Bioactive PMMA-Based Cement Incorporated with Nano-Sized Rutile Particles

2006 ◽  
Vol 309-311 ◽  
pp. 797-800 ◽  
Author(s):  
Masami Hashimoto ◽  
Hiroaki Takadama ◽  
Mineo Mizuno ◽  
Tadashi Kokubo ◽  
Koji Goto ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Simulated Body Fluid ◽  
Mechanical Strength ◽  
Bone Cement ◽  
Body Fluid ◽  
Bone Substitutes ◽  
Hardened Cement ◽  
Pmma Bone Cement

Bioactive bone cement with mechanical properties higher than that of commercial polymethylmethacrylate (PMMA) bone cement are strongly desired to be developed. In the present study, PMMA-based cement incorporated with nano-sized rutile particles was prepared. The PMMA-based cement (rutile content was 50 wt%) shows the compressive strength (136 MPa) higher than that of commercial PMMA bone cement (88 MPa). The hardened cement formed apatite on the surface in a simulated body fluid within 3 days. Therefore, this PMMA-based cement incorporated with rutile particles might be useful as cement for fixation of prostheses as well as self-setting bone substitutes, because of its high apatite forming ability and mechanical strength.

In Vitro Aging Test for Bioactive PMMA-Based Bone Cement Using Simulated Body Fluid

2005 ◽  
Vol 284-286 ◽  
pp. 153-156 ◽  
Author(s):  
S.B. Cho ◽  
Sang Bae Kim ◽  
Keon Joon Cho ◽  
Ill Yong Kim ◽  
Chikara Ohtsuki ◽  
...  
Keyword(s):  
Mechanical Property ◽  
Compressive Strength ◽  
Simulated Body Fluid ◽  
Bone Cement ◽  
Body Fluid ◽  
Sol Gel ◽  
Spherical Shape ◽  
In Vitro Aging ◽  
Living Bone

Novel PMMA-based bone cement using bioactive sol-gel derived CaO-SiO2 powder in order to induce bioactivity as well as to increase its mechanical property. The novel PMMA-based bone cements formed apatite on their surfaces in Simulated Body Fluid(SBF). In the present study, a change in mechanical property of the cement was evaluated using SBF. Before soaking in SBF, its compressive strength showed 80.6±2.1MPa. After soaking in SBF for 2 weeks, 8weeks and 9 weeks, its compressive strength were changed to 83.6±1.6MPa, 87.3±2.4MPa and 85.6±1.8MPa, respectively. It is clear that from the above result, there is no decrease in its compressive strength within 9 weeks soaking in SBF. That it hardly decreases in compressive strength of 7P3S bone cement in SBF is due to the relative small amount of gel powder or its spherical shape and monosize. Therefore, the newly developed PMMA-based cement can bond to the living bone and also be effectively used as bioactive bone cement without decrease in mechanical property.

A Study of Mechanical Properties of Bone Cement Containing Micro- and Nano- Hydroxyapatite Particles

2018 ◽  
Vol 766 ◽  
pp. 117-121
Author(s):  
Phanrawee Sriprapha ◽  
Chaiy Rungsiyakull ◽  
Kamonpan Pengpat ◽  
Tawee Tunkasiri ◽  
Sukum Eitssayeam
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Bone Cement ◽  
Hot Water ◽  
Cylindrical Shape ◽  
Bovine Bone ◽  
Steel Mold ◽  
Micro Particles ◽  
Porosity Reduction ◽  
Pmma Bone Cement

In this research, mechanical properties of bone cement containing micro-and nanohydroxyapatite (HAp) particles were studied. The bone cement was prepared from mixing between polymethyl methacrylate (PMMA) and methyl methacrylate (MMA). Hydroxyapatite powder was prepared from bovine bone. The bone was heated in hot water at 200 oc for the elimination of tissue, after which the bone was dried and calcined at 800 oc for 3 hrs. The calcined bone than was crushed into powder and ball-milled for 24 hrs. The micro-HAp particle was then obtained. The micro particles were then further milled employing the Vibro-milling machine for 2 hrs. The micro-and nanoHAp sizes are about 0.5 μm and 140 nm, respectively. The both size powders were treated with γ-methacrylic-propyl-tri-methoxy silane. The acetic acid was added to control the pH of the solution, until it reached 2.9 before they were mixed into the bone cement with equally wt%. The mixture was casted using the 304 stainless steel mold in order to obtain a cylindrical shape. The low vacuum scanning electron microscope (LV-SEM) and x-ray diffractometer (XRD) were employed to characterize the samples. The porosity of PMMA could be reduced by HAp particle additives. From compressive strength test, it was found that the mixture of bone cement and nanoHAp particle has shown higher compressive strength than pure PMMA bone cement that affected by porosity reduction and force distribution by HAp particles.

