Study on Gypsum-Bonded Particleboard Reinforced with Jute Fibres

Holzforschung ◽  
2002 ◽  
Vol 56 (4) ◽  
pp. 440-445 ◽  
Author(s):  
Y. Deng ◽  
T. Furuno
Keyword(s):  
Mechanical Properties ◽  
High Performance ◽  
Untreated Wood ◽  
Physical And Mechanical Properties ◽  
Fiber Content ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Jute Fibers ◽  
Low Weight ◽  
Wood Particles

Summary This paper deals with the influence of length and content (based on a percentage of wood particles) of jute fibers on the physical and mechanical properties of gypsum-bonded particleboard (GPB). The length and amount of jute fibers had a significant effect on the internal bond strength (IB) and the modulus of rupture (MOR) of GPB. The addition of jute fibers did not obviously influence the modulus of elasticity (MOE), the thickness swelling (TS) or water absorption (WA). The values of IB were prominently high at the 3 mm length and 9–12% contents of jute fibers. The highest value of MOR was attained when the board was made with fibers 12 mm in length and a fiber content of 15%. The optimal amount of jute fibers reinforced the mechanical properties of GPB to achieve high performance. However, too much jute fiber reduced the IB, MOR (except for 12 mm length), and MOE of GPB. The values of TS and WA decreased gradually with an increase in the fiber content for all fiber lengths. In addition, the GPB gave very low weight loss on exposure to wood-decaying fungi of both Tyromyces palustris (TYP) and Coriolus versicolor (COV) as compared with untreated wood. It was concluded that the combination of 3 mm length and 9–12% content or 12 mm length and 15% content of jute fibers was the optimum for producing good performance of

Effect of paraffin application technique on the physical and mechanical properties of particleboard

2014 ◽  
Vol 21 (2) ◽  
pp. 191-195 ◽  
Author(s):  
Mehmet Baharoğlu ◽  
Gökay Nemli ◽  
Bünyamin Sarı ◽  
Nadir Ayrilmis ◽  
Selahattin Bardak ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Roughness ◽  
Contact Angle ◽  
Physical And Mechanical Properties ◽  
Formaldehyde Emission ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Quality Properties ◽  
Application Technique ◽  
Wood Particles

AbstractThe main objective of this study was to investigate the effect of paraffin application technique on the quality properties of particleboard. The paraffin was applied to the wood particles in three different techniques: (1) before resination, (2) after resination, and (3) with resin. The modulus of rupture, modulus of elasticity, internal bond strength, thickness swelling, surface roughness parameters, contact angle, and formaldehyde emission of the boards were determined. Statistical analysis showed that paraffin application technique had a significant influence on all properties of particleboards. The boards made using technique (1) had the highest mechanical properties and lowest surface roughness, formaldehyde emission and contact angle values. The worst properties were obtained from the board made using technique (2).

scholarly journals Composites from Thermoplastic Natural Rubber Reinforced Rubberwood Sawdust: Effects of Sawdust Size and Content on Thermal, Physical, and Mechanical Properties

2018 ◽  
Vol 2018 ◽  
pp. 1-11 ◽  
Author(s):  
Chatree Homkhiew ◽  
Surasit Rawangwong ◽  
Worapong Boonchouytan ◽  
Wiriya Thongruang ◽  
Thanate Ratanawilai
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Natural Rubber ◽  
High Density Polyethylene ◽  
High Performance ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Shore Hardness ◽  
Thermoplastic Natural Rubber ◽  
Plastic Content

The aim of this work is to investigate the effects of rubberwood sawdust (RWS) size and content as well as the ratio of natural rubber (NR)/high-density polyethylene (HDPE) blend on properties of RWS reinforced thermoplastic natural rubber (TPNR) composites. The addition of RWS about 30–50 wt% improved the modulus of the rupture and tensile strength of TPNR composites blending with NR/HDPE ratios of 60/40 and 50/50. TPNR composites reinforced with RWS 80 mesh yielded better tensile strength and modulus of rupture than the composites with RWS 40 mesh. The TPNR/RWS composites with larger HDPE content gave higher tensile, flexural, and Shore hardness properties and thermal stability as well as lower water absorption. The TPNR/RWS composites with larger plastic content were therefore suggested for applications requiring high performance of thermal, physical, and mechanical properties.

scholarly journals KUALITAS PAPAN KOMPOSIT LIMBAH KULIT BATANG SAGU (Metroxylon sp) DAN PLASTIK POLIPROPILENA BERDASARKAN JUMLAH LAPISAN PENYUSUN

