Enhanced Electrical properties in Mn-doped Bi3.25La0.75Ti3O12 thin films

2005 ◽  
Vol 902 ◽  
Author(s):  
Sushil Kumar Singh ◽  
Hiroshi Ishiwara
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Electrical Properties ◽  
Coercive Field ◽  
Remanent Polarization ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
Switching Field ◽  
Mn Doping ◽  
Mn Doped

AbstractMn-doped Bi3.25La0.75Ti3O12 (BLT) thin films were fabricated by depositing sol-gel solutions on Pt/Ti/SiO2/Si <100> substrates. The surface morphology and ferroelectric properties of Mn-doped BLT films depend upon the orientation of the films. Small amount of Mn-doping in BLT films influences the ferroelectric properties of the films, that is, it enhances the remanent polarization and reduces the coercive field. The 1% Mn-doped BLT films show enhanced remanent polarization and reduced the coercive field by about 22%. To the contrary, Mn-doping more than 1% decreases polarization gradually. Mn-doping significantly improves the fatigue resistance of BLT films. The reduced polarization in the 3.3% Mn-doped thin film recovers during switching cycles higher than 5 × 105. Under high switching field, the probability of field-assisted unpinning of domains is expected to be high and this may be the main cause for increase in polarization after 5 × 105 in the 3.3% Mn-doped BLT film.

Ferroelectric Properties of Sol-Gel Derived Ca1-xSrxBi4Ti4O15 Thin Films

2008 ◽  
Vol 368-372 ◽  
pp. 100-102 ◽  
Author(s):  
Su Hua Fan ◽  
Jing Xu ◽  
Guang Da Hu ◽  
Bo He ◽  
Feng Qing Zhang
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Fatigue Resistance ◽  
Coercive Field ◽  
Remanent Polarization ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
High Concentration ◽  
Gel Method ◽  
Si Substrates

Ca1-xSrxBi4Ti4O15 thin films were fabricated by sol-gel method on Pt(100)/Ti/SiO2/Si substrates. Influence of Sr content on the microstructure and ferroelectric properties of Ca1-xSrxBi4Ti4O15 thin films were systematically studied. The results indicate that Ca0.4Sr0.6Bi4Ti4O15 thin film has better ferroelectric properties with remanent polarization (2Pr) of 29.1+C/cm2, coercive field (2Ec) of 220 kV/cm. Furthermore, the film has good fatigue resistance. The better ferroelectric properties of Ca0.4Sr0.6Bi4Ti4O15 thin film originate from the relatively high concentration of a-axis oriented grains.

Preparation and Properties of ferroelectric Bi2SrTa2O9 thin films for FeRAM using Flash-MOCVD

1995 ◽  
Vol 415 ◽  
Author(s):  
T. Ami ◽  
K. Hironaka ◽  
C. Isobel ◽  
N. Nagel ◽  
M. Sugiyama ◽  
...  
Keyword(s):  
Thin Films ◽  
Electrical Properties ◽  
Coercive Field ◽  
Remanent Polarization ◽  
Ferroelectric Properties ◽  
Type Structure ◽  
Structural And Electrical Properties ◽  
Fluorite Type ◽  
Deposited Films ◽  
Flowing Oxygen

ABSTRACTFerroelectric Bi2 SrTa2 O9 thin films were successfully prepared by liquid delivery MOCVD, and structural and electrical properties were investigated. As-deposited films showed sharp distinct peaks, which were indexed assuming a fluorite-type structure. These precursors were transformed to bismuth-layered structures by annealing at 800 °C in flowing oxygen. Reasonable ferroelectric properties were observed in a film with 170 nm-thickness. Remanent polarization and coercive field were estimated to be 5.2 μC/cm2 and 52 kV/cm, respectively, at 5V.

Ferroelectric Characteristics of SrxBi2.4Ta2O9 Thin Films and Electrical Properties of the Pt/SrxBi2.4Ta2O9/TiO2/Si Structure

2004 ◽  
Vol 449-452 ◽  
pp. 477-480
Author(s):  
J.H. Choi ◽  
Tae Sung Oh
Keyword(s):  
Thin Films ◽  
Electrical Properties ◽  
Coercive Field ◽  
Remanent Polarization ◽  
Ferroelectric Properties ◽  
Memory Window ◽  
Low Leakage ◽  
Low Leakage Current ◽  
Metalorganic Decomposition ◽  
Ferroelectric Hysteresis

Ferroelectric characteristics of the 400 nm-thick SrxBi2.4Ta2O9(0.7≤x≤1.3) thin films processed by metalorganic decomposition were investigated, and electrical properties of the Pt/Sr0.85Bi2.4Ta2O9/TiO2/Si structure prepared using TiO2 buffer layer were characterized. The Sr-deficient SrxBi2.4Ta2O9 films exhibited well-developed ferroelectric hysteresis curves compared to those of the Sr-excess films. The Sr0.85Bi2.4Ta2O9 film exhibited optimum ferroelectric properties, such as high remanent polarization and low leakage current density, among SrxBi2.4Ta2O9 films. A memory window of the Pt/SrxBi2.4Ta2O9/TiO2/Si structure was dependent upon the coercive field of the SrxBi2.4Ta2O9 film, and the Pt/SrxBi2.4Ta2O9/TiO2/Si exhibited a maximum memory window of 1.3 V at the sweeping voltage of ±5 V.

