Effects of Zn and Sn Additions on the Mechanical Properties of Mg-3%Al Alloy

2007 ◽  
Vol 539-543 ◽  
pp. 1775-1779 ◽  
Author(s):  
Jeong Min Kim ◽  
Jae Min Lee ◽  
Joong Hwan Jun ◽  
Ki Tae Kim ◽  
Woon Jae Jung
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Dynamic Recrystallization ◽  
Tensile Test ◽  
Room Temperature ◽  
Al Alloy

A small amount of Zn or Sn was added to Mg-3%Al alloy to improve the formability of alloy. The elongation of as-rolled alloy was increased at both room temperature and 300oC by addition of Sn or Zn, even though the tensile strength at room temperature was remarkably increased only by Zn. When the as-rolled alloy was annealed to be fully recrystallized, the ductility at room temperature was significantly enhanced, however the elongation at 300oC was rather decreased probably attributed to the dynamic recrystallization occurred during the tensile test.

Mechanical Properties and Microstructures of 5052 Al Alloy Processed by Asymmetric Cryorolling

2016 ◽  
Vol 850 ◽  
pp. 823-828 ◽  
Author(s):  
Jin Tao Shi ◽  
Long Gang Hou ◽  
Cun Qiang Ma ◽  
Jin Rong Zuo ◽  
Hua Cui ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Aluminum Alloy ◽  
Grain Refinement ◽  
Cryogenic Temperature ◽  
Room Temperature ◽  
Velocity Ratio ◽  
Experimental Results ◽  
Al Alloy ◽  
Cryogenic Temperatures

Aluminum alloy sheets were asymmetrically rolled at room and cryogenic temperatures by imposing different velocity ratios of 1~1.5 between the upper and bottom rolls. After rolling, the stress-strain curves, microhardness as well as the microstructures of the rolled samples were characterized and analyzed. The experimental results showed that the asymmetric cryorolling could improve the grain refinement and offered (~12%) higher room temperature tensile strength than that processed by symmetrical rolling with velocity ration of 1.0 (~280 MPa). However, at cryogenic temperature, the strength of asymmetrically cryorolling sheet (with velocity ratio of 1.5) was 5.1%, which is less than that processed by symmetrical rolling.

Mechanical Properties of Ultrafine-Grained Al Alloy for Engineering Machinery

2012 ◽  
Vol 629 ◽  
pp. 198-202 ◽  
Author(s):  
Ping Yang ◽  
Kai Huai Yang
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Equal Channel Angular Pressing ◽  
Room Temperature ◽  
Al Alloy ◽  
Fracture Modes ◽  
Annealed State ◽  
Angular Pressing ◽  
Ultrafine Grained

Three groups of commercial 1050 Al alloy were subjected to equal channel angular pressing (ECAP) at room temperature using route A, route C and route Bc, respectively. Mechanical properties and fracture modes of as-annealed and ECAPed samples were investigated. The microhardness of 1050 Al fabricated by ECAP increases by a factor of about 1.5 compared to the as-annealed state. The ultimate tensile strength (UTS) increases significantly after ECAP, while the elongation decreases. But they are strongly dependence on the number of ECAP passes and the pressing route. The UTS and elongation of the samples processed by route Bc are best, consequently, the static toughness U of the samples is enhanced. Besides, all specimens subjected to ECAP deformation failed in a ductile manner.

Mechanical Properties of 5052 Al Alloy Processed by Groove Pressing

2012 ◽  
Vol 468-471 ◽  
pp. 1831-1835
Author(s):  
Kai Huai Yang ◽  
Na Lin ◽  
Shao Feng Zeng ◽  
Wen Zhe Chen
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Fracture Surface ◽  
Surface Morphology ◽  
Fracture Mode ◽  
Room Temperature ◽  
Al Alloy ◽  
Fracture Surface Morphology ◽  
Annealed State

Three groups of commercial 5052 Al alloy sheets were subjected to groove pressing (GP) at room temperature using parallel GP, 180° cross GP and 90° cross GP, respectively. Mechanical properties and fracture modes of as-annealed and GPed samples were investigated. The microhardness of the samples processed by parallel GP increases by a factor of about 1.6 compared to the as-annealed state, and that of the samples processed by cross GP is higher. The ultimate tensile strength (UTS) increases significantly after GP, while the elongation decreases. But they are strongly dependence on the number of GP passes and the pressing modes. Besides, fracture surface morphology demonstrates that the fracture mode is ductile even after four passes. With increasing the number of GP pass, the amount of small dimples increases, and the dimples become shallow and more uniform.