2018 ◽  
Vol 7 (1) ◽  
Author(s):  
Mayang Archila ◽  
Farah Diba ◽  
Dina Setyawati ◽  
. Nurhaida
Keyword(s):  
Mechanical Properties ◽  
Moisture Content ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Internal Bonding ◽  
Thickness Swelling ◽  
Composite Board ◽  
Average Value ◽  
Composite Layers ◽  
Sago Bark

The objective of this research is to evaluate the effect of the number of composite layers on the quality of the composite board from sago bark waste and plastic waste, and the number of composite layers that produce the best quality on composite board. The composite board is made with size 30 cm x 30 cm x 1 cm. The composition and division of the material was carried out manually with the polypropylene distribution divided into three parts: the front and rear respectively of 15%, and the center 70% of the plastic weight. Target density of composite boards was 0.7 g / cm3. The treatment used is based on the number of layers composing, which is 5 layers, 7 layers, 9 layers, 11 layers and 13 layers. After mixed the sago bark particle and waste of polypropylene, the materials then compressed with hot press at 180oC with pressure about ± 25 kg / cm2 for 10 minutes. The composite boards then tested the quality included physical and mechanical properties. Testing of physical and mechanical properties refers to JIS A 5908-2003 standard. Physical properties consist of density, moisture content, thickness swelling, and water absorption. Mechanical properties consist of modulus of rupture, modulus of elasticity, internal bonding, and modulus of screw holding strength. The study used a completely randomized design experiment consisting of 5 treatments and 3 replications. The results showed the average value of composite density was range between 0.6962 – 0.7896 g/cm3, the moisture content was range between 4.3388 % - 6.8066%, the thickness swelling was range between 8.2605% - 11.9615%, and water absorption was range between 17.2380% - 22.3867%. The average value of modulus of rupture was range between 60,0632 kg/cm2 – 64,4068 kg/cm2, the modulus of elasticity was range between 17935,1813g/cm2 – 32841,8278 kg/cm2, the internal bonding was range between 1,9268 kg/cm2  - 5,4119 kg/cm2, and the modulus of screw holding strength was range between 78,2530 kg/cm2 – 92,9677 kg/cm2. The composite board made from sago stem bark waste and polypropylene waste plastic with 13 layers treatment is the best composite board and fulfilled the JIS A 5908-2003 standard. Keywords: bark of sago, composite boards, layer of composite, polypropylenes plastic, waste

scholarly journals INFLUENCE OF THERMAL MODIFICATION ON THE PHYSICAL AND MECHANICAL PROPERTIES OF Eucalyptus badjensis MIXED PARTICLEBOARD / OSB PANELS

FLORESTA ◽  
2021 ◽  
Vol 51 (2) ◽  
pp. 419
Author(s):  
Giuliano Ferreira Pereira ◽  
Setsuo Iwakiri ◽  
Rosilani Trianoski ◽  
Polliana D'angelo Rios ◽  
Renan Zunta Raia
Keyword(s):  
Mechanical Properties ◽  
Water Absorption ◽  
Phenol Formaldehyde ◽  
Physical And Mechanical Properties ◽  
Dry Mass ◽  
Thermal Modification ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Swelling Properties ◽  
Different Temperatures

The objective of this research was to evaluate the effects of thermal modifications, at different temperatures and exposure times, on the technological properties of mixed particleboard / OSB panels made out of Eucalyptus badjensis. Using the wood of Eucalyptus badjensis, Particleboard, OSB and mixed Particleboard/OSB panels (control and thermally modified) were manufactured. The mixed panels’ thermal modification was carried out under three temperatures (180ºC, 200ºC and 220ºC) and two exposure times (10 minutes and 12 minutes). For the panels’ manufacturing, 6% of phenol-formaldehyde adhesive and 1% of paraffin were employed, which was calculated based on the particles’ dry mass. The water absorption and thickness swelling properties were evaluated after 2 and 24 hours of immersion, in addition to the panels’ modulus of elasticity, modulus of rupture and internal bond. Based on the results, we were able to conclude that the thermal modification affected most of the physical properties positively. From the different exposure times studied, the most effective one was the period of 12 minutes, especially for water absorption after 2 hours, which caused a reduction of 11.27%. In turn, the most effective temperature was of 220ºC, highlighting the thickness swelling after 24 hours, which caused a swelling decrease of 23.76% in comparison with the control panels. Regarding the mechanical properties, the thermal modification, in terms of the studied exposure times and temperatures, did not affect the results of the mixed particleboard /OSB panels. 

scholarly journals Effects of thermo-hydro-mechanical treatments on various physical and mechanical properties of poplar (Populus) wood

