scholarly journals Characterization and Feasibility Studies on Complete Recovery of Rare Earths from Glass Polishing Waste

Metals ◽  
2019 ◽  
Vol 9 (3) ◽  
pp. 278 ◽  
Author(s):  
Chenna Borra ◽  
Thijs Vlugt ◽  
Jeroen Spooren ◽  
Peter Nielsen ◽  
Yongxiang Yang ◽  
...  
Keyword(s):  
Rare Earth ◽  
Rare Earths ◽  
Alkali Treatment ◽  
Thermo Gravimetric Analysis ◽  
Acid Leaching ◽  
Complete Recovery ◽  
Emission Spectrometry ◽  
Gravimetric Analysis ◽  
X Ray ◽  
Glass Polishing

One of the main applications of ceria (CeO2) is its use in glass polishing. About 16,000 tonnes of rare earth oxides, which is about 10% of total rare earth production, are used for polishing applications. The waste generated in glass polishing contains rare earths, along with other impurities. In this study, two different glass polishing waste samples were characterized and two different processes were proposed for the complete recovery of rare earths from polishing waste, i.e., an acid-based process and an alkali-based process. The polishing waste samples were characterized with inductively coupled plasma optical emission spectrometry (ICP-OES), X-ray fluorescence spectroscopy (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM), thermo-gravimetric analysis (TGA) and particle size analysis. Chemical analysis showed that sample A (CeO2-rich waste from plate glass polishing) contained a high amount of impurities compared to sample B (CeO2-rich waste from mirror polishing). XRD analysis showed that sample B contained CeO2, LaO0.65F1.7 and LaPO4 compounds, whereas sample A contained CaCO3 in addition to rare earth compounds. SEM-EDX analysis showed the presence of alumino-silicates in sample A. Leaching experiments were carried out at 75 °C at different acid concentrations for the recovery of rare earths from polishing waste samples. The leaching results showed that it is difficult to dissolve rare earths completely in acid solutions due to the presence of fluorides and phosphates. Hence, undissolved rare earths in the leach residue were further recovered by an alkali treatment with NaOH. In another approach, polishing waste samples were directly treated with NaOH at 500 °C. After alkali treatment followed by water leaching, rare earths can be completely dissolved during acid leaching. Rare earths from polishing waste can be recovered completely by both the acid-based process and the alkali-based process.

scholarly journals Rapid four-component synthesis of dihydropyrano[2,3-c]pyrazoles using nano-eggshell/Ti(IV) as a highly compatible natural based catalyst

BMC Chemistry ◽  
2021 ◽  
Vol 15 (1) ◽  
Author(s):  
Arefeh Dehghani Tafti ◽  
Bi Bi Fatemeh Mirjalili ◽  
Abdolhamid Bamoniri ◽  
Naeimeh Salehi
Keyword(s):  
Thermo Gravimetric Analysis ◽  
Reaction Times ◽  
Diffraction Field ◽  
Gravimetric Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Solvent Free Conditions ◽  
High Yields ◽  
Work Up

AbstractNano-eggshell/Ti(IV) as a novel naturally based catalyst was prepared, characterized and applied for the synthesis of dihydropyrano[2,3-c]pyrazole derivatives. The characterization of nano-eggshell/Ti(IV) was performed using Fourier Transform Infrared spectroscopy, X-ray Diffraction, Field Emission Scanning Electron Microscopy, Energy-Dispersive X-ray Spectroscopy, and Thermo Gravimetric Analysis. Dihydropyrano[2,3-c]pyrazoles were synthesized in the presence of nano-eggshell/Ti(IV) via a four component reaction of aldehydes, ethyl acetoacetate, malononitrile and hydrazine hydrate at room temperature under solvent free conditions. The principal affairs of this procedure are mild condition, short reaction times, easy work-up, high yields, reusability of the catalyst and the absence of toxic organic solvents.