Effects of Zn on Mechanical Properties of MZK60 Wrought Alloy

2007 ◽  
Vol 546-549 ◽  
pp. 391-394
Author(s):  
Ding Fei Zhang ◽  
Li Ping Ren ◽  
Hong Ju Zhang ◽  
Wei Yuang
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Magnesium Alloy ◽  
Yield Strength ◽  
Tensile Test ◽  
Optical Microscopy ◽  
Magnesium Alloys ◽  
Room Temperature ◽  
Zn Addition ◽  
Zn Content

Developing new alloys and techniques is important for the applications of magnesium alloy products. The greatest challenge in the area is to exploit new wrought magnesium alloys[1]. In this paper, the effects of Zn addition on the microstructures and mechanical properties of the MZK60 wrought alloy which is modified from ZK60 have been investigated. The microstructures of these alloys at various states were evaluated by optical microscopy. The mechanical properties at room temperature of these alloys were studied systematically by tensile test. Experimental results indicated that increasing Zn content to 7~10%wt is able to get not only higher tensile strength and yield strength, but also higher elongation.

Aging Behavior of Mg-9Gd-4Y-0.6Mn Alloy

2007 ◽  
Vol 546-549 ◽  
pp. 425-428 ◽  
Author(s):  
Zhen Zhen Deng ◽  
Xin Ming Zhang ◽  
Yun Lai Deng ◽  
Yang Xiao ◽  
Tian Cai Guo
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Tensile Test ◽  
Heat Resistance ◽  
Room Temperature ◽  
Hardness Measurement ◽  
Aging Behavior ◽  
Solution Treated

Microstructures and properties of rolled Mg-9Gd-4Y-0.6Mn（nominal wt%）sheets solution treated at 793K for 12h, and aged at various combinations of temperatures and time were investigated by hardness measurement, tensile test and TEM. The evolution of the precipitates and their effect on the mechanical properties of the pre-, peak-, and over-aged tempers were determined, and the optimal yield tensile strength (YTS) and ultimate tensile strength (UTS) were 276MPa and 287MPa at room temperature, respectively. It has been found that the addition of Mn into Mg-Gd-Y system contributes to block behavior of matrix diffuse and increase potential of heat resistance of the alloy.

Microstructure Evolution and Mechanical Properties of Mg-Gd-Y-Zn-Zr Alloy Deformed by Multi-Directional Forging with Decreasing Temperature

2021 ◽  
Vol 1035 ◽  
pp. 10-16
Author(s):  
Ying Ze Meng ◽  
Jian Min Yu ◽  
Hui Sheng Yu ◽  
Yao Jin Wu ◽  
Zhi Min Zhang
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Yield Strength ◽  
Dynamic Recrystallization ◽  
Room Temperature ◽  
Forging Process ◽  
Texture Intensity ◽  
Coarse Grains ◽  
Room Temperature Increase ◽  
Zr Alloy

The multi-directional forging process can achieve large plastic deformation, and has great application prospects in industrial production. The Mg-9.55Gd-3.28Y-1.77Zn-0.34Zr (wt%) alloy containing LPSO phase was deformed in different passes and then quenched immediately by the multi-directional forging process with decreasing temperature, and the microstructure and mechanical properties of the alloy were analyzed. It is found that as the number of deformation passes increases, the coarse grains decrease, and the dynamic recrystallization fraction increases. The dynamic recrystallization grains swallow the original grains, promote the continuous refinement of the grains, and greatly improve the uniformity of the microstructure. At the same time, the maximum texture intensity of the (0001) basal plane is significantly reduced, and the pole figure distribution is more dispersed, which is attributed to the random orientation of dynamic recrystallization. Due to the refinement of the microstructure and the weakening of the texture, the tensile strength and yield strength at room temperature increase significantly. After 3 passes of deformation, the alloy has the highest mechanical properties, with tensile strength, yield strength, and elongation reaching 317 MPa, 233 MPa, and 15%, respectively.

scholarly journals Microstructural evolution and mechanical properties of LM6 Al alloy

2021 ◽  
Author(s):  
Shashee Kant Soni ◽  
◽  
S. K. Rajput ◽  
Prabhat Kumar Yadav ◽  
Rohit Sahu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Optical Microscopy ◽  
Axial Compression ◽  
Microstructural Evolution ◽  
Room Temperature ◽  
Al Alloy ◽  
Light Optical Microscopy ◽  
Hardness Tests

