Vacuum Breakdown Behavior of CuWCr Composites

2008 ◽  
Vol 569 ◽  
pp. 125-128
Author(s):  
Peng Xiao ◽  
Zhi Kang Fan
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Powder Metallurgy ◽  
Electrical Properties ◽  
Mechanical Alloying ◽  
Arc Erosion ◽  
Before And After ◽  
Chopping Current ◽  
Uniform Composition ◽  
Scanning Electron

The Cu20W70Cr10 composites were fabricated by two methods which are the conventional powder metallurgy, and mechanical alloying to prepare WCr compound powders, followed by sintering and infiltration. The erosion behavior of CuWCr composites under breakdown was investigated. The surfaces of the composites before and after erosion and the mechanism of arc erosion were studied by scanning electron microscopy. The results show that the CuWCr composites prepared by mechanical alloying have superfine microstructure, uniform composition and high density, thus result in good characteristics of diffusing arcs and arc eroding endurance. Arc erosion zones are dispersive and uniform on the surfaces with some flat eroding pits. The Cu20W70Cr10 composites have excellent electrical properties such as high breakdown voltage, low chopping current and long arc life.

Synthesis of Cu/Cr and Cu/Cr/W Materials by Powder Metallurgy Techniques

2018 ◽  
Vol 880 ◽  
pp. 241-247
Author(s):  
Claudiu Nicolicescu ◽  
Victor Horia Nicoară ◽  
Costel Silviu Bălulescu
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Powder Metallurgy ◽  
Chemical Composition ◽  
Electrical Properties ◽  
Mechanical Alloying ◽  
Ball Mill ◽  
Weight Percent ◽  
Scanning Electron

Alloys based on Cu/Cr and Cu/Cr/W attract the attention due to their presence in different applications that require higher electrical properties which are combined with good mechanical properties. In order to synthesis the material based on Cu/Cr and Cu/Cr/W, mechanical alloying technique was used. Four mixtures, X1 (99%CuCr), X2 (97%CuCr), X3 (94%Cu1%CrW), X4 (92%Cu3%CrW – weight percent), were prepared using a vario planetary ball mill Pulverisette 4 made by Fritsch. The mixtures obtained after 10 hours were analyzed by scanning electron microscopy (SEM). It was found that the presence of chromium and tungsten influence the morphology and the particles tend to be flat. Sinter ability and microhardness are influenced by the chemical composition of the samples.

Mechanical Alloying Synthesis of K2Bi8Se13– type Solid Solutions

2007 ◽  
Vol 1044 ◽  
Author(s):  
Nikolaos Toumpas ◽  
Theodora Kyratsi ◽  
Euripides Hatzikraniotis ◽  
Andreas Tsiappos ◽  
Eleni Pavlidou ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Thermal Conductivity ◽  
Scanning Electron Microscopy ◽  
Electrical Properties ◽  
Mechanical Alloying ◽  
Solid Solutions ◽  
Structural Features ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

AbstractSolid solutions of β-K2Bi8-xSbxSe13are an interesting series of materials for thermoelectric investigations due to their very low thermal conductivity and highly anisotropic electrical properties. In this work, we aimed to synthesize solid solutions of β-K2Bi8-xSbxSe13type materials using powder techniques. The synthesis was based on mechanical alloying as well as sintering procedures. The products were studied in terms of structural features, composition and purity with powder x-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy. Preliminary results on thermoelectric properties as well as IR reflectivity measurements are presented.

scholarly journals Redox Mechanism of Azathioprine and Its Interaction with DNA

2021 ◽  
Vol 22 (13) ◽  
pp. 6805
Author(s):  
Mihaela-Cristina Bunea ◽  
Victor-Constantin Diculescu ◽  
Monica Enculescu ◽  
Horia Iovu ◽  
Teodor Adrian Enache
Keyword(s):  
Electron Microscopy ◽  
Mass Spectrometry ◽  
Scanning Electron Microscopy ◽  
Structural Changes ◽  
Differential Pulse ◽  
Immunosuppressive Drug ◽  
Redox Mechanism ◽  
Before And After ◽  
Dna Film ◽  
Scanning Electron

