2O9. High-density, the growth of AlN grains and the homogenous dispersion of boundary phase were helpful to improve the thermal conductivity of AlN ceramics. The thermal conductivity of 122Wm-1K-1 for the 4.0 mass%Y2O3-doped AlN sample was reached.

Grain Growth, Microstructure and Property of Ultrafine WC-Co Alloy by Spark Plasma Sintering

2007 ◽  
Vol 558-559 ◽  
pp. 959-963 ◽  
Author(s):  
Lan Sun ◽  
Cheng Chang Jia ◽  
Min Xian ◽  
Rui Jun Cao
Keyword(s):  
Grain Size ◽  
Grain Growth ◽  
Spark Plasma Sintering ◽  
Abnormal Grain Growth ◽  
Full Density ◽  
Fine Grain ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
Increasing Temperature ◽  
New Phase

In order to control WC grain size and get a microstructure with fine grain size during the sintering process, WC grain growth in WC-Co cemented carbide was investigated. The possible reason on the grain growth was showed which includes the normal grain growth (NGG) and the abnormal grain growth (AGG). We adopted the SPS (spark plasma sintering) to sinter nanometer WC-Co powder, the range of temperature was 1100 -1250 °C, the pressure was 40MPa, and sintering time was 5min. In this paper, we discuss the density, hardness, microstructures and grain sizes of the sintered samples. The results showed that during the process sintering WC-Co powder, there are two kinds of growths. XRD investigation of the WC–Co samples spark plasma sintered to full density revealed that no new phase was created. Through the observed microstructure of the sintered samples, we analyzed the reason of the abnormal grain growth of WC grain. The density and hardness of samples were increased with increasing temperature.

scholarly journals Synthesis, microstructure, and properties of high purity Mo2TiAlC2 ceramics fabricated by spark plasma sintering

2020 ◽  
Vol 9 (6) ◽  
pp. 759-768
Author(s):  
Yunhui Niu ◽  
Shuai Fu ◽  
Kuibao Zhang ◽  
Bo Dai ◽  
Haibin Zhang ◽  
...  
Keyword(s):  
Grain Size ◽  
Flexural Strength ◽  
Spark Plasma Sintering ◽  
Layered Structure ◽  
High Purity ◽  
High Fracture Toughness ◽  
Temperature Range ◽  
Microstructure And Properties ◽  
Plasma Sintering ◽  
Spark Plasma

AbstractThe synthesis, microstructure, and properties of high purity dense bulk Mo2TiAlC2 ceramics were studied. High purity Mo2TiAlC2 powder was synthesized at 1873 K starting from Mo, Ti, Al, and graphite powders with a molar ratio of 2:1:1.25:2. The synthesis mechanism of Mo2TiAlC2 was explored by analyzing the compositions of samples sintered at different temperatures. It was found that the Mo2TiAlC2 phase was formed from the reaction among Mo3Al2C, Mo2C, TiC, and C. Dense Mo2TiAlC2 bulk sample was prepared by spark plasma sintering (SPS) at 1673 K under a pressure of 40 MPa. The relative density of the dense sample was 98.3%. The mean grain size was 3.5 μm in length and 1.5 μm in width. The typical layered structure could be clearly observed. The electrical conductivity of Mo2TiAlC2 ceramic measured at the temperature range of 2–300 K decreased from 0.95 × 106 to 0.77 × 106 Ω–1·m–1. Thermal conductivity measured at the temperature range of 300–1273 K decreased from 8.0 to 6.4 W·(m·K)–1. The thermal expansion coefficient (TEC) of Mo2TiAlC2 measured at the temperature of 350–1100 K was calculated as 9.0 × 10–6 K–1. Additionally, the layered structure and fine grain size benefited for excellent mechanical properties of low intrinsic Vickers hardness of 5.2 GPa, high flexural strength of 407.9 MPa, high fracture toughness of 6.5 MPa·m1/2, and high compressive strength of 1079 MPa. Even at the indentation load of 300 N, the residual flexural strength could hold 84% of the value of undamaged one, indicating remarkable damage tolerance. Furthermore, it was confirmed that Mo2TiAlC2 ceramic had a good oxidation resistance below 1200 K in the air.

