Vapour Grown Carbon Fibre Reinforced Poly(Propylene) Filament

2013 ◽  
Vol 757 ◽  
pp. 151-164
Author(s):  
Arobindo Chatterjee
Keyword(s):  
Thermal Stability ◽  
Thermal Properties ◽  
Dynamic Modulus ◽  
Processing Route ◽  
Mechanical And Thermal Properties ◽  
Carbon Nanofibres ◽  
Carbon Nanofibre ◽  
High Dynamic ◽  
Poly Propylene ◽  
Very High

Polypropylene filament incorporating carbon nanofibre has been spun using conventional fibre processing route. Nanocomposite filament with very high dynamic modulus of 29 GPa and tenacity of 770 MPa could be obtained at 1% loading of nanofibres. The Nanocomposite filament exhibits higher thermal stability. Influence of carbon nanofibres on the morphology, mechanical and thermal properties of the nanocomposite filament have been studied.

Wool powder: An efficient additive to improve mechanical and thermal properties of poly(propylene carbonate)

2017 ◽  
Vol 153 ◽  
pp. 119-127 ◽  
Author(s):  
Haibo Chang ◽  
Qingshuo Li ◽  
Chaojiang Xu ◽  
Runming Li ◽  
Hongxia Wang ◽  
...  
Keyword(s):  
Thermal Properties ◽  
Propylene Carbonate ◽  
Mechanical And Thermal Properties ◽  
Poly Propylene

Morphology, Mechanical and Thermal Properties of Poly(Lactic Acid)/Propylene-Ethylene Copolymer/Cellulose Composites

2019 ◽  
Vol 972 ◽  
pp. 172-177
Author(s):  
Sirirat Wacharawichanant ◽  
Patteera Opasakornwong ◽  
Ratchadakorn Poohoi ◽  
Manop Phankokkruad
Keyword(s):  
Thermal Stability ◽  
Lactic Acid ◽  
Thermal Properties ◽  
Tensile Stress ◽  
Cellulose Fibers ◽  
Phase Morphology ◽  
Poly Lactic Acid ◽  
Mechanical And Thermal Properties ◽  
Ethylene Copolymer ◽  
Thermal Stability Of

This work studied the effects of various types of cellulose fibers on the morphology, mechanical and thermal properties of poly(lactic acid) (PLA)/propylene-ethylene copolymer (PEC) (90/10 w/w) blends. The PLA/PEC blends before and after adding cellulose fibers were prepared by melt blending method in the internal mixer and molded by compression method. The morphological analysis observed that the presence of cellulose in PLA did not change the phase morphology of PLA, and PLA/cellulose composite surfaces were observed the cellulose fibers inserted in PLA matrix and fiber pull-out. The phase morphology of PLA/PEC blends was changed from brittle fracture to ductile fracture behavior and showed the phase separation between PLA and PEC phases. The presence of celluloses did not improve the compatibility between PLA and PEC phases. The tensile stress and strain curves found that the tensile stress of PLA was the highest value. The addition of all celluloses increased Young’s modulus of PLA. The PEC presence increased the tensile strain of PLA over two times when compared with neat PLA and PLA was toughened by PEC. The incorporation of cellulose fibers in PLA/PEC blends could improve Young’s modulus, tensile strength, and stress at break of the blends. The thermal stability showed that the degradation temperatures of all types of cellulose were less than the degradation temperatures of PLA. Thus, the incorporation of cellulose in PLA could not enhance the thermal stability of PLA composites and PLA/PEC composites. The degradation temperature of PEC was the highest value, but it could not improve the thermal stability of PLA. The incorporation of cellulose fibers had no effect on the melting temperature of the PLA blend and composites.

