Synthesis of High-Purity Fe2TiO5 Powders Utilizing a Local Ironstone

2019 ◽  
Vol 964 ◽  
pp. 50-54 ◽  
Author(s):  
Armayani Armayani ◽  
Irhamsyah Andi ◽  
Pratapa Suminar
Keyword(s):  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
Crystallite Size ◽  
Calcination Temperature ◽  
High Purity ◽  
Ball Mill ◽  
Weight Fraction ◽  
Commercial Product ◽  
X Ray Diffraction ◽  
X Ray

The synthesis of Fe2TiO5 powders has been successfully performed by making use of Fe2O3 and TiO2 powders. The Fe2O3 powder was obtained from local ironstone in Tanah Laut, South Kalimantan, while the TiO2 powder was a commercial product. The Fe2O3 powder was obtained from the local ironstone through coprecipitation method on pH 5, followed by calcination at 800 °C for 1 hour. The synthesis of Fe2TiO5 powder was done by mixing the raw powders using Planetary Ball Mill method for 5 hours. Thermogravimetric dan Differential Thermal Analysis (TG-DTA) was performed to estimate the calcination temperature. The milled mixtures were then calcined at temperatures of 700 – 1100 °C. X-Ray Diffraction (XRD) data showed that Fe2TiO5 formation started at 800 °C with a weight fraction of 3.60 wt%. The XRD data also showed that at 1100 °C the Fe2TiO5 formation has completed. The crystallite size of Fe2TiO5 powders was 50 and 66 nm after calcination at 900 and 1100 °C, respectively.

Synthesis of Nanocrystalline Fe25Al57.5Ni17.5 by Mechanical Alloying

2012 ◽  
Vol 476-478 ◽  
pp. 1318-1321
Author(s):  
Qi Zhi Cao ◽  
Jing Zhang
Keyword(s):  
Thermal Analysis ◽  
Solid Solution ◽  
Differential Thermal Analysis ◽  
Mechanical Alloying ◽  
Ball Mill ◽  
Structural Changes ◽  
Early Stage ◽  
High Energy ◽  
X Ray Diffraction ◽  
X Ray

Nanostructured Fe25Al57.5Ni17.5intermetallics was prepared directly by mechanical alloying (MA) in a high-energy planetary ball-mill. The phase transformations and structural changes occurring in the studied material during mechanical alloying were investigated by X-ray diffraction (XRD). Thermal behavior of the milled powders was examined by differential thermal analysis (DTA). Disordered Al(Fe,Ni) solid solution was formed at the early stage. After 50 h of milling, Al(Fe,Ni) solid solution transformed into Al3Ni2，AlFe3，AlFe0.23Ni0.77 phase. The power annealed at temperature 500 results in forming of intermetallics AlFe3 and FeNi3 after 5h milling. The nanocrystalline intermetallic compound was obtained after 500h milling.

scholarly journals The Effect of Calcination Temperature on the Structure and Performance of Nanocrystalline Mayenite Powders

Materials ◽  
2019 ◽  
Vol 12 (21) ◽  
pp. 3476 ◽  
Author(s):  
Katarzyna Berent ◽  
Sebastian Komarek ◽  
Radosław Lach ◽  
Waldemar Pyda
Keyword(s):  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
Calcination Temperature ◽  
Phase Formation ◽  
Crystalline Phase ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Appreciable Increase ◽  
And Performance

The effect of calcination temperature on the structural properties and phase formation of synthesized CaO-Al2O3 nanopowder was investigated and discussed. The calcination products were identified by differential thermal analysis (DTA) and the crystalline phase formation was analyzed by X-ray diffraction (XRD). The obtained results showed that the crystallization started at 460 °C. Finally, the microstructures of the nanoparticles were observed by scanning (SEM) and transmission electron (TEM) microscopes. The investigation showed that an increase in the calcination temperature led to the appreciable increase in the crystallite size and the crystallinity of the final product. The obtained data confirmed that the prepared materials were mayenite with different surface area in the range of 71.18 m2/g to 10.34 m2/g after annealing in the temperature range of 470 °C to 960 °C.

