Effect of Silver Diamine Fluoride on Microtensile Bond Strength to Dentin

2012 ◽  
Vol 37 (6) ◽  
pp. 610-616 ◽  
Author(s):  
RL Quock ◽  
JA Barros ◽  
SW Yang ◽  
SA Patel
Keyword(s):  
Bond Strength ◽  
Resin Composite ◽  
Bonding Agent ◽  
Microtensile Bond Strength ◽  
Silver Diamine Fluoride ◽  
Microtensile Testing ◽  
Etch And Rinse ◽  
Significant Difference ◽  
Diamond Saw ◽  
Self Etch

SUMMARY The aim of this in vitro study was to investigate the effect of the cariostatic and preventive agent silver diamine fluoride (SDF) on the microtensile bond strength of resin composite to dentin. Forty-two caries-free, extracted molars were flattened occlusally and apically using a diamond saw, and the exposed occlusal dentin was polished with a series of silicon carbide papers, all under water irrigation. The teeth were then randomly divided into six groups of seven teeth each that were treated as follows: 1) Peak SE self-etch bonding agent; 2) 12% SDF + Peak SE; 3) 38% SDF + Peak SE; 4) Peak LC etch-and-rinse bonding agent; 5) 12% SDF + Peak LC; and 6) 38% SDF + Peak LC. Four-millimeter buildups of Amelogen Plus were incrementally placed on all teeth; after a 24-hour storage period in distilled water, the specimens were sectioned perpendicular to the adhesive interface to produce beams of cross-sectional surface area measuring approximately 1 mm2. The beams were placed on a microtensile testing machine, which utilized a single-speed pump motor and force gauge at 20 kgf × 0.01 second to record maximum tensile force before failure occurred. Two-way analysis of variance and post hoc Tukey tests were performed to compare the effects of the SDF on microtensile bond strength, with statistical significance set at α = 0.05. None of the experimental groups treated with different concentrations of SDF showed a significant difference in bond strength compared to the control groups, and there was no significant difference in bond strength between self-etch and etch-and-rinse groups. However, the effect of SDF on self-etch bonded teeth compared to etch-and-rinse bonded teeth was statistically significant (p=0.0363), specifically at the 12% concentration. SDF does not adversely affect the bond strength of resin composite to noncarious dentin.

scholarly journals Effect of adhesive mode and chlorhexidine on microtensile strength of universal bonding agent to sound and caries-affected dentins

2018 ◽  
Vol 12 (04) ◽  
pp. 553-558 ◽  
Author(s):  
Joyce Figueiredo Macedo de Lima ◽  
Danielle Wajngarten ◽  
Fariya Islam ◽  
Johanna Clifford ◽  
Ana Carolina Botta
Keyword(s):  
Phosphoric Acid ◽  
Bond Strength ◽  
Composite Resin ◽  
High Viscosity ◽  
Bonding Agent ◽  
Third Molars ◽  
Microtensile Bond Strength ◽  
Etch And Rinse ◽  
Significant Difference ◽  
Self Etch

ABSTRACT Objective: The main objective of this study is to assess the effect of the adhesive mode and chlorhexidine (CHX) on the microtensile strength of a universal bonding agent to sound and caries-affected dentins. Materials and Methods: Six intact third molars and six decayed third molars were sectioned to obtain two middle dentin specimens per tooth. Prime and Bond Elect Universal (Dentsply) was applied to specimens in two different modes: Etch-and-rinse (ER, phosphoric acid for 15s) and self-etch (SE, no phosphoric acid). 2% CHX (Cavity Cleanser, Bisco) was applied to both dentins for 30 s. Specimens were randomly assigned into eight groups (n = 3) according to the treatments applied to sound and caries-affected dentins: SE; ER; SE + CHX; and ER + CHX. All specimens were restored with TPH Spectra High Viscosity (Dentsply) composite resin and sectioned to obtain specimens of 0.8 ± 0.1 mm2. The microtensile bond strength test was conducted at 1 mm/min. The data were statistically analyzed by ANOVA and multiple comparisons' test (α = 0.05). Results: There was no significant difference between sound dentin and caries-affected dentin (P = 0.132). The highest bond strength was obtained with the application of the ER (31.81MPa). SE + CHX promoted the lowest bond strength with no statistical difference to ER + CHX (P > 0.05). Conclusions: ER mode for the universal bonding agent yielded the highest bond strength to sound and caries-affected dentins. CHX reduced the bond strength to both dentins regardless the application of phosphoric acid. Clinical Significance: The universal bonding agent increased the bond strength to sound and caries-affected dentins when applied by the ER mode.

