Effect of Blend Compositions on Mechanical Properties of Irradiated Titanium Dioxide (TiO2)/Polyvinyl Chloride (PVC)/Epoxidized Natural Rubber (ENR) Nanocomposites

2015 ◽  
Vol 1113 ◽  
pp. 43-49 ◽  
Author(s):  
Nur Azrini Ramlee ◽  
Siti Syuhadah Mohammad Hanapiah ◽  
Fatin Nabilah Suhaimi ◽  
Chantara Thevy Ratnam ◽  
Sivanesan Appadu

In this study, effect of blend compositions of irradiated polyvinyl chloride (PVC)/epoxidized natural rubber (ENR) blends was carried out. In previous work, it was reported that the mechanical properties of 50/50 composition irradiated blend had performed the highest strength with addition of 6 wt% of titanium dioxide (TiO2). However, the combination of PVC/ENR in a certain ratio might results in optimal mechanical properties and other specific properties for the new blends formed. Thus, addition of 6 wt% TiO2 and varies compositional range of PVC/ENR ranging from 30, 50 and 70 wt% were prepared by melt-blending technique and the effects on the mechanical properties were investigated. The blends were exposed to 0-150 kGy of electron beam irradiation before being characterized. With addition of 6 wt% TiO2, the characterization of mechanical properties including tensile strength, impact and hardness shows increment in values for all compositions. The increments of tensile strength were fall within 6-18% and as expected 70/30 PVC/ENR blends have shown the highest value. Based on the result, it revealed tensile and impact strengths achieved the optimum value at 100 kGy, while hardness increased as the radiation dose increased. From scanning microscope electron (SEM), micrographs have illustrated the blends with addition of 6 wt% TiO2 are smooth, continuous phase and less void appearance were seen. At higher dose rate, fracture paths were found to be continuous and penetrate deep into the material and this indicates that the failure is essentially brittle and it supports the above findings.

2017 ◽  
Vol 744 ◽  
pp. 282-287
Author(s):  
Sarawut Prasertsri ◽  
Sansanee Srichan

This research aimed to develop the formulation of natural rubber filled with carbon black, silica and calcium carbonate for rubber calf nipple application. The reverse engineering was performed on the calf nipple product to analyze the rubber type and component by using Soxhlet extraction, thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) techniques. Furthermore, mechanical properties were examined to act as benchmark for the rubber compound design. The results showed that rubber component in the nipple product was natural rubber, whereas two filler types revealed as carbon black and calcium carbonate with 10 and 35 of the total weight. In addition, rubber nipple showed the hardness of 46±1 Shore A and tensile strength of 5.3±0.60 MPa. From the investigation of the properties of developed rubber compounds in this work, it was found that the mechanical properties depended on type and content of filler. The required mechanical properties of vulcanizates were achieved at 20 phr of carbon black (N330), 20 phr of silica and 120 phr of calcium carbonate.


2012 ◽  
Vol 602-604 ◽  
pp. 690-695
Author(s):  
Hua Dong Wang ◽  
Rui Wang ◽  
Mao Fang Huang ◽  
Qi Yang

Thermoplastic vulcanizates (TPVs) based on epoxidized natural rubber (ENR) and polypropylene (PP) were prepared in an internal mixer at 180°C. The effects of curing systems (i.e., sulfur and peroxide) on morphological, rheological, thermal and mechanical properties were studied. It is found that the sulfur cured TPVs show higher tensile strength, tear strength and elongation at break than those cured with the DCP systems. The rheological analysis indicates that TPVs cured with DCP system show lower apparent shear viscosity than those with sulfur system. SEM studies show that TPVs vulcanized with DCP system exhibit smaller and finely dispersed rubber domains, which provides it higher thermal stability than sulfur cured TPVs.