scholarly journals Enhanced Photocatalytic Activity of Cu2O Cabbage/RGO Nanocomposites under Visible Light Irradiation

Polymers ◽  
2021 ◽  
Vol 13 (11) ◽  
pp. 1712
Author(s):  
Appusamy Muthukrishnaraj ◽  
Salma Ahmed Al-Zahrani ◽  
Ahmed Al Otaibi ◽  
Semmedu Selvaraj Kalaivani ◽  
Ayyar Manikandan ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Thermo Gravimetric Analysis ◽  
Visible Region ◽  
Catalytic Performance ◽  
Precipitation Method ◽  
Gravimetric Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Dye Pollutants ◽  
Transmission Electron

Towards the utilization of Cu2O nanomaterial for the degradation of industrial dye pollutants such as methylene blue and methyl orange, the graphene-incorporated Cu2O nanocomposites (GCC) were developed via a precipitation method. Using Hummers method, the grapheme oxide (GO) was initially synthesized. The varying weight percentages (1–4 wt %) of GO was incorporated along with the precipitation of Cu2O catalyst. Various characterization techniques such as Fourier-transform infra-red (FT-IR), X-ray diffraction (XRD), UV–visible diffused reflectance (UV-DRS), Raman spectroscopy, thermo gravimetric analysis (TGA), energy-dispersive X-ray analysis (EDX), and electro chemical impedance (EIS) were followed for characterization. The cabbage-like morphology of the developed Cu2O and its composites were ascertained from field-emission scanning electron microscopy (FESEM) and high-resolution transmission electron microscopy (HR-TEM). In addition, the growth mechanism was also proposed. The results infer that 2 wt % GO-incorporated Cu2O composites shows the highest value of degradation efficiency (97.9% and 96.1%) for MB and MO at 160 and 220 min, respectively. Further, its catalytic performance over visible region (red shift) was also enhanced to an appreciable extent, when compared with that of other samples.

Effect of Synthesis Temperature on Particles Size and Morphology of Zirconium Oxide Nanoparticle

2017 ◽  
Vol 50 ◽  
pp. 18-31 ◽  
Author(s):  
Rudzani Sigwadi ◽  
Simon Dhlamini ◽  
Touhami Mokrani ◽  
Patrick Nonjola
Keyword(s):  
Electron Microscopy ◽  
Particle Size ◽  
Zirconium Oxide ◽  
Thermo Gravimetric Analysis ◽  
Gravimetric Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Crystallite Sizes ◽  
Ft Ir

The paper presents the synthesis and investigation of zirconium oxide (ZrO2) nanoparticles that were synthesised by precipitation method with the effects of the temperatures of reaction on the particles size, morphology, crystallite sizes and stability at high temperature. The reaction temperature effect on the particle size, morphology, crystallite sizes and stabilized a higher temperature (tetragonal and cubic) phases was studied. Thermal decomposition, band structure and functional groups were analyzed by Brunauer-Emmett-Teller (BET), Scanning Electron Microscopy (SEM), Transmission electron microscopy (TEM), X-ray diffraction (XRD), Thermo-gravimetric analysis (TGA) and Fourier transform infrared (FT-IR). The crystal structure was determined using X-ray diffraction. The morphology and the particle size were studied using (SEM) and (TEM). The shaped particles were confirmed through the SEM analysis. The transmission electron microscopic analysis confirmed the formation of the nanoparticles with the particle size. The FT-IR spectra showed the strong presence of ZrO2 nanoparticles.