scholarly journals Bond strength of universal adhesive applied to dry and wet dentin

2020 ◽  
Vol 19 ◽  
pp. e201662
Author(s):  
Maria Luísa de Alencar e Silva Leite ◽  
Caroline de Farias Charamba ◽  
Renally Bezerra Wanderley e Lima ◽  
Sônia Saeger Meireles ◽  
Rosângela Marques Duarte ◽  
...  
Keyword(s):  
Bond Strength ◽  
Storage Time ◽  
Resin Composite ◽  
Adhesive System ◽  
Microtensile Bond Strength ◽  
Universal Adhesive ◽  
Bonding Quality ◽  
Etch And Rinse ◽  
Significant Difference ◽  
One Year

Aim: This study evaluated the influence of dentin wettability on the immediate and extended microtensile bond strength (mTBS) of a universal adhesive system used in the etch-and-rinse strategy. Methods: Twenty human third molars were selected and divided into four groups according to the adhesive system and dentin wettability. The mTBS values of each group were registered 24 h and one year after adhesive system application and resin composite block build-up (n=30). Data were analyzed by the t-test (p<0.05). Results: When both adhesive systems were compared, there was no statistically significant difference when they were applied following wet bonding (p>0.05). However, the dry bonding reduced μTBS values of the Adper Single Bond 2 adhesive (p<0.05). Regarding storage time, both groups presented similar μTBS values at 24 h and one year (p>0.05). Conclusions: Therefore, the Scotchbond Universal Adhesive can be applied to dry or wet dentin without compromising the etch-and-rinse bonding quality and the durability of the restorations.

scholarly journals Effect of Different Adhesion Protocols on the Shear Bond Strength of Universal Adhesive Systems to Sound and Artificial Caries-Affected Dentin

2021 ◽  
Author(s):  
Omnia M. Sami ◽  
Essam A. Naguib ◽  
Rasha H. Afifi ◽  
Shaymaa M. Nagi
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Failure Modes ◽  
Resin Composite ◽  
Single Bond ◽  
Adhesive Systems ◽  
Universal Adhesive ◽  
Etch And Rinse ◽  
Significant Difference ◽  
Self Etch

Abstract Objective Bonding to different dentin substrates influences resin composite restoration outcomes. This study investigated the influence of different adhesion protocols on the shear bond strength of universal adhesive systems to sound and artificial caries-affected dentin (CAD). Materials and Methods Occlusal enamel of 80 premolars were wet grinded to obtain flat midcoronal dentin. Specimens were equally divided according to the substrate condition: sound and CAD by subjecting to pH-cycling for 14 days. Each dentin substrate was bonded with the adhesive systems used in this study: Single Bond universal adhesive or Prime&Bond universal (applied either in etch-and-rinse or self-etch adhesion protocol). Adhesive systems were utilized according to manufacturers’ instructions, then resin composite was built up. Specimens were tested for shear bond strength. The data were analyzed by three-way analysis of variance, and failure modes were determined using stereomicroscope. Results There was no statistically significant difference between the two tested adhesive systems on artificially created CAD with different adhesion protocols. On sound dentin, Single Bond universal, either in the etch-and-rinse or self-etch adhesion protocols, revealed higher statistically significant shear bond strength mean values compared with CAD. Conclusion Single Bond universal adhesive in an etch-and-rinse adhesion protocol improved only bonding to sound dentin, while no added positive effect for the etching step with Prime&Bond universal adhesive was found when bonded to both sound and CAD substrates. The influence of CAD on the performance of the universal adhesives was material-dependent.