scholarly journals Robust ferroelectricity enhancement of PZT thin films by a homogeneous seed layer

2021 ◽  
Author(s):  
jie jiang ◽  
Lei Liu ◽  
Kuo Ouyang ◽  
Zhouyu Chen ◽  
Shengtao Mo ◽  
...  
Keyword(s):  
Thin Films ◽  
Electrical Properties ◽  
Remanent Polarization ◽  
Perovskite Phase ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
Pzt Thin Films ◽  
Large Dielectric Constant ◽  
Sol Gel Process ◽  
A New Technique

Abstract With its excellent ferroelectric properties such as large dielectric constant and large remanent polarization, PZT thin films are extensively used in micro-sensors and other devices. In this study, the sol-gel process was used to fabricate Pb(Zr0.52Ti0.48)O3 thin films with Pb(ZrxTi1−x)O3 seed islands. The experimental consequences demonstrate that all the Pb(Zr0.52Ti0.48)O3 thin films with Pb(ZrxTi1−x)O3 seeds show pure perovskite phase with no other impurity phases, and the electrical properties of Pb(Zr0.52Ti0.48)O3 thin films modified by Pb(ZrxTi1−x)O3 seed islands with different Zr/Ti ratios are improved, such as remanent polarization increased, dielectric properties increased, coercive electric field decreased, leakage current density decreased, etc. In particular, the electrical properties of the Pb(Zr0.52Ti0.48)O3 thin films with Pb(ZrxTi1−x)O3 seed islands are the most optimal when the x is 0.52. This paper provides a new technique for optimizing the electrical properties of PZT thin films, which is of great significance for breaking through the bottleneck of the development of ferroelectric memory.

THICKNESS-DEPENDENT MICROSTRUCTURES AND ELECTRICAL PROPERTIES OF LiTaO3 THIN FILMS PREPARED BY A Sol-Gel PROCESS

2007 ◽  
Vol 21 (18n19) ◽  
pp. 3404-3411
Author(s):  
M. C. KAO ◽  
H. Z. CHEN ◽  
S. L. YOUNG ◽  
C. C. LIN ◽  
C. C. YU
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Grain Size ◽  
Remanent Polarization ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
Relative Dielectric Constant ◽  
Coating Technology ◽  
Si Substrates ◽  
Sol Gel Process

LiTaO 3 thin films were deposited on Pt / Ti / SiO 2/ Si substrates by means of a sol-gel spin-coating technology and rapid thermal annealing (RTA). The influence of various annealing treatments on the characteristics of the thin films were studied by varying the single-annealed-layer thickness (50 ~ 200 nm ) and heating temperatures (500 ~ 800° C ) of the samples. Experimental results reveal that the single-annealed-layer strongly influences grain size, dielectricity and ferroelectricity of LiTaO 3 thin films. The grain size of LiTaO 3 thin film decreases slightly with increasing thickness of the single-annealed-layer, and highly c-axis orientated LiTaO 3 films can be obtained for a single-annealed-layer of 50 nm. When the thickness of the single-annealed-layer was increased from 50 to 200 nm, the relative dielectric constant of LiTaO 3 thin film decreased from 65 to 35, but the dielectric loss factor (tanδ) was increased. The LiTaO 3 films with the single-annealed-layer of 50 nm showed excellent ferroelectric properties in terms of a remanent polarization ( P r) of 12.3 μ C /cm2 (Ec ∼ 60 kV/cm), and a low current density of 5.2×l0-8 A /cm2 at 20 kV/cm.

Improvement in Ferroelectric Properties of Sol-Gel Derived SrBi2Ta2O9 thin films with seeding layers

2002 ◽  
Vol 718 ◽  
Author(s):  
Ching-Chich Leu ◽  
Chao-Hsin Chien ◽  
Ming-Jui Yang ◽  
Ming-Che Yang ◽  
Tiao-Yuan Huang ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Magnetron Sputtering ◽  
Remanent Polarization ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
Strontium Bismuth Tantalate ◽  
Seeding Layer ◽  
Si Substrates ◽  
Nucleation Sites

AbstractThe effects of a seeding layer, which was deposited on Pt/TiO2/SiO2/Si substrates using magnetron sputtering, on the characteristics of sol-gel-deposited strontium-bismuth-tantalate (SBT) thin films are investigated. The seeding layer serves as nucleation sites so homogeneous crystalline SBT films of bismuth-layered structure (BLS) with fine grains are successfully obtained by 750°C rapid thermal annealing in O2 ambient. The remanent polarization (2Pr) improves from 12.1 to 18.8 μC/cm2 with the addition of the seeding layer. In addition, the seeding layer also results in a lower nucleation temperature, allowing the use of 700°C annealing for 10 min to grow SBT films that are fully crystallized with BLS phase and shows good ferroelectric properties. Finally, crystallinity and microstructures of SBT films are found to be strongly dependent on the thickness of the seeding layer. Optimum Ta-seeded SBT thin film crystallized at 700°C for 10min depicts a higher 2Pr value (12.9 μC/cm2 (@5V) than that of the un-seeded films crystallized at 750°C for 1min.