Investigations on Cu2+-substituted Ni–Zn ferrite nanoparticles

2016 ◽  
Vol 30 (32n33) ◽  
pp. 1650347
Author(s):  
Amarjeet ◽  
Vinod Kumar
Keyword(s):  
Spinel Phase ◽  
Thermo Gravimetric Analysis ◽  
Peak Position ◽  
Precipitation Method ◽  
Gravimetric Analysis ◽  
Frequency Range ◽  
X Ray Diffraction ◽  
Absorption Bands ◽  
X Ray ◽  
Zn Ferrite

[Formula: see text] ([Formula: see text] = 0.1, 0.3 and 0.5) nanoparticles were prepared by chemical co-precipitation method. The developed nanoparticles were characterized for structural properties by powder X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) techniques. Peak position in the X-ray diffraction pattern confirmed the single spinel phase of the developed particles. Infrared (IR) spectroscopy in mid-IR range showed the presence of characteristic absorption bands corresponding to octahedral and tetrahedral bonds in the spinel structure of prepared samples. Thermo-gravimetric analysis (TGA) measurements showed a considerable weight loss in the developed samples above 700[Formula: see text]C. Frequency dependence of the electrical properties of the developed material pellets was studied in the frequency range of 1 kHz–5 MHz. Temperature dependence of the dielectric constant of [Formula: see text] was studied at different temperatures, i.e. at 425, 450 and 475 K, in the frequency range of 1 kHz–5 MHz. It was found that the electrical conductivity decreases with increasing Cu[Formula: see text] ion content while it increases with the increase in temperature.

Comparing the Physico-Chemical Characteristics of Formulated and Marketed Yashada Bhasma

2021 ◽  
pp. 6392-6398
Author(s):  
Nitu Bhatnagar ◽  
Avani Pareek
Keyword(s):  
Inductively Coupled Plasma ◽  
Thermo Gravimetric Analysis ◽  
Human Consumption ◽  
Chemical Characteristics ◽  
Gravimetric Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Inductively Coupled ◽  
Physico Chemical ◽  
The Difference

The present study is aimed to observe the difference in the Physico-Chemical characteristics of the marketed and formulated bhasma samples through X-Ray Diffraction analysis (XRD), Dynamic Light Scattering (DLS), Zeta potential, Thermo-Gravimetric analysis (TGA), Scanning Electron Microscopy (SEM) and Energy Dispersive X-Ray analysis (EDAX), apart from organoleptic methods. Inductively Coupled Plasma Mass Spectroscopy (ICPMS) analysis was also done to observe the presence of trace and heavy metals so that the safety of all these samples could be ensured. XRD shows variation in oxide nature of zinc as well crystallite size in all bhasma samples. DLS and SEM results show difference in particle size of marketed bhasma samples as compared to formulated Yashada bhasma. EDAX and ICPMS also confirm the alteration in elemental composition of all these bhasma samples. Thus, it can be concluded that these ayurvedic medicines should be prepared strictly using the formulation methods as mentioned in the Ayurvedic texts. This will help the prepared products to adopt the inherent quality of the ancient system of medicine, which shall be useful and devoid of any side effects for human consumption.

scholarly journals Hydrothermal Synthesis of Rare-Earth Modified Titania: Influence on Phase Composition, Optical Properties, and Photocatalytic Activity

Materials ◽  
2019 ◽  
Vol 12 (5) ◽  
pp. 713 ◽  
Author(s):  
Nejc Rozman ◽  
David Tobaldi ◽  
Uroš Cvelbar ◽  
Harinarayanan Puliyalil ◽  
João Labrincha ◽  
...  
Keyword(s):  
Optical Properties ◽  
Photocatalytic Activity ◽  
Rare Earth ◽  
Hydrothermal Synthesis ◽  
Rare Earth Elements ◽  
Rare Earths ◽  
Light Absorption ◽  
Pure Tio2 ◽  
X Ray ◽  
Hydroxyl Oxygen