scholarly journals Effect of chitosan nanoparticles on microtensile bond strength of resin composite to dentin: an in vitro study

2020 ◽  
Vol 23 (2) ◽  
Author(s):  
Amr Mohsen Mohamed ◽  
Sameh Mahoud Nabih ◽  
Mohamed Ahmed Wakwak
Keyword(s):  
Bond Strength ◽  
Resin Composite ◽  
Testing Machine ◽  
Chitosan Nanoparticles ◽  
Tooth Surface ◽  
Control Group ◽  
Microtensile Bond Strength ◽  
Significant Difference ◽  
Self Etch

Objective: The purpose of this study was to evaluate the effect of chitosan nanoparticles on microtensile bond strength of resin composite to dentin using self etch adhesive after aging. Material and Methods: A total number of 90 freshly extracted, sound human molar teeth. Flat tooth surface was gained after cut of the occlusal surface. Three main groups according to pretreatment of dentin before adhesive application; 0.2 % chitosan, 2.5 % chitosan and no treatment control group. Universal self etch adhesive were applied according to manufacture instruction and 4 mm of Feltik Z250 xt composite. Storage of specimens for 1 day, 3 months and 6 months in 37O C distilled water. After that, the tooth was sectioned to beams of 1 mm x8 mm sticks for microtensile bond strength test using universal testing machine. Scanning electron microscope (SEM) was used to evalute the effect of chitosan nanoparticles on dentin and smear layer. Kruskal-Wallis test was used to compare between the three groups as well as the three aging periods. Dunn’s test was used for pair-wise comparisons. The significance level was set at P ≤ 0.05. Results: chitosan 0.2% is statistically significant increase in bond strength than chitosan 2.5% and control in one day group. Three months chitosan 0.2 % groups have statistically significant increase in bond strength than chitosan 2.5%. It was found in 6 months that control and chitosan 0.2 % have statistically significant increase in bond strength than chitosan 2.5%. There was statistically significant difference found between the three studied groups regarding bond strength at different storage times . Conclusion: Microtensile bond strength was influenced by different chitosan concentration. Different aging periods had no effect on the microtensile bond strength without application of chitosan and with application of 2.5% chitosan concentration.KEYWORDSChitosan nanoparticles; Microtensile bond strength; MMPs.

scholarly journals Hybridization quality and bond strength of adhesive systems according to interaction with dentin

2013 ◽  
Vol 07 (03) ◽  
pp. 315-326 ◽  
Author(s):  
Luciana Andrea Salvio ◽  
Vinicius Di Hipólito ◽  
Adriano Luis Martins ◽  
Mario Fernando de Goes
Keyword(s):  
Bond Strength ◽  
Resin Composite ◽  
Single Step ◽  
Adhesive Systems ◽  
Microtensile Bond Strength ◽  
Etch And Rinse ◽  
One Step ◽  
Self Etch ◽  
Ammoniacal Silver ◽  
One Way Anova

ABSTRACT Objective: To evaluate the hybridization quality and bond strength of adhesives to dentin. Materials and Methods: Ten human molars were ground to expose the dentin and then sectioned in four tooth-quarters. They were randomly divided into 5 groups according to the adhesive used: Two single-step self-etch adhesives - Adper Prompt (ADP) and Xeno III (XE), two two-step self-etching primer systems - Clearfil SE Bond (SE) and Adhe SE (ADSE), and one one-step etch-and-rinse system - Adper Single Bond (SB). Resin composite (Filtek Z250) crown buildups were made on the bonded surfaces and incrementally light-cured for 20 s. The restored tooth-quarters were stored in water at 37΀C for 24 h and then sectioned into beams (0.8 mm 2 in cross-section). Maximal microtensile bond strength (μ-TBS) was recorded (0.5 mm/min in crosshead speed). The results were submitted to one-way ANOVA and Tukey′s test (α = 0.05). Thirty additional teeth were used to investigate the hybridization quality by SEM using silver methenamine or ammoniacal silver nitrate dyes. Results: SE reached significantly higher μ-TBS (P < 0.05); no significance was found between ADSE and XE (P > 0.05), and between SB and ADP (P > 0.05); ADSE and XE were significantly higher than SB and ADP (P < 0.05). The bonding interface of SB showed the most intense silver uptake. SE and ADSE showed more favorable hybridization quality than that observed for ADP and XE. Conclusions: The bond strength and hybridization quality were affected by the interaction form of the adhesives with dentin. The hybridization quality was essential to improve the immediate μ-TBS to dentin.