STRUCTURE CONTROL AND FERROELECTRIC PROPERTIES OF SrBi4Ti4O15 THIN FILMS ON Si SUBSTRATES COATED BY (100)- AND (110)-ORIENTED LaNiO3 ELECTRODES

2007 ◽  
Vol 14 (03) ◽  
pp. 435-438
Author(s):  
PILONG WANG ◽  
GUANGDA HU ◽  
YANXIA DING ◽  
SUHUA FAN
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Coercive Field ◽  
Remanent Polarization ◽  
Annealing Temperature ◽  
Volume Fraction ◽  
Ferroelectric Properties ◽  
Epitaxial Relationship ◽  
Structure Control ◽  
Si Substrates

SrBi 4 Ti 4 O 15 ( SBTi ) thin films were prepared on (100)- and (110)-oriented LaNiO 3( LNO ) electrodes by a metalorgranic decomposition (MOD) technique at an annealing temperature of 650°C. c-axis-oriented SBTi thin film with volume fraction of 0.89 can be formed on a (100)-oriented LNO film due to the epitaxial relationship between c-axis-oriented SBTi and LNO (100). In contrast, SBTi film deposited on LNO (110) shows random orientations with strong (119) and (200) peaks. The remanent polarization (Pr) and coercive field (Ec) of the random oriented SBTi film were 18.1 μC/cm2 and 70 kV/cm, respectively. This suggests that (110)-oriented LNO electrode is a better choice for obtaining SBTi films with higher volume fraction of a(b)-axis-orientated grains.

PREPARATION AND FERROELECTRIC PROPERTY OF (100)-ORIENTED Ca0.4Sr0.6Bi4Ti4O15 THIN FILM ON Pt/Ti/SiO2/Si SUBSTRATE

2010 ◽  
Vol 17 (05n06) ◽  
pp. 445-449 ◽  
Author(s):  
SUHUA FAN ◽  
QUANDE CHE ◽  
FENGQING ZHANG
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Ferroelectric Property ◽  
Remanent Polarization ◽  
Sol Gel ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
Si Substrate ◽  
Degree Of Orientation ◽  
Equiaxed Grains

The (100)-oriented Ca0.4Sr0.6Bi4Ti4O15(C0.4S0.6BTi ) thin film was successfully prepared by a sol-gel method on Pt/Ti/SiO2/Si substrate. The orientation and formation of thin films under different annealing schedules were studied using XRD and SEM. XRD analysis indicated that (100)-oriented C0.4S0.6BTi thin film with degree of orientation of I(200)/I(119) = 1.60 was prepared by preannealing the film at 400°C for 3 min followed by rapid thermal annealing at 800°C for 5 min. SEM analysis further indicated that the (100)-oriented C0.4S0.6BTi thin film with a thickness of about 800 nm was mainly composed of equiaxed grains. The remanent polarization and coercive field of the film were 16.1 μC/cm2 and 85 kV/cm, respectively.

Synthesis and Ferroelectric Properties of Sol–Gel Derived Intergrowth-Superlattice-Structured SrBi4Ti4O15-Bi4Ti3O12 Thin Films

2011 ◽  
Vol 197-198 ◽  
pp. 1781-1784
Author(s):  
Hua Wang ◽  
Jian Li ◽  
Ji Wen Xu ◽  
Ling Yang ◽  
Shang Ju Zhou
Keyword(s):  
Thin Films ◽  
Remanent Polarization ◽  
Annealing Temperature ◽  
Ferroelectric Properties ◽  
Sol Gel ◽  
Hysteresis Loops ◽  
Si Substrates ◽  
Gel Processing ◽  
Coercive Electric Field ◽  
Clockwise Hysteresis

Intergrowth-superlattice-structured SrBi4Ti4O15–Bi4Ti3O12(SBT–BIT) films prepared on p-Si substrates by sol-gel processing. Synthesized SBT–BIT films exhibit good ferroelectric properties. As the annealing temperature increases from 600°C to 700°C, the remanent polarization Prof SBT–BIT films increases, while the coercive electric field Ecdecreases. SBT–BIT films annealed at 700°C have a Prvalue of 18.9µC/cm2which is higher than that of SBT (16.8µC/cm2) and BIT (14.6µC/cm2), and have the lowest Ecof 142 kV/cm which is almost the same as that of SBT and BIT. The C-V curves of Ag/SBT-BIT/p-Si heterostructures show the clockwise hysteresis loops which reveal the memory effect due to the polarization. The memory window in C-V curve of Ag/SBT-BIT/p-Si is larger than that of Ag/SBT/p-Si heterostructure or Ag/BIT/p-Si heterostructure.

Sign in / Sign up

Export Citation Format

Share Document