Mechanical and thermal properties of polyoxymethylene-matrix composites filled with multi-walled carbon nanotubes-coated milled glass fiber

2019 ◽  
Vol 54 (15) ◽  
pp. 1961-1976
Author(s):  
Xu Xiangmin ◽  
Hongxiang Zhang ◽  
Tong Beibei ◽  
Li Binjie ◽  
Yudong Zhang
Keyword(s):  
Carbon Nanotubes ◽  
Thermal Stability ◽  
Thermal Properties ◽  
Electron Microscope ◽  
Glass Fiber ◽  
Crystallization Temperature ◽  
High Performance ◽  
Multiwall Carbon Nanotubes ◽  
Fiber Surface ◽  
Mechanical And Thermal Properties

The advanced multifunctional filler has become one of the main challenges in developing high-performance polymer composites. In this study, the acid-treated multiwall carbon nanotubes (MWCNTs) were adhered to the surface of milled glass fiber under the combined effect of 3-aminopropyltriethyloxy silane and tetraethyl orthosilicate to fabricate a hierarchical fiber (MWCNTs-MGF). The morphologies of the hierarchical fibers were characterized using field-emission scanning electron microscope and transmission electron microscope, which showed evidence of a coating layer of MWCNTs on each fiber surface. The MWCNTs-MGF was employed as a multifunctional filler to prepare polyoxymethylene-based composites using a twin-screw extruder by melt blending. The obtained composites exhibited improved mechanical and thermal properties. The composite tensile strength and notched impact strength and Young's modulus increased by 10%, 32%, and 32%, respectively, as the MWCNTs-MGF content varies from 0 to 10 wt.%. Meanwhile, the reinforcing and toughing mechanisms of MWCNTs-MGF were also elaborated by analyzing the interfacial adhesion and fracture morphologies of the composites. Moreover, the study on thermal stability and crystallization behavior indicated that the polyoxymethylene/MWCNTs-MGF composites had higher thermal stability, crystallization temperature, and crystallinity as compared to the polymer matrix. The improvement of thermal stability originates from the unique surface structure of MWCNTs-MGF, while the increase in crystallization temperature and crystallinity is due to the strong heterogeneous nucleation ability of the hierarchical fibers.

Clay modification with silane compounds and characterization of the silicone rubber/clay composites

2012 ◽  
Vol 32 (8-9) ◽  
pp. 493-502 ◽  
Author(s):  
Kyeong Hoon Jang ◽  
Eung-Soo Kim ◽  
Young Ho Jeon ◽  
Jin-San Yoon
Keyword(s):  
Thermal Stability ◽  
Thermal Properties ◽  
Silicone Rubber ◽  
Cross Linking ◽  
Mechanical And Thermal Properties ◽  
Curing Agent ◽  
Thiol Groups ◽  
Rubber Composites ◽  
Clay Modification

Abstract Na+ montmorillonite (MMT) was modified with benzyldimethyltetradecylammonium chloride (B13) and further with (3-mercaptopropyl)triethoxysilane and vinyltrimethoxysilane to prepare B13-MMT, mercaptomethylorthosilicate modified MMT (MTMO), and vinyltrimethoxysilane modified MMT (VTMO), respectively. The pristine and modified clays were compounded with an HTV-type silicone rubber (GP-30®), and the physical properties and morphology of the resulting rubber composites were examined. Both HTV/MTMO and HTV/VTMO exhibited an intercalated/exfoliated coexisting morphology, but the degree of exfoliation of the former composite was higher than that of the latter. Moreover, the thermal stability, as assessed by the onset temperature of thermal degradation, as well as the tensile stress, elongation at the break, and tear strength of HTV/MTMO was higher than those of HTV/B13-MMT and HTV/VTMO. However, the cross-linking density of HTV/MTMO was the lowest among the composites examined because the thiol groups of MTMO extinguished and abstracted the radicals formed by the curing agent. Accordingly, the improved mechanical and thermal properties of HTV/MTMO were attributed to the enhanced interactions between HTV and MTMO due to the chemical reaction between the thiol groups of MTMO and the vinyl groups of HTV.

