Additive manufacturing of composites made of epoxy resin with magnetite particles fabricated with the direct ink writing technique

2019 ◽  
Vol 54 (5) ◽  
pp. 647-657 ◽  
Author(s):  
Jose J Restrepo ◽  
Henry A Colorado
Keyword(s):  
Additive Manufacturing ◽  
Epoxy Resin ◽  
Large Scale ◽  
Distribution Density ◽  
Particulate Composites ◽  
Resin Matrix ◽  
Direct Ink Writing ◽  
Composites Materials ◽  
Structural Applications ◽  
Magnetite Particles

In this investigation, particulate composites materials made of epoxy resin matrix with magnetite particles were fabricated via additive manufacturing with the direct ink writing technique. Magnetite is an inexpensive material and the direct ink writing process is not only inexpensive but also easy to adapt to any material. A total of eight formulations were investigated, from which only four were feasible for the printing process: 32.6, 33.6, 35.4 and 41 wt.% of particles. The composites were characterized by scanning electron microscopy, compressive strength, particle size distribution, density, and ductility. Results showed that composites exhibit very competitive mechanical properties even though the process was not vacuum assisted, therefore enabling them to be used in large scale and in other structural applications. Composite can be used in electromagnetic shielding.

Control of humping phenomenon and analyzing mechanical properties of Al–Si wire-arc additive manufacturing fabricated samples using cold metal transfer process

2021 ◽  
pp. 095440622199840
Author(s):  
Yashwant Koli ◽  
N Yuvaraj ◽  
Aravindan Sivanandam ◽  
Vipin
Keyword(s):  
Mechanical Properties ◽  
Additive Manufacturing ◽  
Heat Input ◽  
Large Scale ◽  
High Deposition Rate ◽  
Bead Geometry ◽  
Layer By Layer ◽  
Cold Metal Transfer ◽  
Geometrical Shapes ◽  
Wire Arc Additive Manufacturing

Nowadays, rapid prototyping is an emerging trend that is followed by industries and auto sector on a large scale which produces intricate geometrical shapes for industrial applications. The wire arc additive manufacturing (WAAM) technique produces large scale industrial products which having intricate geometrical shapes, which is fabricated by layer by layer metal deposition. In this paper, the CMT technique is used to fabricate single-walled WAAM samples. CMT has a high deposition rate, lower thermal heat input and high cladding efficiency characteristics. Humping is a common defect encountered in the WAAM method which not only deteriorates the bead geometry/weld aesthetics but also limits the positional capability in the process. Humping defect also plays a vital role in the reduction of hardness and tensile strength of the fabricated WAAM sample. The humping defect can be controlled by using low heat input parameters which ultimately improves the mechanical properties of WAAM samples. Two types of path planning directions namely uni-directional and bi-directional are adopted in this paper. Results show that the optimum WAAM sample can be achieved by adopting a bi-directional strategy and operating with lower heat input process parameters. This avoids both material wastage and humping defect of the fabricated samples.

scholarly journals A Review on Additive Manufacturing Possibilities for Electrical Machines

Energies ◽  
2021 ◽  
Vol 14 (7) ◽  
pp. 1940
Author(s):  
Muhammad Usman Naseer ◽  
Ants Kallaste ◽  
Bilal Asad ◽  
Toomas Vaimann ◽  
Anton Rassõlkin
Keyword(s):  
Additive Manufacturing ◽  
Large Scale ◽  
Three Dimensional ◽  
Electrical Machines ◽  
Electromagnetic Properties ◽  
Scale Production ◽  
Performance Parameters ◽  
Large Scale Production ◽  
One Step ◽  
Manufacturing Techniques

This paper presents current research trends and prospects of utilizing additive manufacturing (AM) techniques to manufacture electrical machines. Modern-day machine applications require extraordinary performance parameters such as high power-density, integrated functionalities, improved thermal, mechanical & electromagnetic properties. AM offers a higher degree of design flexibility to achieve these performance parameters, which is impossible to realize through conventional manufacturing techniques. AM has a lot to offer in every aspect of machine fabrication, such that from size/weight reduction to the realization of complex geometric designs. However, some practical limitations of existing AM techniques restrict their utilization in large scale production industry. The introduction of three-dimensional asymmetry in machine design is an aspect that can be exploited most with the prevalent level of research in AM. In order to take one step further towards the enablement of large-scale production of AM-built electrical machines, this paper also discusses some machine types which can best utilize existing developments in the field of AM.

scholarly journals Compression Behaviour of Wire + Arc Additive Manufactured Structures

Metals ◽  
2021 ◽  
Vol 11 (6) ◽  
pp. 877
Author(s):  
Masoud Abbaszadeh ◽  
Volker Ventzke ◽  
Leonor Neto ◽  
Stefan Riekehr ◽  
Filomeno Martina ◽  
...  
Keyword(s):  
Additive Manufacturing ◽  
Large Scale ◽  
Grain Morphology ◽  
Electron Back Scatter Diffraction ◽  
Compression Tests ◽  
Homogeneous Microstructure ◽  
Compression Loading ◽  
Anisotropic Behaviour ◽  
Mechanical And Microstructural Properties ◽  
Wire Arc Additive Manufacturing

