Effect of Mean Stress on 2A12-T4 Aluminum Alloy under Tension-Torsion Constant Amplitude Loading

2016 ◽  
Vol 713 ◽  
pp. 334-337
Author(s):  
Tian Qing Liu ◽  
Xin Hong Shi ◽  
Jian Yu Zhang
Keyword(s):  
Shear Stress ◽  
Aluminum Alloy ◽  
Fatigue Life ◽  
Phase Angle ◽  
Stress Amplitude ◽  
Maximum Shear Stress ◽  
Fatigue Tests ◽  
Mean Stress ◽  
Normal Mean ◽  
Fracture Appearance

Fatigue tests have been carried out to investigate the effects of mean-stress and phase-difference on the tension-torsion fatigue failure of 2A12-T4 aluminum alloy. The results show that for fully reversed tension-torsion loading, the fatigue life increases with the increase of phase angle, but the fatigue life decreases with the increase of phase angle, when mean-stress exists, both for shear mean-stress and normal mean-stress. Fracture appearance shows that the crack initiation is on the direction of maximum shear stress amplitude plane. Critical plane criteria based on the linear combination of the maximum shear stress amplitude and maximum normal stress are studied and further discussion on the drawbacks of this kind of criteria are performed.

scholarly journals Multiaxial fatigue behavior of 2618 aluminum alloy

2019 ◽  
Vol 300 ◽  
pp. 09003
Author(s):  
Benaïssa Malek ◽  
Catherine Mabru ◽  
Michel Chaussumier
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Internal Pressure ◽  
Fatigue Behavior ◽  
Fatigue Tests ◽  
Multiaxial Fatigue ◽  
Mean Stress ◽  
Research Project ◽  
Pressure Tests

The purpose of the present research project is to study multiaxial fatigue behavior of 2618 alloy. The influence of mean stress on the fatigue behavior under tension and torsion is particularly investigated. Fatigue tests under combined tensile-torsion, in or out of phase, as well as combined tensile-torsion-internal pressure tests have also been conducted. Multiaxial fatigue results are analyzed according to Fatemi-Socie criterion to predict the fatigue life.

Relationship Between Fatigue Life Distribution, Notch Configuration, and S-N Curve of a 2024-T4 Aluminum Alloy

1985 ◽  
Vol 107 (3) ◽  
pp. 214-220 ◽  
Author(s):  
T. Shimokawa ◽  
Y. Hamaguchi
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Stress Amplitude ◽  
Fatigue Tests ◽  
Test Results ◽  
Notched Specimens ◽  
Wide Range ◽  
Life Distributions ◽  
The Relationship ◽  
Test Stress

The objective of this study is to identify the most closely related variable to the distribution of fatigue life in unnotched and three kinds of notched 2024-T4 aluminum alloy specimens. Carefully designed fatigue tests under a constant temperature and humidity condition provided fatigue life distributions over a wide range of stress amplitude. This study used about 1000 specimens. On the basis of the test results, the dependence of the scatter in fatigue life on notch configuration, the period to crack initiation, the level of stress amplitude, the median fatigue life, and the slope of the median S-N curve is investigated, and the relationship between the distributional form of fatigue life and the shape of the median S-N curve is discussed. It is concluded that the slope and shape of the median S-N curve in the vicinity of the test stress level are closely related to the scatter and distributional form of fatigue life respectively. This is common to the unnotched and three kinds of notched specimens. A variability hypothesis to correlate the median S-N curve with fatigue life distributions is examined.

Multiaxial Fatigue of 6061-T6 Aluminum Alloy under Corrosive Environment

2016 ◽  
Vol 853 ◽  
pp. 77-82
Author(s):  
Xu Chen ◽  
Rui Si Xing ◽  
Xiao Peng Liu
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Stress Amplitude ◽  
Low Cycle Fatigue ◽  
Cyclic Hardening ◽  
Cyclic Softening ◽  
Fatigue Tests ◽  
Plastic Strain Amplitude ◽  
Multiaxial Fatigue ◽  
Corrosive Environment

Aluminium alloys are widely used in the fields of automobile, machinery and naval construction. To investigate the effect of non-proportional loadings and corrosive environment on the fatigue resistance of 6061-T6 aluminum alloy, a set of uniaxial and multiaxial low cycle fatigue tests were carried out. Firstly, the results of uniaxial tests showed that the alloy exhibited cyclic hardening then cyclic softening. With the increase of stress amplitude the cyclic softening became pronounced. The increasing of plastic deformation was basically cyclically stable with small plastic strain amplitude accumulation when the stress amplitude was lower than 200MPa ,while it was increasing rapidly when the stress amplitude was higher than 220MPa. Secondly, it was observed that non-proportional cycle additional hardening of 6061-T6 aluminum alloy was little. While the fatigue life was badly affected by the loading paths. Thirdly ,the fatigue corrosion interactions were also talked about in details by performing the tests under the same loading conditions with corrosive environment. The experiment proved that the seawater corrosion has huge impact on fatigue life under pH 3. Finally, a multi-axial fatigue life prediction model was used to predict the fatigue life with or without the corrosive environment which showed a good agreement with experimental data.