BioResources ◽  
2020 ◽  
Vol 15 (4) ◽  
pp. 9596-9610
Author(s):  
Yali Shao ◽  
Lili Li ◽  
Zhangjing Chen ◽  
Sunguo Wang ◽  
Ximing Wang
Keyword(s):  
Mechanical Properties ◽  
Thermal Treatment ◽  
Modulus Of Elasticity ◽  
Mechanical Treatment ◽  
Elasticity Modulus ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Compression Rate ◽  
Thickness Swelling ◽  
Maximum Thickness

Poplar (Populus) wood was subjected in this work to thermo-hydro-mechanical treatment. The influence of the treatment parameters on the physical and mechanical properties were investigated. The wood samples were densified under three compression ratios (0%, 30%, and 50%), and thermally treated at three temperatures (180 °C, 200 °C, and 220 °C), at three thermal treatment durations (3 h, 4 h, and 5 h). The density, modulus of elasticity, modulus of rupture, radial hardness, and thickness swelling were measured. The results showed that the densities of the samples increased by 36.6% to 49.7%. As the compression rate increased, the temperature, duration, modulus of elasticity, modulus of rupture, and hardness increased. However, the dimensions of the densified samples were less stable. Compared to the densified samples, the maximum thickness swelling could be reduced by 74% (from 29.7% to 7.8%) when subjected to a thermal treatment at 220 °C for 3 h.

scholarly journals Physical and Mechanical Properties Evaluation of Corncob and Sawdust Cement Bonded Ceiling Boards

2019 ◽  
Vol 42 ◽  
pp. 65-75 ◽  
Author(s):  
Atoyebi Olumoyewa Dotun ◽  
Odeyemi Samson Olalekan ◽  
Azeez Lateef Olugbenga ◽  
Modupe Abayomi Emmanuel
Keyword(s):  
Mechanical Properties ◽  
Modulus Of Elasticity ◽  
Cement Content ◽  
Physical And Mechanical Properties ◽  
American National Standard Institute ◽  
Mechanical Tests ◽  
Industrial Wastes ◽  
Modulus Of Rupture ◽  
National Standard ◽  
Thickness Swelling

This study considered the production of composite ceiling boards from both agricultural and industrial wastes. Boards with different blending proportions by weight of cement, corncob and sawdust (Cem:Ccb:Swd) were produced and tested. Physical and mechanical tests such as Water Absorption (WA), Thickness Swelling (TS), Modulus of Elasticity (MOE) and Modulus of Rupture (MOR) were carried out on the products. The findings revealed that the board with Cem:Ccb:Swd blending proportion 50:10:40 gave the highest values of MOE and MOR and also had the lowest values of WA and TS. The MOE and MOR values of 3.432 are both higher than the minimum values of 550 N/mm2 and 3 N/mm2 specified for MOE and MOR respectively by the American National Standard Institute, for general-use particle boards. The cement content is inversely proportional to the physical properties and directly proportional to the mechanical properties.

Particleboard Manufactured with Variation of Press Time

2015 ◽  
Vol 1088 ◽  
pp. 644-647
Author(s):  
Cristiane Inácio de Campos ◽  
Bruno Santos Ferreira ◽  
André Luis Christoforo ◽  
Francisco Antonio Rocco Lahr ◽  
Juliana Cortez Barbosa ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Physical And Mechanical Properties ◽  
Mechanical Tests ◽  
Modulus Of Rupture ◽  
Test Results ◽  
Thickness Swelling ◽  
Mean Values ◽  
Tukey Test ◽  
Press Time ◽  
Brazilian Standard

This research aimed to produce and determine physical and mechanical properties of three-layered particleboard produced with Pinussp. wood particlesand three different times of press, i.e., 3, 5 and 7 minutes. Recommendations of the Brazilian standard ABNT NBR 14810 [1] were adopted to fundament physical and mechanical tests. The properties evaluated were the modulus of rupture (MOR) and modulus of elasticity (MOE) in static bending; internal bond; thickness swelling; water absorption; moisture content and apparent density.The mean values showed, for the physical properties, that all the panels manufactured achievedthe requirements of theBrazilian standard, and for mechanical properties, only the panelsmanufacturedwith 7minutesofpressing timemet therequirements. From the Tukey test results, timesof the pressingcycleinfluencedsignificantlyin allinvestigatedphysical and mechanicalproperties, showed better results the panels madewithseven minutesof the pressingcycle, implyingthat the time ofseven minutesof the pressingcycle is thebest among theinvestigatedperiodsin the manufactureofparticleboard.

scholarly journals Sifat Fisis dan Mekanis Papan Semen dari Serat Tandan Kosong Kelapa Sawit (The Physical and Mechanical Properties of Cement Board Made from Oil Palm Empty Fruit Bunches Fibers)