Increasing demand for producing large-scale metal components via additive manufacturing requires relatively high building rate processes, such as wire + arc additive manufacturing (WAAM). For the industrial implementation of this technology, a throughout understanding of material behaviour is needed. In the present work, structures of Ti-6Al-4V, AA2319 and S355JR steel fabricated by means of WAAM were investigated and compared with respect to their mechanical and microstructural properties, in particular under compression loading. The microstructure of WAAM specimens is assessed by scanning electron microscopy, electron back-scatter diffraction, and optical microscopy. In Ti-6Al-4V, the results show that the presence of the basal and prismatic crystal planes in normal direction lead to an anisotropic behaviour under compression. Although AA2319 shows initially an isotropic plastic behaviour, the directional porosity distribution leads to an anisotropic behaviour at final stages of the compression tests before failure. In S355JR steel, isotropic mechanical behaviour is observed due to the presence of a relatively homogeneous microstructure. Microhardness is related to grain morphology variations, where higher hardness near the inter-layer grain boundaries for Ti-6Al-4V and AA2319 as well as within the refined regions in S355JR steel is observed. In summary, this study analyzes and compares the behaviour of three different materials fabricated by WAAM under compression loading, an important loading condition in mechanical post-processing techniques of WAAM structures, such as rolling. In this regard, the data can also be utilized for future modelling activities in this direction.

scholarly journals Use of Cement Suspension as an Alternative Matrix Material for Textile-Reinforced Concrete

Materials ◽  
2021 ◽  
Vol 14 (9) ◽  
pp. 2127
Author(s):  
Richard Fürst ◽  
Eliška Fürst ◽  
Tomáš Vlach ◽  
Jakub Řepka ◽  
Marek Pokorný ◽  
...  
Keyword(s):  
Reinforced Concrete ◽  
Epoxy Resin ◽  
High Performance Concrete ◽  
Bending Test ◽  
Resin Matrix ◽  
Cement Matrix ◽  
Sample Type ◽  
Textile Reinforced Concrete ◽  
Epoxy Resin Matrix ◽  
Four Point Bending

Textile-reinforced concrete (TRC) is a material consisting of high-performance concrete (HPC) and tensile reinforcement comprised of carbon roving with epoxy resin matrix. However, the problem of low epoxy resin resistance at higher temperatures persists. In this work, an alternative to the epoxy resin matrix, a non-combustible cement suspension (cement milk) which has proven stability at elevated temperatures, was evaluated. In the first part of the work, microscopic research was carried out to determine the distribution of particle sizes in the cement suspension. Subsequently, five series of plate samples differing in the type of cement and the method of textile reinforcement saturation were designed and prepared. Mechanical experiments (four-point bending tests) were carried out to verify the properties of each sample type. It was found that the highest efficiency of carbon roving saturation was achieved by using finer ground cement (CEM 52.5) and the pressure saturation method. Moreover, this solution also exhibited the best results in the four-point bending test. Finally, the use of CEM 52.5 in the cement matrix appears to be a feasible variant for TRC constructions that could overcome problems with its low temperature resistance.

scholarly journals Assessing the Flexural Properties of Epoxy Composites with Extremely Low Addition of Cellulose Nanofiber Content

2020 ◽  
Vol 10 (3) ◽  
pp. 1159 ◽  
Author(s):  
Yingmei Xie ◽  
Hiroki Kurita ◽  
Ryugo Ishigami ◽  
Fumio Narita
Keyword(s):  
Mechanical Properties ◽  
Epoxy Resin ◽  
Flexural Modulus ◽  
Strengthening Mechanism ◽  
Short Fiber ◽  
Cellulose Nanofiber ◽  
Resin Matrix ◽  
Element Analysis ◽  
Epoxy Resin Matrix ◽  
The Matrix

Epoxy resins are a widely used common polymer due to their excellent mechanical properties. On the other hand, cellulose nanofiber (CNF) is one of the new generation of fibers, and recent test results show that CNF reinforced polymers have high mechanical properties. It has also been reported that an extremely low CNF addition increases the mechanical properties of the matrix resin. In this study, we prepared extremely-low CNF (~1 wt.%) reinforced epoxy resin matrix (epoxy-CNF) composites, and tried to understand the strengthening mechanism of the epoxy-CNF composite through the three-point flexural test, finite element analysis (FEA), and discussion based on organic chemistry. The flexural modulus and strength were significantly increased by the extremely low CNF addition (less than 0.2 wt.%), although the theories for short-fiber-reinforced composites cannot explain the strengthening mechanism of the epoxy-CNF composite. Hence, we propose the possibility that CNF behaves as an auxiliary agent to enhance the structure of the epoxy molecule, and not as a reinforcing fiber in the epoxy resin matrix.

Sign in / Sign up

Export Citation Format

Share Document