ASME Sec VIII Div 3 Fatigue Life Predictions Using Critical Plane Approach

2015 ◽  
Author(s):  
Kumarswamy Karpanan ◽  
William Thomas
Keyword(s):  
Shear Stress ◽  
Fatigue Life ◽  
Principal Stress ◽  
Stress Amplitude ◽  
Maximum Shear Stress ◽  
Fe Model ◽  
Critical Plane ◽  
Principal Stress Direction ◽  
Stress Direction ◽  
Surface Node

ASME VIII Div 3 fatigue evaluation is based on the theory that cracks tend to nucleate along the slip lines oriented in the maximum shear stress planes. This code provides methods to calculate the fatigue stresses when the principal stress direction does not change (proportional loading) and axes change (nonproportional loading). When principal stress direction does not change within a fatigue cycle, shear stress amplitude is calculated only on the three maximum shear stress planes. But when the principal stress directions do change within a loading cycle, the plane carrying the maximum shear stress amplitude (also known as critical plane) cannot be easily identified and all planes at a point needs to be searched for the maximum shear stress amplitude. This paper describes the development of an ANSYS-APDL macro to predict the critical plane at each surface node of an FE model using the FEA stress results. This macro searches through 325 planes (at 10° increments along two angles) at each surface node and for each load step to identify the maximum shear stress and the corresponding normal stress for each surface node. The fatigue life is calculated for each surface node and is plotted as a color contour on the FEA model. This macro can be extended to calculate the fatigue life using other critical plane approaches such as the Findley and Brown-Miller models.

Uniaxial Ratcheting and Low-Cycle Fatigue Failure of U75V Rail Steel

2016 ◽  
Vol 853 ◽  
pp. 246-250 ◽  
Author(s):  
Tao Fang ◽  
Qian Hua Kan ◽  
Guo Zheng Kang ◽  
Wen Yi Yan
Keyword(s):  
Fatigue Life ◽  
Strain Amplitude ◽  
Stress Ratio ◽  
Stress Amplitude ◽  
Rail Steel ◽  
Low Cycle Fatigue ◽  
Mean Stress ◽  
Cycle Fatigue ◽  
Ratcheting Strain ◽  
Cyclic Straining

Experiments on U75V rail steel were carried out to investigate the cyclic feature, ratcheting behavior and low-cycle fatigue under both strain- and stress-controlled loadings at room temperature. It was found that U75V rail steel shows strain amplitude dependent cyclic softening feature, i.e., the responded stress amplitude under strain-controlled decreases with the increasing number of cycles and reaches a stable value after about 20th cycle. Ratcheting strain increases with an increasing stress amplitude and mean stress, except for stress ratio, and the ratcheting strain in failure also increases with an increasing stress amplitude, mean stress and stress ratio. The low-cycle fatigue lives under cyclic straining decrease linearly with an increasing strain amplitude, the fatigue lives under cyclic stressing decrease with an increasing mean stress except for zero mean stress, and decrease with an increasing stress amplitude. Ratcheting behavior with a high mean stress reduces fatigue life of rail steel by comparing fatigue lives under stress cycling with those under strain cycling. Research findings are helpful to evaluate fatigue life of U75V rail steel in the railways with passenger and freight traffic.

scholarly journals Effects of Actual Marine Atmospheric Pre-Corrosion and Pre-Fatigue on the Fatigue Property of 7085 Aluminum Alloy

Metals ◽  
2022 ◽  
Vol 12 (1) ◽  
pp. 81
Author(s):  
Laixin Shi ◽  
Lin Xiang ◽  
Jianquan Tao ◽  
Jun Liu ◽  
Qiang Chen ◽  
...  
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Pitting Corrosion ◽  
Atmospheric Corrosion ◽  
Fatigue Property ◽  
Outdoor Exposure ◽  
Fatigue Tests ◽  
Constant Amplitude ◽  
Fatigue Fractography ◽  
Corrosion Mode

Effects of actual marine atmospheric precorrosion and prefatigue on the fatigue property of 7085-T7452 aluminum alloy were investigated by using the methods of marine atmospheric outdoor exposure tests and constant amplitude axial fatigue tests. Marine atmospheric corrosion morphologies, fatigue life, and fatigue fractography were analyzed. After three months of outdoor exposure, both pitting corrosion and intergranular corrosion (IGC) occurred, while the latter was the dominant marine atmospheric corrosion mode. Marine atmospheric precorrosion could result in a dramatical decrease in the fatigue life of the as-received 7085-T7452 aluminum alloy, while selective prefatigue can improve the total fatigue life of the precorroded specimen. The mechanism of the actual marine atmospheric corrosion and its effects on the fatigue life of the 7085-T7452 aluminum alloy were also discussed.