scholarly journals Enhancing the mechanical properties and cytocompatibility of magnesium potassium phosphate cement by incorporating oxygen-carboxymethyl chitosan

2020 ◽  
Author(s):  
Changtian Gong ◽  
Shuo Fang ◽  
Kezhou Xia ◽  
Jingteng Chen ◽  
Liangyu Guo ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Physicochemical Properties ◽  
Bone Cement ◽  
Ph Value ◽  
Setting Time ◽  
Potassium Phosphate ◽  
Carboxymethyl Chitosan ◽  
Bioactive Substances ◽  
Magnesium Potassium Phosphate Cement

Abstract Incorporating bioactive substances into synthetic bioceramic scaffolds is challenging. In this work, oxygen-carboxymethyl chitosan (O-CMC), a natural biopolymer that is nontoxic, biodegradable and biocompatible, was introduced into magnesium potassium phosphate cement (K-struvite) to enhance its mechanical properties and cytocompatibility. This study aimed to develop O-CMC/magnesium potassium phosphate composite bone cement (OMPC), thereby combining the optimum bioactivity of O-CMC with the extraordinary self-setting properties and mechanical intensity of the K-struvite. Our results indicated that O-CMC incorporation increased the compressive strength and setting time of K-struvite and decreased its porosity and pH value. Furthermore, OMPC scaffolds remarkably improved the proliferation, adhesion and osteogenesis related differentiation of MC3T3-E1 cells. Therefore, O-CMC introduced suitable physicochemical properties to K-struvite and enhanced its cytocompatibility for use in bone regeneration.

Development of Novel Bioactive PMMA-Based Bone Cement and its In Vitro and In Vivo Evaluation

2006 ◽  
Vol 309-311 ◽  
pp. 801-804 ◽  
Author(s):  
S.B. Cho ◽  
Akari Takeuchi ◽  
Ill Yong Kim ◽  
Sang Bae Kim ◽  
Chikara Ohtsuki ◽  
...  
Keyword(s):  
Mechanical Property ◽  
Compressive Strength ◽  
Bone Cement ◽  
The Novel ◽  
In Vivo Evaluation ◽  
Natural Bone ◽  
Pmma Bone Cement ◽  
Rabbit Tibia

In order to overcome the disadvantage of commercialized PMMA bone cement, we have developed novel PMMA-based bone cement(7P3S) reinforced by 30 wt.% of bioactive CaO-SiO2 gel powders to induce the bioactivity as well as to increase mechanical property for the PMMA bone cement. The novel 7P3S bone cement hardened after mixing for about 7 minutes. For in vitro evaluation, apatite forming ability of it was investigated using SBF. When the novel 7P3S bone cement was soaked into SBF, it formed apatite on its surfaces within 1 week Furthermore; there is no decrease in its compressive strength within 9 weeks soaking in SBF. It is though that hardly decrease in compressive strength of 7P3S bone cement in SBF is due to the relative small amount of gel powder or its spherical shape and monosize. In vivo evaluation of the novel 7P3S bone cement was carried out using rabbit. After implantion into rabbit tibia for several periods, the interface between novel bone cement and natural bone was evaluated by CT images. According to the results, the novel bone cement directly contact to the natural bone without fibrous tissue after implantation for 4 weeks. This results indicates that the newly developed 7P3S bone cement can bond to the living bone and also be effectively used as bioactive bone cement without decrease in mechanical property.

In Vitro and In Vivo Degradation, Mechanical Properties, and Histocompatibility of Weft-Knitted Silk Mesh-Like Grafts

2022 ◽  
Vol 12 (2) ◽  
pp. 411-416
Author(s):  
Liang Tang ◽  
Si-Yu Zhao ◽  
Ya-Dong Yang ◽  
Geng Yang ◽  
Wen-Yuan Zhang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Simulated Body Fluid ◽  
Body Fluid ◽  
Degradation Rate ◽  
Maximum Load ◽  
Artificial Ligament ◽  
In Vivo Degradation