scholarly journals Effect Of Chitosan Treatment On Shear Bond Strength Of Composite To Deep Dentin Using Self-Etch And Total-Etch Adhesive Systems

2021 ◽  
Vol 24 (2) ◽  
Author(s):  
Fateme Vasei ◽  
Farahnaz Sharafeddin
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Resin Composite ◽  
Testing Machine ◽  
Adhesive System ◽  
Single Bond ◽  
Adhesive Systems ◽  
Etch And Rinse ◽  
Significant Difference ◽  
Self Etch

Objective: To assess the shear bond strength (SBS) of resin composite to deep dentin, using 1 and 2.5% chitosan pretreatment as well as different adhesive systems. Material and Methods: 80 human maxillary molars were randomly divided to eight groups according to the type of adhesive system and dentin pretreatment (n = 10): I) two-step self-etch system (Clearfil SE bond); II) two-step etch-andrinse system (Adper single bond 2); III) 2.5% chitosan + Clearfil SE bond; IV) 2.5% chitosan +etch + Adper single bond 2; V) etch + 2.5% chitosan + Adper single bond 2; VI) 1% chitosan + Clearfil SE bond; VII) 1% chitosan + etch + Adper single bond 2; VIII) etch + 1% chitosan + Adper single bond 2 (chitosan solution (w/v): 2.5 g and 1 g of chitosan (Sigma Aldrich, USA) was dissolved in 100 ml of 1% acetic acid). Plastic molds were positioned on dentin and filled with composite (Z350, 3M ESPE, USA). SBS (MPa) was tested using a universal testing machine. ANOVA tests, Tukey’s test, and independent t test were used to analyze data (p < 0.05). Results: The highest SBS value among self-etch groups was observed with 1% chitosan (p = 0.001). In the etch-and-rinse group, the SBS of 1% chitosan was significantly lower than the other groups. Chitosan treatment following acid etching led to higher SBS in comparison to when chitosan was applied before etching, with the significant difference in 1% concentration (p = 0.030). A predominance of mix fractures was observed in dentin. Conclusion: Improved dentin bond strength can be achieved through immediate dentin pretreatment with 1% chitosan in self-etch adhesive systems. Chitosan Pretreatment may not be advantageous for etch-and-rinse adhesive systems. Keywords Adhesive system; Chitosan; Deep dentin; Shear strength.

scholarly journals Bonding Performance of Universal Adhesives Applied to Nano-Hydroxyapatite Desensitized Dentin Using Etch-and-Rinse or Self-Etch Mode

Materials ◽  
2021 ◽  
Vol 14 (16) ◽  
pp. 4746
Author(s):  
Yuchen Meng ◽  
Fan Huang ◽  
Silin Wang ◽  
Meiwen Li ◽  
Yi Lu ◽  
...  
Keyword(s):  
Bond Strength ◽  
Laser Scanning ◽  
Resin Composite ◽  
Laser Scanning Microscopy ◽  
Confocal Laser ◽  
Bonding Performance ◽  
Etch And Rinse ◽  
Significant Difference ◽  
Universal Adhesives ◽  
Self Etch