scholarly journals Effect of Nano-Y2O3 Addition on Microstructure and Tensile Properties of High-Nb TiAl Alloy Prepared by Spark Plasma Sintering

Metals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 1048
Author(s):  
Yingchao Guo ◽  
Yongfeng Liang ◽  
Junpin Lin ◽  
Fei Yang
Keyword(s):  
Tensile Strength ◽  
Spark Plasma Sintering ◽  
Tial Alloy ◽  
Second Phase ◽  
Fine Grain ◽  
Fine Grain Strengthening ◽  
Plasma Sintering ◽  
Spark Plasma ◽  
Y2o3 Addition ◽  
Powder Metallurgy Route

Nano-Y2O3 reinforced Ti-47.7Al-7.1Nb-(V, Cr) alloy was fabricated by a powder metallurgy route using spark plasma sintering (SPS), and the influence of nano-Y2O3 contents on the microstructure and mechanical properties were investigated systematically. The results revealed that the ultimate tensile strength and elongation of the alloy were 570 ± 28 MPa and 1.7 ± 0.6% at 800 °C, 460 ± 23 MPa and 6.1 ± 0.4% at 900 °C with no nano-Y2O3, 662 ± 24 MPa and 5.5 ± 0.5% at 800 °C, and 466 ± 25 MPa and 16.5 ± 0.8% at 900 °C with 0.05 at% nano-Y2O3 addition, respectively. Due to the fine-grain strengthening and the second-phase strengthening, both tensile strength and elongation of the high-Nb TiAl alloy were enhanced with the addition of nano-Y2O3.

Synthesis of Bulk Quasicrystals by Spark Plasma Sintering

2000 ◽  
Vol 643 ◽  
Author(s):  
E. Fleury ◽  
J.H. Lee ◽  
S.H. Kim ◽  
G.S. Song ◽  
J.S. Kim ◽  
...  
Keyword(s):  
Fracture Toughness ◽  
Spark Plasma Sintering ◽  
Vickers Microhardness ◽  
Secondary Phases ◽  
Hot Press ◽  
Plasma Sintering ◽  
Short Period ◽  
Spark Plasma ◽  
Powder Particles ◽  
Sintering Method

AbstractSpark plasma sintering method was applied to Al-Cu-Fe and Al-Si-Cu-Fe gas-atomized powders to prepare almost pore-free cylindrical specimens with icosahedral and 1/1 cubic approximant phases, respectively. This investigation has revealed that a high density could be obtained despite the short period and low temperature imposed during spark plasma sintering. In comparison to hot press technique, these conditions are favorable since they limit the formation of secondary phases and avoid exaggerated grain growth. The Vickers microhardness and fracture toughness of these two alloy systems were found to be larger than those obtained from cast and hot pressed samples, which could be attributed to a strong bonding between powder particles and the small-grained microstructure of the bulk SPS quasicrystalline specimens.

Fabrication of MgO/Graphene Composites by Combustion Synthesis and Spark Plasma Sintering

2018 ◽  
Vol 281 ◽  
pp. 125-130
Author(s):  
Nan Lu ◽  
Jia Xi Liu ◽  
Gang He ◽  
Jiang Tao Li
Keyword(s):  
Mechanical Properties ◽  
Combustion Synthesis ◽  
Spark Plasma Sintering ◽  
Sintering Temperature ◽  
Ceramic Composites ◽  
Combustion Reaction ◽  
Sintering Additive ◽  
Microstructure And Mechanical Properties ◽  
Plasma Sintering ◽  
Spark Plasma

MgO/Graphene ceramic composites were fabricated by combining combustion synthesis with spark plasma sintering. MgO/Graphene mixture powders were prepared by the combustion reaction between Mg powders and CO2 gas. Dense MgO/Graphene composites were fabricated by spark plasma sintering (SPS) using LiF as the sintering additive. The effect of the sintering temperature on microstructure and mechanical properties of the prepared MgO/Graphene ceramics was discussed. The sintering temperature of the MgO/Graphene mixture powders increased from 900°C to 1300°C. The highest density of 3.43g/cm3 and hardness of 2133MPa were obtained at 1100°C. Compared with monolithic MgO ceramics, the hardness of MgO/Graphene ceramics at the same sintering temperature was increased from 840MPa to 2133MPa.

Sign in / Sign up

Export Citation Format

Share Document