In this paper, multi-axial compression of LM6 Al alloy were performed at room temperature using strain of 0.2 in each pass. Total cumulative strains 0.6, 1.2 and 1.8, were applied in three, six and nine passes, respectively. Microstructural evolution is studied using light optical microscopy of the compressed specimen. Properties (tensile strength, hardness, toughness) of deformed specimens were studied using tensile and hardness tests, and relate them with their microstructures and fractographs. As passes increased from zero to nine, 62% of tensile strength of the material is increased along with hardness from 52 VHN to 74VHN.

scholarly journals Effects of Substitution of Y with Yb and Ce on the Microstructures and Mechanical Properties of Mg88.5Zn5Y6.5

Metals ◽  
2020 ◽  
Vol 11 (1) ◽  
pp. 31
Author(s):  
Hongxin Liao ◽  
Taekyung Lee ◽  
Jiangfeng Song ◽  
Jonghyun Kim ◽  
Fusheng Pan
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
Creep Resistance ◽  
Room Temperature ◽  
High Thermal Stability ◽  
Long Period ◽  
Microstructures And Mechanical Properties

The microstructures and mechanical properties of the Mg88.5Zn5Y6.5-XREX (RE = Yb and Ce, X = 0, 1.5, 3.0, and 4.5) (wt.%) alloys were investigated in the present study. Mg88.5Zn5Y6.5 is composed of three phases, namely, α-Mg, long-period stacking ordered (LPSO) phases, and intermetallic compounds. The content of the LPSO phases decreased with the addition of Ce and Yb, and no LPSO phases were detected in Mg88.5Zn5Y2.0Yb4.5. The alloys containing the LPSO phases possessed a stratified microstructure and exhibited excellent mechanical properties. Mg88.5Zn5Y5.0Ce1.5 exhibited the highest creep resistance and mechanical strength at both room temperature and 200 °C, owing to its suitable microstructure and high thermal stability. The yield strength of Mg88.5Zn5Y5.0Ce1.5 at room temperature was 358 MPa. The ultimate tensile strength of Mg88.5Zn5Y5.0Ce1.5 at room temperature and 200 °C was 453 MPa and 360 MPa, respectively.

Effect of Small Iron, Chromium and Boron Additions as Alloying Elements on Microstructure and Mechanical Properties of Ni3Al

2007 ◽  
Vol 23 ◽  
pp. 123-126
Author(s):  
Radu L. Orban ◽  
Mariana Lucaci
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Room Temperature ◽  
Alloying Elements ◽  
Alloyed Powder ◽  
Mechanically Alloyed ◽  
Powder Mixtures ◽  
B Additions ◽  
Strength And Ductility ◽  
Iron Chromium

This paper investigates the effect of Fe, Cr and B additions, in small proportions, as alloying elements in Ni3Al with the purpose to reduce its intrinsic fragility and extrinsic embrittlement and to enhance, in the same time, its mechanical properties. It represents a development of some previous research works of the authors, proving that Ni3Al-Fe-Cr-B alloys obtained by reactive synthesis (SHS) starting from Mechanically Alloyed powder mixtures have superior both room temperature tensile strength and ductility, and compression ones at temperatures up to 800 °C, than pure Ni3Al. These create premises for their using as superalloys substitutes.

Size Effect on Mechanical Properties of LVL

2014 ◽  
Vol 887-888 ◽  
pp. 824-829
Author(s):  
Qing Fang Lv ◽  
Ji Hong Qin ◽  
Ran Zhu
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Size Effect ◽  
Tensile Test ◽  
Compression Test ◽  
Test Results ◽  
Laminated Veneer Lumber ◽  
Object Of Study ◽  
The Relationship

Laminated veneer lumber is taken as an object of study, and use LVL specimens of different sizes for compression test and tensile test. The goal of the experiment is to investigate the size effect on compressive strength and tensile strength as well as the influence of the secondary glued laminated face, which appears in the secondary molding processes. The results show that both compressive strength and tensile strength have the size effect apparently and the existence of the secondary glued laminated face lower the compressive strength of LVL specimens. Afterwards, the relationship between compressive strength and volume along with tensile strength and area are obtained by the test results.

Sign in / Sign up

Export Citation Format

Share Document