To investigate the degradation, mechanical properties, and histocompatibility of weft-knitted silk mesh-like grafts, we carried out the In Vitro and In Vivo silk grafts degradation assay. The In Vitro degradation experiment was performed by immersing the silk grafts in simulated body fluid for 1 year, and the results showed that the degradation rate of the silk mesh-like grafts was very slow, and there were few changes in the mechanical properties and quality of the silk mesh-like graft. In Vivo degradation assay was taken by implantation of the silk mesh-like grafts into the subcutaneous muscles of rabbits. At 3, 6, and 12 months postoperation, the rate of mass loss was 19.36%, 31.84%, and 58.77%, respectively, and the maximum load was 63.85%, 34.63%, and 10.76%, respectively of that prior to degradation. The results showed that the degradation rate of the silk graft and the loss of mechanical properties In Vivo were faster than the results obtained in the In Vitro experiments. In addition, there were no significant differences in secretion of serum IL-6 and TNF-α between the experimental and normal rabbits (P >0.05), suggesting no obvious inflammatory reaction. The findings suggest that the weft-knitted silk mesh-like grafts have good mechanical properties, histocompatibility, and In Vivo degradation rate, and therefore represent a candidate material for artificial ligament

scholarly journals Effect of Ground Slag on Mechanical Properties of Concrete under Low Temperature

2021 ◽  
Vol 2109 (1) ◽  
pp. 012019
Author(s):  
Xuelian Yuan ◽  
Jie Hu
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Compressive Strength ◽  
Low Temperature ◽  
Cement Paste ◽  
High Volume ◽  
Hardened Cement ◽  
Micro Structure ◽  
Hardened Cement Paste ◽  
Fracture Properties

Abstract Through using cube resisting compression test, fracture properties and micro-structure, the mechanical properties of high volume ground slag concrete under low temperature are studied in this paper. The results show that low temperature can improve the compressive strength of high volume ground slag concrete. And strength increased with the decreased of temperature. Low temperature can also improve the fracture energy and fracture toughness. Not only can ground slag reduce the content of calcium hydroxide in hardened cement paste, but ground slag can improve the compactness of hardened cement paste, reduce porosity and improve the strength of the interface.

Behaviour of Calcium Alkali Orthophosphate Cements under Simulated Implantation Conditions

2008 ◽  
Vol 396-398 ◽  
pp. 213-216 ◽  
Author(s):  
Daniela Jörn ◽  
Renate Gildenhaar ◽  
Georg Berger ◽  
Michael Stiller ◽  
Christine Knabe
Keyword(s):  
Compressive Strength ◽  
Simulated Body Fluid ◽  
Clinical Application ◽  
Body Fluid ◽  
Setting Time ◽  
Great Decrease ◽  
Final Setting Time ◽  
Laboratory Conditions ◽  
Setting Times

The setting behaviour, the compressive strength and the porosity of four calcium alkali orthophosphate cements were examined under laboratory conditions (dry) and under conditions similar to those during clinical application (37°C, contact with body fluid). The results showed an increase of the setting times when specimens were covered with simulated body fluid. Especially, the final setting time (FHZ) was significantly higher for three of the four cements. Furthermore, when specimens were stored in SBF for 16h, an extensive decrease of the compressive strength was noted. The porosity was more than twice as high after 16h in SBF and this may be the cause for the great decrease of the compressive strength.

Biodegradable Bone Cement Using Calcium Phosphate Glass

2006 ◽  
Vol 309-311 ◽  
pp. 861-864 ◽  
Author(s):  
Byung Hyun Lee ◽  
Min Chul Kim ◽  
Kyoung Nam Kim ◽  
Kwang Mahn Kim ◽  
Seong Ho Choi ◽  
...  
Keyword(s):  
Weight Loss ◽  
Compressive Strength ◽  
Calcium Phosphate ◽  
Simulated Body Fluid ◽  
Dissolution Rate ◽  
Phosphate Glass ◽  
Body Fluid ◽  
Setting Time ◽  
Ageing Test ◽  
Dynamic Assay

In preliminary ageing test, the cement using only calcium phosphate glass as power phase cracked with 1 day in simulated body fluid because of high dissolution rate of the cement. We added 30 wt% of either β-TCP or HA to 70 wt% calcium phosphate glass as powder phase to control the dissolution rate of the cement and performed in vitro ageing test in simulated body fluid by dynamic protocol as well as static protocol to confirm the possibility of controlling. Adding either β-TCP or HA to the cement increases the setting time and decreases the compressive strength. In dynamic assay, the pH of extract is maintained over 7. However, pH decreased to around 5 in static assay. Therefore, weight loss by static protocol continuously increased for 14 days, while weight loss by dynamic protocol almost saturated. In XRD patterns of ageing cements, CaO peaks appeared. CaO peak was maximized most lately in dynamic assay of the cement adding HA and within 7 days, the cement adding HA showed higher weight loss. It is indicated that CaO formed in surface of the cement hinder the dissolution of the cement. In addition, compressive strength increased when the CaO peak was maximized.