PEMANFAATAN BATANG KELAPA DAN KAYU KARET SEBAGAI BAHAN BAKU GLULAM

2012 ◽  
Vol 4 (2) ◽  
pp. 22
Author(s):  
Dwi Harsono
Keyword(s):  
Mechanical Properties ◽  
Construction Materials ◽  
Physical And Mechanical Properties ◽  
Wood Products ◽  
Building Construction ◽  
Raw Material ◽  
Stem Wood ◽  
Rubber Wood ◽  
Number Of Layers ◽  
Wood Utilization

The research of coconut and rubber wood utilization as raw material for glulam has been done. This research aims to optimize the function of rubber wood and palm stem by the incorporation of technology and adhesion to wood products in the form of building construction materials. In addition, knowing the physical and mechanical properties of glulam based on three variations of the type of timber (rubber wood, coconut, coconut stem wood + rubber), and various number of layers (5 layers, 6 layers, and 7 layers). Each combination treatment was repeated three times. The best mechanical physical properties of glulam for type of rubber wood, with 7 layers. Keywords : glulam, coconut wood, rubber wood, characters physical, characters mechanic

scholarly journals In Polymerization of Environment Friendly Melamine-Urea-Glyoxal Resin in Rubber Wood for Improved Physical and Mechanical Properties

2021 ◽  
Vol 2021 ◽  
pp. 1-10
Author(s):  
Lijuan Ping ◽  
Yubo Chai ◽  
Fangwen Zhang ◽  
Bailing Sun ◽  
Junliang Liu
Keyword(s):  
Mechanical Properties ◽  
Wood Sample ◽  
Treated Wood ◽  
Physical And Mechanical Properties ◽  
Weight Percent Gain ◽  
Wood Products ◽  
Environment Friendly ◽  
Promising Alternative ◽  
Rubber Wood ◽  
Structural Applications

In the study, we report that a safe and simple way for upgrading inferior rubber wood through the combined modification of environment-friendly MUG resin was synthesized from glyoxal, melamine, urea, and other additives. MUG-treated wood samples were prepared with six different MUG resin concentrations (5, 15, 25, 35, 45, and 55 wt %) into the wood matrix and then heated and polymerized to form a solid and hydrophobic MUG resin in the wood scaffold, and the physico-mechanical properties were evaluated. As the MUG resin concentration increased, the weight percent gain and density increased, water uptake and leachability decreased, and the antiswelling efficiency increased at first and then decreased. MUG-treated wood sample can be prepared when the MUG resin concentration was set as 25%, and the physical properties of treated wood was optimum. Scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy analysis showed that the MUG resin is widely distributed in the cell lumens and cell walls. With enhanced physico-mechanical properties, MUG-treated wood sample can be well used as a promising alternative to existing engineered wood products for structural applications.

Frost Heaving Soil Road Use Synthetic Adhesive Reinforcement Method

2013 ◽  
Vol 740 ◽  
pp. 759-762
Author(s):  
Hao Zeng Bao
Keyword(s):  
Mechanical Properties ◽  
Industrial Waste ◽  
Construction Materials ◽  
Reference Value ◽  
Physical And Mechanical Properties ◽  
Road Construction ◽  
Experimental Methods ◽  
Frost Heaving ◽  
The World ◽  
Rock And Soil

In many areas, there are still a development road construction materials, traditionally, often use reinforced concrete, asphalt and other adhesive method to strengthen the low strength of rock and soil anti-freeze expansion coefficient; And now all countries in the world are studying how to use industrial production waste development of new composite materials. One of the most development potential, the production of industrial waste - slime. This paper USES the Russian kazan national construction university experimental methods, in the experiment to improve frost heaving soil physical and mechanical properties of the method for the synthesis of adhesive, based on the feasibility and applicability, environmental assessment of research and analysis, for the use of adhesive put forward a lot of reference value.