PENINGKATAN LAJU DISOLUSI ACYCLOVIR DENGAN METODE SISTEM DISPERSI PADAT MENGGUNAKAN POLOXAMER 188

2016 ◽  
Vol 5 (1) ◽  
pp. 6
Author(s):  
Budi Setiawan ◽  
Erizal Zaini ◽  
Salman Umar
Keyword(s):  
Electron Microscopy ◽  
Thermal Analysis ◽  
Scanning Electron Microscopy ◽  
Fourier Transform ◽  
Differential Thermal Analysis ◽  
Fourier Transform Infrared ◽  
X Ray Diffraction ◽  
Poloxamer 188 ◽  
X Ray ◽  
Scanning Electron

Sebuah penelitian tentang sistem dispersi padat dari asiklovir dengan poloxamer 188 telah dilakukan formulasi dengan pencampuran secara fisika dengan rasio 1 : 1, 1 : 3, 1 : 5 dan dispersi padat 1 : 1, 1 : 3, 1 : 5 dan penggilingan 1:1 sebagai pembanding. Dispersi padat dibuat menggunakan metode pencairan (fusi), yang digabung dengan poloxamer 188 pada hotplate kemudian asiklovir dimasukkan ke dalam hasil poloxamer 188 lalu di kocok hingga membentuk masa homogen. Semua formula yang terbentuk termasuk asiklovir poloxamer 188 murni dianalisis karakterisasinya dengan Differential Thermal Analysis (DTA), X-ray Diffraction, Scanning Electron Microscopy (SEM), dan Fourier Transform Infrared (FTIR), kemudian pengambilan dilakukan  (penentuan kadar) mengunakan spektrofotometer UV pada panjang gelombang 257,08 nm dan uji laju disolusi dengan aquadest bebas CO2 menggunakan metode dayung. Hasil pengambilan  (penentuan kadar) menunjukkan bahwa semua formula memenuhi persyaratan farmakope Amerika edisi 30 dan farmakope Indonesia edisi 4 yaitu 95-110%. Sedangkan hasil uji laju disolusi untuk campuran fisik 1: 1, dan dispersi padat 1: 1, dan penggilingan 1: 1 menunjukkan peningkatan yang nyata dibandingkan asiklovir murni. Hal ini juga dapat dilihat dari hasil perhitungan statistik  menggunakan analisis varian satu arah  SPSS 17.

scholarly journals The Potential for Natural Stones from Northeastern Brazil to Be Used in Civil Construction

Minerals ◽  
2021 ◽  
Vol 11 (5) ◽  
pp. 440
Author(s):  
Fabiana Pereira da Costa ◽  
Jucielle Veras Fernandes ◽  
Luiz Ronaldo Lisboa de Melo ◽  
Alisson Mendes Rodrigues ◽  
Romualdo Rodrigues Menezes ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
Chemical Resistance ◽  
Mechanical Analysis ◽  
Northeastern Brazil ◽  
X Ray Diffraction ◽  
X Ray ◽  
Chemical Agents ◽  
Natural Stones

Natural stones (limestones, granites, and marble) from mines located in northeastern Brazil were investigated to discover their potential for use in civil construction. The natural stones were characterized by chemical analysis, X-ray diffraction, differential thermal analysis, and optical microscopy. The physical-mechanical properties (apparent density, porosity, water absorption, compressive and flexural strength, impact, and abrasion) and chemical resistance properties were also evaluated. The results of the physical-mechanical analysis indicated that the natural stones investigated have the potential to be used in different environments (interior, exterior), taking into account factors such as people’s circulation and exposure to chemical agents.

The Roman Ceramics of Salobrena (Granada-Spain) and their Raw Materials

1992 ◽  
Vol 267 ◽  
Author(s):  
Ana M De Andres ◽  
Isabel MuÑOZ
Keyword(s):  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
Raw Materials ◽  
Third Century ◽  
Western Coast ◽  
X Ray Diffraction ◽  
X Ray ◽  
The Third ◽  
Good Number ◽  
Scanning Electron

ABSTRACTNineteen roman ceramic sherds found near Salobreña (Granada, Spain), in the western coast of the Mediterranean Sea, as well as different ceramic clays from the surroundingsare studied. Both clays and ceramic sherds are characterizad by X-ray diffraction and spectrometry, differential thermal analysis, and scanning electron and optical microscopies. A good number of the ceramic pieces, among which some “Terrae Sigillatae”, have a composition similar to that of the local clays and, thus, have been probably manufactured at Salobreña. Only a few of them have a foreign origin. For most of them, the firing temperature was about 800-850 °C, although some have been produced at 900-1000 °C, and some others at 1000-1100 °C. It is concluded that Salobreña appearsto have been an important settlement just in the third century of the Christian era.