2016 ◽  
Vol 8 (2) ◽  
pp. 43-52 ◽  
Author(s):  
Djoko Purwanto
Keyword(s):  
Mechanical Properties ◽  
Water Absorption ◽  
Oil Palm ◽  
Modulus Of Elasticity ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Empty Fruit Bunches ◽  
Screw Withdrawal ◽  
Cement Board

Oil palm empty fruit bunches (OPEFB) fiber were industrial waste that has not been widely used by the community, only stacked and cause odors that interfere with the surrounding environment. This research studied the utilization of OPEFB fiber for cement board products using cement as resin and CaCl2 as accelerator. Laboratory scale cement board made from OPEFB fiber were mixed with cement, and CaCl2. The composition of fiber and cement were 1:1, 1:1.5, 1:2, and CaCl2 variations were 0%, 1% and 3%. A mixture of fibers, cement and CaCl2 was compressed at the pressure of 4 ton for 24 hours. The cement boards were tested for physical and mechanical properties according to JIS A 5417-1992, and the results were compared to the requirements of the cement board JIS A 5417-1992. Cement board made from fiber and cement composition 1:1.5 and CaCl2 content 3% produced moisture content, thickness swelling, water absorption, density, modulus of rupture/MOR, modulus of elasticity/MOE and screw withdrawal strength that met the requirement of JIS A 5417-1992. The composition of fiber and cement and the variations of CaCl2 content produced significant effect on water content, water absorption, thickness swelling, modulus of rupture/MOR, modulus of elasticity/MOE and screw withdrawal strength on cement boards.Keywords : oil palm empty fruit bunches fiber, cement boards, physical and mechanical properties

scholarly journals PENGARUH PERENDAMAN PARTIKEL TERHADAP SIFAT FISIS DAN MEKANIS PAPAN PARTIKEL DARI AMPAS TEBU (Saccharum officinarum)

PERENNIAL ◽  
2008 ◽  
Vol 4 (1) ◽  
pp. 6
Author(s):  
Apri Heri Iswanto ◽  
Zahrial Coto ◽  
Kurniawansyah Effendy
Keyword(s):  
Mechanical Properties ◽  
Moisture Content ◽  
Modulus Of Elasticity ◽  
Internal Bond ◽  
Physical And Mechanical Properties ◽  
Saccharum Officinarum ◽  
Hot Water ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Holding Power

The objective of this research is to research the effect of particle soaking to physical and mechanical properties particleboard that resulted. The best result of particleboard is particleboard with treatment of hot water soaking. From this result obtained average of physical properties of particleboard (i.e. density, moisture content, water absorption, and thickness swelling) are 0.7 g/cm3; 9.58%; 52.27%; 10.05%. While the result average of mechanical properties of particleboard (i.e. Modulus of Rupture, Modulus of Elasticity, Internal Bond and Screw Holding Power) are 118.79 kg/cm2; 8.909 kg/cm2; 1.85 kg/cm2; 28.40 kg. Key words: Soaking, bagasse, particleboard, physical and mechanical properties References

Dimensional stability and mechanical properties of bio-based composites produced from hydro-thermal treated wheat straw

BioResources ◽  
2021 ◽  
Vol 16 (4) ◽  
pp. 7901-7915
Author(s):  
Ümit Büyüksarı ◽  
Ömer Özyürek
Keyword(s):  
Mechanical Properties ◽  
Thermal Treatment ◽  
Wheat Straw ◽  
Dimensional Stability ◽  
Internal Bond ◽  
Steam Explosion ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Wood Particles ◽  
Particle Ratio

Bio-composites were produced from untreated (UT) and hydro-thermally treated (HTT) wheat straw (WS) particles and wood, and their dimensional stability and mechanical properties were investigated. The HTT treatment consisted of subjecting the WS particles to a steam explosion process for 8 min at 180 °C. The HTT and UT WS particles were mixed with the wood particles at 10, 20, 30, and 40% ratios. The physical properties, including density, water absorption (WA), and thickness swelling (TS), were determined for the bio-based composites. The mechanical properties evaluated included the modulus of rupture, modulus of elasticity, and internal bond strength. Statistical analyses showed that the hydro-thermal treatment and the WS ratio had significant effects on the dimensional stability and mechanical properties of the bio-composites. The WA of the composites after 2-h and 24-h rose significantly when the HTT WS particle ratio was increased from 10 to 40%. The 2-h and 24-h WA values of HTT-10 were 6.3% and 5.3% lower than those of UT-10, respectively. Improvements in the 2-h TS value were achieved by the HTT WS particles at the 10% ratio, and in the 24-h TS value at the 10 and 40% ratios. The mechanical properties of the composites were higher in the HTT group, but decreased in both the UT and HTT groups as the WS ratio increased.

Sign in / Sign up

Export Citation Format

Share Document