Dispersion, mechanical and thermal properties of nano graphite platelets reinforced flouroelastomer composites

e-Polymers ◽  
2008 ◽  
Vol 8 (1) ◽  
Author(s):  
Deng Xu ◽  
V. Sridhar ◽  
Thanh Tu Pham ◽  
Jin Kuk Kim
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Tensile Strength ◽  
Thermal Properties ◽  
Thermogravimetric Analysis ◽  
Fracture Surface ◽  
Exfoliated Graphite ◽  
Mechanical And Thermal Properties ◽  
Reinforcing Fillers ◽  
Processing Of Composites

AbstractThe potential of exfoliated graphite nano platelets (xGnP™) as reinforcing fillers in flouroelastomer has been investigated. The dispersion of the nano graphite platelets in the polymer matrix has been investigated by WAXD, SEM, TEM, EPMA and AFM. WAXD studies indicated that the processing of composites did not change the inter-gallery distance (d-spacing) of the graphite platelets. The effect of increasing nano graphite loadings on mechanical properties like tensile strength, modulus and tear resistance has been studied. Formation of weld lines on the fracture surface of the composite has been observed by SEM. The thermal stability was determined using thermogravimetric analysis. The composites showed higher thermal stability in comparison with nonreinforced polymer.

scholarly journals Mechanical and Thermal Properties of Montmorillonite-Reinforced Polypropylene/Rice Husk Hybrid Nanocomposites

Polymers ◽  
2019 ◽  
Vol 11 (10) ◽  
pp. 1557 ◽  
Author(s):  
Khaliq Majeed ◽  
Ashfaq Ahmed ◽  
Muhammad Saifullah Abu Bakar ◽  
Teuku Meurah Indra Mahlia ◽  
Naheed Saba ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Thermal Properties ◽  
Rice Husk ◽  
Hybrid Nanocomposites ◽  
Commercial Application ◽  
Mechanical And Thermal Properties ◽  
Melt Mixing ◽  
Compatibilizing Agent ◽  
Thermal Stability Of

In recent years, there has been considerable interest in the use of natural fibers as potential reinforcing fillers in polymer composites despite their hydrophilicity, which limits their widespread commercial application. The present study explored the fabrication of nanocomposites by melt mixing, using an internal mixer followed by a compression molding technique, and incorporating rice husk (RH) as a renewable natural filler, montmorillonite (MMT) nanoclay as water-resistant reinforcing nanoparticles, and polypropylene-grafted maleic anhydride (PP-g-MAH) as a compatibilizing agent. To correlate the effect of MMT delamination and MMT/RH dispersion in the composites, the mechanical and thermal properties of the composites were studied. XRD analysis revealed delamination of MMT platelets due to an increase in their interlayer spacing, and SEM micrographs indicated improved dispersion of the filler(s) from the use of compatibilizers. The mechanical properties were improved by the incorporation of MMT into the PP/RH system and the reinforcing effect was remarkable as a result of the use of compatibilizing agent. Prolonged water exposure of the prepared samples decreased their tensile and flexural properties. Interestingly, the maximum decrease was observed for PP/RH composites and the minimum was for MMT-reinforced and PP-g-MAH-compatibilized PP/RH composites. DSC results revealed an increase in crystallinity with the addition of filler(s), while the melting and crystallization temperatures remained unaltered. TGA revealed that MMT addition and its delamination in the composite systems improved the thermal stability of the developed nanocomposites. Overall, we conclude that MMT nanoclay is an effective water-resistant reinforcing nanoparticle that enhances the durability, mechanical properties, and thermal stability of composites.

Novel Biobased Materials from Tung Oil-Based Monomer and Tung Oil-Modified Unsaturated Polyester

2012 ◽  
Vol 581-582 ◽  
pp. 121-124
Author(s):  
Cheng Guo Liu ◽  
Yong Hong Zhou ◽  
Li Hong Hu
Keyword(s):  
Thermal Stability ◽  
Thermal Properties ◽  
Thermogravimetric Analysis ◽  
Polymer Matrix ◽  
Unsaturated Polyester ◽  
Mechanical And Thermal Properties ◽  
Tung Oil ◽  
Biobased Materials

Two kinds of novel biobased materials were obtained by copolymerization of tung oil -based monomer (TOPERMA) or tung oil-modified unsaturated polyester (UPE-TO) with styrene. Mechanical and thermal properties of the two TO-based biopolymers were presented and compared. It was shown that the UPE-TO polymer matrix showed better toughness than the pure unsaturated polyester (UPE) matrix, while the TOPERMA polymer matrix had better thermal stability than the UPE-TO and the pure UPE matrixes by thermogravimetric analysis (TGA). These tung oil-based polymers show promise as an alternative to replace petroleum-based materials.

Sign in / Sign up

Export Citation Format

Share Document