In order to expand the use of titania indoor as well as to increase its overall performance, narrowing the band gap is one of the possibilities to achieve this. Modifying with rare earths (REs) has been relatively unexplored, especially the modification of rutile with rare earth cations. The aim of this study was to find the influence of the modification of TiO2 with rare earths on its structural, optical, morphological, and photocatalytic properties. Titania was synthesized using TiOSO4 as the source of titanium via hydrothermal synthesis procedure at low temperature (200 °C) and modified with selected rare earth elements, namely, Ce, La, and Gd. Structural properties of samples were determined by X-ray powder diffraction (XRD), and the phase ratio was calculated using the Rietveld method. Optical properties were analyzed by ultraviolet and visible light (UV-Vis) spectroscopy. Field emission scanning electron microscope (FE-SEM) was used to determine the morphological properties of samples and to estimate the size of primary crystals. X-ray photoelectron spectroscopy (XPS) was used to determine the chemical bonding properties of samples. Photocatalytic activity of the prepared photocatalysts as well as the titania available on the market (P25) was measured in three different setups, assessing volatile organic compound (VOC) degradation, NOx abatement, and water purification. It was found out that modification with rare earth elements slows down the transformation of anatase and brookite to rutile. Whereas the unmodified sample was composed of only rutile, La- and Gd-modified samples contained anatase and rutile, and Ce-modified samples consisted of anatase, brookite, and rutile. Modification with rare earth metals has turned out to be detrimental to photocatalytic activity. In all cases, pure TiO2 outperformed the modified samples. Cerium-modified TiO2 was the least active sample, despite having a light absorption tail up to 585 nm wavelength. La- and Gd-modified samples did not show a significant shift in light absorption when compared to the pure TiO2 sample. The reason for the lower activity of modified samples was attributed to a greater Ti3+/Ti4+ ratio and a large amount of hydroxyl oxygen found in pure TiO2. All the modified samples had a smaller Ti3+/Ti4+ ratio and less hydroxyl oxygen.

scholarly journals Synthesis of calcium-phosphate and chitosan bioceramics for bone regeneration

2001 ◽  
Vol 73 (4) ◽  
pp. 525-532 ◽  
Author(s):  
MELLATIE R. FINISIE ◽  
ATCHE JOSUÉ ◽  
VALFREDO T. FÁVERE ◽  
MAURO C. M. LARANJEIRA
Keyword(s):  
Bone Regeneration ◽  
Solid Phase ◽  
Thermo Gravimetric Analysis ◽  
Analytical Techniques ◽  
Bone Substitutes ◽  
Gravimetric Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Beneficial Effects ◽  
Fourier Transformed Infrared Spectroscopy

Bioceramic composites were obtained from chitosan and hydroxyapatite pastes synthesized at physiological temperature according to two different syntheses approaches. Usual analytical techniques (X-ray diffraction analysis, Fourier transformed infrared spectroscopy, Thermo gravimetric analysis, Scanning electron microscopy, X-ray dispersive energy analysis and Porosimetry) were employed to characterize the resulting material. The aim of this investigation was to study the bioceramic properties of the pastes with non-decaying behavior from chitosan-hydroxyapatite composites. Chitosan, which also forms a water-insoluble gel in the presence of calcium ions, and has been reported to have pharmacologically beneficial effects on osteoconductivity, was added to the solid phase of the hydroxyapatite powder. The properties exhibited by the chitosan-hydroxyapatite composites were characteristic of bioceramics applied as bone substitutes. Hydroxyapatite contents ranging from 85 to 98% (w/w) resulted in suitable bioceramic composites for bone regeneration, since they showed a non-decaying behavior, good mechanical properties and suitable pore sizes.

Effect of Alkali and Silane Treatment on the Thermal Stability of Hemp Fibers as Reinforcement in Composite Structures

2011 ◽  
Vol 415-417 ◽  
pp. 666-670 ◽  
Author(s):  
Na Lu ◽  
Shubhashini Oza ◽  
Ian Ferguson
Keyword(s):  
Thermal Stability ◽  
Composite Structures ◽  
Natural Fiber ◽  
Alkali Treatment ◽  
Thermo Gravimetric Analysis ◽  
Natural Fibers ◽  
Gravimetric Analysis ◽  
Silane Treatment ◽  
Hemp Fibers ◽  
Thermal Stability Of