The study assessed the bonding performance of three universal adhesives on desensitized dentin with etch-and-rinse mode or self-etch mode after nano-hydroxyapatite (nHAp)-based desensitizers application. Simulated sensitive dentin specimens were prepared and separated into four groups: no treatment as the negative control, groups desensitized by Biorepair toothpaste, Dontodent toothpaste, or nHAp paste. Three universal adhesives of All-Bond Universal, Single Bond Universal, and Clearfil Universal Bond with etch-and-rinse or self-etch mode were bonded to the desensitized dentin specimens separately, followed by resin composite build-ups. Micro-tensile bond strength was measured using a micro-tensile tester. The wettability of desensitized dentin was evaluated by the contact angle of the adhesives. Resin infiltration was observed by confocal laser scanning microscopy. Dentin tubular occlusion and nanoleakage were observed by scanning electron microscope. The results showed that the etch-and-rinse or self-etch mode of each adhesive showed similar bond strength when bonding to nHAp-based desensitized dentin. The dentin surface was partially covered by desensitizers after desensitization. Compared with the self-etch mode, stronger demineralization and more reopened dentin tubules were observed in the etch-and-rinse mode after acid etching; longer resin tags and more nanoleakage in the resin–dentin interface were observed when using the etch-and-rinse mode. When bonding to nHAp-based desensitized dentin with universal adhesives, no significant difference in bond strength was found between self-etch mode or etch-and-rinse mode; while the latter produced more nanoleakage in the resin–dentin interfaces.

scholarly journals Impact of Immediate Dentin Sealing Using Universal Adhesive under Simulated Pulp Pressure on Microtensile Bond Strength of Indirect Resin Composite Restorations and Dentin Permeability

2021 ◽  
Author(s):  
Emad Abd Elfatah Abo-Alazm ◽  
Rehab Khalil Safy
Keyword(s):  
Bond Strength ◽  
Resin Composite ◽  
Water Storage ◽  
Microtensile Bond Strength ◽  
Universal Adhesive ◽  
Dentin Permeability ◽  
Composite Restorations ◽  
Significant Difference ◽  
Cad Cam ◽  
Self Etch

Abstract Objective The aim of this study was to investigate the effect of immediate dentin sealing (IDS) technique using universal adhesive under simulated pulp pressure on microtensile bond strength (µTBS) of indirect resin composite restorations and dentin permeability. Materials and Methods Fifty extracted caries-free human third molars were used for specimens' preparation. Each molar's occlusal table was abraded flat and their roots were separated under continuous water cooling. Forty specimens were used for microtensile bond strength test (µTBST) evaluation. The µTBST specimens were randomly assigned to two groups according to the dentin sealing time; Immediate dentin sealing (IDS) and delayed dentin sealing (DDS). Each group was further subdivided into two subgroups according to the adhesive system used for dentin sealing: iBOND self-etch adhesive and GLUMA Bond Universal. All specimens were exposed to simulated pulp pressure for 1 week then restored using computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite blocks. The µTBS was evaluated for all tested subgroups after 24 hours and 6 months of water storage. The remaining 10 teeth were used for the preparation of dentin discs for dentin permeability evaluation. They were divided into two groups according to type of self-etch adhesive used. Fluid filtration rate was evaluated after etching, with smear layer and after adhesive application. Results obtained were statistically analyzed using Shapiro–Wilk test and Weibull analysis. Results Statistically significant difference was recorded between μTBS mean values of both IDS and DDS techniques at 24 hours and after 6 months of water storage. GLUMA Bond Universal adhesive had significantly higher bond strength compared with iBond at both IDS and DDS techniques, but both adhesives showed a significant reduction in the Weibull characteristic strength after 6 months of water storage. Significant reduction in dentin permeability was recorded by both adhesives without any significant difference between them. Conclusions The IDS technique using universal adhesive in self-etch mode is an effective strategy for improving the final bond strength of CAD/CAM resin composite restorations and reducing dentin permeability.

scholarly journals Influence of Water Aging on Microtensile Bond Strength of a Flowable and a Packable Bulk-fill Resin Composites to Dentin

2020 ◽  
Vol 8 (D) ◽  
pp. 112-117
Author(s):  
Ayah Atif Selim ◽  
Ahmed Fawzy Abo Elezz ◽  
Rehab Khalil Safy
Keyword(s):  
Bond Strength ◽  
Storage Time ◽  
Resin Composite ◽  
Water Storage ◽  
Aging Effect ◽  
Mean Value ◽  
Control Group ◽  
Microtensile Bond Strength ◽  
Significant Difference ◽  
Influence Of Water