The Effects of Periodic High Loads on Fretting Fatigue

1981 ◽  
Vol 103 (3) ◽  
pp. 223-228 ◽  
Author(s):  
A. Kantimathi ◽  
J. A. Alic
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Growth Retardation ◽  
Fretting Fatigue ◽  
Fatigue Tests ◽  
Constant Amplitude ◽  
Axial Loads ◽  
Prolonged Fatigue ◽  
Stress Ratios ◽  
Crack Growth Retardation

Fretting fatigue tests have been conducted on 7075-T7351 aluminum alloy coupons with fretting pads of the same material. Three different stress ratios were used, the otherwise constant amplitude axial loads being interrupted every 1000 cycles by either tensile overloads to 400 MPa or compressive underloads to −200 MPa. Tensile overloads greatly prolonged fatigue life for low stresses where the overload ratios were 1.6 and above; compressive underloads had comparatively little effect. The results are discussed in terms of crack growth retardation phenomena.

S–N curves for fatigue life estimation of friction stir welded 19501 aluminum alloy T-joint

2018 ◽  
Vol 233 (2) ◽  
pp. 664-674
Author(s):  
Prakash Chandra Gope ◽  
Harshit Kumar ◽  
Himanshu Purohit ◽  
Manish Dayal
Keyword(s):  
Aluminum Alloy ◽  
Fatigue Life ◽  
Fatigue Strength ◽  
Weld Zone ◽  
Stress Effect ◽  
Mean Stress ◽  
Friction Stir ◽  
Fracture Surfaces ◽  
Mean Stress Effect ◽  
Metallic Bonding

In this study, the mechanical properties and fatigue life of 19501 aluminum alloy friction stir welded T-joint is investigated. Tensile properties of friction stir welded joint show that there is a marginal reduction of about 5% in strength and ductility as compared to unwelded 19501 aluminum alloy. Fatigue test results of T-joint specimen at two stress ratios of 0 and -1 show that there is a reduction of 15% in fatigue strength due to change of stress ratio from -1 to 0. Also, higher variation is seen in fatigue strength in low cycle zone than the high cycle zone. Effect of mean stress on fatigue life is discussed on the basis of different mean stress effect models. Morrow’s mean stress effect model is found to be better than other models. Micrographs from the fracture surfaces of retreating side, mid weld zone, and advancing side of the T-joint indicates that fracture surfaces are cleavage fracture. Different sizes of inter-metallic bonding are seen in the micrographs, which indicate that fracture is initiated due to breaking of the brittle inter-metallic bonding.

scholarly journals A Fatigue Life Prediction Model Based on Modified Resolved Shear Stress for Nickel-Based Single Crystal Superalloys

Metals ◽  
2019 ◽  
Vol 9 (2) ◽  
pp. 180 ◽  
Author(s):  
Jialiang Wang ◽  
Dasheng Wei ◽  
Yanrong Wang ◽  
Xianghua Jiang
Keyword(s):  
Shear Stress ◽  
Fatigue Life ◽  
Prediction Model ◽  
Single Crystal ◽  
Life Prediction ◽  
Stress Amplitude ◽  
Damage Parameter ◽  
Fatigue Life Prediction ◽  
Model Based ◽  
Life Prediction Model

In this paper, the viewpoint that maximum resolved shear stress corresponding to the two slip systems in a nickel-based single crystal high-temperature fatigue experiment works together was put forward. A nickel-based single crystal fatigue life prediction model based on modified resolved shear stress amplitude was proposed. For the four groups of fatigue data, eight classical fatigue life prediction models were compared with the model proposed in this paper. Strain parameter is poor in fatigue life prediction as a damage parameter. The life prediction results of the fatigue life prediction model with stress amplitude as the damage parameter, the fatigue life prediction model with maximum resolved shear stress in 30 slip directions as the damage parameter, and the McDiarmid (McD) model, are better. The model proposed in this paper has higher life prediction accuracy.

scholarly journals Cyclic Tests of Smooth and Notched Specimens Subjected to Bending and Torsion Taking into Account the Effect of Mean Stress

Materials ◽  
2020 ◽  
Vol 13 (9) ◽  
pp. 2141 ◽  
Author(s):  
Roland Pawliczek ◽  
Dariusz Rozumek
Keyword(s):  
Experimental Data ◽  
Fatigue Life ◽  
Fatigue Tests ◽  
Mean Stress ◽  
Regression Equations ◽  
Allowable Stress ◽  
Cyclic Tests ◽  
Mean Values ◽  
Notched Specimens ◽  
Fatigue Characteristics

The paper contains the results of fatigue tests of smooth and notched specimens made of 10HNAP (S355J2G1W) subjected to proportional cyclic loading with use of mean values stress. The results obtained for specimens under bending, torsion and one combination of bending with torsion for four mean values have been compared. The experimental data have been collected in the tables and shown in the figures with use of various σa(τa)-N fatigue characteristics for which parameters of the regression equations have been determined. The influence of average values on the allowable stress amplitudes and amplitude of moments at the level close to the fatigue limit depending on the angle α determining loading combination and the average stress is also shown. The greatest effect of the notch on fatigue life compared to smooth specimens is observed at symmetrical loads. At unsymmetrical loads with non-zero mean stress, this effect clearly weakens or disappears.

Sign in / Sign up

Export Citation Format

Share Document