Natural fiber reinforced composites are being used as reinforcement material in composite system due to their positive environmental benefits. Added to that, natural fibers offer advantages such as low density, low cost, good toughness, high specific strength, relatively non-abrasive and wide availability. However, the low thermal stability of natural fibers is one of the major challenges to increase their use as reinforcing component. In this study, a thorough investigation has been done to compare the effect of two chemical treatment methods on the thermal stability of hemp fibers. 5wt% sodium hydroxide and 5wt% triethoxyvinylsilane was used for the treatment of hemp fibers. Fourier transform infrared spectroscopy, scanning electron microscopy and thermo gravimetric analysis were used for characterization of untreated and treated fiber. The results indicated that 24 hours alkali treatment and 3 hours silane treatment time enhanced the thermal stability of the hemp fiber. However, alkali treatment shows better improvement compared to silane treatment.

The Influence of Calcination Temperature on Quantitative Phase of Hematite from Iron Stone Tanah Laut

2015 ◽  
Vol 1112 ◽  
pp. 489-492
Author(s):  
Ali Mufid ◽  
M. Zainuri
Keyword(s):  
Particle Size ◽  
Calcination Temperature ◽  
Thermo Gravimetric Analysis ◽  
Precipitation Method ◽  
Gravimetric Analysis ◽  
X Ray Diffraction ◽  
Scanning Calorimetry ◽  
X Ray ◽  
Particle Size Analyzer ◽  
Co Precipitation

This research aims to form particles of hematite (α-Fe2O3) with a basis of mineral iron ore Fe3O4 from Tanah Laut. Magnetite Fe3O4 was synthesized using co-precipitation method. Further characterization using X-ray fluorescence (XRF) to obtain the percentage of the elements, obtained an iron content of 98.51%. Then characterized using thermo-gravimetric analysis and differential scanning calorimetry (TGA-DSC) to determine the calcination temperature, that at a temperature of 445 °C mass decreased by 0.369% due to increase in temperature. Further Characterization of X-ray diffraction (XRD) to determine the phases formed at the calcination temperature variation of 400 °C, 445 °C, 500 °C and 600 °C with a holding time of 5 hours to form a single phase α-Fe2O3 hematite. Testing with a particle size analyzer (PSA) to determine the particle size distribution, where test results indicate that the α-Fe2O3 phase of each having a particle size of 269.7 nm, 332.2 nm, 357.9 nm, 412.2 nm. The best quantity is shown at a temperature of 500 °C to form the hematite phase. This result is used as the calcination procedure to obtain a source of Fe ions in the manufacture of Lithium Ferro Phosphate.

Physical and Thermal Properties of Chitosan

2014 ◽  
Vol 979 ◽  
pp. 315-318 ◽  
Author(s):  
W. Siriprom ◽  
K. Chantarasunthon ◽  
K. Teanchai
Keyword(s):  
Physical Properties ◽  
Thermo Gravimetric Analysis ◽  
Raw Material ◽  
Hydroxyl Groups ◽  
Gravimetric Analysis ◽  
Biodegradable Films ◽  
X Ray Diffraction ◽  
Xrd Pattern ◽  
X Ray ◽  
Good Agreement

This work aims at characterizing the thermal and physical properties of chitosan. The samples were evaluated for potentiality to use as raw material for biodegradable films raw material. Their thermal and physical properties have been also discussed in detail which Fourier Transform Infrared Spectroscopy (FTIR), Thermo-Gravimetric Analysis (TGA), Energy Dispersive X-Ray Fluorescence (EDXRF) and X-Ray Diffraction (XRD), respectively. The result of the XRD pattern indicated the sample has amorphous-crystalline structure and FTIR results confirmed the formation of intermolecular hydrogen bonding between the amino and hydroxyl groups of the sample. In good agreement between the EDXRF and TGA results, noticed that the removal of moisture and volatile material.

Sign in / Sign up

Export Citation Format

Share Document