2013 ◽  
Vol 747 ◽  
pp. 375-378 ◽  
Author(s):  
Chaiwat Ruksakulpiwat ◽  
Wasaphon Wanasut ◽  
Apikiat Singkum ◽  
Ruksakulpiwat Yupaporn

This research shows a great potential of cogon grass fiber to be used as a reinforcement in epoxidized natural rubber composites. The thermal and mechanical properties of cogon grass fiber-epoxidized natural rubber composites were studied. The chemical treatment of cogon grass fiber to be used as a reinforcing filler was revealed. Effects of fiber treatment method and treatment time of cogon grass fiber on thermal properties of the fibers and their composites were elucidated. The addition of cogon grass fiber into epoxidized natural rubber (ENR) improved the mechanical properties of the composites.The result indicated that alkaline treatment followed by acid treatment of cogon grass fiber led to an increase in thermal decomposition temperature and mechanical properties of the composites more than that without acid treatment. With increasing the amount of fiber, tensile strength of ENR composites were significantly increased while elongation at break was insignificantly changed. ENR with the addition of 4-Amino-6-hydroxy-2-mercaptopyrimidine monohydrate as coupling agent (ENRC) was shown to have higher tensile strength, modulus at 200% elongation and elongation at break than ENR. Improved mechanical properties were also obtained in ENRC composites compared to those of ENR composites.


2014 ◽  
Vol 644-650 ◽  
pp. 4760-4762 ◽  
Author(s):  
Bao Feng Xu ◽  
Sheng Lai ◽  
Zhi Dan Lin ◽  
Jiang Ming Chen ◽  
Jun Lin

Graphene nanoplatelets (GNP) and thermoplastic polyurethane (TPU) have been often used as filler and matrix, respectively, to produce composites. In this work, TPU/GNP composites were prepared via a melt blending method. The mechanical properties and frictional properties of TPU/GNP composites were investigated. Because the GNP is very expensive, we investigated to use graphite as the filler, to use PP-g-MAH as the compatibilizer and examined the characteristics of the prepared composites. Frictional properties and mechanical properties of GNP/TPU composites remarkably improve when adding PP-g-MAH as the compatibilizer. Tensile strength of composite containing 10wt % of GNP and 10wt% PP-g-MAH was measured as 25.5MPa. When the graphite was used to replace for GNP, the frictional properties of composites decreased, but the mechanical properties improved.


2012 ◽  
Vol 576 ◽  
pp. 394-397 ◽  
Author(s):  
Noor Azlina Hassan ◽  
Hassan Norita ◽  
Sahrim Haji Ahmad ◽  
Rozaidi Rasid ◽  
Hazleen Anuar ◽  
...  

Thermoplastic natural rubber (TPNR) nanocomposites were prepared by melt blending method with the optimum mixing parameters (140oC, 100 rpm, 12 min) using internal mixer (Haake 600 P). The aim of this work is to study the effects of organo-montmorillonite (OMMT) on the physical and mechanical properties of TPNR with and without coupling agent (maleic anhydride grafted polyethylene, MA-PE). Significant improvement in tensile strength and modulus of TPNR nanocomposites were obtained with the presence of MA-PE.


2014 ◽  
Vol 983 ◽  
pp. 179-182 ◽  
Author(s):  
Maneewong Chutamas ◽  
Sunthornvarabhas Jackapon ◽  
Joong Kim Hyun ◽  
Sriroth Klanarong

Poly-β-hydroxybutyrate-co-β-hydroxyvalerate (PHBV) is a bacterial-synthesized biopolymer. Moreover, PHBV is a biodegradable, it is an interesting biopolymer for disposable products. PHBV is difficult to process due to its low toughness, an elastic polymer such as natural rubber is introduced to develop toughness. In this experiment, PHBV mechanical properties were improved by blending with natural rubber (NR) and epoxidized natural rubber (ENR). The NR/PHBV and ENR/PHBV blends with the same ratio of 10/90 (wt/wt) could be extruded, whereas other conditions could not. This ratio was then used throughout this study to examine effect of maleic anhydride (MA) and benzoyl peroxide (BPO) to improve toughness of the blends. Result showed at composition where 1.0 % (wt/wt) MA and 0.05 % (wt/wt) BPO was mixed (coding EPMB2), several aspects of mechanical properties were improved. The blend, EPMB2 revealed the highest impact strength, significantly improved of elongation but drastically decreased of tensile strength. Storage modulus slightly decreased, tangent delta significantly increased when compared with neat PHBV.


