Improved Wear-Resistant Performance of Epoxy Resin Composites Using Ceramic Particles

This work investigated the effects of using a new fabrication technique to prepare polymer composite on the wear-resistant performance of epoxy resin composites under dry friction conditions. Polymer composite samples with different weight contents of silicon carbide (SiC) particles were manufactured. This paper addresses the wear behavior of the obtained samples. With the suggested technique, the samples were prepared from epoxy/silicon carbide particles using a layer of thin kraft paper to prevent the sedimentation of the ceramic particles and to control the weight content of ceramic in the polymer. Kraft paper was used as a layer in the polymer composite. The hardness, wear resistance, and water absorption capacity of the produced epoxy composite samples prepared using the kraft paper technique were evaluated. The morphology of epoxy composite samples showed a significant improvement in the ceramic distribution and enhancement of interface bonding between ceramic and the polymer. The hardness values of the developed polymer composites were enhanced by up to 42.8%, which was obtained at 18 wt.% SiC particles. Increasing the ceramic content in the epoxy also led to the enhancement of wear resistance compared with pure epoxy. The results of the microstructure study also showed that the kraft paper layers helped in maintaining the distribution of the ceramic particles according to the previously specified content in each layer in the sample. Wear tests showed that the wear rate of the polymer composite decreased with the increase in the ceramic content. This study provides a new recycling method for using old kraft paper in polymer composite manufacturing to improve the distribution of ceramic particles in the polymer matrix.

Effect of the Composition of Mixed Recycled Aggregates on Physical–Mechanical Properties

Recycled aggregates (RA) from construction and demolition waste are an alternative to natural aggregates in the construction sector. They are usually classified according to their composition. The main constituent materials are separated into the following categories: unbound natural aggregates, ceramic particles, cementitious particles, bituminous materials, and other materials considered impurities, such as glass, plastic, wood, or gypsum. In this research, a large number of samples of RA were collected from three different recycling plants and their properties were studied. After that, 35 samples were selected randomly, and their RA constituents were separated under laboratory conditions. Cementitious particles were differentiated into two subcategories: masonry mortar and concrete particles. Subsequently, their physical–mechanical properties were measured. The statistical analysis carried out exhibited that the constituents had a statistically significant influence on the physical–mechanical properties studied. Specifically, masonry mortar particles had higher water absorption and worse mechanical properties than concrete and ceramic particles. Secondly, multiple regression models were performed to predict the physical–mechanical properties of RA from their composition since mean absolute percentage error (MAPE) ranged between 0.9% and 8.6%. The differentiation in the subcategories of concrete and masonry mortar particles in compositional testing is useful for predicting the physical–mechanical properties of RA.

In Situ Printing and Functionalization of Hybrid Polymer-Ceramic Composites Using a Commercial 3D Printer and Dielectrophoresis—A Novel Conceptual Design

Three-dimensional printing-based additive manufacturing has emerged as a new frontier in materials science, with applications in the production of functionalized polymeric-based hybrid composites for various applications. In this work, a novel conceptual design was conceived in which an AC electric field was integrated into a commercial 3D printer (-based fused filament fabrication (FFF) working principle) to in situ manufacture hybrid composites having aligned ceramic filler particles. For this work, the thermoplastic poly lactic acid (PLA) was used as a polymer matrix while 10 vol% KNLN (K0.485Na0.485Li0.03NbO3) ceramic particles were chosen as a filler material. The degree of alignment of the ceramic powders depended upon print speed, printing temperature and distance between electrodes. At 210 °C and a 1 kV/mm applied electric field, printed samples showed nearly complete alignment of ceramic particles in the PLA matrix. This research shows that incorporating electric field sources into 3D printing processes would result in in situ ceramic particle alignment while preserving the other benefits of 3D printing.