scholarly journals Silica-Kaolin Mix Effect on Evaporative Pattern Castings Surface Roughness

2016 ◽  
Vol 16 (3) ◽  
pp. 83-88 ◽  
Author(s):  
B.V. Omidiji ◽  
R.H. Khan ◽  
M.S. Abolarin
Keyword(s):  
Thermal Analysis ◽  
Surface Roughness ◽  
Differential Thermal Analysis ◽  
Ratio Method ◽  
Gating System ◽  
X Ray Diffraction ◽  
Pouring Temperature ◽  
Material Loss ◽  
Refractory Coating ◽  
X Ray

Abstract The influence of the refractory coating which is a mixture of silica flour and kaolin on the surface roughness of the plate castings produced using evaporative patterns had been considered in this work. The kaolin was used as a binder and ratio method was employed to form basis for the factorial design of experiment which led to nine runs of experiments. Methyl alcohol at 99% concentration was used as the carrier for the transfer of the coating to the surface of the patterns. Pouring temperature was observed as a process parameter alongside the mix ratios of the coating. Attempts were made to characterize the refractory coating by using two methods; differential thermal analysis (DTA) and X-ray diffraction. Attempt was also made to characterize the casting material. Gating system design was done for the plate casting to determine the correct proportions of the gating parameters in order to construct the gating system properly to avoid turbulence during pouring of liquid metal. A digital profilometer was used to take the measurements of the surface roughness. It was observed that the mix ratio 90% silica flour-10% kaolin produced the lowest value of the surface roughness of the plate castings and had the lowest material loss in the DTA test. The pouring temperature of 650°C produced best casting.

scholarly journals SOLUBILITY OF GERMANIUM DISELENIDE IN THE Cu3AsSe4

2021 ◽  
Vol 0 (4) ◽  
pp. 67-70
Author(s):  
Z.T. Hasanova ◽  
Keyword(s):  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
Phase Equilibria ◽  
Solid Solutions ◽  
X Ray Diffraction ◽  
X Ray

Differential thermal analysis and powder X-ray diffraction methods were used for phase equilibria studying in the Cu3AsSe4-GeSe2 system. It was established that wide (up to 30 mol.%) solid solutions based on Cu3AsSe4 are formed. GeSe2-rich alloys consist of various heterogeneous mixtures, including phases outside the T–x plane of this section

The (AgInSe2)1-x(VSe)x system (0 ≤x ≤ 0.5): X-ray diffraction and differential thermal analysis measurements

2005 ◽  
Vol 2 (10) ◽  
pp. 3766-3769 ◽  
Author(s):  
S. Durán ◽  
P. Grima ◽  
M. Muñoz ◽  
M. Quintero ◽  
J. Ruiz ◽  
...  
Keyword(s):  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
X Ray Diffraction ◽  
X Ray

Purification of Bentonite Clays from Cubati, PB, Brazil, for Diversified Applications

2014 ◽  
Vol 805 ◽  
pp. 486-491
Author(s):  
J.M.R. Figueirêdo ◽  
Juliana Melo Cartaxo ◽  
I.A. Silva ◽  
C.D. Silva ◽  
Gelmires Araújo Neves ◽  
...  
Keyword(s):  
Thermal Analysis ◽  
Differential Thermal Analysis ◽  
Chemical Analysis ◽  
Laser Diffraction ◽  
The State ◽  
X Ray Diffraction ◽  
X Ray ◽  
Granulometric Analysis ◽  
Bentonite Clays

The State of Paraíba, Brazil, retains about 88.5% of all Brazilian bentonite, and much of this production comes from deposits in the District of Boa Vista, PB. Nevertheless, the deposits are almost depleted. Recently, new deposits were found, which will increases the reserves of the State, in the regions of Cubati and Pedra Lavrada, PB. The objective of this work is to characterize and develop purified clays, through sieving and hydrocycloning techniques, from those recently discovered bentonites for several applications. The characterization of the sample was done through granulometric analysis by laser diffraction, X-ray diffraction, chemical analysis by X-ray fluorescence, and thermogravimetric and differential thermal analysis. The results show that the samples are typical of bentonite clays, and that the purification solely by hydrocyclone presents the best results.

Sign in / Sign up

Export Citation Format

Share Document