2015 ◽  
Vol 761 ◽  
pp. 426-430
Author(s):  
Mohd Asyadi Azam ◽  
Aisyah Hassan ◽  
Noraiham Mohamad ◽  
Elyas Talib ◽  
Nor Syafira Abdul Manaf ◽  
...  

Despite the rapid increase in the utilization of reinforced nanomaterials composites, micromaterials may also have the potential to be utilized as filler in polymer composites. In this study, the activated carbon (AC) filled epoxidized natural rubber (ENR) composite was fabricated using the solvent casting method. AC was used as the filler at different filler addition in range from 0 to 7 parts per hundred rubbers (phr). The intention was to investigate the effect of AC filled ENR on mechanical properties and interaction between AC and ENR matrix. Overall, the result shows high improvement in mechanical properties. At 7 phr, the tensile strength was 7.0 MPa compared to 2.6 MPa for 0 phr, which indicates the increase by almost 2 times. The elongation also increases for all phr, which indicates the good filler effect.


2012 ◽  
Vol 581-582 ◽  
pp. 659-662
Author(s):  
Ming Zhao ◽  
Pei Xu ◽  
Ye Chen

A series of calcium silicate/rubber composites with different CaSiO3 contents was prepared. micro-morphology, vulcanizing properties and mechanical properties of CaSiO3/rubber were were characterized. It can be observed that mean particle size of CaSiO3 was 2.627 µm. The micro-morphology of particles were honeycomb structure on the particles of CaSiO3. As compared with NR, the least torque enhanced wtih increasing CaSiO3 content. Curing rate reduced with a rise of CaSiO3 content. The tensile strength and the elongation of composites was increased with increasing CaSiO3 content.


2013 ◽  
Vol 844 ◽  
pp. 255-258 ◽  
Author(s):  
Suradet Matchawet ◽  
Charoen Nakason ◽  
Azizon Kaesaman

Electrical and mechanical properties of epoxidized natural rubber (ENR-25) filled with conductive carbon black (CCB) have been investigated. SEM was used to analyze dispersion of CCB particles in rubber matrix. The results indicated that the AC conductivity increase with increasing volume fraction of carbon black as well as frequency. The percolation thresholds of the electrical conductivity was found at 0.10 volume fraction of CCB. Furthermore, addition of CCB at volume fraction 0.05 caused the highest tensile strength of the composites. The tensile strength and elongation at break were decreased with increasing content of CCB greater than 0.05 volume fraction. However, the volume fraction of CCB at 0.10 demonstrated the most suitable proportion for the ENR composites with superior electrical and mechanical properties.


2018 ◽  
Vol 14 (3) ◽  
pp. 348-352 ◽  
Author(s):  
Nur Amira Sahirah Abdullah ◽  
Zurina Mohamad

Poly (lactic acid)/epoxidized natural rubber (PLA/ENR) was prepared by using counter-rotating twin-screw extruder. For dynamic vulcanization process, ENR was compounded with 3 phr of N, N’-m-phenylenebismaleimide (HVA-2) as a crosslinking agent. The aim of this study is to determine the effect of unvulcanized and dynamically vulcanized of ENR on the properties of PLA/ENR blend. The blending of PLA with ENR was prepared with the various composition of ENR (0 wt% to 30 wt%). The morphology and mechanical properties of the blends were investigated by using scanning electron microscope (SEM), tensile test, and impact test. The unvulcanized blend produced a co-continuous morphology of PLA and ENR and the dynamically vulcanized blend shows the dispersed ENR rubber particles in PLA continuous matrix.  For both systems, the tensile strength value was dropped with the increasing amount of ENR content. The impact strength of both systems shows the maximum value at 20 wt% of ENR content. However, dynamically vulcanized PLA/ENR blend shows a better tensile strength and impact strength value as compared with unvulcanized blend.