The electrochemical behavior and the interaction of the immunosuppressive drug azathioprine (AZA) with deoxyribonucleic acid (DNA) were investigated using voltammetric techniques, mass spectrometry (MS), and scanning electron microscopy (SEM). The redox mechanism of AZA on glassy carbon (GC) was investigated using cyclic and differential pulse (DP) voltammetry. It was proven that the electroactive center of AZA is the nitro group and its reduction mechanism is a diffusion-controlled process, which occurs in consecutive steps with formation of electroactive products and involves the transfer of electrons and protons. A redox mechanism was proposed and the interaction of AZA with DNA was also investigated. Morphological characterization of the DNA film on the electrode surface before and after interaction with AZA was performed using scanning electron microscopy. An electrochemical DNA biosensor was employed to study the interactions between AZA and DNA with different concentrations, incubation times, and applied potential values. It was shown that the reduction of AZA molecules bound to the DNA layer induces structural changes of the DNA double strands and oxidative damage, which were recognized through the occurrence of the 8-oxo-deoxyguanosine oxidation peak. Mass spectrometry investigation of the DNA film before and after interaction with AZA also demonstrated the formation of AZA adducts with purine bases.

The Synthesis of Cu0.81Ni0.19 Intermetallics by Mechanical Alloying

2012 ◽  
Vol 496 ◽  
pp. 379-382
Author(s):  
Rui Song Yang ◽  
Ming Tian Li ◽  
Chun Hai Liu ◽  
Xue Jun Cui ◽  
Yong Zhong Jin
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Grain Size ◽  
Mechanical Alloying ◽  
Milling Time ◽  
Elemental Powder ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scherrer Equation ◽  
Scanning Electron

The Cu0.81Ni0.19 has been synthesized directly from elemental powder of nickel and copper by mechanical alloying. The alloyed Cu0.81Ni0.19 alloy powders are prepared by milling of 8h. The grain size calculated by Scherrer equation of the NiCu alloy decreased with the increasing of milling time. The end-product was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM)

Synthesis and Film Investigation of Titania

2013 ◽  
Vol 832 ◽  
pp. 128-131
Author(s):  
Sharipah Nadzirah ◽  
Uda Hashim
Keyword(s):  
Thin Film ◽  
Electron Microscopy ◽  
Thin Films ◽  
Scanning Electron Microscopy ◽  
Titanium Dioxide ◽  
Sol Gel ◽  
Titanium Butoxide ◽  
Before And After ◽  
Scanning Electron ◽  
Spin Coater

Titania or titanium dioxide (TiO2) thin film has been synthesized via sol-gel method with monoethanolamine (MEA) as a catalyst. The mixing of titanium butoxide as a precursor, ethanol as a solvent and MEA were stirred using magnetic stirrer under ambient temperature [. The TiO2solution prepared then was deposited on SiO2substrates using spin-coater and the coated films were annealed at 600°C. Finally, both before and after annealed TiO2thin films were characterized using Field Emission Scanning Electron Microscopy (FESEM). The obtained results show the different TiO2particles formation before and after annealed.

scholarly journals Effect of Different Cooling Regimes on the Mechanical Properties of Cementitious Composites Subjected to High Temperatures

2014 ◽  
Vol 2014 ◽  
pp. 1-7 ◽  
Author(s):  
Jiangtao Yu ◽  
Wenfang Weng ◽  
Kequan Yu
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
High Temperature ◽  
Significant Influence ◽  
Microstructural Characterization ◽  
Cementitious Composite ◽  
Engineered Cementitious Composite ◽  
Before And After ◽  
Scanning Electron

The influence of different cooling regimes (quenching in water and cooling in air) on the residual mechanical properties of engineered cementitious composite (ECC) subjected to high temperature up to 800°C was discussed in this paper. The ECC specimens are exposed to 100, 200, 400, 600, and 800°C with the unheated specimens for reference. Different cooling regimens had a significant influence on the mechanical properties of postfire ECC specimens. The microstructural characterization was examined before and after exposure to fire deterioration by using scanning electron microscopy (SEM). Results from the microtest well explained the mechanical properties variation of postfire specimens.

Comparison of Implant-Abutment Interface Misfits After Casting and Soldering Procedures

2013 ◽  
Vol 40 (2) ◽  
pp. 129-135 ◽  
Author(s):  
Flávio Domingues das Neves ◽  
Gisele Araújo Elias ◽  
João Paulo da Silva-Neto ◽  
Lucas Costa de Medeiros Dantas ◽  
Adérito Soares da Mota ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Statistical Analysis ◽  
Casting Process ◽  
Chi Square ◽  
Implant Abutment ◽  
Before And After ◽  
Scanning Electron