AIM: Investigation of the aging effect on the microtensile bond strength (μTBS) of bulk-fill resin composite (RC) versus a conventionally incrementally applied one. MATERIALS AND METHODS: A total number of 45 sound human impacted third molars extracted molars have been selected to prepare specimens for the μTBS test. Teeth were randomly divided into three groups (C) according to type of RC material which used for restoring the teeth. Where nanohybrid RC (Grandio®SO) was used as the control Group (C1), packable bulk-fill RC (X-tra fil®) was used for restoring teeth in C2 group and flowable bulk-fill RC (X-tra base®) was used for restoring teeth in C3 group. Each group was further subdivided into 3 subgroups (n = 5) according to the water storage time, where in subgroup 1; teeth were stored for 24 h, subgroup 2; teeth were stored for 3 months while for subgroup 3; and teeth were stored for 6 months. After water storage, teeth were sectioned for preparation of μTBS testing beams. Maximum tensile stresses were recorded in megapascal (MPa). RESULTS: After 24 h of water storage, the X-tra base® showed a higher statistically significant μTBS to dentin (33.82 ± 9.84 MPa) than did the other two types of RCs. After 3 months, the X-tra fil® showed the lowest mean value of μTBS (10.90 ± 5.66 MPa), meanwhile, after 6 months of water storage Grandio®SO showed the highest mean value of μTBS (15.85 ± 6.76 MPa). Regardless of the time the X-tra fil® showed the lowest mean of μTBS (15.07 ± 11.73 MPa), while there is no significant difference between the X-tra base® and Grandio®SO. Furthermore, the water aging adversely affects μTBS values which deceased gradually by time. CONCLUSION: The packable bulk-fill RC characterized by lower μTBS to dentin in comparison to the flowable bulk fill and the incrementally applied nanohybrid RCs. Furthermore, the μTBS of the three tested materials decreased gradually by aging.

scholarly journals Effect of Chitosan as a Cross-Linker on Matrix Metalloproteinase Activity and Bond Stability with Different Adhesive Systems

Marine Drugs ◽  
2020 ◽  
Vol 18 (5) ◽  
pp. 263 ◽  
Author(s):  
Eugenia Baena ◽  
Sandra R Cunha ◽  
Tatjana Maravić ◽  
Allegra Comba ◽  
Federica Paganelli ◽  
...  
Keyword(s):  
Matrix Metalloproteinase ◽  
Bond Strength ◽  
Adhesive Systems ◽  
Microtensile Bond Strength ◽  
Bond Stability ◽  
Etch And Rinse ◽  
Mechanical Durability ◽  
Human Dentine ◽  
Self Etch ◽  
Metalloproteinase Activity

The aim of the present study was to evaluate the effect of 0.1% chitosan (Ch) solution as an additional primer on the mechanical durability and enzymatic activity on dentine using an etch-and-rinse (E&R) adhesive and a universal self-etch (SE) adhesive. Microtensile bond strength and interfacial nanoleakage expression of the bonded interfaces for all adhesives (with or without pretreatment with 0.1% Ch solution for 1 min and air-dried for 5 s) were analyzed immediately and after 10,000 thermocycles. Zymograms of protein extracts from human dentine powder incubated with Optibond FL and Scotchbond Universal on untreated or Ch-treated dentine were obtained to examine dentine matrix metalloproteinase (MMP) activities. The use of 0.1% Ch solution as an additional primer in conjunction with the E&R or SE adhesive did not appear to have influenced the immediate bond strength (T0) or bond strength after thermocycling (T1). Zymography showed a reduction in MMP activities only for mineralized and demineralized dentine powder after the application of Ch. Application of 0.1% Ch solution does not increase the longevity of resin–dentine bonds. Nonetheless, the procedure appears to be proficient in reducing dentine MMP activities within groups without adhesive treatments. Further studies are required to comprehend the cross-linking of Ch with dentine collagen.