Alternative Concrete – Geopolymer Concrete

2021 ◽  
Keyword(s):  
Mechanical Properties ◽  
Fly Ash ◽  
Construction Industry ◽  
Building Material ◽  
Construction Materials ◽  
Raw Material ◽  
Geopolymer Concrete ◽  
Sustainable Solutions ◽  
New Construction ◽  
Alkali Activated

Concrete is the most versatile, durable and reliable material and is the most used building material. It requires large amounts of Portland cement which has environmental problems associated with its production. Hence, an alternative concrete – geopolymer concrete is needed. The general aim of this book is to make significant contributions in understanding and deciphering the mechanisms of the realization of the alkali-activated fly ash-based geopolymer concrete and, at the same time, to present the main characteristics of the materials, components, as well as the influence that they have on the performance of the mechanical properties of the concrete. The book deals with in-depth research of the potential recovery of fly ash and using it as a raw material for the development of new construction materials, offering sustainable solutions to the construction industry.

Study of the Effect of PP and LDPE Thermoplastic Binder Addition on the Mechanical Properties and Physical Properties of Particulate Composites for Building Material Application

2019 ◽  
Vol 964 ◽  
pp. 115-123
Author(s):  
Sigit Tri Wicaksono ◽  
Hosta Ardhyananta ◽  
Amaliya Rasyida ◽  
Feisha Fadila Rifki
Keyword(s):  
Mechanical Properties ◽  
Compression Strength ◽  
Building Materials ◽  
Construction Material ◽  
Construction Materials ◽  
Physical And Mechanical Properties ◽  
Waste Recycling ◽  
Plastic Waste ◽  
Particulate Composites ◽  
Water Absorbability

Plastic waste is majority an organic material that cannot easily decomposed by bacteria, so it needs to be recycled. One of the utilization of plastic waste recycling is become a mixture in the manufacture of building materials such as concrete, paving block, tiles, roof. This experiment purpose to find out the effect of addition of variation of LDPE and PP thermoplastic binder to physical and mechanical properties of LDPE/PP/Sand composite for construction material application. In this experiment are using many tests, such are SEM, FTIR, compression strength, density, water absorbability, and hardness. the result after the test are the best composition of composite PP/LDPE/sand is 70/0/30 because its have compression strength 14,2 MPa, while density value was 1.30 g/cm3, for the water absorbability is 0.073%, and for the highest hardness is 62.3 hardness of shore D. From the results obtained, composite material can be classified into construction materials for mortar application S type with average compression strength is 12.4 MPa.

High-Density Fiberboard from Wood and Keratin Fibers: Physical and Mechanical Properties

2021 ◽  
Vol 14 ◽  
Author(s):  
Menandro N. Acda
Keyword(s):  
Mechanical Properties ◽  
Construction Materials ◽  
Physical And Mechanical Properties ◽  
High Volume ◽  
High Density ◽  
Wood Fibers ◽  
Solid Waste Disposal ◽  
Renewable Materials ◽  
Polyurethane Resin ◽  
Keratin Fibers

Background: High-density fiberboards (HDF) are widely used as a substitute for solid wood in furniture, cabinet, construction materials, etc. Wood fibers are often used in the production of HDF but the use of renewable materials has gained worldwide interest brought about by global pressure to pursue sustainable development. An abundant source of renewable fibers that can be used to produce HDF is keratin from waste chicken feathers. The goal of the study is to investigate the use of keratin fibers in combination with wood fibers to produce HDF. No or limited studies have been conducted in this area and if successful, it could offer an alternative utilization for the billions of kilograms of waste feather produced by the poultry industry. HDF is a high volume feather utilization that can reduce pollution and help solve solid waste disposal problems in many countries. Methods: A series of dry-formed HDFs containing varying ratios of wood and keratin fibers bonded by polyurethane resin were produced. The physical and mechanical properties of the HDFs were determined. Results : The properties of the HDFs were affected by varying ratios of wood particles and keratin fibers. Dimensional stability as indicated by low levels of thickness swelling (<4.6%) and water absorption (<10%) was observed. Internal bond (2.47 MPa), MOE (5.8 GPa) and MOR (45 MPa) values were higher or comparable to those reported in the literature. Conclusion: HDF formed using a combination of wood and keratin fibers bonded together by polyurethane resin to as much as 50% keratin fibers were dimensionally stable with stiffness and strength above the minimum requirements for general use HDF as prescribed by EN 622-5.