The aim of this study was to compare vertical and horizontal adjustments of castable abutments after conducting casting and soldering procedures. Twelve external hexagonal implants (3.75 × 10 mm) and their UCLA abutments were divided according their manufacturer and abutment type: PUN (plastic UCLA, Neodent), PUC (plastic UCLA, Conexão), PU3i (plastic UCLA, Biomet 3i), and PUTN (plastic UCLA with Tilite milled base, Neodent). Three infrastructures of a fixed partial implant–supported bridge with 3 elements were produced for each group. The measurements of vertical (VM) and horizontal (HM) misfits were obtained via scanning electron microscopy after completion of casting and soldering. The corresponding values were determined to be biomechanically acceptable to the system, and the results were rated as a percentage. Statistical analysis establishes differences between groups by chi-square after procedures, and McNeman's test was applied to analyze the influence of soldering over casting (α ≤ .05). For the values of VM and HM, respectively, when the casting process was complete, it was observed that 83.25% and 100% (PUTN), 33.3% and 27.75% (PUN), 33.3% and 88.8% (PUC), 33.3% and 94.35% (PU3i) represented acceptable values. After completing the requisite soldering, acceptable values were 50% and 94.35% (PUTN), 16.6% and 77.7% (PUN), 38.55% and 77.7% (PUC), and 27.75% and 94.35% (PU3i). Within the limitations of this study, it can be concluded that the premachined abutments presented more acceptable VM values. The HM values were within acceptable limits before and after the soldering procedure for most groups. Further, the soldering procedure resulted in an increase of VM in all groups.

Effect of Joining Process on the Coatings of Self-Piercing Rivets

2012 ◽  
Vol 488-489 ◽  
pp. 1501-1505 ◽  
Author(s):  
Mahsa Esfahani ◽  
Yvonne Durandet ◽  
James Wang ◽  
Yat Choy Wong
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Optical Microscopy ◽  
Mechanical Joining ◽  
X Ray ◽  
Before And After ◽  
Riveting Process ◽  
Al Coating ◽  
Joining Process ◽  
Scanning Electron

In this study, effects of laser assisted self-pierce riveting (LSPR) as a mechanical joining technique were investigated on the coatings of self- piercing rivets. Zn-Sn and Al plated rivets were used to join magnesium sheets by LSPR. Microstructure, surface topography and roughness of the rivet’s coatings were characterized by optical microscopy, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and surface profilometry. A comparison of results before and after joining process showed that under joining conditions, Zn-Sn coating was deformed during riveting process and its thickness and microstructure varied along the rivet shank, while Al coating remained unchanged and no effects of riveting process was detected.

Preparation of Molybdenum High Speed Tool Steels with Addition of Niobium Carbide by Powder Metallurgy Techniques

2014 ◽  
Vol 802 ◽  
pp. 102-107 ◽  
Author(s):  
Oscar Olimpio de Araújo Filho ◽  
Rodrigo Tecchio Antonello ◽  
Cezar Henrique Gonzalez ◽  
Severino Leopoldino Urtiga Filho ◽  
Francisco Ambrozio Filho
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Powder Metallurgy ◽  
Liquid Phase ◽  
High Speed ◽  
Niobium Carbide ◽  
High Energy ◽  
Tool Steels ◽  
Vacuum Sintering ◽  
Scanning Electron

High speed steels processed by Powder Metallurgy (PM) techniques present better mechanical properties when compared with similar steels obtained by the conventional process of cast to ingot and hot working. PM techniques produce improved microstructures with smaller and better distribution of carbides. Liquid phase sintering high speed steel seems to be a cheaper processing route in the manufacturing of tool steels if compared to the well-known and expansive hot isostatic pressing high speed steels. The introduction of niobium as alloying element began with the object of replacing elements like vanadium (V) and tungsten (W). Phase liquid sintering consists in a manufacturing technique to process high speed steels by powder metallurgy. The aim of this work of research is to process and obtain AISI M2 and M3:2 with and without the addition of niobium carbide by high energy milling, cold uniaxial compaction and vacuum sintering in the presence of a liquid phase. The powders of the AISI M2 and M3:2 were processed by high energy milling adding a small quantity of niobium carbide (6% in mass), then the powders were characterized by means of X-ray diffraction (XRD) and scanning electron Microscopy (SEM) plus energy dispersion spectroscopy (EDS) in order to evaluate the milling process. The powders of the AISI M2 and M3:2 with the addition of niobium carbide (NbC) were uniaxially cold compacted and then submitted to vacuum sintering. The sintered samples had their microstructure, porosity and carbide distribution observed and evaluated by means of Scanning Electron Microscopy (SEM) and the mechanical property of hardness was investigated by means of Vickers hardness tests. At least five samples of each steel were investigated.

Sign in / Sign up

Export Citation Format

Share Document