Mechanical Properties of Mortars Prepared by Alkali Activated Fly Ash Coming from Different Production Batches

2015 ◽  
Vol 244 ◽  
pp. 140-145 ◽  
Author(s):  
Matej Špak ◽  
Pavel Raschman
Keyword(s):  
Mechanical Properties ◽  
Fly Ash ◽  
Construction Materials ◽  
Chemical Properties ◽  
Raw Material ◽  
Fly Ashes ◽  
Coal Burning ◽  
Alkali Solutions ◽  
One Year ◽  
Alkali Activated

Fly ash is a well utilizable secondary raw material for the production of alkali activated construction materials. It is a significant alumina-silicates source suitable for the chemical reaction resulting in hardened composites. Physical and chemical properties of fly ashes as a co-product of coal burning mainly depend on characteristics of coal, burning temperature and combustion conditions. High variability of the properties of fly ash causes an uncertainty in the properties of alkali activated mortars. Time behaviour of the composition of the fly ash produced in a heating plant located in Košice, Slovakia as well as leaching behaviour of both alumina and silica from particular batches during one-year period was documented. Leaching tests were carried out using the distilled water and alkali solutions with three different concentrations. Both compressive and tensile strengths of alkali activated mortars were measured, and the correlation between the mechanical properties of hardened mortars and the chemical composition of fly ashes as well as their leaching characteristics was investigated.

The Effect of Lithium Alumina Silicate Phases on Elastic Modulus of Porcelain Tiles

2014 ◽  
Vol 92 ◽  
pp. 188-193 ◽  
Author(s):  
Tuna Aydin ◽  
Alpagut Kara
Keyword(s):  
Mechanical Properties ◽  
Elastic Modulus ◽  
Liquid Phase ◽  
Bulk Density ◽  
Bending Strength ◽  
Physical And Mechanical Properties ◽  
Raw Material ◽  
Closed Porosity ◽  
Low Viscosity ◽  
Porcelain Tiles

Spodumene, which is a lithium alumina silicate, has been used as a raw material in the production of thermal shock resistant whitewares and sanitarywares. The presence of spodumene results in enhancement of mullitization and imparts better physical and mechanical properties to ceramics. In this study, the influence of Lithium alumina silicate phases on the mechanical properties of standard porcelain stoneware body was investigated. Especially solid-solid reactions were observed between spodumene and quartz or spodumene and clay. These solid-solid reactions bring about a newly formed lithium alumina silicate (LAS) phases. Spodumene allows the development of a low viscosity liquid phase and results in a decrease in closed porosity, also with increase in bulk density, bending strength and elastic modulus.

Modeling of Building Materials as Complex Systems

2017 ◽  
Vol 730 ◽  
pp. 412-417 ◽  
Author(s):  
Irina Garkina ◽  
Alexander Danilov ◽  
Yuri Skachkov
Keyword(s):  
Mathematical Modeling ◽  
Complex System ◽  
Differential Equation ◽  
Mechanical Properties ◽  
Time Series ◽  
Building Materials ◽  
Construction Materials ◽  
Physical And Mechanical Properties ◽  
Epoxy Composites ◽  
Damping Properties

We considered the problems of mathematical modeling of composite materials in the example of the development of materials for the protection against ionizing radiation. Construction materials are provided as a complex system with the appropriate attributes. The structure and physico-mechanical properties of the material were determined by the results of the modeling of kinetic processes. Process of forming properties is described by the differential equation in deviations from the equilibrium state (as for dispersion system). It is taken into account the elastic and damping properties of the material. To predict the behavior of the building material and the formation of his private mathematical models are used a representation of the processes as of time series. It is given the algorithm for studies (with considering prehistory) of formation of the basic physical and mechanical properties of epoxy composites for radiation protection. We present an example of the identification of building materials with special properties. Approaches used effectively in the development of materials with special properties.

Sign in / Sign up

Export Citation Format

Share Document